CN107495535A - Footwear dehumidifying sheet and its manufacture method - Google Patents
Footwear dehumidifying sheet and its manufacture method Download PDFInfo
- Publication number
- CN107495535A CN107495535A CN201610419612.3A CN201610419612A CN107495535A CN 107495535 A CN107495535 A CN 107495535A CN 201610419612 A CN201610419612 A CN 201610419612A CN 107495535 A CN107495535 A CN 107495535A
- Authority
- CN
- China
- Prior art keywords
- dehumidifying sheet
- finished product
- footwear
- dehumidifying
- leather
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of footwear dehumidifying sheet and its manufacture method, take a leather substance of musculus cutaneus layer or two bulky layers in natural cladding, leather substance has been subjected to full vegetable tanning processing, leather substance is cut into flake, to form a dehumidifying sheet semi-finished product, and dehumidifying sheet semi-finished product at least have a cut surface, dehumidifying sheet semi-finished product are inserted in a mould, a fiber blanket is laid in mould in advance, the cut surface of dehumidifying sheet semi-finished product corresponds to fiber blanket, dehumidifying sheet semi-finished product are heated with 50 DEG C Celsius to 60 DEG C temperature again, while with 1,800 2000 lb/cm2Pressure make pressurized treatments, fibrous material loose in leather substance is passed through into mould pressurized treatment, the fibrous material in leather substance is set to become consolidation, and its material surface hardness is maintained to shore hardness 40HA between 60HA, it is then turned on after mould so that dehumidifying sheet semi-finished product separate with fiber blanket, a dehumidifying sheet finished product is formed, now the cut surface of dehumidifying sheet semi-finished product has formed coarse shape, and become dehumidifying sheet one tramples face.
Description
Technical field
The invention relates to a kind of dehumidifying sheet, and in particular to one kind tool exsiccation and reusable footwear
With dehumidifying sheet and its manufacture method.
Background technology
The reason for general common people can produce foot odour, after mainly flowing pin sweat, aqueous vapor is vexed for a long time to be stayed in inside shoes, long
And long it, it is just mouldy smelly in footwear, therefore after taking off one's shoes, just with pungent stink on pin, suitable is indecency.
The existing mode that can improve the smelly foot odour of footwear, the first is to use drying mode, and shoes are imposed with hot baking, or will
Shoe-pad takes out reheating and dried, however, can no doubt dry shoes, shoe-pad using hot baking mode, still, shoe body material is easy to by high temperature
Destroy, cause shoe-pad to lose the effect of moisture absorption, and shoe body is largely cemented with seccotine, in the case where high warm is dried, footwear
Viscose between face, shoe-pad, sole is melted by high temperature, it is easy to causes shoes rhegma.
Second is that the powder of antibacterial and deodouring is sprinkling upon in footwear, or on socks, absorbs moisture in footwear by powder, this
Though kind of a deodorization mode still has part moisture absorption function, not persistently, for the big human body of diaphoretic volume, a small amount of powder
End is insufficiently resistant to a large amount of pin sweats disengaged for one day at all, moreover, occupation mode is also pretty troublesome, powder is easy to scatter in shoes
Outside, quite unsightly, even, slided if being sprinkled into a large amount of powder and may also result in foot when wearing, cause inconvenient walking
Problem.
The third mode is that drier is placed in footwear, when shoes produce stink when, drier is placed in footwear, so as to up to
To the using effect for absorbing moisture, still, drier deodorization mode speed is slow, thereby increases and it is possible to containing chemical substance, meeting after discarding
The generation of environmental issue is caused, should not largely be used.
In addition, though shoe-pad made of a kind of leather, can absorb moisture by the fiber in leather, still, conventional
Its preparation method of leather shoe-pad is to adopt the leather of chrome tanning processing, and in order to increase usage time, leather surface can be coated with benzene class or
The organic solvent of alcohols, surface is formed thin film, so also filled and led up the pore of leather surface, so not only influence to inhale
Water efficiency, and organic solvent is also harmful to human body.Furthermore the leather shoe-pad even after chrome tanning is handled, its after water suction,
Or can be mouldy smelly, it will be gathered mould typically after using two to three days smelly.
