CN107486382A - Armouring anti-corrosion process for protecting method - Google Patents
Armouring anti-corrosion process for protecting method Download PDFInfo
- Publication number
- CN107486382A CN107486382A CN201710712203.7A CN201710712203A CN107486382A CN 107486382 A CN107486382 A CN 107486382A CN 201710712203 A CN201710712203 A CN 201710712203A CN 107486382 A CN107486382 A CN 107486382A
- Authority
- CN
- China
- Prior art keywords
- brush
- brushing
- time
- brushed
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of armouring anti-corrosion process for protecting method, comprise the following steps：Protection body is treated to be pre-processed；Treat that protection body is completed repeatedly to brush by the way of round brush to pretreated, and after multiple brush, kept for the drying time not less than 7 days to realize that armouring anti-corrosion is protected.This method solve conventional art in work progress and after the completion of disaster hidden-trouble be present；Construction technology is cumbersome, environmental requirement is harsh, personnel qualifications are high；Easily leave cracking, play the defects of drum, anticorrosion ability is poor；Long construction period, pre-processed by treating protection body, and treat that protection body completes four brushings by the way of round brush to pretreated, and after four times are brushed, kept for the drying time not less than 7 days to realize that armouring anti-corrosion is protected, wide in range property, the simplicity, high efficiency used and the flexibility with application.
Description
Technical field
The present invention relates to engineer equipment technical field, more particularly to a kind of armouring anti-corrosion process for protecting method.
Background technology
Existing aseptic production, such as glass flake etc. and construction technology have the disadvantages that：Work progress and after the completion of deposit
In disaster hidden-trouble；Construction technology is cumbersome, environmental requirement is harsh, personnel qualifications are high；Easily leave cracking, play the defects of drum, prevent
Corrosive effect is poor；Long construction period.As can be seen here, how to help user to solve the raising of anticorrosion ability in conventional art to use
The limitation of pattern and complicated inefficiencies are a urgent problems to be solved.
The content of the invention
Based on this, it is necessary to the problem of existing for conventional art, there is provided a kind of armouring anti-corrosion process for protecting method, can
Solve conventional art in work progress and after the completion of disaster hidden-trouble be present；Construction technology is cumbersome, environmental requirement is harsh, peopleware
It is it is required that high；Easily leave cracking, play the defects of drum, anticorrosion ability is poor；Long construction period, located in advance by treating protection body
Reason, and treat that protection body completes four brushings by the way of round brush to pretreated, and after four times are brushed, keep being not less than
The drying time of 7 days to realize that armouring protects, wide in range property, the simplicity, high efficiency used and the flexibility with application.
In a first aspect, the embodiments of the invention provide a kind of armouring anti-corrosion process for protecting method, including：Protection body is treated to enter
Row pretreatment；To it is pretreated it is described treat that protection body is completed repeatedly to brush by the way of round brush, and after multiple brush, protect
The drying time not less than 7 days is held to realize that armouring anti-corrosion is protected.
In one of the embodiments, described to treat that protection body is metal, the pretreatment includes：To the metallic surface
By corrosion, skin is stuck up, come off and complete grinding process, greasy dirt or other chemicals caused by metal covering attachment are completed at chemistry
Reason, and cleaned；
In one of the embodiments, described repeatedly brush includes：To it is pretreated it is described treat protection body brushing rust go out
Agent living, basis of formation layer, and kept for the drying time no less than 4 hours brushed for the first time to realize.
In one of the embodiments, described repeatedly brush also includes：On the basis of being brushed based on the first time, brush
Macromolecule protection isolation ester, and kept for the drying time no less than 3 hours realize second of brushing.
In one of the embodiments, described repeatedly brush also includes：On the basis of being brushed based on described second, complete
The brushing for the combination that ester isolate in the protection of carborundum and macromolecule forms structure sheaf, and keep being no less than drying time of 3 hours with
Realize that third time is brushed.
In one of the embodiments, described repeatedly brush also includes：On the basis of the third time brushing, complete
The brushing for the combination that brushing graphite isolates ester with macromolecule protection forms enhancement layer, and is kept for the drying time no less than 3 hours
To realize the 4th brushing.
