CN107497772A - A kind of cleaning machine cleaning spray coating technology - Google Patents
A kind of cleaning machine cleaning spray coating technology Download PDFInfo
- Publication number
- CN107497772A CN107497772A CN201710965395.2A CN201710965395A CN107497772A CN 107497772 A CN107497772 A CN 107497772A CN 201710965395 A CN201710965395 A CN 201710965395A CN 107497772 A CN107497772 A CN 107497772A
- Authority
- CN
- China
- Prior art keywords
- cleaning machine
- cleaning
- spray coating
- coating technology
- spray
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is a kind of cleaning machine cleaning spray coating technology, it is characterised in that is comprised the following steps：(1) degreasing；(2) high-pressure washing；(3) anodic oxidation；(5) high-pressure washing；(6) spray；(7) solidify.A kind of cleaning machine cleaning spray coating technology of the present invention, cleaning is thorough, and spraying is uniform, and solidification effect is good, it is not easy to falls paint, surface smoothness is good.
Description
Technical field
The present invention relates to cleaning machine cleaning spraying field, more particularly to a kind of cleaning machine cleaning spray coating technology.
Background technology
Cleaning machine, for washing and filtering hydraulic system in manufacture, assembling, generate using process and when safeguarding or the dirt of intrusion
Contaminate thing；Be readily applicable to work fluid periodic maintenance filter, improve cleannes, avoid or reduce because pollution and caused by
Failure, so as to ensure the high-performance of hydraulic system equipment, high-reliability and long-life.
Cleaning machine needs to be cleaned before operation, sprays, solidifies, existing technique, also the technological operation without specialty
It is surface-treated before solving the operation of cleaning machine.
Therefore, designing a kind of cleaning machine cleaning spray coating technology, solves problem above.
The content of the invention
The present invention is to overcome the above insufficient, there is provided a kind of cleaning machine cleaning spray coating technology, it is characterised in that including following step
Suddenly：
(1) degreasing：
Under normal temperature, cleaning machine is placed in the phosphoric acid solution that mass fraction is 80% and soaks 5-10min, then is put into
5-10min is soaked in 1mol/LNa2CO3 solution；
(2) high-pressure washing：
Cleaning machine is taken out, cleaning machine surface is rinsed with giant, continues 1h；
(3) anodic oxidation：
Cleaning machine after washing is placed in the H2SO4 solution of concentration 98% as anode, makes anodic oxygen with impressed current
Change, make cleaning machine surface passivation, form the oxide-film of 5-20 μ m thicks；
(5) high-pressure washing：
Cleaning machine is taken out, cleaning machine surface is rinsed with giant；
(6) spray：
After drying, in cleaning machine surface even application anti-fouling paint, 1.5-1.9min, spray pressure 0.05- are sprayed
0.06Mpa, thickness are 10-20 μm；
(7) solidify：
In the baking oven that temperature is 240 DEG C ± 10 DEG C after baking 25-29min, natural cooling.
The beneficial effects of the invention are as follows：
A kind of cleaning machine cleaning spray coating technology of the present invention, cleaning is thorough, and spraying is uniform, and solidification effect is good, does not allow
Easily fall paint, surface smoothness is good.
Embodiment
It is described in detail below with reference to embodiments of the invention.
A kind of cleaning machine cleaning spray coating technology, it is characterised in that comprise the following steps：
(1) degreasing：
Under normal temperature, cleaning machine is placed in the phosphoric acid solution that mass fraction is 80% and soaks 5-10min, then is put into
5-10min is soaked in 1mol/LNa2CO3 solution；
(2) high-pressure washing：
Cleaning machine is taken out, cleaning machine surface is rinsed with giant, continues 1h；
(3) anodic oxidation：
Cleaning machine after washing is placed in the H2SO4 solution of concentration 98% as anode, makes anodic oxygen with impressed current
Change, make cleaning machine surface passivation, form the oxide-film of 5-20 μ m thicks；
(5) high-pressure washing：
Cleaning machine is taken out, cleaning machine surface is rinsed with giant；
(6) spray：
After drying, in cleaning machine surface even application anti-fouling paint, 1.5-1.9min, spray pressure 0.05- are sprayed
0.06Mpa, thickness are 10-20 μm；
(7) solidify：
In the baking oven that temperature is 240 DEG C ± 10 DEG C after baking 25-29min, natural cooling.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (1)
1. a kind of cleaning machine cleaning spray coating technology, it is characterised in that comprise the following steps：
(1) degreasing：
Under normal temperature, cleaning machine is placed in the phosphoric acid solution that mass fraction is 80% and soaks 5-10min, then is put into 1mol/
5-10min is soaked in LNa2CO3 solution；
(2) high-pressure washing：
Cleaning machine is taken out, cleaning machine surface is rinsed with giant, continues 1h；
(3) anodic oxidation：
Cleaning machine after washing is placed in the H2SO4 solution of concentration 98% as anode, makes anodic oxidation with impressed current, make
Cleaning machine surface passivation, form the oxide-film of 5-20 μ m thicks；
(5) high-pressure washing：
Cleaning machine is taken out, cleaning machine surface is rinsed with giant；
(6) spray：
After drying, in cleaning machine surface even application anti-fouling paint, 1.5-1.9min, spray pressure 0.05-0.06Mpa are sprayed,
Thickness is 10-20 μm；
(7) solidify：
In the baking oven that temperature is 240 DEG C ± 10 DEG C after baking 25-29min, natural cooling.