According to upper, shoe insoles can be destroyed by drying deodorization mode due to heat, and antibacterial and deodouring powder using effect is not evident and inconvenient, does
Drying prescription deodorization speed slowly and not environmentally, and the leather of general chrome tanning is not because grow by service life, and also easily mouldy smelly, the above is each
Kind mode can not effectively solve stink generation, and this is also one of the reason for foot odour problem can not be broken off.
The content of the invention
A kind of footwear dehumidifying sheet provided by the present invention and its manufacture method, the leather substance treated using full vegetable tanning,
And be cut into flake, then impose heating and pressurization after, fibrous material loose in leather substance is become into the appropriate degree of packing,
And coarse shape is processed into the face of trampling, to obtain the good use effect of effect on moisture extraction.The footwear dehumidifying sheet of the present invention and its manufacture
Method, the effect of moisture absorption is effectively carried out to foot, dehumidifying sheet can be re-covered and is used for multiple times, and service life can reach as long as several moons.
The footwear dehumidifying sheet and its manufacture method, dehumidifying sheet of the present invention is made up of natural leather, natural leather substance
Can crack naturally, without using and after abandoning, will not generation environment pollution, therefore with environmentally friendly effect.Therefore, the present invention is carried
A kind of footwear dehumidifying sheet gone out, this kind of dehumidifying sheet, which has, accords with the footwear component surface region to be used, and includes：One
Leather substrate, it is to take the laminar leather substance for having been subjected to full vegetable tanning processing, the leather substrate of the dehumidifying sheet has conversely
What is set one tramples face, a binding face, and it is multiple be formed at this and trample fibrous material between face and binding face, and this is trampled
Face is coarse shape, and it is 0.5mm to 1.3mm that this, which tramples face and the spacing of binding face, and maintains its material surface hardness to shore
Hardness 40HA is between 60HA.
According to the footwear dehumidifying sheet of the invention described above, wherein, the leather substrate is the Animal Skin treated by full vegetable tanning,
As ox, pig, sheep, deer any Animal Skin.
According to the footwear dehumidifying sheet of the invention described above, wherein, the leather substrate is to can be made into the tool consistent with human foot
The pad of water imbibition.
A kind of manufacture method of footwear dehumidifying sheet proposed by the invention, manufacturing step are as follows：Step A：Stock, takes day
A leather substance of musculus cutaneus layer or two bulky layers in right cladding, the leather substance have been subjected to full vegetable tanning processing；Step B：Cut processing,
The leather substance after the processing of full vegetable tanning is cut into flake, to form a dehumidifying sheet semi-finished product；Step C：Mould is inserted, will
The dehumidifying sheet semi-finished product are inserted in a mould, and the mould inside is equipped with a fiber blanket in advance, the dehumidifying sheet semi-finished product
One, which tramples face, corresponds to the fiber blanket；Step D：Pressurized treatments are heated, with 50 DEG C Celsius to 60 DEG C temperature to the dehumidifying sheet
Semi-finished product heat, and simultaneously with 1,800 2000 lb/cm2Pressure make pressurized treatments, by undulation degree loose in leather substance
Material promotes the fibrous material in leather substance to become consolidation, and maintain its material surface hardness extremely by the pressurized treatment of the mould
Shore hardness 40HA is between 60HA；Step E：Mould is removed, so that the dehumidifying sheet semi-finished product and the fiber after opening mold
Overcoat separates, that is, forms a dehumidifying sheet finished product, now the cut surface of the dehumidifying sheet semi-finished product has formed coarse shape, and becomes this
The one of dehumidifying sheet tramples face.
According to the manufacture method of the footwear dehumidifying sheet of the invention described above, wherein, in stepb, the leather substance is imposed
The pressurized treatments of ten seconds.
According to the manufacture method of the footwear dehumidifying sheet of the invention described above, wherein, the leather substance is handled by full vegetable tanning
The Animal Skin crossed, as ox, pig, sheep, deer any Animal Skin.
According to the manufacture method of the footwear dehumidifying sheet of the invention described above, wherein, the dehumidifying sheet finished product is to can be made into and human body
The pad of the consistent tool water imbibition of foot.
According to the manufacture method of the footwear dehumidifying sheet of the invention described above, wherein, the fiber blanket in step C, it is that matter is soft
And textile cloth, adhesive-bonded fabric or mesh cloth with porous fibre.
According to the manufacture method of the footwear dehumidifying sheet of the invention described above, wherein, in step C, the mould have a backform and
One bed die, the dehumidifying sheet semi-finished product are placed between the backform and the bed die, and the fiber blanket is placed in the dehumidifying sheet semi-finished product
Between bed die.
