CN107476123A - A kind of high-flatness minute surface transfer paper - Google Patents
A kind of high-flatness minute surface transfer paper Download PDFInfo
- Publication number
- CN107476123A CN107476123A CN201710518705.6A CN201710518705A CN107476123A CN 107476123 A CN107476123 A CN 107476123A CN 201710518705 A CN201710518705 A CN 201710518705A CN 107476123 A CN107476123 A CN 107476123A
- Authority
- CN
- China
- Prior art keywords
- flatness
- minute surface
- layer
- transfer paper
- surface transfer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-flatness minute surface transfer paper, including original paper layer, is coated with priming coat in the front of original paper layer, chemical industry composite coating is provided with priming coat；The back side of original paper layer is provided with PVA emulsion layers；Priming coat is aqueous acrylic emulsion layer, and chemical industry composite coating is aqueous acrylic modified polyaminoester emulsion layer.The high-flatness minute surface transfer paper of the present invention, product minute surface flatness is good, suitable for high glaze label, cigarette bag prints, the high-grade printing packaging product such as advanced picture album, also Compound Machining can be further carried out with various membrane materials and forms high saturating packaging material, manufacture craft is simple, low manufacture cost, has wide market prospects.
Description
Technical field
The present invention relates to a kind of high-flatness minute surface transfer paper.
Background technology
Traditional minute surface paperboard carries out supercalendering again after casting painting is carried out on the basis of common art post paperboard more, passes through bloom
Bright minute surface smooth roll grinds mirror effect, the complex manufacturing technology of this minute surface paperboard, although product flatness and mirror effect are all
Well, but the coating content used in casting applies is big, and poor performance causes that the surface folding of minute surface paperboard is poor, and brightness is general.
The content of the invention
The technical problem to be solved in the present invention is to overcome minute surface paperboard surface folding in the prior art poor, brightness in general
A kind of defect, there is provided high-flatness minute surface transfer paper.
In order to solve the above-mentioned technical problem, the invention provides following technical scheme：
A kind of high-flatness minute surface transfer paper of the present invention, including original paper layer, bottom is coated with the front of the original paper layer
Coating, chemical industry composite coating is provided with priming coat；The back side of the original paper layer is provided with PVA emulsion layers；The primary coat
Layer is aqueous acrylic emulsion layer, and the chemical industry composite coating is aqueous acrylic modified polyaminoester emulsion layer.
Preferably, in the priming coat, 3~5 grams every square metre of the coating weight of aqueous acrylic emulsion.
Further, in the chemical industry composite coating, 4~7 grams of the coating weight of aqueous acrylic modified polyaminoester emulsion
Every square metre.
Further, in the PVA emulsion layers, the coating weight of PVA emulsions is 3~5 grams every square metre.
Further, the original paper layer is weight in the every square meters of 28~400g, body paper of the water content 3.0~5.0%.
The making step of high-flatness minute surface transfer paper of the present invention is：
1), body paper surface painting bottom coating is pre-processed；
A good aqueous acrylic emulsion of laminar flow levelling is coated with former recto by three roller coat glue modes, is coated with
Measure as 3~5 grams every square metre；
2), chemical industry composite coating is formed in base coating surface；
First, one layer of good brightness, the good height of printability are coated with highlighted PET light films by 200# ceramic anilox roller
Bright chemical industry compounded chemical coating, in the chemical industry compounded chemical coating, the coating of aqueous acrylic modified polyaminoester emulsion
4~7 grams every square metre of amount；Then this is highlighted into PET light film and the body paper progress in step 1) is compound so that the shape on priming coat
Into chemical industry compounded chemical coating；
3), in the backsize PVA emulsion layers of body paper：
It is coated with the back side of body paper by steel rider in one layer of PVA emulsion layer, the coating weight of PVA emulsions is 3~5 grams every square
Rice；
4), drying process
At 70 DEG C -110 DEG C, the drying time 10-15 seconds；
5) highlighted PET light films, are peeled off
Line peels off highlighted PET light films after drying, produces.The highlighted PET light film stripped down can recycle more than ten
It is secondary, cost can be not only saved, also can be energy-saving very well.
The beneficial effect that is reached of the present invention is：The high-flatness minute surface transfer paper of the present invention, product minute surface flatness is good,
Suitable for high-grade printing packaging product such as high glaze label, the printing of cigarette bag, advanced pictures album, further can also be answered with various membrane materials
Close processing and form high saturating packaging material, manufacture craft is simple, low manufacture cost, has wide market prospects.