In one of the embodiments, described to treat that protection body is concrete, the pretreatment includes：Concrete surface is led to
Cross giant or sandblasting mode by the dust of cement-based surface, dirt completion handle, then by mica cream ester repair leak with
And crackle, polished after to be dried round and smooth；Or
Described to treat that protection body is Wood surface, the pretreatment includes：Wood surface dirt, dust are removed by sand paper,
If there is oil stain on surface, and the scouring of surface and oil contaminant is completed with No. 200 gasoline.
In one of the embodiments, described repeatedly brush includes：Described protection body brushing is treated to pretreated
Macromolecule protection isolation ester, basis of formation layer, and kept for the drying time no less than 4 hours brushed for the first time to realize；
In one of the embodiments, described repeatedly brush includes：On the basis of being brushed based on the first time, stone is completed
Ink isolates the brushing of the combination of ester with macromolecule protection, forms structure sheaf, and kept for the drying time no less than 3 hours realize
Second of brushing.
In one of the embodiments, described repeatedly brush includes：On the basis of being brushed based on described second, complete high
The brushing of molecule protection isolation ester, forms enhancement layer, and is kept for the drying time no less than 3 hours to realize that third time is brushed.
In one of the embodiments, the mode of the round brush can select spraying method or brush mode.
Armouring anti-corrosion process for protecting method provided by the invention, treats protection body and is pre-processed；Treated to pretreated
Protection body completes four brushings by the way of round brush, and after four times are brushed, is kept for the drying time not less than 7 days realize
Armouring protects.This method solve conventional art in work progress and after the completion of disaster hidden-trouble be present；Construction technology is cumbersome, environment is wanted
Seek harsh, personnel qualifications height；Easily leave cracking, play the defects of drum, anticorrosion ability is poor；Long construction period, by treating
Protection body is pre-processed, and treats that protection body completes four brushings by the way of round brush to pretreated, and in four paintings
After brush, keep not less than 7 days drying time with realize armouring protect, have application wide in range property, use it is simplicity, efficient
Property and flexibility.
Brief description of the drawings
Fig. 1 is a kind of schematic flow sheet of armouring anti-corrosion process for protecting method in one embodiment of the invention；And
Fig. 2 is a kind of Structure Mechanism figure of armouring anti-corrosion process for protecting method in one embodiment of the invention.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, below in conjunction with drawings and Examples pair
Armouring anti-corrosion process for protecting method of the present invention is further elaborated.It should be appreciated that specific embodiment described herein
Only to explain the present invention, it is not intended to limit the present invention.
As shown in figure 1, be a kind of schematic flow sheet of armouring anti-corrosion process for protecting method in one embodiment, specific bag
Include following steps：
Step 102, protection body is treated to be pre-processed.
In the present embodiment, if treating, protection body is metal, and pretreatment includes：To metallic surface by corrosion, stick up skin, come off
Complete grinding process；Chemical treatment is completed to greasy dirt or other chemicals caused by metal covering attachment, and cleaned.
If in addition, treating that protection body is concrete, pretreatment also includes：Then pass through giant or sandblasting side to coagulating native surface
Formula handles the dust of cement-based surface, dirt completion；Leak and crackle are repaired by mica cream ester again, polished after to be dried
It is round and smooth.
If in addition, treating that protection body is Wood surface, pretreatment also includes：Wood surface dirt, ash are then removed by sand paper
There is oil stain on dirt, surface and the scouring of surface and oil contaminant are completed with No. 200 gasoline.
Step 104, treat that protection body is completed repeatedly to brush by the way of round brush to pretreated, and repeatedly brushing
Afterwards, the drying time not less than 7 days is kept to realize that armouring protects.Wherein, the mode of round brush can select spraying method or brush
Painting mode.Thus, the multi-selection for choosing round brush mode is improved.
In one of the embodiments, if treating, protection body is metal, treats that protection body uses the side of round brush to pretreated
Formula, which completes four brushings, to be included：Treat that protection body brushing becomes rusty inactivator, basis of formation layer, and holding no less than 4 to pretreated
The drying time of hour is brushed for the first time with realizing.
