CN107419865A - Deck wall face fire-type water-proof, heat-insulating, heat-preserving decorative panel and preparation method thereof - Google Patents

Deck wall face fire-type water-proof, heat-insulating, heat-preserving decorative panel and preparation method thereof Download PDF

Info

Publication number
CN107419865A
CN107419865A CN201610382099.5A CN201610382099A CN107419865A CN 107419865 A CN107419865 A CN 107419865A CN 201610382099 A CN201610382099 A CN 201610382099A CN 107419865 A CN107419865 A CN 107419865A
Authority
CN
China
Prior art keywords
heat
proof
mixing
wall face
perlite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610382099.5A
Other languages
Chinese (zh)
Inventor
梁奉君
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610382099.5A priority Critical patent/CN107419865A/en
Publication of CN107419865A publication Critical patent/CN107419865A/en
Pending legal-status Critical Current

Abstract

Deck wall face fire-type water-proof, heat-insulating, heat-preserving decorative panel and preparation method thereof,It is characterized in utilizing the flyash after perlite and burning or the water slag 60Kg of perlite 50 by weight after metal smelt,The 13kg of V-type asphalt polyurethane shellac varnish 10 is used again after flyash or the 180Kg of grain slag 160 mixing,The 8kg of cement 5 mixing does blanket raw material as adhesive,Turn into blanket after decorated plate rolloff mechanism,Make adhesive with the 5kg of two type polyurethane shellac varnish 3 again,It is molded after adding appropriate pigment and the mixing of 18 26kg white cements through the secondary rolloff of mill,High Temperature Curing room is delivered to after vertical cut-out carry out chemical reaction solidification by required length,With heat-insulation and heat-preservation,Sound isolating decorative is beautiful,It is prolonged resistance to gather around,It is capable of washing,Keep metope Chang Xin beneficial effect,It is adapted to deck wall face fire-proof and water-proof thermal insulation decorative.

