CN107455971A - A kind of production technology of seat - Google Patents

A kind of production technology of seat Download PDF

Info

Publication number
CN107455971A
CN107455971A CN201710670527.9A CN201710670527A CN107455971A CN 107455971 A CN107455971 A CN 107455971A CN 201710670527 A CN201710670527 A CN 201710670527A CN 107455971 A CN107455971 A CN 107455971A
Authority
CN
China
Prior art keywords
seat
base cloth
synthetic leather
superfine fiber
modified
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710670527.9A
Other languages
Chinese (zh)
Inventor
万隆鑫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANJI WANCHANG FURNITURE Co Ltd
Original Assignee
ANJI WANCHANG FURNITURE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANJI WANCHANG FURNITURE Co Ltd filed Critical ANJI WANCHANG FURNITURE Co Ltd
Priority to CN201710670527.9A priority Critical patent/CN107455971A/en
Publication of CN107455971A publication Critical patent/CN107455971A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of production technology of seat：The first step：The selection of the material of chair framework：The selection of chair framework material is solid wood material, wherein the solid wood material is pine or poplar, has carried out high temperature cabonization processing；Second step：Material polishing is shaped to skeleton as needed；3rd step：The processing of seat annex, seat annex, suitable bending precision is worked into, there is satisfactory flatness, wooden annex needs polishing, and unnecessary leftover pieces are removed；4th step：The making of backrest；5th step：Skeleton and backrest are combined；6th step：The making of surface cover：7th step:After surface cover deburring, filling pad, foamed plastics, sponge；8th step：Seat assembles, and, sewing, forms seat webbing by surface cover set on the seat.

