CN107470103A - 一种纺织品表面用的流涂式pc装饰膜 - Google Patents

一种纺织品表面用的流涂式pc装饰膜 Download PDF

Info

Publication number
CN107470103A
CN107470103A CN201610393820.0A CN201610393820A CN107470103A CN 107470103 A CN107470103 A CN 107470103A CN 201610393820 A CN201610393820 A CN 201610393820A CN 107470103 A CN107470103 A CN 107470103A
Authority
CN
China
Prior art keywords
films
flow coat
coating
decorating
textile surface
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610393820.0A
Other languages
English (en)
Inventor
孟莉莉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGYIN YONGTAI PLASTIC Co Ltd
Original Assignee
JIANGYIN YONGTAI PLASTIC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGYIN YONGTAI PLASTIC Co Ltd filed Critical JIANGYIN YONGTAI PLASTIC Co Ltd
Priority to CN201610393820.0A priority Critical patent/CN107470103A/zh
Publication of CN107470103A publication Critical patent/CN107470103A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种纺织品表面用的流涂式PC装饰膜，是在PC膜的外表面采用流涂的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷、过渡金属络合物和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至8～9范围，静置2～4小时，然后采用流涂的方式施加到PC膜的外表面，于80℃环境下烘干0.5小时，于110～140℃环境下固化1～1.5小时，最后在自然条件下平衡8小时以上。过流涂涂层保护后，提高了PC装饰膜的表面质感和功能强度，使该PC装饰膜能够更好地与纺织品表面贴合，提高装饰效果。

Description

一种纺织品表面用的流涂式PC装饰膜
技术领域
本发明属于装饰膜技术领域，具体涉及一种适于贴覆在纺织品表面的PC装饰膜。
背景技术
装饰膜具有隔热保温安全防爆等作用的，同时还有装饰的作用，而且透明的装饰膜还不会影响室内光线。具体地，装饰膜的优点包括：节能环保,减少空调，暖气带来的高额电费；隔阻紫外线入侵，保护室内物品褪色和老化；过滤强光，减少眩光，保护皮肤和视力；增加玻璃强度，减少人身伤害和保护财产，构筑隐形防护网；单向透视性，保护隐私，让居住空间尽享安逸，宁静舒适；改善建筑外观和美化室内居住环境；易装贴，易清洁，耐摩擦，无需特殊维护；经济实用，不褪色，不气泡，使用时间长。
装饰膜通过阻隔高达79%的太阳热能，夏季可大大降低空调的制冷成本；冬季可控制室内热量透过窗户散失，不仅不会使室内人员感到不适，而且减少了不必要的能耗费用，从而已经成为很多人会选择的在冬季室内保暖一种方式。
发明内容
本发明的目的是提供一种耐划伤的适用于纺织品表面使用的PC装饰膜。
本发明解决上述问题所采用的技术方案为：一种纺织品表面用的流涂式PC装饰膜，是在PC膜的外表面采用流涂的方式装饰一层功能涂层，所述功能涂层所涉及涂层浆的制备是将涂层胶、硅烷、过渡金属络合物和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至8～9范围，静置2～4小时，然后采用流涂的方式施加到PC膜的外表面，于80℃环境下烘干0.5小时，于110～140℃环境下固化1～1.5小时，最后在自然条件下平衡8小时以上。
优选地，所述过渡金属络合物为钛、铝、锡或锆的络合物。
优选地，硅烷的分子量介于200～2000。
优选地，所述硅烷在有机侧链中具有适于形成氢桥键的极性化基团。
与现有技术相比，本发明的优点在于：提供了一种流涂式的PC装饰膜，经过流涂涂层保护后，提高了PC装饰膜的表面质感和功能强度，使该PC装饰膜能够更好地与纺织品表面贴合，提高装饰效果。
具体实施方式
以下结合实施例对本发明作进一步详细描述。
实施例1
适用于纺织品的PC装饰膜，是在PC膜的外表面采用流涂的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷、钛、铝的络合物和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至8范围，静置2～4小时，然后采用流涂的方式施加到PC膜表面，于80℃环境下烘干0.5小时，于120℃环境下固化1.5小时，最后在自然条件下平衡8小时以上。
实施例2
适用于纺织品的PC装饰膜，是在PC膜的外表面采用流涂的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷、钛、锡的络合物和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至9范围，静置2～4小时，然后采用流涂的方式施加到PC膜表面，于80℃环境下烘干0.5小时，于130℃环境下固化1小时，最后在自然条件下平衡8小时以上。
实施例3
适用于纺织品的PC装饰膜，是在PC膜的外表面采用流涂的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷、铝、锆的络合物和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至9范围，静置2～4小时，然后采用流涂的方式施加到PC膜表面，于80℃环境下烘干0.5小时，于110℃环境下固化1小时，最后在自然条件下平衡8小时以上。

Claims (4)

1.一种纺织品表面用的流涂式PC装饰膜，其特征在于：是在PC膜的外表面采用流涂的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷、过渡金属络合物和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至8～9范围，静置2～4小时，然后采用流涂的方式施加到PC膜的外表面，于80℃环境下烘干0.5小时，于110～140℃环境下固化1～1.5小时，最后在自然条件下平衡8小时以上。
2.根据权利要求1所述的纺织品表面用的流涂式PC装饰膜，其特征在于：所述过渡金属络合物为钛、铝、锡或锆的络合物。
3.根据权利要求2所述的纺织品表面用的流涂式PC装饰膜，其特征在于：所述硅烷的分子量介于200～2000。
4.根据权利要求2所述的纺织品表面用的流涂式PC装饰膜，其特征在于：所述硅烷在有机侧链中具有适于形成氢桥键的极性化基团。
CN201610393820.0A 2016-06-07 2016-06-07 一种纺织品表面用的流涂式pc装饰膜 Pending CN107470103A (zh)