CN107473596A - Sliding door of bathroom knock-sedative dope and preparation method thereof - Google Patents
Sliding door of bathroom knock-sedative dope and preparation method thereof Download PDFInfo
- Publication number
- CN107473596A CN107473596A CN201710634503.8A CN201710634503A CN107473596A CN 107473596 A CN107473596 A CN 107473596A CN 201710634503 A CN201710634503 A CN 201710634503A CN 107473596 A CN107473596 A CN 107473596A
- Authority
- CN
- China
- Prior art keywords
- parts
- knock
- bathroom
- sliding door
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Sliding door of bathroom knock-sedative dope, is related to field of glass production technology, is prepared from the following components:EVA films, silicon sand, soda ash, sodium carbonate, potassium carbonate, lime, alum clay, manganese dioxide, selenium, cobalt oxide, bromine oxide, sodium oxide molybdena, softened water, sodium tetraborate, toothpaste, Te Jila wine and anti-knock agent.Explosion-proof effect of the present invention is obvious, can resist the critical conditions such as humidity, high temperature, cold, and reduces probability and the reduction glass explosive spalling damages degree that glass bursts, and reduces the chip size after explosion, prevents from causing human body unnecessary injury.
Description
Technical field:
The present invention relates to clearing glass production technical field, and in particular to a kind of sliding door of bathroom knock-sedative dope and its system
Preparation Method.
Background technology:
Glass have the advantages that smooth, transparent, hardness is high, reasonable price and be widely used in the doors such as building and automobile
On window.In daily life because the glass types project used is various, therefore various type of glass are all operated and formed, according to property
It is firm that some different glass of energy need penetrating, some glass to need, wherein the glass door used in bathroom is due in bathroom
Environment rather harsh, therefore need to carry out corresponding technological processing for explosion protection feature for this kind of glass, this patent is just to provide a kind of bathroom
Glass door knock-sedative dope, good explosion-proof work can be played to glass door by being added thereto when glass door production is carried out
With.
The content of the invention:
The technical problems to be solved by the invention are to provide a kind of explosion-proof effect obvious, can resist humidity, high temperature, cold
The critical conditions such as cold, and reduce probability that glass bursts and reduce the sliding door of bathroom of glass explosive spalling damages degree and use
Knock-sedative dope and preparation method thereof.
The technical problems to be solved by the invention are realized using following technical scheme:
Sliding door of bathroom knock-sedative dope, is prepared from the following components:EVA films, silicon sand, soda ash, sodium carbonate,
Potassium carbonate, lime, alum clay, manganese dioxide, selenium, cobalt oxide, bromine oxide, sodium oxide molybdena, softened water, sodium tetraborate, toothpaste, Te Jila
Wine and anti-knock agent;
The anti-knock agent is prepared from the following components:Galvanizing anti-knock agent, ethanol, explosion-proof fiber, zinc naphthenate, castor-oil plant
Oil, deionized water are prepared;
Above-mentioned sliding door of bathroom is with the mass fraction of each group of knock-sedative dope:EVA film 20-30 parts, silicon sand 80-90
Part, soda ash 30-40 parts, sodium carbonate 40-50 parts, potassium carbonate 20-30 parts, lime 5-10 parts, alum clay 3-8 parts, manganese dioxide 5-8
Part, selenium 8-10 parts, cobalt oxide 3-5 parts, bromine oxide 4-6 parts,
Sodium oxide molybdena 3-9 parts, softened water 1-10 parts, sodium tetraborate 3-9 parts, toothpaste 20-50 parts, Te Jila wine 3-9 parts and anti-
Detonator 5-10 parts;
Anti-knock agent described above is prepared by the component of following mass fraction:Galvanizing anti-knock agent 0.1-0.3 parts, ethanol
1-3 parts, explosion-proof fiber 0.5-1 parts, zinc naphthenate 3-5 parts, castor oil 8-10 parts, deionized water 10-15 parts;