Description

A kind of production technology of seat
Technical field
The present invention relates to a kind of production technology of seat, more particularly to the production technology of environmentally friendly seat.
Background technology
Traditional chair is that wooden or sheet metal makes mostly, and seat is mainly by skeleton, spring buffer part, seat Seat set, governor motion and servicing unit composition, wherein, skeleton is the foundation structure of seat, subject it is various load with, spring delays The general filled and process in part is rushed, surface cover uses corium or dermatine, and governor motion is mainly that the direction of seat is adjusted, seat Front and rear regulation and seat cushion regulation up and down, headrest is additionally provided with seat surface sleeve, traditional Chinese chair is more numerous in processing It is trivial, streamline form is not formed, process velocity is slow.
Artificial leather is a kind of outward appearance, feel like leather and can replace its plastic products that use.Generally using fabric as base, Coating synthetic resin and the addition of various plastics are made.Last century the eighties, expensive fur clothing cladding common people can not consume, should The market demand, the artificial leather of counterfeit leather once came into vogue, and were widely used in clothing, system bag.The people of so counterfeit leather Fabricate-leather clothes, bag are once full of street corner, meet the hope that people wear Pi Daipi.Compared with leather, artificial leather is easy to aging Abrasion, because producing harm to health of human body containing a large amount of chemical raw materials, and also it is gradual because not being durable with the clothing bag of its making Market is lost, until being substituted by other raw materials.For natural leather, it emphasizes the synthesis performance of " material ".It is with day The institutional framework of right leather is target, and with flexible high polymer material (such as polyurethane) impregnated fiber layer, (such as polyamide is fine Dimension, polyester fiber etc.), fibrous layer imitates the random 3-D solid structure of natural leather lamina reticularis, elastic polymer material shape Into the film with continuous microcellular structure, the composite that a kind of structure and performance all exactly like natural leather is made.With ultra-fine fibre The continuous development of synthetic leather industry is tieed up, its application field also constantly expands, although its many aspect is all excellent than natural leather Different (such as mechanical performance), but its sanitation performance, dyeability still suffer from larger gap compared with natural leather.It is reported that day The crust leather vapor pervious amount of right leather is 800mg/ (10cm224h) left and right, and the vapor pervious amount of superfine fiber chemical leather is only 400mg/ (10cm224h) left and right.In fact, superfine fiber chemical leather has been water vapour permeability among current all synthetic leather It is optimal, it with the main reason for natural leather sanitation performance difference in the hydrophilic radical ratio in natural leather on collagenous fibres Hydrophilic radical in superfine fiber chemical leather is more.Prior art someone is modified using microorganism, makes more ventilative artificial leather, so And microbial fermentation is not easy stabilization.
The present inventor is in long-term production practices, it was found that a kind of production technology of seat, the people from skeleton to surface cover Fabricate-leather is optimized, and obtains comfortable, ventilative, good hand touch, wear-resisting environment-friendlyartificial artificial leather and robust skeleton.
The content of the invention
The invention aims to solve the deficiencies in the prior art, there is provided a kind of production technology of seat, from skeleton to The artificial leather of surface cover is optimized, and obtains comfortable, ventilative, good hand touch, wear-resisting environment-friendlyartificial artificial leather and robust bone Frame.
The technical solution adopted by the present invention is as follows：
A kind of production technology of seat, its preparation process are as follows：
The first step：The selection of the material of chair framework：
The selection of chair framework material is solid wood material, wherein the solid wood material is pine or poplar, has carried out high temperature cabonization Processing；
Second step：Material polishing is shaped to skeleton as needed；
3rd step：The processing of seat annex, seat annex, suitable bending precision is worked into, there is satisfactory flatness, it is wooden attached Part needs polishing, and unnecessary leftover pieces are removed；
4th step：The making of backrest；
5th step：Skeleton and backrest are combined；
6th step：The making of surface cover：
(1) superfine fiber synthetic leather base cloth citric acid solution pre-processes：
The citric acid solution that mass fraction is 0.2% is prepared, by superfine fiber synthetic leather base cloth input wherein, is kept for 80 DEG C and boiled 30-35min is pre-processed；
(2) laccase is modified：
Using 10,000 U laccase, the 0.5-0.8% aqueous solution is configured to, pretreated superfine fiber synthetic leather base cloth is put into Wherein, 40 DEG C of modification 25min；
(3) composite pawpaw glycoprotein protease is twice-modified：
Configure following solution：
Using 5000U papain, the 0.5-0.8% aqueous solution is configured to；Then Tea Polyphenols is added, trehalose, is turned into The Tea Polyphenols of final concentration 0.2%, 0.3-0.5% trehalose；
By the modified superfine fiber synthetic leather base cloth input of laccase wherein, 40 DEG C of modification 50-70min；
(4) stable processing：
The superfine fiber synthetic leather base cloth after step (3) processing is put into 0.5% SP protein solution, kept for 20 DEG C surely Surely handle 2 hours；
(5) modified base fabric is covered with paint, lacquer, colour wash, etc. using the Coating technology of natural leather；
(6) acid one-bath one-step dyeing dyeing：Bath raio 1:20,60 DEG C, 60-85min, pH=5.5.
7th step:After surface cover deburring, filling pad, foamed plastics, sponge；
8th step：Seat assembles, and, sewing, forms seat webbing by surface cover set on the seat.
Compared with prior art, its advantage is the present invention：
A kind of production technology of seat is provided, the artificial leather from skeleton to surface cover is optimized, and obtains comfortable, ventilative, feel It is good, wear-resisting environment-friendlyartificial artificial leather and robust skeleton.
Embodiment 1：
Superfine fiber synthetic leather base cloth used in all embodiments of the invention is to be commercially available.
A kind of production technology of seat, its preparation process are as follows：
The first step：The selection of the material of chair framework：
The selection of chair framework material is solid wood material, wherein the solid wood material is pine or poplar, has carried out high temperature cabonization Processing；Second step：Material polishing is shaped to skeleton as needed；
3rd step：The processing of seat annex, seat annex, suitable bending precision is worked into, there is satisfactory flatness, it is wooden attached Part needs polishing, and unnecessary leftover pieces are removed；