Description

Deck wall face fire-type water-proof, heat-insulating, heat-preserving decorative panel and preparation method thereof
Technical field：
The invention belongs to deck, technical field made of wall face fire-proof and water-proof heat-insulating decorative plate, and in particular to A kind of deck wall face fire-type water-proof, heat-insulating, heat-preserving decorative panel and preparation method thereof.
Background technology：
Multifunction decorative board production technology was all manual batch mixing in the past, manual operation, the mould punching demoulding, High Temperature Curing life Production. art, product quality waste raw material, the low grade of production cost high efficiency lacks it is difficult to ensure that yield poorly and labor intensity is high again Fall into.Existing all kinds of building national regulations must use novel energy saving thermal insulation building materials, therefore building materials market expands, and original process can not expire Needed for sufficient market, so deck, wall face fire-type multifunction decorative sheet material demand increases, but existing market does not have also A kind of it was found that more advanced auto-processes streamline.
The content of the invention：
The purpose of the present invention is exactly to overcome the above insufficient, there is provided and it is a kind of to revolutionize traditional production technology, make more It the substantially all mechanization production of functional decoration sheet material, that is, ensure that product quality reduces production cost again, it is strong to alleviate work Degree, makes deck wall face fire-type water-proof, heat-insulating, heat-preserving decorative panel that the yields have increased considerably and preparation method thereof.
The present invention is achieved in that described deck wall face fire-type water-proof, heat-insulating, heat-preserving decorative panel and its preparation Method, comprise the following steps：
1. utilize the flyash after perlite and burning or the water slag perlite 50- by weight after metal smelt Made again with V-type asphalt polyurethane shellac varnish 10-13kg, cement 5-8Kg mixing after 60Kg, flyash or grain slag 160-180Kg mixing Adhesive does blanket raw material, turns into blanket after decorated plate rolloff mechanism.
2. making adhesive with two type polyurethane shellac varnish 3-5Kg again, passed through after adding appropriate pigment and 18-26Kg white cement mixing The secondary rolloff shaping of mill.
3. it is delivered to by required length after vertical cut-out after High Temperature Curing room carries out chemical reaction solidification, it is qualified through examining Packaging and storage side is finished product again.
Deck wall face fire-type water-proof, heat-insulating, heat-preserving decorative panel of the present invention and preparation method thereof, there is every cubic metre Finished weight 250-280Kg, every cubic metre 10-20 square metres.Every square metre centimetre of adhesive strength is more than 1.6MPA, and compression is strong Degree is more than or equal to 0.4MPA, thermal conductivity factor 25+-5 degree, 0.090-0.142%M.K technical requirements, as long as any surface finish is beautiful Fire-proof and water-proof, heat-insulation and heat-preservation, sound insulation dress can once be completed with the floating whole exterior wall surface of cement by being sticked at I type polyurethane shellac varnishes Adorn beautiful exterior wall surface or deck, it is prolonged it is resistance to gather around, and can often clean, metope is kept often washing Chang Xin exterior wall table The beneficial effect in face.
Embodiment
Embodiment；
1. perlite Pengization stove is to be by the expanded perlite formed of ore, its performance for thermal source using coal gas or natural gas Light to have fire-retardant, heat-insulation and heat-preservation, sound insulation effect, 30 meters of tunnel furnace length, 2 waste heat boilers are to utilize waste heat caused by puffing furnace The generation steam supply of supply boiler work needs gas process to do work, and 3A feed bins, 3B additives are inputted through 1 expanded good perlite material Feed bin, 3A.B raw materials are fed to 4 tubular particle raw material Luo Xuan conveyers in proportion, and perlite matches somebody with somebody additive 160- for 50-60Kg 180Kg, it is slowly added in Luo Xuan conveyers, while is all dried raw material using steam injection shell heating, and with 120 seconds Convey 1m3Speed is fed to 5 timing reversing switch bodies, and change in 120 seconds once flows to, and is divided to two 6 measuring tanks and is fed, 6A.B It is particulate material 1 cubic metre of tank volume of metering, is divided to two sets of feed of batch mixing rabbling mechanism 76 and was stirred material injection batch mixing with 20 seconds Machine is started working, while V-type asphalt polyurethane shellac varnish 10-13kg and 5-8kg cement is stirred into pasty state by adhesive rabbling mechanism 8 Add 7 to be sufficiently stirred 240 seconds with particulate material, lake shape adhesive is completely encapsulated in particulate material surface, then will with 20 seconds Mixed raw material emptying waits working cycles again.20 meters of 4-9 active lengths, 9 be decorative panel mill system, and mixed material enters 9 The Luo Xuan Fabric material mechanisms of system uniformly apply raw material Fabric in advancing fiber cloth surface, and last layer fiber is applied again on the surface of material Cloth does work into roll, turns into blanket and moves on, then is added two type polyurethane shellac varnish 3-5KG in right amount by colored mixing mechanism Pigment and 20-26kg white cements are mixed evenly into thick input color spiral Fabric material mechanism, uniform Fabric in blanket surface, It is template that plastic protective film for plastics is applied again through secondary rolloff rear, and length is cut off through vertical shut-off mechanism on demand, is re-fed into lower road work Sequence, 9 decorative panel mill system tasks just calculate completion, 10 conveying-type High Temperature Curing tunnel bodies, and the template after cut-out is slow Into after 10, it is advanced slowly 105 degree of high temp tunnel internal diameter, 30 meters of high temperature is long, promotes the sheet material sizing rear that chemically reacts as early as possible to be Finished section bar, after the completion of 10 by 2 supply steam heating actings, into after 11 cooling 30 meters of natural coolings of conveying, 12 close through examining Load the whole process sides of foldable packing box storage after lattice to be fully completed.

Claims (1)

1. deck wall face fire-type water-proof, heat-insulating, heat-preserving decorative panel and preparation method thereof, it is characterised in that including following step Suddenly：
1) utilizes the flyash after perlite and burning or the water slag perlite 50-60kg by weight after metal smelt, powder Made again of V-type asphalt polyurethane shellac varnish 10-13kg, cement 5-8kg mixing as adhesive after coal ash or grain slag 160-180kg mixing Blanket raw material, turn into blanket after decorated plate rolloff mechanism；
2) makees adhesive with two type polyurethane shellac varnish 3-5Kg again, adds after appropriate pigment and 18-26Kg white cement mixing through grinding The secondary rolloff shaping of milling train；
3) is delivered to after vertical cut-out by required length after High Temperature Curing room carries out chemical reaction solidification, through examine it is qualified again Packaging and storage side is finished product.
CN201610382099.5A 2016-05-24 2016-05-24 Deck wall face fire-type water-proof, heat-insulating, heat-preserving decorative panel and preparation method thereof Pending CN107419865A (en)