Further technology, above-mentioned sliding door of bathroom is with the toothpaste in the component of knock-sedative dope using preceding carrying out at refrigeration
Reason, refrigerated storage temperature are set as 3-5 DEG C, after refrigerating 20 minutes, add light-coloured vinegar and are at the uniform velocity stirred, carried out again after stirring cold
Hide, wherein the addition of light-coloured vinegar is the 2-3% of toothpaste quality;
Above-mentioned sliding door of bathroom is with the preparation method of knock-sedative dope:
(1) silicon sand, soda ash, sodium carbonate, potassium carbonate, lime, alum clay are pulverized, then add manganese dioxide, selenium,
Cobalt oxide, bromine oxide, sodium oxide molybdena, softened water, sodium tetraborate uniformly mix, stirring, and just liquid is made;
(2) by just liquid is mixed evenly after the fusing stirring of EVA films;
(3) toothpaste and Te Jila wine are added sequentially in the mixed liquor in step 2, then set mixed liquor feeding microwave
Standby middle carry out microwave treatment;
(4) mixed liquor after microwave treatment is mixed with anti-knock agent, is then fed into Centrifugal dispersion 10-12 in centrifugal blender
Minute;
(5) mixed liquor is stood into 3-5 hours after the completion of disperseing, you can use, so far sliding door of bathroom knock-sedative dope
Prepare and complete;
Further technology, the microwave treatment in the step 3, using intermediate frequency microwave treatment 30-35S;
Further technology, environment temperature is set as 3-5 DEG C when being stood to mixed liquor in the step 5;
Castor oil is with the addition of in anti-knock agent simultaneously, can also increase the explosion-proof capabilities of anti-knock agent, and pass through ethanol, hot dip
The use of zinc anti-knock agent etc. can improve the wellability of glass surface, reduce the tension force of glass, improve explosion-proof capabilities;
After sliding door of bathroom knock-sedative dope is prepared for using the above method, glass life is carried out using the additive
Production, and the explosion-proof capabilities of glass are tested, laboratory is contrasted respectively using three groups of glass, and relevant experimental data is shown in
Following table:
With reference to upper table understand the beneficial effects of the invention are as follows:Explosion-proof effect is obvious, can resist humidity, high temperature, cold etc.
Critical conditions, and reduce probability and reduce glass explosive spalling damages degree that glass bursts, and after reducing explosion
Chip size, prevent from causing human body unnecessary injury.
Embodiment:
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific example is closed, the present invention is expanded on further.
Embodiment 1:
Sliding door of bathroom knock-sedative dope, is prepared from the following components:EVA films, silicon sand, soda ash, sodium carbonate,
Potassium carbonate, lime, alum clay, manganese dioxide, selenium, cobalt oxide, bromine oxide, sodium oxide molybdena, softened water, sodium tetraborate, toothpaste, Te Jila
Wine and anti-knock agent;
The anti-knock agent is prepared from the following components:Galvanizing anti-knock agent, ethanol, explosion-proof fiber, zinc naphthenate, castor-oil plant
Oil, deionized water are prepared;
Above-mentioned sliding door of bathroom is with the mass fraction of each group of knock-sedative dope:20 parts of EVA films, 80 parts of silicon sand, Soviet Union
Beat 30 parts of ash, 40 parts of sodium carbonate, 20 parts of potassium carbonate, 5 parts of lime, 3 parts of alum clay, 5 parts of manganese dioxide, 8 parts of selenium, 3 parts of cobalt oxide, oxygen
Change 5 parts of 4 parts of bromine, sodium oxide molybdena 3,1 part of softened water, 3 parts of sodium tetraborate, 20 parts of toothpaste, 3 parts of Te Jila wine and anti-knock agent;
Anti-knock agent described above is prepared by the component of following mass fraction:0.1 part of galvanizing anti-knock agent, 1 part of ethanol,
0.5 part of explosion-proof fiber, 3 parts of zinc naphthenate, 8 parts of castor oil, 10 parts of deionized water;
