CN107418686A - Calcium base lubricating agent constituent - Google Patents
Calcium base lubricating agent constituent Download PDFInfo
- Publication number
- CN107418686A CN107418686A CN201710729345.4A CN201710729345A CN107418686A CN 107418686 A CN107418686 A CN 107418686A CN 201710729345 A CN201710729345 A CN 201710729345A CN 107418686 A CN107418686 A CN 107418686A
- Authority
- CN
- China
- Prior art keywords
- parts
- lubricating agent
- agent constituent
- base lubricating
- calcium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of calcium base lubricating agent constituent, belong to field of lubricant, for the lubrication of plant equipment, it includes viscosity number under the conditions of 100 DEG C for 10 ~ 15 50 ~ 100 parts of crude mineral oils, 10 ~ 15 parts of tricresyl phosphate, 1 ~ 2 part of dinonyl naphthalene, 5 ~ 10 parts of hydroxy stearic acid, 10 ~ 15 parts of calcium mahogany sulfonate, 1 ~ 3 part of C6 C20 alicyclic primary amines.In view of above-mentioned technical proposal; the present invention can realize adaptability of the lubricant to high temperature and low temperature; influence of the temperature to self-lubrication performance is avoided, while there is certain water repelling property and anti-wear performance again, improves the usage time of lubricant and the protection to mechanical service life.
Description
Technical field
The invention belongs to field of lubricant, specifically, more particularly to a kind of calcium base lubricating agent constituent.
Background technology
Plant equipment needs to be lubricated operation to the mechanical part of operating in the process of running, allows it to be maintained at
In good Operation Conditions, the abrasion condition of itself is reduced, improves running efficiency.Thus need to be moved through in mechanical device
Lubricant is injected in journey to ensure above-mentioned operating.
Lubricant is in addition to it should possess resistant to elevated temperatures performance, it is also necessary to focus on low temperature resistant performance, so as to ensure
It is happy during the temperature cycles that mechanical device goes round and begins again at all seasons that there is stable greasy property.And above-mentioned lubrication
Agent, which still needs satisfaction, has certain water repelling property and abrasion resistance, and extra protective effect is played to machinery.
The content of the invention
It is an object of the invention to provide a kind of calcium base lubricating agent constituent, and it can realize lubricant to high temperature and low temperature
Adaptability, avoid influence of the temperature to self-lubrication performance, while there is certain water repelling property and anti-wear performance again, improve
The usage time of lubricant and the protection to mechanical service life.
To reach above-mentioned purpose, the present invention is achieved by the following technical solutions:
A kind of calcium base lubricating agent constituent, it is composed of the following components in parts by weight:
It is 10 ~ 15 50 ~ 100 parts of crude mineral oils, 10 ~ 15 parts of tricresyl phosphate, two including the viscosity number under the conditions of 100 DEG C
1 ~ 2 part of nonyl naphthalene, 5 ~ 10 parts of hydroxy stearic acid, 10 ~ 15 parts of calcium mahogany sulfonate, 1 ~ 3 part of C6-C20 alicyclic primary amines.
Further speaking, heretofore described C6-C20 alicyclic primary amines are the positive structure Armeens of C6-C20, C6-
C20 alicyclic primary amines mix according to the ratio of parts by weight 1 ~ 1.5.
Further speaking, heretofore described calcium base lubricating agent constituent also includes 0.5 ~ 1 part of boric acid.
Further speaking, heretofore described crude mineral oils include paraffine base crude oil, one kind in naphthene base crude oil or
According to parts by weight 1:2 ratio mixes.
Compared with prior art, the beneficial effects of the invention are as follows:
The present invention can realize adaptability of the lubricant to high temperature and low temperature, avoid influence of the temperature to self-lubrication performance, together
When there is certain water repelling property and anti-wear performance again, improve the usage time of lubricant and the protection to mechanical service life.
And in the present invention using the oil based on the crude mineral oils of certain viscosity value, by adding a small amount of feature
Raw material reaches the effect compared to original lubricant, and manufacturing cost is relatively low.