Further, described treat that protection body is completed four brushings by the way of round brush and included to pretreated：It is based on
On the basis of brushing for the first time, brushing macromolecule protection isolation ester, and kept for the drying time no less than 3 hours realize second
Secondary brushing；On the basis of being brushed based on second, the brushing formation for completing the combination that carborundum isolates ester with macromolecule protection is tied
Structure layer, and kept for the drying time no less than 3 hours to realize that third time is brushed；On the basis of being brushed based on third time, complete
The brushing for the combination that brushing graphite isolates ester with macromolecule protection forms enhancement layer, and is kept for the drying time no less than 3 hours
To realize the 4th brushing.
In one of the embodiments, if described treat that protection body is concrete or Wood surface, wait to prevent to pretreated
Watch box complete to brush three times by the way of round brush including：Protection body brushing macromolecule protection isolation ester is treated to pretreated,
Basis of formation layer, and kept for the drying time no less than 4 hours brushed for the first time to realize.
Further, to it is pretreated treat protection body complete to brush three times by the way of round brush including：Based on first
On the basis of secondary brushing, the brushing that graphite isolates the combination of ester with macromolecule protection is completed, forms structure sheaf, and keep being no less than
The drying time of 3 hours is to realize second of brushing；On the basis of being brushed based on second, macromolecule protection isolation ester is completed
Brush, form enhancement layer, and kept for the drying time no less than 3 hours to realize that third time is brushed.
It should be noted that armouring anti-corrosion protective mechanism is implanted into Organic fluoride 201, organosilicon 202 in the main chain 200 of resin.
Specifically, as shown in Fig. 2 the fluorine silicon resin of macromolecular is degraded into small molecule in order to permeate, then passed through based on fluorine silicon resin
Active gene 204 adds isocyanates (NCO) group 203 plus activity, then pre-buried catalyst, can quickly hand in atmosphere
Connection reaction forms interpenetrating networks (PIN) and solidified.I.e. it includes basal layer, structure sheaf and enhancement layer.Basal layer is with active
The matrix protective layer of the rust inactivator conversion of ion, structure sheaf are embedded carborundum and macromolecule protection isolation ester perfect combinations
Separation layer, enhancement layer are that graphite isolates the protective layer that the combination of ester prevents the external world from corroding with macromolecule protection.
In summary, method proposed by the present invention is macromolecule protection isolation ester and the organic knot of rust inactivator with rust antirust
Close, be a kind of brand-new construction process, construction process can be increased and decreased according to the operating mode of anti-corrosion medium.With following characteristic：Apply
Work technique is simple, not high to environmental requirement, can be combined with matrix strength, good toughness, not expanded with heat and contract with cold and ftractureed by matrix,
With good fire resistance；Used by this flow and method product contain it is homemade there is wetting and infiltration function material, can be with
Penetrate into inside rusty scale, form parcel, while can also carry rust inactivator, it is reacted with rust, make reaction than conventional method more
Add thoroughly；Used by this flow and method product contain acidic materials can well with unstable iron rust composition (γ-
Fe2O3) react, convert it into complex steady in a long-term, rust inactivator can carry out complex reaction again to rust and form stabilization
Compound, play dual rust transformation function；Contained organic compound resin in product used by this flow and method, in homemade tool
Have under wetting and the effect of infiltration function material, closely combined with iron rust, the iron rust material for inactivator conversion of becoming rusty is wrapped up, after solidification
Row prevents the generation of corrosion reaction into stable coating；All resin components of product finally all enter used by this flow and method
Row crosslinking, forms three-dimensional-structure, has good sealing process, prevent the intrusion of water and corrosive deposit, reach anti-corrosion purpose.
A kind of armouring anti-corrosion process for protecting method provided by the invention, treats protection body and is pre-processed；After pretreatment
Treat that protection body is completed repeatedly to brush by the way of round brush, and after multiple brush, keep drying time not less than 7 days with
Realize that armouring anti-corrosion is protected.This method solve conventional art in work progress and after the completion of disaster hidden-trouble be present；Construction technology is numerous
It is trivial, environmental requirement is harsh, personnel qualifications are high；Easily leave cracking, play the defects of drum, anticorrosion ability is poor；Long construction period,
Pre-processed by treating protection body, and treat that protection body completes four brushings by the way of round brush to pretreated, and
After four times are brushed, kept for the drying time not less than 7 days to realize that armouring protects, there is the wide in range property of application, the letter used
Victory, high efficiency and flexibility.