Further technology, above-mentioned sliding door of bathroom is with the toothpaste in the component of knock-sedative dope using preceding carrying out at refrigeration
Reason, refrigerated storage temperature are set as 3 DEG C, after refrigerating 20 minutes, add light-coloured vinegar and are at the uniform velocity stirred, carried out again after stirring cold
Hide, wherein the addition of light-coloured vinegar is the 2% of toothpaste quality;
Above-mentioned sliding door of bathroom is with the preparation method of knock-sedative dope:
(1) silicon sand, soda ash, sodium carbonate, potassium carbonate, lime, alum clay are pulverized, then add manganese dioxide, selenium,
Cobalt oxide, bromine oxide, sodium oxide molybdena, softened water, sodium tetraborate uniformly mix, stirring, and just liquid is made;
(2) by just liquid is mixed evenly after the fusing stirring of EVA films;
(3) toothpaste and Te Jila wine are added sequentially in the mixed liquor in step 2, then set mixed liquor feeding microwave
Standby middle carry out microwave treatment;
(4) mixed liquor after microwave treatment is mixed with anti-knock agent, is then fed into Centrifugal dispersion 10 in centrifugal blender and divides
Clock;
(5) mixed liquor is stood 3 hours after the completion of disperseing, you can use, so far sliding door of bathroom knock-sedative dope system
It is standby to complete;
Embodiment 2:
Sliding door of bathroom knock-sedative dope, is prepared from the following components:EVA films, silicon sand, soda ash, sodium carbonate,
Potassium carbonate, lime, alum clay, manganese dioxide, selenium, cobalt oxide, bromine oxide, sodium oxide molybdena, softened water, sodium tetraborate, toothpaste, Te Jila
Wine and anti-knock agent;
The anti-knock agent is prepared from the following components:Galvanizing anti-knock agent, ethanol, explosion-proof fiber, zinc naphthenate, castor-oil plant
Oil, deionized water are prepared;
Above-mentioned sliding door of bathroom is with the mass fraction of each group of knock-sedative dope:30 parts of EVA films, 90 parts of silicon sand, Soviet Union
Beat ash 40 parts, 50 parts of sodium carbonate, 30 parts of potassium carbonate, 10 parts of lime, 8 parts of alum clay, 8 parts of manganese dioxide, 10 parts of selenium, 5 parts of cobalt oxide,
10 parts of 6 parts of bromine oxide, sodium oxide molybdena 9,10 parts of softened water, 9 parts of sodium tetraborate, 50 parts of toothpaste, 9 parts of Te Jila wine and anti-knock agent;
Anti-knock agent described above is prepared by the component of following mass fraction:0.3 part of galvanizing anti-knock agent, 3 parts of ethanol,
1 part of explosion-proof fiber, 5 parts of zinc naphthenate, 10 parts of castor oil, 15 parts of deionized water;
Further technology, above-mentioned sliding door of bathroom is with the toothpaste in the component of knock-sedative dope using preceding carrying out at refrigeration
Reason, refrigerated storage temperature are set as 5 DEG C, after refrigerating 20 minutes, add light-coloured vinegar and are at the uniform velocity stirred, carried out again after stirring cold
Hide, wherein the addition of light-coloured vinegar is the 3% of toothpaste quality;
Above-mentioned sliding door of bathroom is with the preparation method of knock-sedative dope:
(1) silicon sand, soda ash, sodium carbonate, potassium carbonate, lime, alum clay are pulverized, then add manganese dioxide, selenium,
Cobalt oxide, bromine oxide, sodium oxide molybdena, softened water, sodium tetraborate uniformly mix, stirring, and just liquid is made;
(2) by just liquid is mixed evenly after the fusing stirring of EVA films;
(3) toothpaste and Te Jila wine are added sequentially in the mixed liquor in step 2, then set mixed liquor feeding microwave
Standby middle carry out microwave treatment;
(4) mixed liquor after microwave treatment is mixed with anti-knock agent, is then fed into Centrifugal dispersion 12 in centrifugal blender and divides
Clock;
(5) mixed liquor is stood 5 hours after the completion of disperseing, you can use, so far sliding door of bathroom knock-sedative dope system
It is standby to complete.
