CN107471364B - A kind of preparation method of Mothproof veneer board - Google Patents
A kind of preparation method of Mothproof veneer board Download PDFInfo
- Publication number
- CN107471364B CN107471364B CN201710716600.1A CN201710716600A CN107471364B CN 107471364 B CN107471364 B CN 107471364B CN 201710716600 A CN201710716600 A CN 201710716600A CN 107471364 B CN107471364 B CN 107471364B
- Authority
- CN
- China
- Prior art keywords
- veneer
- insect
- adhesive
- prevention treatment
- treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention belongs to glued board processing technique fields, more particularly to a kind of preparation method of Mothproof veneer board, including veneer insect-prevention treatment and adhesive insect-prevention treatment, wherein veneer insect-prevention treatment includes that treatment fluid dipping and acid treated paulownia wood are stifling, and the insect-prevention treatment mode of adhesive is that the composite particles with vermins-proof effect are added in adhesive.The present invention has the advantage that glued board prepared by the present invention can resist termite and rot fungi well compared with prior art, moreover it is possible to improve the corrosion resistance of veneer, vermins-proof effect persistence is good, extends the service life of glued board.
Description
Technical field
The invention belongs to glued board processing technique fields, and in particular to a kind of preparation method of Mothproof veneer board.
Background technique
Glued board is an important board kind in wood-based plate, and since glued board has, deformation is small, breadth is big, construction is inconvenient, no
Easy warpage, the features such as tensile strength perpendicular to grain is big, obtain extensively in furniture, compartment, shipbuilding, military project, packaging and other industrial departments
Using, but since glued board is a kind of wood materials, easily by bacterium, worm, the raw drilling worm invasion in sea, it is easy to rot, so common glue
The corrosion resistance of plywood is not high, and pest-resistant performance is poor, is restricted in use, therefore, carries out preservative treatment right and wrong to glued board
It is often necessary, with constantly improve for glued board processing technology, chemical agent is generallyd use in the prior art, glued board is carried out
Preservative treatment plays antisepsis although infringement of the microorganism to timber can be effectively prevented, these preservatives are to environment
Safety and health of human body have a certain impact, and the use of part material is gradually restricted or forbids, therefore low toxicity is efficient simultaneously
It is to need the technical issues of researching and solving at present that antisepsis, which can be played, to glued board.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of preparation method of Mothproof veneer board is provided.
The present invention is achieved by the following technical solutions: a kind of preparation method of Mothproof veneer board, including veneer insect prevention
Processing and adhesive insect-prevention treatment, the veneer with a thickness of 0.6-2mm, water content 10-12%, the side of veneer insect-prevention treatment
Method are as follows: veneer is immersed in treatment fluid, includes 2-4g hydrogen peroxide, 0.7-1.5g fraxinellone in every 100ml treatment fluid, in vacuum condition
Then lower dipping 1.5-2 hours is forced into 0.6-0.8MPa and is kept for 30-40 minutes, taking out drying to water content is 5-8%, then
Handle 25-30 minute in stifling drying oven, fumigates in drying oven sootiness material as sour treated paulownia wood;
The insect-prevention treatment mode of the adhesive is that the composite particles for being equivalent to its weight 4-7% are added in adhesive, institute
State composite particles the preparation method comprises the following steps: fraxinellone, carbon nanotube and polyvinyl alcohol are mixed with weight ratio 5:9:1, then will mixing
Material ultrasonic disperse in the ethanol solution that the mass concentration for being equivalent to 3 times of its weight is 40-50% is 450-500 DEG C in temperature
Under conditions of be spray-dried, it is composite particles that obtain partial size, which be 10-50 μm of powder,.
As further improvement of these options, the vacuum condition is that vacuum degree reaches -0.04 ~ -0.12MPa.
As further improvement of these options, the drying condition is that temperature is 60-80 DEG C, relative humidity 90-
95%。
As further improvement of these options, acid treated the paulownia wood volume is not more than 1.8cm3;Processing
Method is to be dried to paulownia wood after water content is 15% or less, in the sulfuric acid solution that mass concentration is 8-10% in ultrasonic oscillation
Under conditions of handle 6-8 minutes, be rinsed with water after the completion 10 minutes, be dried to water content be 6-8%.
As further improvement of these options, the treatment conditions of the stifling drying oven are as follows: furnace pressure 0.14-
0.18MPa, vapor (steam) temperature are 140-160 DEG C.
As further improvement of these options, the adhesive is by phenolic resin and flour with weight ratio 7:2-3 group
At.
The present invention has the advantage that in the present invention veneer through treatment fluid under negative pressure to pressurized conditions compared with prior art
Processing, can be such that insect-prevention treatment liquid is effectively immersed in veneer, then by acid treated paulownia wood suffocating treatment, can make veneer surface
Wood fibre structure changes, and when by multilayer single plate adhesive hot-press gluing, adhesive intermediate ion and veneer ion can be made abundant
It engages and puts to good use, prevent the loss of insect-prevention treatment liquid in veneer in use process, composite particles can be uniformly dispersed in viscose
In agent, termite and rot fungi can be resisted well, moreover it is possible to improve the corrosion resistance of veneer, vermins-proof effect persistence is good, extends
The service life of glued board.
