CN107502142A - A kind of aluminum alloy pattern plate surface coating and its preparation method and application - Google Patents
A kind of aluminum alloy pattern plate surface coating and its preparation method and application Download PDFInfo
- Publication number
- CN107502142A CN107502142A CN201710848373.8A CN201710848373A CN107502142A CN 107502142 A CN107502142 A CN 107502142A CN 201710848373 A CN201710848373 A CN 201710848373A CN 107502142 A CN107502142 A CN 107502142A
- Authority
- CN
- China
- Prior art keywords
- component
- parts
- aluminum alloy
- plate surface
- surface coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aluminum alloy pattern plate surface coating and its preparation method and application, it is 3 that the aluminum alloy pattern plate surface coating, which includes weight ratio,：1 component A and component B；The component A includes the raw material of following parts by weight：40 60 parts of epoxy resin；40 60 parts of phenolic resin；30 50 parts of polyimide resin；5 10 parts of diluent A；10 20 parts of titanium white；12 parts of levelling agent；The component B includes the raw material of following parts by weight：45 65 parts of curing agent；5 10 parts of accelerator；5 10 parts of diluent B；The preparation method of aluminum alloy pattern plate surface coating includes：(1) component A preparation；(2) component B preparation；(3) component A, component B are well mixed.The aluminum alloy pattern plate surface coating of the present invention can completely cut off concrete and be chemically reacted with aluminium, keep the mechanical strength of aluminium alloy, reduce the loss of metal, substantially increase template utilizes number and the smoothness of metope.
Description
Technical field
The present invention relates to aluminum alloy pattern plate surface-coating technology field, more particularly to a kind of aluminum alloy pattern plate surface coating and its preparation side
Method and application.
Background technology
Aluminum alloy pattern plate, full name are aluminum alloy mould plate system for building.It is a new generation occurred after bamboo and wood template, steel form
New type formwork support system.Aluminum alloy pattern plate is made after special equipment extrudes, by aluminum deck, support and connector three parts system
Uniting, it is whole into various sizes of overall dimensions complexity with complete matching used universal accessories, energy composite assembly to be formed
Body mould bases, assembling, the system template of industrialized construction, solves the defects of conventional conventional template is present, substantially increases and apply
Work efficiency rate.Aluminum template system improves the integral construction efficiency of building trade, is included in Building wood in the application of building trade
Material, it is artificial to arrange all greatly to save a lot.
In recent years, aluminum alloy mould plate substitutes conventional template and has obtained extensive utilization, with component is light, intensity is high, plate width
Face is big, and piece is few, and access times are high, the features such as residual value recovery, has greatly saved cost.But in actual use
Also with some challenges, for wherein aluminum alloy mould plate during being contacted with concrete formation, concrete has extremely strong alkalescence, pH
Up to 12, it can be easy to corrode aluminum alloy material, after several times, the metope of shaping has very serious roughness, have impact on wall
The outward appearance of body, it then becomes necessary to carry out the protection of coating to aluminum alloy surface, isolation concrete chemically reacts with aluminium, protects
The mechanical strength of aluminium alloy is held, reduces the loss of metal, substantially increase template utilizes number and the smoothness of metope.
The content of the invention
Chemically reacted, protected with aluminium with completely cutting off concrete it is an object of the invention to provide a kind of aluminum alloy pattern plate surface coating
The mechanical strength of aluminium alloy is held, reduces the loss of metal, substantially increase template utilizes number and the smoothness of metope.
Another object of the present invention is the preparation method for providing above-mentioned aluminum alloy pattern plate surface coating.
Still a further object of the present invention is the application for providing above-mentioned aluminum alloy pattern plate surface coating.
A kind of aluminum alloy pattern plate surface coating according to embodiments of the present invention, it is 3 that the aluminum alloy pattern plate surface coating, which includes weight ratio,：
1 component A and component B；
The component A includes the raw material of following parts by weight：
The component B includes the raw material of following parts by weight：
Curing agent 45-65 parts；
Accelerator 5-10 parts；
Diluent B 5-10 parts.
On the basis of such scheme, the component A also includes the raw material of following parts by weight：Dipropylene 1-3 parts.
On the basis of such scheme, the component A also includes the raw material of following parts by weight：Dispersant 1-3 parts.
On the basis of such scheme, the diluent A includes aliphatic hydrocarbon, fatty alcohol, organic acid esters, aliphatic ketone, the fat
Fat hydrocarbon, fatty alcohol, organic acid esters, aliphatic ketone weight ratio are 1：0.4：0.6：0.1.
On the basis of such scheme, the diluent B is rosin.