Then it is respectively adopted embodiment 1 and after embodiment 2 is prepared for sliding door of bathroom knock-sedative dope, uses the addition
Agent carries out glass production, and the explosion-proof capabilities of glass are tested, and laboratory is contrasted respectively using three groups of glass, phase
Experimental data is closed to see the table below:
Table one:Embodiment 1
Classification | Explosion dynamics | Spalling degree | The size of explosion fragment |
One group | 350N | 28% | 2㎝ |
Two groups | 370N | 20% | 3㎝ |
Three groups | 400N | 25% | 2㎝ |
Table 2:Embodiment 2
Classification | Explosion dynamics | Spalling degree | The size of explosion fragment |
One group | 390N | 30% | 1㎝ |
Two groups | 380N | 24% | 2㎝ |
Three groups | 400N | 27% | 2㎝ |
By understanding that explosion-proof effect of the present invention is obvious to upper table analysis and summary, it is harsh that humidity, high temperature, cold etc. can be resisted
Condition, while castor oil is with the addition of in anti-knock agent, it can also increase the explosion-proof capabilities of anti-knock agent, and pass through ethanol, galvanizing
The use of anti-knock agent etc. can improve the wellability of glass surface, reduce the tension force of glass, improve explosion-proof capabilities, and reduce glass
The probability and reduce glass explosive spalling damages degree that glass bursts, and reduce the chip size after explosion, prevent to human body
Cause unnecessary injury.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (8)
1. sliding door of bathroom knock-sedative dope, it is characterised in that:It is prepared from the following components:EVA films, silicon sand, soda
Ash, sodium carbonate, potassium carbonate, lime, alum clay, manganese dioxide, selenium, cobalt oxide, bromine oxide, sodium oxide molybdena, softened water, sodium tetraborate,
Toothpaste, Te Jila wine and anti-knock agent.
2. sliding door of bathroom knock-sedative dope according to claim 1, it is characterised in that:By following components preparation
Into:Galvanizing anti-knock agent, ethanol, explosion-proof fiber, zinc naphthenate, castor oil, deionized water are prepared.
3. sliding door of bathroom knock-sedative dope according to claim 1, it is characterised in that:The mass fraction of each group is:
EVA film 20-30 parts, silicon sand 80-90 parts, soda ash 30-40 parts, sodium carbonate 40-50 parts, potassium carbonate 20-30 parts, lime 5-10
Part, alum clay 3-8 parts, manganese dioxide 5-8 parts, selenium 8-10 parts, cobalt oxide 3-5 parts, bromine oxide 4-6 parts, sodium oxide molybdena 3-9 parts, softening
Water 1-10 parts, sodium tetraborate 3-9 parts, toothpaste 20-50 parts, Te Jila wine 3-9 parts and anti-knock agent 5-10 parts.
4. sliding door of bathroom knock-sedative dope according to claim 1, it is characterised in that:Galvanizing anti-knock agent 0.1-
0.3 part, ethanol 1-3 parts, explosion-proof fiber 0.5-1 parts, zinc naphthenate 3-5 parts, castor oil 8-10 parts, deionized water 10-15 parts.
5. the sliding door of bathroom knock-sedative dope according to claim 1 or 3, it is characterised in that:Sliding door of bathroom is used anti-
Toothpaste in the component of quick-fried additive carries out chilling treatment before use, and refrigerated storage temperature is set as 3-5 DEG C, after refrigerating 20 minutes,
Add light-coloured vinegar at the uniform velocity to be stirred, refrigerated again after stirring, wherein the addition of light-coloured vinegar is the 2- of toothpaste quality
3%.
6. the preparation method of sliding door of bathroom knock-sedative dope, it is characterised in that:Comprise the following steps:
Above-mentioned sliding door of bathroom is with the preparation method of knock-sedative dope:
(1) silicon sand, soda ash, sodium carbonate, potassium carbonate, lime, alum clay are pulverized, then adds manganese dioxide, selenium, oxidation
Cobalt, bromine oxide, sodium oxide molybdena, softened water, sodium tetraborate uniformly mix, stirring, and just liquid is made;
(2) by just liquid is mixed evenly after the fusing stirring of EVA films;
(3) toothpaste and Te Jila wine are added sequentially in the mixed liquor in step 2, then mixed liquor is sent into microwave equipment
Carry out microwave treatment;
(4) mixed liquor after microwave treatment is mixed with anti-knock agent, is then fed into centrifugal blender Centrifugal dispersion 10-12 points
Clock;
(5) mixed liquor is stood into 3-5 hours after the completion of disperseing, you can use, so far sliding door of bathroom is prepared with knock-sedative dope
Complete.
7. the preparation method of sliding door of bathroom knock-sedative dope according to claim 7, it is characterised in that:The step
Microwave treatment in 3, using intermediate frequency microwave treatment 30-35S.
8. the preparation method of sliding door of bathroom knock-sedative dope according to claim 7, it is characterised in that:The step
Environment temperature is set as 3-5 DEG C when being stood in 5 to mixed liquor.