Specific embodiment
Embodiment 1
A kind of preparation method of Mothproof veneer board, including veneer insect-prevention treatment and adhesive insect-prevention treatment, the veneer
With a thickness of 1.2mm, water content 11%;
The method of veneer insect-prevention treatment are as follows: will veneer immerse treatment fluid in, in every 100ml treatment fluid comprising 3g hydrogen peroxide,
1.2g fraxinellone impregnates 1.8 hours under vacuum conditions, is then forced into 0.7MPa and is kept for 35 minutes, takes out dry to water content
It is 6%, then handle 28 minutes in stifling drying oven, fumigating sootiness material in drying oven is sour treated paulownia wood;
The insect-prevention treatment mode of the adhesive is that the composite particles for being equivalent to its weight 6% are added in adhesive, described
Composite particles the preparation method comprises the following steps: Jiang fraxinellone, carbon nanotube and polyvinyl alcohol with weight ratio 5:9:1 mix, then by mixture
The ultrasonic disperse in the ethanol solution that the mass concentration for being equivalent to 3 times of its weight is 45% is expected, under conditions of temperature is 480 DEG C
Spray drying, obtaining the powder that partial size is 10-50 μm is composite particles.
Wherein, the vacuum condition is that vacuum degree reaches -0.08MPa;The drying condition is that temperature is 70 DEG C, relatively wet
Degree is 92%;The adhesive is made of phenolic resin and flour with weight ratio 7:2.
Wherein, acid treated the paulownia wood volume is not more than 1.8cm3;Processing method is to be dried to paulownia wood to contain
After water is 15% or less, processing 6 minutes under conditions of the sulfuric acid solution that mass concentration is 9% is in ultrasonic oscillation, after the completion
It is rinsed with water 10 minutes, being dried to water content is 7%.
Wherein, the treatment conditions of the stifling drying oven are as follows: furnace pressure 0.16MPa, vapor (steam) temperature are 150 DEG C.
Embodiment 2
A kind of preparation method of Mothproof veneer board, including veneer insect-prevention treatment and adhesive insect-prevention treatment, the veneer
With a thickness of 1.2mm, water content 10%;
The method of veneer insect-prevention treatment are as follows: will veneer immerse treatment fluid in, in every 100ml treatment fluid comprising 2g hydrogen peroxide,
1.5g fraxinellone impregnates 1.5 hours under vacuum conditions, is then forced into 0.6MPa and is kept for 30 minutes, takes out dry to water content
It is 5%, then handle 25 minutes in stifling drying oven, fumigating sootiness material in drying oven is sour treated paulownia wood;
The insect-prevention treatment mode of the adhesive is that the composite particles for being equivalent to its weight 4% are added in adhesive, described
Composite particles the preparation method comprises the following steps: Jiang fraxinellone, carbon nanotube and polyvinyl alcohol with weight ratio 5:9:1 mix, then by mixture
The ultrasonic disperse in the ethanol solution that the mass concentration for being equivalent to 3 times of its weight is 40% is expected, under conditions of temperature is 450 DEG C
Spray drying, obtaining the powder that partial size is 10-50 μm is composite particles.
Wherein, the vacuum condition is that vacuum degree reaches -0.04MPa;The drying condition is that temperature is 60 DEG C, relatively wet
Degree is 95%;The adhesive is made of phenolic resin and flour with weight ratio 7:2.
Wherein, acid treated the paulownia wood volume is not more than 1.8cm3;Processing method is to be dried to paulownia wood to contain
After water is 15% or less, processing 6 minutes under conditions of the sulfuric acid solution that mass concentration is 8% is in ultrasonic oscillation, after the completion
It is rinsed with water 10 minutes, being dried to water content is 6%.
Wherein, the treatment conditions of the stifling drying oven are as follows: furnace pressure 0.18MPa, vapor (steam) temperature are 140 DEG C.
Embodiment 3
A kind of preparation method of Mothproof veneer board, including veneer insect-prevention treatment and adhesive insect-prevention treatment, the veneer
With a thickness of 1.2mm, water content 12%;
The method of veneer insect-prevention treatment are as follows: will veneer immerse treatment fluid in, in every 100ml treatment fluid comprising 4g hydrogen peroxide,
0.7g fraxinellone impregnates 2 hours under vacuum conditions, is then forced into 0.8MPa and is kept for 40 minutes, takes out drying to water content and is
8%, then handle 30 minutes in stifling drying oven, fumigating sootiness material in drying oven is sour treated paulownia wood;
The insect-prevention treatment mode of the adhesive is that the composite particles for being equivalent to its weight 7% are added in adhesive, described
Composite particles the preparation method comprises the following steps: Jiang fraxinellone, carbon nanotube and polyvinyl alcohol with weight ratio 5:9:1 mix, then by mixture
The ultrasonic disperse in the ethanol solution that the mass concentration for being equivalent to 3 times of its weight is 50% is expected, under conditions of temperature is 500 DEG C
Spray drying, obtaining the powder that partial size is 10-50 μm is composite particles.
