CN107501711A - A kind of EVA heat-barrier materials and preparation method thereof - Google Patents
A kind of EVA heat-barrier materials and preparation method thereof Download PDFInfo
- Publication number
- CN107501711A CN107501711A CN201710893210.1A CN201710893210A CN107501711A CN 107501711 A CN107501711 A CN 107501711A CN 201710893210 A CN201710893210 A CN 201710893210A CN 107501711 A CN107501711 A CN 107501711A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixture
- preparation
- strong
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of EVA heat-barrier materials and preparation method thereof, raw material constituent is made up of following ratio in parts by weight:60 80 parts of ethene, 40 50 parts of vinyl acetate, 10 15 parts of aerosil, 5 10 parts of glass fibre, 38 parts of lauryl sodium sulfate, 10 15 parts of stearmide, 10 15 parts of fatty acid methyl ester, 58 parts of polystyrene resin, 5 10 parts of phenolic resin, 6 12 parts of organic siliconresin, 20 30 parts of ethanol.Material of the present invention is easy to get, and cost is low, and environment-friendly and green, density is big, heat insulation and preservation effect, anti-pressure ability is strong, prevents from shaking, and caking property is strong, and chemical property is stable, and oxidation resistance is strong, flame retardant type can reach A1 levels, and insulating properties is strong, applied widely, light weight, be readily transported use.
Description
Technical field
The present invention relates to heat-barrier material field, and in particular to a kind of EVA heat-barrier materials and preparation method thereof.
Background technology
Into 21st century, with the increasingly depleted of the energy and the deterioration of environment, national governments want to energy-saving and emission-reduction
Ask more and more higher, the green product of the more energy-conserving and environment-protective of people's active demand.The use of heat-barrier material is increasingly by vast
Consumer's likes, heat-barrier material on the market is a lot, although having the function that cool in summer and warm in winter, still having light pollution and makes
With the life-span it is low the defects of, the use of heat-barrier material is further restricted.
The content of the invention
A kind of EVA heat-barrier materials and preparation method thereof are provided the invention aims to overcome the shortcomings of the above.
Technical scheme includes:A kind of EVA heat-barrier materials and preparation method thereof, raw material constituent is by weight
Number is made up of following ratio:Ethene 60-80 parts, vinyl acetate 40-50 parts, aerosil 10-15 parts, glass fibre 5-
10 parts, lauryl sodium sulfate 3-8 parts, stearmide 10-15 parts, fatty acid methyl ester 10-15 parts, polystyrene resin 5-8 parts,
Phenolic resin 5-10 parts, organic siliconresin 6-12 parts, ethanol 20-30 parts.
Further improvement of the present invention is:Its preparation method is as follows:
A, by ethene and vinyl acetate input reactor, polymerisation, time are carried out under 100-120 DEG C, 1.3-1.5MPa
For 40-80min, aerosil is added after the completion of copolymerization, obtains mixture A;
B, stearmide, fatty acid methyl ester are added in ethanol and mixed, adding polystyrene resin and phenolic aldehyde tree
Fat carries out heating for dissolving polycondensation, and temperature is set to 200-250 DEG C, pressure 6000-8000KPa, adds glass fibre and is stirred,
Stir speed (S.S.) is 600-800R/MIN, and mixture B is obtained to thick;
C, mixture B is added in mixture A, adds lauryl sodium sulfate and be stirred, by the mixing after stirring
Thing is put into mould and cooled down with 5-10 DEG C/min speed, is stripped after its precuring, is obtained mixture C;
D, organic siliconresin is sprayed at mixture C surface, is being stretched, extrude, forged, is being pressurized as 150-250N/cm2,
Obtain product.
Beneficial effects of the present invention:Material of the present invention is easy to get, and cost is low, and environment-friendly and green, density is big, heat insulation and preservation effect,
Anti-pressure ability is strong, prevents from shaking, and caking property is strong, and chemical property is stable, and oxidation resistance is strong, and flame retardant type can reach A1 levels, waterproof
Property is good, and insulating properties is strong, applied widely, light weight, is readily transported use.
Embodiment:
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and the embodiment is only used
In explaining the present invention, it is not intended to limit the scope of the present invention..
Embodiment 1
A kind of EVA heat-barrier materials and preparation method thereof, raw material constituent is made up of following ratio in parts by weight:Ethene 75
Part, 46 parts of vinyl acetate, 12 parts of aerosil, 8 parts of glass fibre, 6 parts of lauryl sodium sulfate, stearmide 13
Part, 14 parts of fatty acid methyl ester, 6 parts of polystyrene resin, 8 parts of phenolic resin, 10 parts of organic siliconresin, 25 parts of ethanol.