According to the manufacture method of the footwear dehumidifying sheet of the invention described above, wherein, in step D, in advance to this before hot pressing
Backform heats.
Mode mentioned above, smelly compared to existing improvement foot odour, footwear, its drying mode can destroy shoe body structure, dusting
Last mode is not lasting, places drier mode not environmentally, easy mouldy smelly, the equal nothing of each mode of the above of the leather of chrome tanning processing
Method effectively overcomes the generation of stink in footwear, based on it is foregoing it is existing use problem, be using complete due to the footwear dehumidifying sheet of the present invention
The treated leather substance of vegetable tanning, then by cutting, after heating and pressurization, fibrous material loose in leather substance is become
Into consolidation, consequently, it is possible to because the leather substance of full vegetable tanning includes tannic acid, hydrolyzable tannic acid is powerful antioxidants, energy
Inhibiting substances reactions change, thus the dehumidifying sheet in using process after tinea pedis is absorbed, can't be mouldy smelly, therefore, this hair
Bright dehumidifying sheet is being put into footwear in use, with regard to that can reach splendid moisture sorption effect, after foot substantial amounts of aqueous vapor is absorbed,
Pin would not be smelly, improves the smelly puzzlement of foot odour, footwear completely, and obtains dehumidifying deodorizing effect work(that is good, and repeatedly using
Effect.And natural leather material can crack naturally, dehumidifying sheet without using and abandon after, environmental pollution can't be caused, therefore have concurrently
Environmental-protection function.
Brief description of the drawings
Fig. 1 is the flow chart of the manufacture method of footwear dehumidifying sheet of the present invention；
Fig. 2 is the appearance assumption diagram corresponding to the product of processing procedure in Fig. 1；
Fig. 3 is the sectional view of the dehumidifying sheet finished product of the invention；
Fig. 4 is the sectional view that the dehumidifying sheet finished product of the invention is placed in inside boot last footwear.
【Symbol description】
The leather substrate of 1 leather substance 10
The cut surface of 10 ' dehumidifying sheet semi-finished product 11 '
11 fibrous materials 12 trample face
The mould of 13 binding face 20
The bed die of 21 backform 22
The binder course of 30 fiber blanket 40
The vamp of 50 boot last footwear 51
100 dehumidifying sheets.
Embodiment
In order to which technical scheme is explained further, the present invention is explained in detail below by specific embodiment
State.
Referring to figs. 1 to shown in Fig. 3, the preferred embodiment of one of manufacture method of footwear dehumidifying sheet of the invention, manufacturing step
It is as follows：
Step A：Stock, takes musculus cutaneus layer in natural cladding（Grain）Or two bulky layer（corium）A leather substance 1, the skin
Leather material 1 has been subjected to full vegetable tanning processing.There are multiple fibrous materials 11 inside the leather substance 1, and the leather substance 1 is by complete
The treated Animal Skin of vegetable tanning, such as ox, pig, sheep, bird, any Animal Skin of snake.In the present embodiment, it is made as using ox-hide
Most preferably.In addition, musculus cutaneus layer is also known as pearl surface layer or first layer lether.
Step B：Processing is cut, the leather substance 1 after the processing of full vegetable tanning is cut into flake, to form a dehumidifying sheet
Semi-finished product 10 ', and the dehumidifying sheet semi-finished product 10 ' at least have a cut surface 11 '.Further, since the outermost top layer of leather substance 1
It will not be cut, so, it is not cut that dehumidifying sheet semi-finished product 10 ', which have one side, and is at least simultaneously cut surface, is also removed
The two sides of humidity strip semi-finished product is cut surface.
Step C：Mould is inserted, the dehumidifying sheet semi-finished product 10 ' are inserted in a mould 20, the inside of mould 20 laying in advance
There is a fiber blanket 30, a cut surface 11 ' of the dehumidifying sheet semi-finished product 10 ' corresponds to the fiber blanket 30.And the mould
20 have a backform 21 and a bed die 22, and the dehumidifying sheet semi-finished product 10 ' are placed between the backform 21 and the bed die 22, and the fiber
Overcoat 30 is placed between the dehumidifying sheet semi-finished product 10 ' and bed die 22.