Wherein, the vacuum condition is that vacuum degree reaches -0.12MPa;The drying condition is that temperature is 80 DEG C, relatively wet
Degree is 90%;The adhesive is made of phenolic resin and flour with weight ratio 7:3.
Wherein, acid treated the paulownia wood volume is not more than 1.8cm3;Processing method is to be dried to paulownia wood to contain
After water is 15% or less, processing 8 minutes under conditions of the sulfuric acid solution that mass concentration is 10% is in ultrasonic oscillation, after the completion
It is rinsed with water 10 minutes, being dried to water content is 8%.
Wherein, the treatment conditions of the stifling drying oven are as follows: furnace pressure 0.14MPa, vapor (steam) temperature are 160 DEG C.
Control group 1 is set, treatment fluid Zhong fraxinellone in embodiment 1 is removed, remaining content is constant;Control group 2 is set, it will be real
The part for applying stifling drying oven processing in example 1 is removed, remaining content is constant;Control group 3 is set, sootiness material in embodiment 1 is replaced
It is changed to without acid treated paulownia wood, remaining content is constant;Control group 4 is set, composite particles in embodiment 1 are replaced with
Weight fraxinellone, remaining content are constant;Control group 5 is set, without the glued board of contents processing in embodiment 1;
Setting experiment, conventionally by 5 pieces of veneer hot pressing, the veneer is obtained by log through peeling, rotary-cut, respectively
Plywood character is made to each group to detect, it is 10 detection averaging of income values that wherein intensity, which is bonding strength, while according to
The test method detection pest of (wealth) Japanese Environment health center escapes effect and duration, that is, after being coated with 1 day, after 40 days with
And the escape rate after 6 months, experimental period are on August 1st, 2016, the Close Date is on January 31st, 2017, obtains following knot
Fruit:
Table 1
Group | Intensity (MPa) | Burst size of methanal (mg/L) | Escape rate (%) after 1 day | Escape rate (%) after 40 days | Escape rate (%) after 6 months |
Standard | ≥0.70 | E0≤0.5 | / | / | / |
Embodiment 1 | 4.28 | 0.04 | 100 | 91.6 | 78.2 |
Embodiment 2 | 4.15 | 0.05 | 100 | 92.4 | 77.5 |
Embodiment 3 | 4.23 | 0.03 | 100 | 91.8 | 77.6 |
Control group 1 | 3.76 | 0.04 | 96.8 | 86.3 | 61.2 |
Control group 2 | 3.92 | 0.05 | 90.4 | 79.5 | 54.6 |
Control group 3 | 3.85 | 0.04 | 93.5 | 84.6 | 57.2 |
Control group 4 | 3.94 | 0.06 | 94.8 | 85.7 | 59.4 |
Control group 5 | 3.46 | 0.05 | / | / | / |
It can be seen that method in the present invention treated that glued board vermins-proof effect is preferable by data in table 1, persistence
By force, burst size of methanal is substantially unchanged, Environmental Safety, is suitable for promoting the use of.
Claims (1)
1. a kind of preparation method of Mothproof veneer board, including veneer insect-prevention treatment and adhesive insect-prevention treatment, which is characterized in that institute
State veneer with a thickness of 0.6-2mm, water content 10-12%, the method for veneer insect-prevention treatment are as follows: by veneer immerse treatment fluid in,
Include 2-4g hydrogen peroxide, 0.7-1.5g fraxinellone in every 100ml treatment fluid, impregnates 1.5-2 hours, then pressurize under vacuum conditions
It is kept for 30-40 minutes to 0.6-0.8MPa, taking out drying to water content is 5-8%, then handles 25-30 in stifling drying oven
Minute, fumigating sootiness material in drying oven is acid treated paulownia wood, treatment conditions of the stifling drying oven are as follows: in furnace
Pressure is 0.14-0.18MPa, and vapor (steam) temperature is 140-160 DEG C;
The vacuum condition is that vacuum degree reaches -0.04 ~ -0.12MPa;The drying condition is that temperature is 60-80 DEG C, relatively wet
Degree is 90-95%;Acid treated the paulownia wood volume is not more than 1.8cm3;Processing method is aqueous for paulownia wood to be dried to
After amount is 15% or less, handles 6-8 minutes, complete under conditions of the sulfuric acid solution that mass concentration is 8-10% is in ultrasonic oscillation
After be rinsed with water 10 minutes, be dried to water content be 6-8%;
The insect-prevention treatment mode of the adhesive is that the composite particles for being equivalent to its weight 4-7% are added in adhesive, described multiple
Close particle the preparation method comprises the following steps: Jiang fraxinellone, carbon nanotube and polyvinyl alcohol with weight ratio 5:9:1 mix, then by mixed material
The ultrasonic disperse in the ethanol solution that the mass concentration for being equivalent to 3 times of its weight is 40-50%, the item for being 450-500 DEG C in temperature
It is spray-dried under part, obtaining the powder that partial size is 10-50 μm is composite particles;The adhesive by phenolic resin and flour with
Weight ratio 7:2-3 composition.