4th step：The making of backrest；
5th step：Skeleton and backrest are combined；
6th step：The making of surface cover：
(1) superfine fiber synthetic leather base cloth citric acid solution pre-processes：
The citric acid solution that mass fraction is 0.2% is prepared, by superfine fiber synthetic leather base cloth input wherein, is kept for 80 DEG C and boiled 30min is pre-processed；
(2) laccase is modified：
Using 10,000 U laccase, 0.5% aqueous solution is configured to, pretreated superfine fiber synthetic leather base cloth is put into it In, 40 DEG C of modification 25min；
(3) composite pawpaw glycoprotein protease is twice-modified：
Configure following solution：
Using 5000U papain, 0.5% aqueous solution is configured to；Then Tea Polyphenols is added, trehalose, turns into dense eventually The Tea Polyphenols of degree 0.2%, 0.3% trehalose；
By the modified superfine fiber synthetic leather base cloth input of laccase wherein, 40 DEG C of modification 50min；
(4) stable processing：
The superfine fiber synthetic leather base cloth after step (3) processing is put into 0.5% SP protein solution, kept for 20 DEG C surely Surely handle 2 hours；
(5) modified base fabric is covered with paint, lacquer, colour wash, etc. using the Coating technology of natural leather；
(6) acid one-bath one-step dyeing dyeing：Bath raio 1:20,60 DEG C, 60min, pH=5.5.
7th step:After surface cover deburring, filling pad, foamed plastics, sponge；
8th step：Seat assembles, and, sewing, forms seat webbing by surface cover set on the seat.
Modified base fabric performance is as follows：
Embodiment 2:
With embodiment 1, wherein the 6th step：Surface cover is made as：
(1) superfine fiber synthetic leather base cloth citric acid solution pre-processes：
The citric acid solution that mass fraction is 0.2% is prepared, by superfine fiber synthetic leather base cloth input wherein, is kept for 80 DEG C and boiled 35min is pre-processed；
(2) laccase is modified：
Using 10,000 U laccase, 0.8% aqueous solution is configured to, pretreated superfine fiber synthetic leather base cloth is put into it In, 40 DEG C of modification 25min；
(3) composite pawpaw glycoprotein protease is twice-modified：
Configure following solution：
Using 5000U papain, 0.8% aqueous solution is configured to；Then Tea Polyphenols is added, trehalose, turns into dense eventually The Tea Polyphenols of degree 0.2%, 0.5% trehalose；
By the modified superfine fiber synthetic leather base cloth input of laccase wherein, 40 DEG C of modification 70min；
(4) stable processing：
The superfine fiber synthetic leather base cloth after step (3) processing is put into 0.5% SP protein solution, kept for 20 DEG C surely Surely handle 2 hours；
(5) modified base fabric is covered with paint, lacquer, colour wash, etc. using the Coating technology of natural leather；
(6) acid one-bath one-step dyeing dyeing：Bath raio 1:20,60 DEG C, 85min, pH=5.5.
Modified base fabric performance is as follows：
Embodiment 3:
With embodiment 1, wherein the 6th step：Surface cover is made as：
(1) superfine fiber synthetic leather base cloth citric acid solution pre-processes：
The citric acid solution that mass fraction is 0.2% is prepared, by superfine fiber synthetic leather base cloth input wherein, is kept for 80 DEG C and boiled 35min is pre-processed；
(2) laccase is modified：
Using 10,000 U laccase, 0.5% aqueous solution is configured to, pretreated superfine fiber synthetic leather base cloth is put into it In, 40 DEG C of modification 25min；
(3) composite pawpaw glycoprotein protease is twice-modified：
Configure following solution：
Using 5000U papain, 0.8% aqueous solution is configured to；Then Tea Polyphenols is added, trehalose, turns into dense eventually The Tea Polyphenols of degree 0.2%, 0.5% trehalose；
By the modified superfine fiber synthetic leather base cloth input of laccase wherein, 40 DEG C of modification 70min；
(4) stable processing：
The superfine fiber synthetic leather base cloth after step (3) processing is put into 0.5% SP protein solution, kept for 20 DEG C surely Surely handle 2 hours；
(5) modified base fabric is covered with paint, lacquer, colour wash, etc. using the Coating technology of natural leather；
(6) acid one-bath one-step dyeing dyeing：Bath raio 1:20,60 DEG C, 60min, pH=5.5.
Modified base fabric performance is as follows：
Embodiment 4:
With embodiment 1, wherein the 6th step：Surface cover is made as：
(1) superfine fiber synthetic leather base cloth citric acid solution pre-processes：
The citric acid solution that mass fraction is 0.2% is prepared, by superfine fiber synthetic leather base cloth input wherein, is kept for 80 DEG C and boiled 32min is pre-processed；
(2) laccase is modified：
Using 10,000 U laccase, 0.6% aqueous solution is configured to, pretreated superfine fiber synthetic leather base cloth is put into it In, 40 DEG C of modification 25min；
(3) composite pawpaw glycoprotein protease is twice-modified：
Configure following solution：
Using 5000U papain, 0.7% aqueous solution is configured to；Then Tea Polyphenols is added, trehalose, turns into dense eventually The Tea Polyphenols of degree 0.2%, 0.4% trehalose；
By the modified superfine fiber synthetic leather base cloth input of laccase wherein, 40 DEG C of modification 60min；
(4) stable processing：
The superfine fiber synthetic leather base cloth after step (3) processing is put into 0.5% SP protein solution, kept for 20 DEG C surely Surely handle 2 hours；
(5) modified base fabric is covered with paint, lacquer, colour wash, etc. using the Coating technology of natural leather；
(6) acid one-bath one-step dyeing dyeing：Bath raio 1:20,60 DEG C, 75min, pH=5.5.
Modified base fabric performance is as follows：
Embodiment 5:
With embodiment 1, wherein the 6th step：Surface cover is made as：
(1) superfine fiber synthetic leather base cloth citric acid solution pre-processes：
The citric acid solution that mass fraction is 0.2% is prepared, by superfine fiber synthetic leather base cloth input wherein, is kept for 80 DEG C and boiled 35min is pre-processed；
(2) laccase is modified：
Using 10,000 U laccase, 0.7% aqueous solution is configured to, pretreated superfine fiber synthetic leather base cloth is put into it In, 40 DEG C of modification 25min；
(3) composite pawpaw glycoprotein protease is twice-modified：
Configure following solution：
Using 5000U papain, 0.7% aqueous solution is configured to；Then Tea Polyphenols is added, trehalose, turns into dense eventually The Tea Polyphenols of degree 0.2%, 0.5% trehalose；
By the modified superfine fiber synthetic leather base cloth input of laccase wherein, 40 DEG C of modification 60min；
(4) stable processing：
The superfine fiber synthetic leather base cloth after step (3) processing is put into 0.5% SP protein solution, kept for 20 DEG C surely Surely handle 2 hours；
(5) modified base fabric is covered with paint, lacquer, colour wash, etc. using the Coating technology of natural leather；
(6) acid one-bath one-step dyeing dyeing：Bath raio 1:20,60 DEG C, 60-85min, pH=5.5.
Modified base fabric performance is as follows：
It can be seen that, there is provided a kind of production technology of seat, the artificial leather from skeleton to surface cover are optimized, and obtain comfortably, breathe freely, Good hand touch, wear-resisting environment-friendlyartificial artificial leather and robust skeleton.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto, Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.

