CN107500615A - A kind of construction material and its processing method - Google Patents
A kind of construction material and its processing method Download PDFInfo
- Publication number
- CN107500615A CN107500615A CN201710917537.8A CN201710917537A CN107500615A CN 107500615 A CN107500615 A CN 107500615A CN 201710917537 A CN201710917537 A CN 201710917537A CN 107500615 A CN107500615 A CN 107500615A
- Authority
- CN
- China
- Prior art keywords
- parts
- construction material
- stirring
- stabilizer
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of construction material and its processing method, the construction material is process according to mass fraction by following raw material:40 ~ 60 parts of rubber grain;10 ~ 18 parts of thickener;8 ~ 16 parts of resin-oatmeal;9 ~ 14 parts of powdered whiting;8 ~ 12 parts of catalyst;5 ~ 8 parts of stabilizer;4 ~ 7 parts of methylcellulose;5 ~ 10 parts of converted starch;8 ~ 17 parts of polyacrylonitrile fibre, the intensity of the construction material is high, and environmental protection is reliable.
Description
Technical field
The present invention relates to a kind of material, more particularly to a kind of construction material and its processing method.
Background technology
At present, clay class used in building field and the wall body building material using cement as gelling agent, there is height to consume
Resource and fuel, complex process, easily environment is polluted.Most construction material quality loosely, insufficient strength, are held
Overall construction quality is easily influenceed, and the raw material storage having is seldom, is limited by regional condition, large-scale production is unrealistic.
The content of the invention
In view of the above-mentioned problems of the prior art, a kind of construction material provided by the invention, the intensity of the construction material
Height, environmental protection are reliable.
To achieve these goals, the present invention provides a kind of construction material, the construction material according to mass fraction by with
Lower raw material are process:40 ~ 60 parts of rubber grain;10 ~ 18 parts of thickener;8 ~ 16 parts of resin-oatmeal;9 ~ 14 parts of powdered whiting;
8 ~ 12 parts of catalyst;5 ~ 8 parts of stabilizer;4 ~ 7 parts of methylcellulose;5 ~ 10 parts of converted starch;8 ~ 17 parts of polyacrylonitrile fibre.
In addition, according to a kind of construction material of the present invention, there can also be following technical characteristic:
Further, the construction material is process according to mass fraction by following raw material:50 ~ 60 parts of rubber grain;Increase
Thick dose 14 ~ 18 parts;12 ~ 16 parts of resin-oatmeal;10 ~ 14 parts of powdered whiting;10 ~ 12 parts of catalyst;6 ~ 8 parts of stabilizer;Methyl is fine
5 ~ 7 parts of dimension element;7 ~ 10 parts of converted starch;12 ~ 17 parts of polyacrylonitrile fibre.
Further, the construction material is process according to mass fraction by following raw material:55 parts of rubber grain;Increase
Thick dose 16 parts;14 parts of resin-oatmeal;12 parts of powdered whiting;11 parts of catalyst;7 parts of stabilizer;6 parts of methylcellulose;Denaturation is formed sediment
8 parts of powder;15 parts of polyacrylonitrile fibre.
The preparation method of the construction material comprises the following steps:
I, by rubber grain, thickener, resin-oatmeal, powdered whiting, catalyst, stabilizer, methylcellulose, converted starch,
Polyacrylonitrile fibre is poured into stirring pool, after stirring, is dried 20 minutes;
II, elder generation are 3 according to material-water ratio:1~5:1 is stirred, and is dried 40 minutes after stirring;
III then according to material-water ratio be 1:1~2:1 is stirred, and dries after stirring 1 hour and can be used.
By adopting the above-described technical solution, the invention has the advantages that:The construction material as made from the preparation method
Intensity it is high, environmental protection is reliable.
Embodiment
Embodiment 1
The construction material is process according to mass fraction by following raw material:55 parts of rubber grain;16 parts of thickener;Resin
14 parts of powder;12 parts of powdered whiting;11 parts of catalyst;7 parts of stabilizer;6 parts of methylcellulose;8 parts of converted starch;Polyacrylonitrile
15 parts of fiber.
The preparation method of the construction material comprises the following steps:
I, by 55 parts of rubber grain;16 parts of thickener;14 parts of resin-oatmeal;12 parts of powdered whiting;11 parts of catalyst;Stabilizer 7
Part;6 parts of methylcellulose;8 parts of converted starch;15 parts of polyacrylonitrile fibre is poured into stirring pool, after stirring, dries 20 points
Clock;
II, elder generation are 4 according to material-water ratio:1 is stirred, and is dried 40 minutes after stirring;
III then according to material-water ratio be 3:2 are stirred, and dry after stirring 1 hour and can be used.