Its preparation method is as follows:
A, polymerisation will be carried out under 110 DEG C, 1.3MPa in ethene and vinyl acetate input reactor, time 60min,
Aerosil is added after the completion of copolymerization, obtains mixture A;
B, stearmide, fatty acid methyl ester are added in ethanol and mixed, adding polystyrene resin and phenolic aldehyde tree
Fat carries out heating for dissolving polycondensation, and temperature is set to 230 DEG C, pressure 7500KPa, adds glass fibre and is stirred, stir speed (S.S.)
For 800R/MIN, mixture B is obtained to thick;
C, mixture B is added in mixture A, adds lauryl sodium sulfate and be stirred, by the mixing after stirring
Thing is put into mould and cooled down with 6 DEG C/min speed, is stripped after its precuring, is obtained mixture C;
D, organic siliconresin is sprayed at mixture C surface, is being stretched, extrude, forged, is being pressurized as 200N/cm2, must produce
Thing.
Embodiment 2
A kind of EVA heat-barrier materials and preparation method thereof, raw material constituent is made up of following ratio in parts by weight:Ethene 80
Part, 40 parts of vinyl acetate, 15 parts of aerosil, 10 parts of glass fibre, 8 parts of lauryl sodium sulfate, stearmide 14
Part, 12 parts of fatty acid methyl ester, 5 parts of polystyrene resin, 10 parts of phenolic resin, 6 parts of organic siliconresin, 26 parts of ethanol.
Its preparation method is as follows:
A, polymerisation will be carried out under 120 DEG C, 1.3MPa in ethene and vinyl acetate input reactor, time 80min,
Aerosil is added after the completion of copolymerization, obtains mixture A;
B, stearmide, fatty acid methyl ester are added in ethanol and mixed, adding polystyrene resin and phenolic aldehyde tree
Fat carries out heating for dissolving polycondensation, and temperature is set to 240 DEG C, pressure 6000KPa, adds glass fibre and is stirred, stir speed (S.S.)
For 600R/MIN, mixture B is obtained to thick;
C, mixture B is added in mixture A, adds lauryl sodium sulfate and be stirred, by the mixing after stirring
Thing is put into mould and cooled down with 6 DEG C/min speed, is stripped after its precuring, is obtained mixture C;
D, organic siliconresin is sprayed at mixture C surface, is being stretched, extrude, forged, is being pressurized as 150N/cm2, must produce
Thing.
Embodiment 3
A kind of EVA heat-barrier materials and preparation method thereof, raw material constituent is made up of following ratio in parts by weight:Ethene 60
Part, 50 parts of vinyl acetate, 15 parts of aerosil, 5 parts of glass fibre, 3 parts of lauryl sodium sulfate, stearmide 10
Part, 10 parts of fatty acid methyl ester, 8 parts of polystyrene resin, 5 parts of phenolic resin, 6 parts of organic siliconresin, 20 parts of ethanol.
Its preparation method is as follows:
A, polymerisation will be carried out under 100 DEG C, 1.5MPa in ethene and vinyl acetate input reactor, time 50min,
Aerosil is added after the completion of copolymerization, obtains mixture A;
B, stearmide, fatty acid methyl ester are added in ethanol and mixed, adding polystyrene resin and phenolic aldehyde tree
Fat carries out heating for dissolving polycondensation, and temperature is set to 210 DEG C, pressure 7000KPa, adds glass fibre and is stirred, stir speed (S.S.)
For 700R/MIN, mixture B is obtained to thick;
C, mixture B is added in mixture A, adds lauryl sodium sulfate and be stirred, by the mixing after stirring
Thing is put into mould and cooled down with 9 DEG C/min speed, is stripped after its precuring, is obtained mixture C;
D, organic siliconresin is sprayed at mixture C surface, is being stretched, extrude, forged, is being pressurized as 250N/cm2, must produce
Thing.
Embodiment 4
A kind of EVA heat-barrier materials and preparation method thereof, raw material constituent is made up of following ratio in parts by weight:Ethene 80
Part, 45 parts of vinyl acetate, 11 parts of aerosil, 8 parts of glass fibre, 6 parts of lauryl sodium sulfate, stearmide 13
Part, 13 parts of fatty acid methyl ester, 6 parts of polystyrene resin, 7 parts of phenolic resin, 10 parts of organic siliconresin, 28 parts of ethanol.