Claims (5)

1. a kind of production method of seat, its preparation process are as follows：
The first step：The selection of the material of chair framework：
The selection of chair framework material is solid wood material, wherein the solid wood material is pine or poplar, has carried out high temperature cabonization Processing；
Second step：Material polishing is shaped to skeleton as needed；
3rd step：The processing of seat annex, seat annex, suitable bending precision is worked into, there is satisfactory flatness, it is wooden attached Part needs polishing, and unnecessary leftover pieces are removed；
4th step：The making of backrest；
5th step：Skeleton and backrest are combined；
6th step：The making of surface cover：
（1）Superfine fiber synthetic leather base cloth citric acid solution pre-processes；
（2）Laccase is modified；
（3）Composite pawpaw glycoprotein protease is twice-modified：
Configure following solution：
Using 5000U papain, the 0.5-0.8% aqueous solution is configured to；Then Tea Polyphenols is added, trehalose, is turned into eventually The Tea Polyphenols of concentration 0.2%, 0.3-0.5% trehalose；
By the modified superfine fiber synthetic leather base cloth input of laccase wherein, 40 DEG C of modification 50-70min；
（4）Stable processing：
By step（3）Superfine fiber synthetic leather base cloth after processing, put into 0.5% SP protein solution, keep 20 DEG C of stabilizations Processing 2 hours；
（5）Modified base fabric is covered with paint, lacquer, colour wash, etc. using the Coating technology of natural leather；
（6）Acid one-bath one-step dyeing dyeing；
7th step:After surface cover deburring, filling pad, foamed plastics, sponge；
8th step：Seat assembles, and, sewing, forms seat webbing by surface cover set on the seat.
2. the method described in claim 1, it is characterised in that：
Described 6th is step by step rapid（1）For：The citric acid solution that mass fraction is 0.2% is prepared, superfine fiber synthetic leather base cloth is thrown Enter wherein, kept for 80 DEG C boil 30-35min pretreatments.
3. the method described in claim 1, it is characterised in that：
Described 6th is step by step rapid（2）For：Using 10,000 U laccase, the 0.5-0.8% aqueous solution is configured to, will be pretreated super Fine fibre synthetic leather base cloth is put into wherein, 40 DEG C of modification 25min.
4. the method described in claim 1, it is characterised in that：
Described 6th is step by step rapid（6）For：：Bath raio 1:20,60 DEG C, 60-85 min, pH=5.5.
5. the artificial leather being prepared with the method described in claim 1-4.
CN201710670527.9A 2017-08-08 2017-08-08 A kind of production technology of seat Pending CN107455971A (en)