Embodiment 2
The construction material is process according to mass fraction by following raw material:40 parts of rubber grain;10 parts of thickener;Resin
8 parts of powder;9 parts of powdered whiting;8 parts of catalyst;5 parts of stabilizer;4 parts of methylcellulose;5 parts of converted starch;Polyacrylonitrile is fine
8 parts of dimension.
The preparation method of the construction material comprises the following steps:
I, by 40 parts of rubber grain;10 parts of thickener;8 parts of resin-oatmeal;9 parts of powdered whiting;8 parts of catalyst;5 parts of stabilizer;
4 parts of methylcellulose;5 parts of converted starch;8 parts of polyacrylonitrile fibre is poured into stirring pool, after stirring, is dried 20 minutes;
II, elder generation are 3 according to material-water ratio:1 is stirred, and is dried 40 minutes after stirring;
III then according to material-water ratio be 1:1 is stirred, and dries after stirring 1 hour and can be used.
Embodiment 3
The construction material is process according to mass fraction by following raw material:60 parts of rubber grain;18 parts of thickener;Resin
16 parts of powder;14 parts of powdered whiting;12 parts of catalyst;8 parts of stabilizer;7 parts of methylcellulose;10 parts of converted starch;Polypropylene
17 parts of nitrile fiber.
The preparation method of the construction material comprises the following steps:
I, by 60 parts of rubber grain;18 parts of thickener;16 parts of resin-oatmeal;14 parts of powdered whiting;12 parts of catalyst;Stabilizer 8
Part;7 parts of methylcellulose;10 parts of converted starch;17 parts of polyacrylonitrile fibre is poured into stirring pool, after stirring, dries 20
Minute;
II, elder generation are 5 according to material-water ratio:1 is stirred, and is dried 40 minutes after stirring;
III then according to material-water ratio be 2:1 is stirred, and dries after stirring 1 hour and can be used.
Although embodiments of the invention have been shown and described above, it is to be understood that above-described embodiment is example
Property, it is impossible to limitation of the present invention is interpreted as, one of ordinary skill in the art within the scope of the invention can be to above-mentioned
Embodiment is changed, changed, replacing and modification.
Claims (4)
1. a kind of construction material, it is characterised in that the construction material is process according to mass fraction by following raw material:
40 ~ 60 parts of rubber grain;10 ~ 18 parts of thickener;8 ~ 16 parts of resin-oatmeal;9 ~ 14 parts of powdered whiting;8 ~ 12 parts of catalyst;
5 ~ 8 parts of stabilizer;4 ~ 7 parts of methylcellulose;5 ~ 10 parts of converted starch;8 ~ 17 parts of polyacrylonitrile fibre.
2. construction material according to claim 1, it is characterised in that the construction material is according to mass fraction by following
Raw material are process:50 ~ 60 parts of rubber grain;14 ~ 18 parts of thickener;12 ~ 16 parts of resin-oatmeal;10 ~ 14 parts of powdered whiting;
10 ~ 12 parts of catalyst;6 ~ 8 parts of stabilizer;5 ~ 7 parts of methylcellulose;7 ~ 10 parts of converted starch;12 ~ 17 parts of polyacrylonitrile fibre.
3. construction material according to claim 1, it is characterised in that the construction material is according to mass fraction by following
Raw material are process:55 parts of rubber grain;16 parts of thickener;14 parts of resin-oatmeal;12 parts of powdered whiting;11 parts of catalyst;
7 parts of stabilizer;6 parts of methylcellulose;8 parts of converted starch;15 parts of polyacrylonitrile fibre.
4. construction material according to claim 1, it is characterised in that the preparation method of the construction material includes following step
Suddenly:
I, by rubber grain, thickener, resin-oatmeal, powdered whiting, catalyst, stabilizer, methylcellulose, converted starch,
Polyacrylonitrile fibre is poured into stirring pool, after stirring, is dried 20 minutes;
II, elder generation are 3 according to material-water ratio:1~5:1 is stirred, and is dried 40 minutes after stirring;
III then according to material-water ratio be 1:1~2:1 is stirred, and dries after stirring 1 hour and can be used.