Embodiment
Technical scheme described herein is described further with reference to embodiment.
Embodiment 1:A kind of calcium base lubricating agent constituent, it is composed of the following components in parts by weight:
It is 10 ~ 15 50 ~ 100 parts of crude mineral oils, 10 ~ 15 parts of tricresyl phosphate, two including the viscosity number under the conditions of 100 DEG C
1 ~ 2 part of nonyl naphthalene, 5 ~ 10 parts of hydroxy stearic acid, 10 ~ 15 parts of calcium mahogany sulfonate, 1 ~ 3 part of C6-C20 alicyclic primary amines.
Embodiment 2:A kind of calcium base lubricating agent constituent, wherein the C6-C20 alicyclic primary amines are the positive structure fat of C6-C20
Race's primary amine, C6-C20 alicyclic primary amines mix according to the ratio of parts by weight 1 ~ 1.5.The calcium base lubricating agent constituent also wraps
Include 0.5 ~ 1 part of boric acid.The crude mineral oils include paraffine base crude oil, one kind in naphthene base crude oil or according to parts by weight 1:2
Ratio mixes.The composition of remainder is identical with the constituent described in embodiment 1.
In view of above-described embodiment, when in use, its course of work and principle are as follows by the application:
Heretofore described base oil is crude mineral oils, but the oils that crude mineral oils can be single kind also includes
Two or more mineral oil oil, such as one kind in paraffine base crude oil, naphthene base crude oil, or it is above-mentioned both according to parts by weight into
Point, close to ratio 1:It is well mixed in the case of 2, the oily use condition based on reaching.It should be noted that
Even if two parts base oil is mixed, it is still desirable to meets that viscosity number remains 10 ~ 15 in the case of 100 DEG C.
Common practice increases corresponding composition the performance of base oil is improved and lifted in base oil, basis
Important component of the oil as whole lubricant, its effect are self-evident.And the material added plays further strengthened effect, such as
The compositions such as the tricresyl phosphate, dinonyl naphthalene, hydroxy stearic acid and the calcium mahogany sulfonate that add in the present invention, these composition energy
The improvement for enough be combineding with each other and promoting base oil in correlation properties, by reduce unnecessary composition addition realize it is equivalent
Technique effect.
For example, in order to realize that modified base oil has the characteristic such as water resistant, high temperature resistance, low-temperature resistance, wear-resisting, it is necessary to add
Dinonyl naphthalene, hydroxy stearic acid etc., and a small amount of boric acid is also added into as guiding, the linkage that material is added with protrusion is made
With, the effect of raising effect, and then realize corresponding temperature characterisitic and water-resistant, wearing-resistant energy.
Claims (4)
- A kind of 1. calcium base lubricating agent constituent, it is characterised in that:It is composed of the following components in parts by weight:It is 10 ~ 15 50 ~ 100 parts of crude mineral oils, 10 ~ 15 parts of tricresyl phosphate, two including the viscosity number under the conditions of 100 DEG C 1 ~ 2 part of nonyl naphthalene, 5 ~ 10 parts of hydroxy stearic acid, 10 ~ 15 parts of calcium mahogany sulfonate, 1 ~ 3 part of C6-C20 alicyclic primary amines.
- 2. calcium base lubricating agent constituent according to claim 1, it is characterised in that:The C6-C20 alicyclic primary amines are The positive structure Armeens of C6-C20, C6-C20 alicyclic primary amines mix according to the ratio of parts by weight 1 ~ 1.5.
- 3. calcium base lubricating agent constituent according to claim 1, it is characterised in that:The calcium base lubricating agent constituent also wraps Include 0.5 ~ 1 part of boric acid.
- 4. calcium base lubricating agent constituent according to claim 1, it is characterised in that:The crude mineral oils include paraffinic base Oil, one kind in naphthene base crude oil or according to parts by weight 1:2 ratio mixes.