The present invention also provides a kind of preparation method of aluminum alloy pattern plate surface coating, comprises the following steps：
(1) component A preparation：It is according to formula quantity that various measuring raw materials are accurately standby, by epoxy resin, phenolic aldehyde tree
Fat, polyimide resin, diluent A, titanium white mixing are put into dispersion cylinder, are stirred evenly, are ground under 500-700rpm rotating speed
Fineness is less than 55um, adds levelling agent, dipropylene, dispersant, and 10-15 minutes are disperseed under 300-400rpm rotating speeds
To system bubble-free, it is standby to obtain component A；
(2) component B preparation：Curing agent, accelerator, diluent B are added in dispersion cylinder under 100-200rpm rotating speeds
It is well mixed that to obtain component B standby；
(3) component A, component B are well mixed, that is, obtain aluminum alloy pattern plate surface coating.
A kind of described aluminum alloy pattern plate surface coating is preparing the application in building aluminum alloy mould plate.
The present invention has an advantageous effect in that compared with prior art：
1st, epoxy resin chemical-resistant of the present invention is excellent, especially alkali resistance, the isolation effect to concrete
Fruit is good, strong to the paint film adhesion of metal, and phenolic resin, polyimide resin have good acid resistance, mechanical property,
Heat resistance, can effectively improve the weather resistance of aluminum alloy pattern plate surface coating, and levelling agent uses organosilicon levelling agent and acrylic acid stream
Flat agent compatible use, coating is formed a smooth, smooth, uniform film during drying and forming-film, possess slipping and
Scratch resistance, avoid concrete from being chemically reacted with aluminium, keep the mechanical strength of aluminium alloy, reduce the loss of metal.
2nd, in dipropylene simultaneously have alcohol and Mi Liangge functional groups, different phases can be coupled, moreover it is possible to it is numerous hydrophilic
It is miscible with hydrophobic solvent, it is good coalescents, its unique hydrophilic and lipophilic balance enables alcohol ether to improve 20%-30%'s
Film-formation result, there is good synergy with levelling agent.
3rd, be used as dispersant with polyalcohol-more aziridines block copolymer using more interior, its anchoring group one and
Resin Wound is adsorbed, and other end and pigment particles bag are attached, can improve the dispersion effect of pigment 45%~65%, avoid titanium white from disperseing
Uneven generation spot caking phenomenon.
4th, after component A, component B are well mixed aluminum alloy pattern plate surface coating could be used as to use, and needs to use in 8 hours
It is complete, therefore component A, component B can separate packaging and preserve, and matched on demand according to dosage is estimated, extend and preserve the life-span, avoid producing wave
Take.
5th, aluminum alloy pattern plate surface coating of the invention isolation concrete and aluminium chemically react, and keep the machinery of aluminium alloy strong
Degree, reduce the loss of metal, substantially increase template using number and the smoothness of metope, effectively reduce cost.
Embodiment
For feature, technological means and the concrete function reached of the present invention can be further appreciated that, below with specific implementation
Mode is described in further detail to the present invention.
The dipropylene once used in embodiment is Tao Shi DOW productions, and levelling agent is the energy chemical industry that rubs
The SE-493 acrylic acid levelling agent compatibilities of your chemical industry of MONENG-1081 organosilicon levelling agents and Guangzhou gentry, curing agent is Ba Ling stones
Change T-31, accelerator is the DMP-30 of auspicious safe chemical industry.
Embodiment 1
A kind of aluminum alloy pattern plate surface coating is present embodiments provided, including weight ratio is 3：1 component A and component B；
The component A includes the raw material of following parts by weight：40 parts of epoxy resin；40 parts of phenolic resin；Polyimide resin
30 parts；5 parts of diluent A；10 parts of titanium white；1 part of levelling agent；1 part of dipropylene；1 part of dispersant.
The component B includes the raw material of following parts by weight：45 parts of curing agent；5 parts of accelerator；5 parts of diluent B.
Wherein, diluent A includes aliphatic hydrocarbon, fatty alcohol, organic acid esters, aliphatic ketone, the aliphatic hydrocarbon, fatty alcohol, organic
Acid esters, aliphatic ketone weight ratio are 1：0.4：0.6：0.1；Diluent B is rosin.
Aluminum alloy pattern plate surface coating is prepared as steps described below：
(1) component A preparation：It is according to formula quantity that various measuring raw materials are accurately standby, by epoxy resin, phenolic aldehyde tree
Fat, polyimide resin, diluent A, titanium white mixing are put into dispersion cylinder, are stirred evenly under 500rpm rotating speed, are ground to fineness
Less than 55um, levelling agent, dipropylene, dispersant are added, 10 minutes are disperseed under 300rpm rotating speeds to system without gas
Bubble, it is standby to obtain component A；
(2) component B preparation：It will be mixed in curing agent, accelerator, diluent B addition dispersion cylinders under 100rpm rotating speeds
It is standby uniformly to obtain component B；
(3) component A, component B are well mixed, that is, obtain aluminum alloy pattern plate surface coating.