Brief description of the drawings
Accompanying drawing is used for providing a further understanding of the present invention, and a part for constitution instruction, the reality with the present invention
Apply example to be used to explain the present invention together, be not construed as limiting the invention.In the accompanying drawings：
Fig. 1 is the structural representation of the present invention.
Embodiment
The preferred embodiments of the present invention are illustrated below in conjunction with accompanying drawing, it will be appreciated that described herein preferred real
Apply example to be merely to illustrate and explain the present invention, be not intended to limit the present invention.
Embodiment 1
As shown in figure 1, a kind of high-flatness minute surface transfer paper, including original paper layer 1, the weight of original paper layer 1 are often to be put down in 28g
Rice, body paper of the water content 3.0% are coated with priming coat 2 in the front of original paper layer 1, and it is compound to be provided with chemical industry on priming coat 2
Coating 3；PVA emulsion layers 4 are provided with the back side of original paper layer 1, the coating weight of PVA emulsions is 3 grams every square metre；Priming coat 2 is
Aqueous acrylic emulsion layer, 3 grams every square metre of the coating weight of aqueous acrylic emulsion；Chemical industry composite coating 3 is water soluble acrylic acid
Modified polyaminoester emulsion layer, 7 grams every square metre of coating weight.
Embodiment 2
As shown in figure 1, a kind of high-flatness minute surface transfer paper, including original paper layer 1, the weight of original paper layer 1 are often put down for 400g
Rice, body paper of the water content 5.0% are coated with priming coat 2 in the front of original paper layer 1, and it is compound to be provided with chemical industry on priming coat 2
Coating 3；PVA emulsion layers 4 are provided with the back side of original paper layer 1, the coating weight of PVA emulsions is 5 grams every square metre；Priming coat 2 is
Aqueous acrylic emulsion layer, 5 grams every square metre of the coating weight of aqueous acrylic emulsion；Chemical industry composite coating 3 is water soluble acrylic acid
Modified polyaminoester emulsion layer, 4 grams every square metre of coating weight.
Embodiment 3
As shown in figure 1, a kind of high-flatness minute surface transfer paper, including original paper layer 1, original paper layer 1 are that weight is that 200g is often put down
Rice, body paper of the water content 4.0% are coated with priming coat 2 in the front of original paper layer 1, and it is compound to be provided with chemical industry on priming coat 2
Coating 3；PVA emulsion layers 4 are provided with the back side of original paper layer 1, the coating weight of PVA emulsions is 4 grams every square metre；Priming coat 2 is
Aqueous acrylic emulsion layer, 4 grams every square metre of the coating weight of aqueous acrylic emulsion；Chemical industry composite coating 3 is water soluble acrylic acid
Modified polyaminoester emulsion layer, 6 grams every square metre of coating weight.
Finally it should be noted that：The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention,
Although the present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art, it still may be used
To be modified to the technical scheme described in foregoing embodiments, or equivalent substitution is carried out to which part technical characteristic.
Within the spirit and principles of the invention, any modification, equivalent substitution and improvements made etc., it should be included in the present invention's
Within protection domain.
Claims (5)
1. a kind of high-flatness minute surface transfer paper, it is characterised in that including original paper layer, bottom is coated with the front of the original paper layer
Coating, chemical industry composite coating is provided with priming coat；The back side of the original paper layer is provided with PVA emulsion layers；The primary coat
Layer is aqueous acrylic emulsion layer, and the chemical industry composite coating is aqueous acrylic modified polyaminoester emulsion layer.
A kind of 2. high-flatness minute surface transfer paper as claimed in claim 1, it is characterised in that in the priming coat, water-based third
3~5 grams every square metre of the coating weight of olefin(e) acid emulsion.
A kind of 3. high-flatness minute surface transfer paper as claimed in claim 1, it is characterised in that in the chemical industry composite coating,
4~7 grams every square metre of the coating weight of aqueous acrylic modified polyaminoester emulsion.
A kind of 4. high-flatness minute surface transfer paper as claimed in claim 1, it is characterised in that in the PVA emulsion layers, PVA
The coating weight of emulsion is 3~5 grams every square metre.
5. a kind of high-flatness minute surface transfer paper as claimed in claim 1, it is characterised in that the original paper layer is weight 28
~400g is per square meter, body paper of the water content 3.0~5.0%.