CN107434370A - A kind of high-strength light composite building material - Google Patents
A kind of high-strength light composite building material Download PDFInfo
- Publication number
- CN107434370A CN107434370A CN201710767499.2A CN201710767499A CN107434370A CN 107434370 A CN107434370 A CN 107434370A CN 201710767499 A CN201710767499 A CN 201710767499A CN 107434370 A CN107434370 A CN 107434370A
- Authority
- CN
- China
- Prior art keywords
- parts
- building material
- composite building
- lignocellulosic
- quartz
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of high-strength light composite building material, including Foamex, laurate, graphite powder, bentonite, calcium stearate, lignocellulosic, silicone acrylic emulsion, quartz and rutile type titanium white, its feed components by weight, 18 25 parts of 15 19 parts of the Foamex, 30 47 parts of laurate, 20 24 parts of graphite powder, 10 14 parts of bentonite, 58 parts of calcium stearate, 38 parts of lignocellulosic, 15 19 parts of silicone acrylic emulsion, 18 22 parts of quartz and rutile type titanium white.The present invention can effectively improve composite building material rupture strength and toughness, the fracture width of limitation, resist composite building material surface checking, can be widely applied to the composite building material structure in the fields such as building, water conservancy, municipal traffic, ocean military project.
Description
Technical field
The invention belongs to building field, is related to a kind of high-strength light composite building material.
Background technology
Construction material it is long-term bear wind, Exposure to Sunlight, drench with rain, wear, the ectocine such as corrode after, performance can gradually become
Change, the rational formula of construction material is most important, first should safely, it is durable in use, construction material dosage is very big, directly affects
To the cost of engineering, usual building materials expense accounts for more than half of project total cost, therefore is considering technical performance and structural strength
It is required that when, also result in the rise of building cost.Need a kind of proportion low, the construction material of lightweight.
The content of the invention
The technical problem to be solved in the present invention is:Overcome the technical problem that house sidings moisture-sensitive is gone mouldy in the prior art,
A kind of waterproof, anti-mildew, light high-strength light composite building material are provided.
The technical solution adopted for the present invention to solve the technical problems is:A kind of high-strength light composite building material is provided, including
Foamex, laurate, graphite powder, bentonite, calcium stearate, lignocellulosic, silicone acrylic emulsion, quartz and rutile type titanium
White powder, its feed components are by weight, described Foamex 15-19 parts, laurate 30-47 parts, graphite powder 20-24 parts, swollen
Moisten native 10-14 parts, calcium stearate 5-8 parts, lignocellulosic 3-8 parts, silicone acrylic emulsion 15-19 parts, quartz 18-22 parts and golden red
Stone-type titanium dioxide 18-25 parts.
Preferably, described high-strength light composite building material, it is characterized in that:Its feed components by weight, set by foaming
15 parts of fat, 30 parts of laurate, 20 parts of graphite powder, 10 parts of bentonite, 5 parts of calcium stearate, 3 parts of lignocellulosic, silicone acrylic emulsion 15
18 parts of part, 18 parts of quartz and rutile type titanium white.
Preferably, described high-strength light composite building material, it is characterized in that having following steps:
(1) good various raw materials are configured by weight ratio;
(2) the various raw materials configured are added in stirred reactor one by one, stirred under conditions of rotating speed is 60rpm
2h, you can be made.
The present invention can effectively realize the rapid-curing cutback of composite building material, while improve composite building material rupture strength and toughness, limitation
Fracture width, resist composite building material surface checking and antiknock fire resistance property, can be widely applied to building, water conservancy, municipal administration and hand over
The composite building material structure in the fields such as logical, ocean military project.
Embodiment
A kind of high-strength light composite building material of the present invention, its feed components by weight, including Foamex, the moon
Cinnamic acid, graphite powder, bentonite, calcium stearate, lignocellulosic, silicone acrylic emulsion, quartz and rutile type titanium white, its raw material
Each component by weight, described Foamex 15-19 parts, laurate 30-47 parts, graphite powder 20-24 parts, bentonite 10-14 parts,
Calcium stearate 5-8 parts, lignocellulosic 3-8 parts, silicone acrylic emulsion 15-19 parts, quartz 18-22 parts and rutile type titanium white
18-25 parts.
Preferably, described high-strength light composite building material, it is characterized in that:Its feed components by weight, set by foaming
15 parts of fat, 30 parts of laurate, 20 parts of graphite powder, 10 parts of bentonite, 5 parts of calcium stearate, 3 parts of lignocellulosic, silicone acrylic emulsion 15
18 parts of part, 18 parts of quartz and rutile type titanium white.
Preferably, described high-strength light composite building material, it is characterized in that having following steps:
(1) good various raw materials are configured by weight ratio;
(2) the various raw materials configured are added in stirred reactor one by one, stirred under conditions of rotating speed is 60rpm
2h, you can be made.
Described above is only the preferred embodiment of the present invention, is not intended to limit the invention, it is noted that for this
For the those of ordinary skill of technical field, without departing from the technical principles of the invention, some improvement can also be made
And modification, these improvement and modification also should be regarded as protection scope of the present invention.
Claims (3)
1. a kind of high-strength light composite building material, it is characterized in that:Including Foamex, laurate, graphite powder, bentonite, stearic acid
Calcium, lignocellulosic, silicone acrylic emulsion, quartz and rutile type titanium white, its feed components by weight, set by the foaming
Fat 15-19 parts, laurate 30-47 parts, graphite powder 20-24 parts, bentonite 10-14 parts, calcium stearate 5-8 parts, lignocellulosic
3-8 parts, silicone acrylic emulsion 15-19 parts, quartz 18-22 parts and rutile type titanium white 18-25 parts.
2. high-strength light composite building material as claimed in claim 1, it is characterized in that:Its feed components by weight, set by foaming
15 parts of fat, 30 parts of laurate, 20 parts of graphite powder, 10 parts of bentonite, 5 parts of calcium stearate, 3 parts of lignocellulosic, silicone acrylic emulsion 15
18 parts of part, 18 parts of quartz and rutile type titanium white.
3. the high-strength light composite building material as described in claim 1-2, it is characterized in that having following steps:
(1) good various raw materials are configured by weight ratio;
(2) the various raw materials configured are added in stirred reactor one by one, stirred under conditions of rotating speed is 60rpm
2h, you can be made.