Embodiment 2
A kind of aluminum alloy pattern plate surface coating is present embodiments provided, including weight ratio is 3：1 component A and component B；
The component A includes the raw material of following parts by weight：45 parts of epoxy resin；45 parts of phenolic resin；Polyimide resin
35 parts；6 parts of diluent A；12 parts of titanium white；1.2 parts of levelling agent；1.5 parts of dipropylene；1.5 parts of dispersant.
The component B includes the raw material of following parts by weight：50 parts of curing agent；6 parts of accelerator；6 parts of diluent B.
Wherein, diluent A includes aliphatic hydrocarbon, fatty alcohol, organic acid esters, aliphatic ketone, the aliphatic hydrocarbon, fatty alcohol, organic
Acid esters, aliphatic ketone weight ratio are 1：0.4：0.6：0.1；Diluent B is rosin.
Aluminum alloy pattern plate surface coating is prepared as steps described below：
(1) component A preparation：It is according to formula quantity that various measuring raw materials are accurately standby, by epoxy resin, phenolic aldehyde tree
Fat, polyimide resin, diluent A, titanium white mixing are put into dispersion cylinder, are stirred evenly under 550rpm rotating speed, are ground to fineness
Less than 55um, levelling agent, dipropylene, dispersant are added, 12 minutes are disperseed under 320rpm rotating speeds to system without gas
Bubble, it is standby to obtain component A；
(2) component B preparation：It will be mixed in curing agent, accelerator, diluent B addition dispersion cylinders under 120rpm rotating speeds
It is standby uniformly to obtain component B；
(3) component A, component B are well mixed, that is, obtain aluminum alloy pattern plate surface coating.
Embodiment 3
A kind of aluminum alloy pattern plate surface coating is present embodiments provided, including weight ratio is 3：1 component A and component B；
The component A includes the raw material of following parts by weight：50 parts of epoxy resin；50 parts of phenolic resin；Polyimide resin
40 parts；8 parts of diluent A；15 parts of titanium white；1.5 parts of levelling agent；2 parts of dipropylene；2 parts of dispersant.
The component B includes the raw material of following parts by weight：55 parts of curing agent；8 parts of accelerator；8 parts of diluent B.
Wherein, diluent A includes aliphatic hydrocarbon, fatty alcohol, organic acid esters, aliphatic ketone, the aliphatic hydrocarbon, fatty alcohol, organic
Acid esters, aliphatic ketone weight ratio are 1：0.4：0.6：0.1；Diluent B is rosin.
Aluminum alloy pattern plate surface coating is prepared as steps described below：
(1) component A preparation：It is according to formula quantity that various measuring raw materials are accurately standby, by epoxy resin, phenolic aldehyde tree
Fat, polyimide resin, diluent A, titanium white mixing are put into dispersion cylinder, are stirred evenly under 600rpm rotating speed, are ground to fineness
Less than 55um, levelling agent, dipropylene, dispersant are added, 13 minutes are disperseed under 350rpm rotating speeds to system without gas
Bubble, it is standby to obtain component A；
(2) component B preparation：It will be mixed in curing agent, accelerator, diluent B addition dispersion cylinders under 150rpm rotating speeds
It is standby uniformly to obtain component B；
(3) component A, component B are well mixed, that is, obtain aluminum alloy pattern plate surface coating.
Embodiment 4
A kind of aluminum alloy pattern plate surface coating is present embodiments provided, including weight ratio is 3：1 component A and component B；
The component A includes the raw material of following parts by weight：55 parts of epoxy resin；55 parts of phenolic resin；Polyimide resin
45 parts；9 parts of diluent A；18 parts of titanium white；1.8 parts of levelling agent；2.5 parts of dipropylene；2.5 parts of dispersant.
The component B includes the raw material of following parts by weight：60 parts of curing agent；9 parts of accelerator；9 parts of diluent B.
Wherein, diluent A includes aliphatic hydrocarbon, fatty alcohol, organic acid esters, aliphatic ketone, the aliphatic hydrocarbon, fatty alcohol, organic
Acid esters, aliphatic ketone weight ratio are 1：0.4：0.6：0.1；Diluent B is rosin.
Aluminum alloy pattern plate surface coating is prepared as steps described below：
(1) component A preparation：It is according to formula quantity that various measuring raw materials are accurately standby, by epoxy resin, phenolic aldehyde tree
Fat, polyimide resin, diluent A, titanium white mixing are put into dispersion cylinder, are stirred evenly under 650rpm rotating speed, are ground to fineness
Less than 55um, levelling agent, dipropylene, dispersant are added, 14 minutes are disperseed under 380rpm rotating speeds to system without gas
Bubble, it is standby to obtain component A；
(2) component B preparation：It will be mixed in curing agent, accelerator, diluent B addition dispersion cylinders under 180rpm rotating speeds
It is standby uniformly to obtain component B；
(3) component A, component B are well mixed, that is, obtain aluminum alloy pattern plate surface coating.