Further, armouring anti-corrosion process for protecting method proposed by the present invention changes traditional pretreatment mode, solution
The problem of having determined inside active factors into rust, shortens the derusting duration；Unique armouring anti-corrosion process for protecting method, reduces rust
The motion of active factors；It is formulated using flake graphite, carborundum, quartz sand etc., strengthens the adhesive force of aging layer, with high-strength
Degree, high weather resisteant and wear-resistant feature；Flow and method is protected using armouring anti-corrosion, has prevented the condition of electrochemical corrosion, to gold
Belong to the protection that matrix implements armor formula in terms of physics and chemistry two to matrix.
Each technical characteristic of embodiment described above can be combined arbitrarily, to make description succinct, not to above-mentioned reality
Apply all possible combination of each technical characteristic in example to be all described, as long as however, the combination of these technical characteristics is not deposited
In contradiction, the scope that this specification is recorded all is considered to be.
Embodiment described above only expresses the several embodiments of the present invention, and its description is more specific and detailed, but simultaneously
Therefore the limitation to the scope of the claims of the present invention can not be interpreted as.It should be pointed out that for one of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect scope.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (10)
1. a kind of armouring anti-corrosion process for protecting method, including：
Protection body is treated to be pre-processed；
To it is pretreated it is described treat that protection body is completed repeatedly to brush by the way of round brush, and after multiple brush, keep not
Drying time less than 7 days is to realize that armouring anti-corrosion is protected.
2. according to the method for claim 1, wherein, described to treat that protection body is metal, the pretreatment includes：To the gold
The surface of category by corrosion, stick up skin, come off and complete grinding process, greasy dirt or other chemicals caused by metal covering attachment are completed
Chemical treatment, and cleaned.
3. according to the method for claim 2, wherein, described repeatedly brush includes：Described protection body is treated to pretreated
Rust inactivator, basis of formation layer are brushed, and is kept for the drying time no less than 4 hours brushed for the first time to realize.
4. according to the method for claim 3, wherein, described repeatedly brush also includes：The base brushed based on the first time
On plinth, brushing macromolecule protection isolation ester, and kept for the drying time no less than 3 hours realize second of brushing.
5. according to the method for claim 4, wherein, described repeatedly brush also includes：Based on second of base brushed
On plinth, the brushing for completing the combination that carborundum isolates ester with macromolecule protection forms structure sheaf, and keeps dry no less than 3 hours
The dry time is brushed for the third time with realizing.
6. according to the method for claim 5, wherein, described repeatedly brush also includes：Base based on the third time brushing
On plinth, the brushing for completing the combination that brushing graphite isolates ester with macromolecule protection forms enhancement layer, and keeps no less than 3 hours
Drying time is brushed with realizing the 4th time.
7. according to the method for claim 1, wherein, described to treat that protection body is concrete, the pretreatment includes：To coagulation
Native surface is handled the dust of cement-based surface, dirt completion by giant or sandblasting mode, then is repaiied by mica cream ester
Plug a hole and crackle, rear polishing to be dried are round and smooth；Or
Described to treat that protection body is Wood surface, the pretreatment includes：Wood surface dirt, dust are removed by sand paper, if
There is oil stain on surface, and the scouring of surface and oil contaminant is completed with No. 200 gasoline.
8. according to the method for claim 7, wherein, described repeatedly brush includes：Described wait to prevent to pretreated
Watch box brushing macromolecule protection isolation ester, basis of formation layer, and kept for the drying time no less than 4 hours applied for the first time to realize
Brush.
9. according to the method for claim 8, wherein, described repeatedly brush includes：The basis brushed based on the first time
On, the brushing that graphite isolates the combination of ester with macromolecule protection is completed, forms structure sheaf, and keep the drying no less than 3 hours
Time is to realize second of brushing.
10. according to the method for claim 9, wherein, described repeatedly brush includes：Based on second of basis brushed
On, the brushing of macromolecule protection isolation ester is completed, forms enhancement layer, and is kept for the drying time no less than 3 hours to realize the
Brush three times.