Step D：Pressurized treatments are heated, the backform 21 is heated in advance before hot pressing, then with 50 DEG C Celsius to 60 DEG C temperature
The dehumidifying sheet semi-finished product 10 ' are heated, and simultaneously with 1,800 2000 lb/cm2Pressure make pressurized treatments, by leather substance 1
In loose fibrous material 11 by the pressurized treatment of the mould, promote the fibrous material 11 in leather substance 1 to become consolidation, and tie up
Its material surface hardness is held to shore hardness 40HA between 60HA, there is the dehumidifying sheet of style-ability effect to form one.
Step E：Mould is removed, so that the dehumidifying sheet semi-finished product 10 ' divide with the fiber blanket 30 behind opening mold 20
From forming the finished product of a dehumidifying sheet 100, now the cut surface 11 ' of the dehumidifying sheet semi-finished product 10 ' has formed coarse shape, and becomes
The one of the dehumidifying sheet 100 tramples face 12.In addition, when the heated pressurization of 100 one of cut surface 11 ' of dehumidifying sheet becomes the face of trampling
After 12, whether cut surface or non-cut surface, the face are exactly a binding face 13 of the dehumidifying sheet 100 to another side.This implementation
In example, thickness circle of the finished product of dehumidifying sheet 100 is optimal in 0.5mm to 1.3mm, to allow user to adapt to inside script shoes
Wearing space.
In addition, in abovementioned steps C, the fiber blanket 30 can be soft for matter and the textile cloth with porous fibre, adhesive-bonded fabric
Or mesh cloth etc., in pressure process, when a bed die 21 of the equipment 20 brings pressure to bear on the face 12 of trampling, prevent by the fiber
The concrete dynamic modulus characteristic of sheath 30, the few fibers of the leather substance 1 still relief can be made on the face of trampling 12, so, when being walked
After rapid E opens bed die 21 and makes dehumidifying sheet semi-finished product 10 ' be separated with the fiber blanket 30, this is trampled face 12 and will not be pressed into entirely
Smooth shape and keep appropriate roughness.In this way, when the dehumidifying sheet 100 is placed in inside shoes, the dehumidifying sheet 100 tramples face
12 are sticked in footwear, and after user's foot is penetrated in footwear, vola is trampling trampling on face 12 in the dehumidifying sheet 100, with
Frictional force is produced with vola by roughish face 12 of trampling, to acquire good moisture absorption anti-sliding function, with reference to figure 4.
Continue referring to figs. 1 to shown in Fig. 3, an embodiment of footwear dehumidifying sheet of the present invention, this kind of dehumidifying sheet 100, which has, to be met
In the surface region that footwear component to be used, and include a leather substrate 10, the leather substrate 10 is to take to have been subjected to entirely
One laminar leather substance 1 of vegetable tanning processing, the leather substrate 10 of the dehumidifying sheet 100 have be reversed one trample face 12,
One binding face 13, and it is multiple be formed at this and trample fibrous material 11 between face 12 and binding face 13, and this is trampled face 12 and is in
Existing coarse shape, and it is 0.5mm to 1.3mm that this, which tramples face 12 and the spacing of binding face 13, and its material surface hardness is maintained to Shao
Family name's hardness 40HA is between 60HA.It has been observed that the leather substance 1 be by full vegetable tanning treat Animal Skin, such as ox, pig,
Sheep, any Animal Skin of deer.In the present embodiment, it is made as most preferably using ox-hide.
Secondly, the leather substrate 10 is the pad (dehumidifying sheet 100) that can be made into the tool water imbibition consistent with human foot, should
The profile of dehumidifying sheet 100 can also need what is dehumidified in addition to it can be cut according to human foot profile and help palm shape according to foot
Position is cut, such as：The preceding metacarpus of human foot, rear heel, toes portion etc..
In addition, in the processing procedure of the present invention, the leather substance is bestowed to the purpose of heating, is leather substance to be determined as integumentary pattern
Type, allow cladding surface moderately to produce hardening effect, with the follow-up pressurization of profit, and in the present embodiment, control its heating-up temperature to take the photograph
50 DEG C to 60 DEG C or so of family name be it is optimal, using optimized proper temperature can softening fibre material in advance, in this step, if plus
Hot temperature is too low, and integumentary pattern sizing efficiency can be made unevident, if conversely, heating-up temperature is too high, can cause leather maturation, and after maturation
Leather do not absorb water not only and lose dehumidifying effectiveness, and during slight curvature, the fibrous material of leather just deformation at once and be broken, make
It will be split into wearer when trampling is walked.And leather substance is after the heating, i.e., through pressure process（About ten seconds）, can
Fibrous material is promoted integrally to become consolidation without spallation (as shown in Figure 3), it is not necessary to as existing leather shoe-pad is also organic through adding
Solvent makees pore to leather surface and tightens operation.
