CN107487771A - A kind of spherical coal mass active carbon ball making process - Google Patents
A kind of spherical coal mass active carbon ball making process Download PDFInfo
- Publication number
- CN107487771A CN107487771A CN201710832582.3A CN201710832582A CN107487771A CN 107487771 A CN107487771 A CN 107487771A CN 201710832582 A CN201710832582 A CN 201710832582A CN 107487771 A CN107487771 A CN 107487771A
- Authority
- CN
- China
- Prior art keywords
- active carbon
- making process
- carbon ball
- mass active
- coal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of spherical coal mass active carbon ball making process, comprise the following steps：（1）Coal is all crushed to the meshes of ＜ 100, moisture control 12% ~ 15%,（2）After coal dust and moisture, binding agent are mixed uniformly, disk balling machine is fed, its revolution is 5 ~ 25r/min, 55 ° of disk inclination angle 45 °；（3）Hopper screw feeder is had, scraper and sprayer are arranged at marble forming machine side and bottom, can arbitrarily adjust the size of pelletizing.The beneficial effect of the invention is：It is high, homogeneous to be firmly combined with degree, shaping is quick, moreover it is possible to twice laid.
Description
Technical field
The present invention relates to activated carbon preparing technical field, specially a kind of spherical coal mass active carbon ball making process.
Background technology
Spherical coal mass active carbon using high quality brown coal or anthracite and adhesive, catalyst etc. through crushing, mixing, balling-up,
Dry, be carbonized, activate and be made.Spherical coal mass active carbon is used for sewage disposal, and effect is preferable；In addition spherical activated charcoal is also
Wooden making can be used, its proportion is lighter, and using effect is more preferable.
This technique is from pelletizing moulding process unlike other ature of coal particle charcoals, it is necessary to which being made fine and close has some strength
Charcoal ball, activation procedure are essentially identical.
The content of the invention
It is an object of the invention to provide a kind of spherical coal mass active carbon ball making process, to solve to carry in above-mentioned background technology
The problem of going out.
To achieve the above object, the present invention provides following technical scheme：A kind of spherical coal mass active carbon ball making process, including
Following steps：
（1）Coal is all crushed to the meshes of ＜ 100, moisture control 12% ~ 15%,
（2）After coal dust and moisture, binding agent are mixed uniformly, disk balling machine is fed, its revolution is 5 ~ 25r/min, disk inclination angle
45°-55°；
（3）Hopper screw feeder is had, scraper and sprayer are arranged at marble forming machine side and bottom, can arbitrarily adjust the big of pelletizing
It is small.
Preferably, the binding agent is one kind in sulfite liquor, blackstrap, starch, methylcellulose of betraing.
Preferably, wherein more than 90% in the meshes of ＜ 200.
Preferably, the marble forming machine pelletizing capacity is 100kg/h, power 3.5kw.
Compared with prior art, the beneficial effects of the invention are as follows：It is high, homogeneous to be firmly combined with degree, shaping is quick, also
Can twice laid.
Embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment one
The present invention provides a kind of technical scheme：A kind of spherical coal mass active carbon ball making process, comprises the following steps：
（1）Coal is all crushed to more than 90% in the meshes of ＜ 200, moisture control 12% ~ 15%,
（2）After coal dust and moisture, binding agent are mixed uniformly, disk balling machine is fed, its revolution is 5r/min, 45 ° of disk inclination angle, its
Middle binding agent is sulfite liquor；
（3）Hopper screw feeder is had, scraper and sprayer are arranged at marble forming machine side and bottom, can arbitrarily adjust the big of pelletizing
It is small, pelletizing capacity 100kg/h, power 3.5kw.
Ball yield rate processed is high, and in 1000 coal briquettes of production, yield rate is 990, and substandard products are few.
Preferably, the binding agent be sulfite liquor, starch, in one kind.
Preferably, wherein more than 90% in the meshes of ＜ 200.
Preferably, the marble forming machine.
Embodiment two
A kind of spherical coal mass active carbon ball making process, comprises the following steps：
（1）Coal is all crushed to more than 95% in the meshes of ＜ 200, moisture control 12% ~ 15%,
（2）After coal dust and moisture, binding agent are mixed uniformly, disk balling machine is fed, its revolution is 15r/min, 50 ° of disk inclination angle,
Wherein binding agent is blackstrap；
（3）Hopper screw feeder is had, scraper and sprayer are arranged at marble forming machine side and bottom, can arbitrarily adjust the big of pelletizing
It is small, pelletizing capacity 100kg/h, power 3.5kw.
Ball yield rate processed is high, and in 1000 coal briquettes of production, yield rate is 999, and substandard products are few.
Embodiment three
A kind of spherical coal mass active carbon ball making process, comprises the following steps：
（1）Coal is all crushed to more than 90% in the meshes of ＜ 200, moisture control 12% ~ 15%,
（2）After coal dust and moisture, binding agent are mixed uniformly, disk balling machine is fed, its revolution is 25r/min, 55 ° of disk inclination angle,
Wherein binding agent is methylcellulose of betraing；
（3）Hopper screw feeder is had, scraper and sprayer are arranged at marble forming machine side and bottom, can arbitrarily adjust the big of pelletizing
It is small, pelletizing capacity 100kg/h, power 3.5kw.
Ball yield rate processed is high, and in 1000 coal briquettes of production, yield rate is 995, and substandard products are few.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (4)
- A kind of 1. spherical coal mass active carbon ball making process, it is characterised in that：Comprise the following steps：（1）Coal is all crushed to the meshes of ＜ 100, moisture control 12% ~ 15%,（2）After coal dust and moisture, binding agent are mixed uniformly, disk balling machine is fed, its revolution is 5 ~ 25r/min, disk inclination angle 45°-55°；（3）Hopper screw feeder is had, scraper and sprayer are arranged at marble forming machine side and bottom, can arbitrarily adjust the big of pelletizing It is small.
- A kind of 2. spherical coal mass active carbon ball making process according to claim 1, it is characterised in that：The binding agent is Asia One kind in Sulfate paper pulp waste liquid, blackstrap, starch, methylcellulose of betraing.
- A kind of 3. spherical coal mass active carbon ball making process according to claim 1, it is characterised in that：Wherein more than 90% The meshes of ＜ 200.
- A kind of 4. spherical coal mass active carbon ball making process according to claim 1, it is characterised in that：The marble forming machine pelletizing Ability is 100kg/h, power 3.5kw.