Embodiment 5
A kind of aluminum alloy pattern plate surface coating is present embodiments provided, including weight ratio is 3：1 component A and component B；
The component A includes the raw material of following parts by weight：60 parts of epoxy resin；60 parts of phenolic resin；Polyimide resin
50 parts；10 parts of diluent A；20 parts of titanium white；2 parts of levelling agent；3 parts of dipropylene；3 parts of dispersant.
The component B includes the raw material of following parts by weight：65 parts of curing agent；10 parts of accelerator；Diluent B10 parts.
Wherein, diluent A includes aliphatic hydrocarbon, fatty alcohol, organic acid esters, aliphatic ketone, the aliphatic hydrocarbon, fatty alcohol, organic
Acid esters, aliphatic ketone weight ratio are 1：0.4：0.6：0.1；Diluent B is rosin.
Aluminum alloy pattern plate surface coating is prepared as steps described below：
(1) component A preparation：It is according to formula quantity that various measuring raw materials are accurately standby, by epoxy resin, phenolic aldehyde tree
Fat, polyimide resin, diluent A, titanium white mixing are put into dispersion cylinder, are stirred evenly under 700rpm rotating speed, are ground to fineness
Less than 55um, levelling agent, dipropylene, dispersant are added, 15 minutes are disperseed under 400rpm rotating speeds to system without gas
Bubble, it is standby to obtain component A；
(2) component B preparation：It will be mixed in curing agent, accelerator, diluent B addition dispersion cylinders under 200rpm rotating speeds
It is standby uniformly to obtain component B；
(3) component A, component B are well mixed, that is, obtain aluminum alloy pattern plate surface coating.
The relevant parameter and explanation item of the aluminum alloy pattern plate surface coating of the present invention are as follows：
Surface treatment：Painting base will all dirt such as cleaning, no greasy dirt, rusty stain, dust.
Coating process：After two components are well mixed, direct application, suitable for airless spraying, aerial spraying, roller coating/brush
Apply etc..
Shelf life：In shady and cool, dry, ventilation, component A 1 year, B component six months, two-component is after mixing, business
It must be finished in 8 hours.
Part is not described in detail by the present invention, is the known technology of those skilled in the art.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. a kind of aluminum alloy pattern plate surface coating, it is characterised in that it is 3 that the aluminum alloy pattern plate surface coating, which includes weight ratio,：1 component A
With component B；
The component A includes the raw material of following parts by weight：
The component B includes the raw material of following parts by weight：
Curing agent 45-65 parts；
Accelerator 5-10 parts；
Diluent B 5-10 parts.
2. a kind of aluminum alloy pattern plate surface coating according to claim 1, it is characterised in that the component A also includes following heavy
Measure the raw material of part：Dipropylene 1-3 parts.
3. a kind of aluminum alloy pattern plate surface coating according to claim 1, it is characterised in that the component A also includes following heavy
Measure the raw material of part：Dispersant 1-3 parts.
A kind of 4. aluminum alloy pattern plate surface coating according to claim 1, it is characterised in that the diluent A include aliphatic hydrocarbon,
Fatty alcohol, organic acid esters, aliphatic ketone, the aliphatic hydrocarbon, fatty alcohol, organic acid esters, aliphatic ketone weight ratio are 1：0.4：0.6：
0.1。
5. a kind of aluminum alloy pattern plate surface coating according to claim 1, it is characterised in that the diluent B is rosin.
A kind of 6. preparation method of aluminum alloy pattern plate surface coating according to claim any one of 1-5, it is characterised in that including
Following steps：
(1) component A preparation：According to formula quantity various measuring raw materials are accurately standby, by epoxy resin, phenolic resin,
Polyimide resin, diluent A, titanium white mixing are put into dispersion cylinder, are stirred evenly under 500-700rpm rotating speed, are ground to fineness
Less than 55um, levelling agent, dipropylene, dispersant are added, 10-15 minutes are disperseed under 300-400rpm rotating speeds to body
It is bubble-free, it is standby obtains component A；
(2) component B preparation：It will be mixed in curing agent, accelerator, diluent B addition dispersion cylinders under 100-200rpm rotating speeds
It is standby uniformly to obtain component B；
(3) component A, component B are well mixed, that is, obtain aluminum alloy pattern plate surface coating.
7. a kind of aluminum alloy pattern plate surface coating according to claim 1 is preparing the application in building aluminum alloy mould plate.