Its preparation method is as follows:
A, polymerisation will be carried out under 110 DEG C, 1.4MPa in ethene and vinyl acetate input reactor, time 70min,
Aerosil is added after the completion of copolymerization, obtains mixture A;
B, stearmide, fatty acid methyl ester are added in ethanol and mixed, adding polystyrene resin and phenolic aldehyde tree
Fat carries out heating for dissolving polycondensation, and temperature is set to 230 DEG C, pressure 6500KPa, adds glass fibre and is stirred, stir speed (S.S.)
For 650R/MIN, mixture B is obtained to thick;
C, mixture B is added in mixture A, adds lauryl sodium sulfate and be stirred, by the mixing after stirring
Thing is put into mould and cooled down with 10 DEG C/min speed, is stripped after its precuring, is obtained mixture C;
D, organic siliconresin is sprayed at mixture C surface, is being stretched, extrude, forged, is being pressurized as 250N/cm2, must produce
Thing.
Embodiment 5
A kind of EVA heat-barrier materials and preparation method thereof, raw material constituent is made up of following ratio in parts by weight:Ethene 70
Part, 48 parts of vinyl acetate, 14 parts of aerosil, 6 parts of glass fibre, 8 parts of lauryl sodium sulfate, stearmide 12
Part, 12 parts of fatty acid methyl ester, 7 parts of polystyrene resin, 8 parts of phenolic resin, 6 parts of organic siliconresin, 22 parts of ethanol.
Its preparation method is as follows:
A, polymerisation will be carried out under 105 DEG C, 1.5MPa in ethene and vinyl acetate input reactor, time 80min,
Aerosil is added after the completion of copolymerization, obtains mixture A;
B, stearmide, fatty acid methyl ester are added in ethanol and mixed, adding polystyrene resin and phenolic aldehyde tree
Fat carries out heating for dissolving polycondensation, and temperature is set to 240 DEG C, pressure 7500KPa, adds glass fibre and is stirred, stir speed (S.S.)
For 800R/MIN, mixture B is obtained to thick;
C, mixture B is added in mixture A, adds lauryl sodium sulfate and be stirred, by the mixing after stirring
Thing is put into mould and cooled down with 5 DEG C/min speed, is stripped after its precuring, is obtained mixture C;
D, organic siliconresin is sprayed at mixture C surface, is being stretched, extrude, forged, is being pressurized as 150N/cm2, must produce
Thing.
In above example, embodiment 1 is most preferred embodiment, good heat-insulation effect, high temperature resistance, and oxidation resistance is strong;It is above-mentioned
By organic siliconresin spraying and surface in step D, air pollution can be effectively reduced, there is excellent waterproof effect, insulating properties is strong.
Explanation embodiments of the present invention are the foregoing is only, are not intended to limit the invention, for the technology of this area
For personnel, within the spirit and principles of the invention, any modification, equivalent substitution and improvements made etc., it should be included in
Within protection scope of the present invention.
Claims (2)
- A kind of 1. EVA heat-barrier materials and preparation method thereof, it is characterised in that:Raw material constituent is in parts by weight by following ratio Composition:Ethene 60-80 parts, vinyl acetate 40-50 parts, aerosil 10-15 parts, glass fibre 5-10 parts, dodecane Base sodium sulphate 3-8 parts, stearmide 10-15 parts, fatty acid methyl ester 10-15 parts, polystyrene resin 5-8 parts, phenolic resin 5- 10 parts, organic siliconresin 6-12 parts, ethanol 20-30 parts.
- A kind of 2. EVA heat-barrier materials according to claim 1 and preparation method thereof, it is characterised in that:Its preparation method is such as Under:A, by ethene and vinyl acetate input reactor, polymerisation, time are carried out under 100-120 DEG C, 1.3-1.5MPa For 40-80min, aerosil is added after the completion of copolymerization, obtains mixture A;B, stearmide, fatty acid methyl ester are added in ethanol and mixed, adding polystyrene resin and phenolic aldehyde tree Fat carries out heating for dissolving polycondensation, and temperature is set to 200-250 DEG C, pressure 6000-8000KPa, adds glass fibre and is stirred, Stir speed (S.S.) is 600-800R/MIN, and mixture B is obtained to thick;C, mixture B is added in mixture A, adds lauryl sodium sulfate and be stirred, by the mixing after stirring Thing is put into mould and cooled down with 5-10 DEG C/min speed, is stripped after its precuring, is obtained mixture C;D, organic siliconresin is sprayed at mixture C surface, is being stretched, extrude, forged, is being pressurized as 150-250N/cm2, obtain Product.