To sum up, in the various modes smelly compared to existing improvement foot odour, footwear, its drying mode shoe body easily goes to pot, dusting
Last deodorization mode is not lasting, places drier mode not environmentally, easy mouldy smelly, the above-mentioned each mode of the leather of chrome tanning processing
Can not effectively solve the generation of stink, and based on it is foregoing it is existing respectively use problem, be to adopt due to footwear dehumidifying sheet of the invention
The natural leather material 1 treated with full vegetable tanning, then by cutting, after heating and pressurization, will be loose in leather substance 1
Fibrous material 11 becomes consolidation (shore hardness 40HA is between 60HA), consequently, it is possible to because the leather substance 1 of full vegetable tanning includes list
Peaceful acid, hydrolyzable tannic acid is powerful antioxidants, energy inhibiting substances reactions change, so the dehumidifying sheet 100 uses process
, can't be mouldy smelly after foot moisture is absorbed, therefore, dehumidifying sheet 100 of the invention is being put into footwear in use, with regard to energy
Reach splendid moisture sorption effect, after foot substantial amounts of aqueous vapor is absorbed, pin would not be smelly, not only completely inhibits stink
Produce, and it is good to obtain the deodorizing effect that dehumidifies, and the effect of repeatedly use.In addition, dehumidifying sheet 100 can be according to the portion used
Position and cut randomly, such as the preceding metacarpus of human foot, rear heel, toes portion etc..
In addition, because the dehumidifying sheet 100 is in use state, directly contacted with foot by roughish face 12 of trampling, institute
With, except frictional force can be produced by roughish face 12 and the vola (ankle) of trampling, and obtain outside preferable hygroscopic effect,
Use problem that is too smooth and causing foot to slide can be avoided.
Secondly, the dehumidifying sheet of this case, in the program for heat pressurization, the backform 21 heated is to correspond to hot pressing in this
The binding face 13 of dehumidifying sheet 100, rather than trample face 12.It is general known, because the die face (backform 21) of heating directly bears against fitting
During face 13, the maturation of binding face 13, discoloration (color burn) can be caused, however, because the face 12 of trampling of this case dehumidifying sheet 100 is to carry
For the actual use face of foot trampling, the outward appearance for trampling face 12 of not maturation discoloration can possess the primary colors of cladding, and rich with height
The cladding aesthetic property of texture, because the binding face 13 is sticked in footwear, even if therefore become dark brown because of maturation, just as tire
The general color and luster of note is uneven, nor affects on aesthetic property.
Furthermore the problem of compared to drier is placed in footwear in the past not environmentally, because the dehumidifying sheet 100 of the present invention is to take
It is main material with natural cladding, in addition to the good characteristic of tool moisture sorption effect, when not using after abandon, natural leather can nature
Cracking, will not cause environmental pollution, therefore with environmentally friendly effect.
It is noted that it is upper using, after dehumidifying sheet 100 has absorbed moisture, it can take out for every two to four days laggard
Row natural air drying, such usage dehumidifying sheet 100 can be used eight to ten months, if forgetting and dehumidifying sheet 100 not being taken out into nature
Air-dry, it is possible to use by four to six months, suitable was economical and practical, and moisture absorbing and deodorizing effect is quite good.
Conclude it is above-mentioned, because the present invention dehumidifying sheet 100 only in flake, can conveniently be cut into needed for foot position size
Size (preceding metacarpus, toes portion, rear heel or whole sufficient type), can more be convenient and easy to be positioned in footwear and use, without by shoes
Internal structure inner sole (shoe-pad) take out, more need not destroy shoes internal structure, it is easy-to-use and eliminate change also easily, make
It is also very long with the life-span, it is quite practical and economical and practical.
In addition, as shown in figure 4, the dehumidifying sheet 100 of the present invention, more can be according to the different use demands of user, further
It is used on vamp, that is, if user wears boot last footwear 50, because space is deeper in the footwear of boot last footwear 50, necessarily less
Ventilative reason, at this moment, dehumidifying sheet 100 can be placed in the inner side of vamp 51, and close to the opening position of ankle, in this way, can enter
One step absorbs the moisture of ankles bit through the dehumidifying sheet 100, is detained with solving moisture inside boot last footwear 50 without easily shedding
Puzzlement, while can also meet the larger use demand of foot's diaphoretic volume.
Preferable embodiment is above are only, it is when the scope that implementation of the invention can not be limited with this, i.e., big
All simple equivalent changes and modificationss made according to scope of the present invention patent and invention description content, it all should still belong to the present invention
In the range of patent covers.
Claims (10)
1. a kind of footwear dehumidifying sheet, this kind of dehumidifying sheet, which has, accords with the footwear component surface region to be used, and its feature exists
In including：
One leather substrate, it is to take the laminar leather substance for having been subjected to full vegetable tanning processing, the leather substrate, which has, conversely to be set
One put tramples face, a binding face, and it is multiple be formed at this and trample fibrous material between face and binding face, and this tramples face
For coarse shape, and it is 0.5mm to 1.3mm that this, which tramples face and the spacing of binding face, and maintains its material surface hardness hard to shore
40HA is spent between 60HA.
2. footwear dehumidifying sheet as claimed in claim 1, it is characterised in that：The leather substrate is moved by what full vegetable tanning treated
Thing skin, as ox, pig, sheep, deer any Animal Skin.
3. footwear dehumidifying sheet as claimed in claim 1, it is characterised in that：The leather substrate be can be made into it is consistent with human foot
Tool water imbibition pad.
4. a kind of manufacture method of footwear dehumidifying sheet, manufacturing step are as follows：
Step A：Stock, takes a leather substance of musculus cutaneus layer or two bulky layers in natural cladding, the leather substance has been subjected to full plant
Tan processing；
Step B：Cut processing, the leather substance after the processing of full vegetable tanning cut into flake, with formed a dehumidifying sheet half into
Product, and the dehumidifying sheet semi-finished product at least have a cut surface；
Step C：Mould is inserted, the dehumidifying sheet semi-finished product are inserted in a mould, the mould inside is equipped with a fiber in advance to be prevented
Sheath, the cut surface of the dehumidifying sheet semi-finished product correspond to the fiber blanket；
Step D：Heat pressurized treatments, with 50 DEG C Celsius to 60 DEG C temperature to the dehumidifying sheet semi-finished product heat, and simultaneously with
1800 2000 lb/cm2Pressure make pressurized treatments, by fibrous material loose in leather substance pass through the mould supercharging
Processing, promote the fibrous material in leather substance to become consolidation, and maintain its material surface hardness to shore hardness 40HA to 60HA
Between；
Step E：Mould is removed, so that the dehumidifying sheet semi-finished product separate with the fiber blanket after opening mold, that is, forms one
Dehumidifying sheet finished product, now the cut surface of the dehumidifying sheet semi-finished product has formed coarse shape, and become the dehumidifying sheet one tramples face.
5. the manufacture method of footwear dehumidifying sheet as claimed in claim 4, it is characterised in that：In step C, to the leather substance
Impose the pressurized treatments of ten seconds.
6. the manufacture method of footwear dehumidifying sheet as claimed in claim 4, it is characterised in that：The leather substance is by full vegetable tanning
Treated Animal Skin, as ox, pig, sheep, deer any Animal Skin.
7. the manufacture method of footwear dehumidifying sheet as claimed in claim 4, it is characterised in that：The dehumidifying sheet finished product be can be made into
The pad of the consistent tool water imbibition of human foot.
8. the manufacture method of footwear dehumidifying sheet as claimed in claim 4, it is characterised in that：Fiber blanket in step C, it is
Matter is soft and has textile cloth, adhesive-bonded fabric or the mesh cloth of porous fibre.
9. the manufacture method of footwear dehumidifying sheet as claimed in claim 4, it is characterised in that：In step C, the mould has a top
Mould and a bed die, the dehumidifying sheet semi-finished product are placed between the backform and the bed die, and the fiber blanket is placed in the dehumidifying sheet half
Between finished product and bed die.
10. the manufacture method of footwear dehumidifying sheet as claimed in claim 4, it is characterised in that：It is pre- before hot pressing in step D
First the backform is heated.