CN107414255A - The soldering method of metal mesh belt - Google Patents
The soldering method of metal mesh belt Download PDFInfo
- Publication number
- CN107414255A CN107414255A CN201710726505.XA CN201710726505A CN107414255A CN 107414255 A CN107414255 A CN 107414255A CN 201710726505 A CN201710726505 A CN 201710726505A CN 107414255 A CN107414255 A CN 107414255A
- Authority
- CN
- China
- Prior art keywords
- metal mesh
- mesh belt
- welding
- soldering method
- inert gas
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of soldering method of metal mesh belt, and this method is welded using argon arc welding to adjacent helical end, and the process that solder joint reddens in welding is passed through inert gas.Wherein, the inert gas is argon gas, and the mode that is passed through of the inert gas is blown on the surface of the solder joint, and the inert gas is passed through before solder joint blackening, the soldering method of the metal mesh belt also includes a polishing operation, and the pad surface after welding is polished.The soldering method of the metal mesh belt also includes a polishing process, and the metal mesh belt after welding or after polishing is polished.Due to being that the process that solder joint reddens in welding is passed through inert gas; therefore air can be blown away; protected on butt welding point surface; avoid solder joint oxidation blackening; butt welding point is finely polished; the burr of pad surface can be removed, the metal mesh belt after welding is polished so that the metal mesh belt after processing has more glossiness.
Description
【Technical field】
The present invention relates to a kind of welding method, and in particular to a kind of soldering method of metal mesh belt.
【Background technology】
Metal foraminous conveyer and metal finishing guipure can usually produce helical using helical machine, then by interlocking between helical
Braiding, forms spiral metal mesh belt.The edge of such metal mesh belt, the mode of bending or welding can be usually used, is used
The mode of welding, edge can be more smooth, and guipure associative perception is more preferable, and are not easy to produce with other things and hang.
However, using the welding method of prior art, by technique is limited, the guipure edge for welding out blacks, and meeting
There are some burrs.
Referring to Fig. 1, Fig. 1 is schematically shown as the metal mesh belt schematic diagram of the welding method production of prior art.As illustrated, should
The surface blackening of solder joint 101 of metal mesh belt 100 and there is burr 102.
In view of this, it is necessary to develop a kind of soldering method of metal mesh belt in fact, to solve the above problems.
【The content of the invention】
It is therefore an object of the present invention to provide a kind of soldering method of metal mesh belt, solves metal mesh belt edge welding
The problem of blacking after connecing.
In order to achieve the above object, the soldering method of metal mesh belt of the invention, this method is using argon arc welding to phase
Adjacent helical end welding, the process that solder joint reddens in welding are passed through inert gas.
Optionally, the inert gas is argon gas.
Optionally, the mode that is passed through of the inert gas is blown on the surface of the solder joint.
Optionally, the inert gas is passed through before solder joint blackening.
Optionally, the inert gas was passed through at -5 seconds 0.5 second after solder joint reddens.
Optionally, the soldering method of the metal mesh belt also includes a polishing operation, and the pad surface after welding is entered
Row polishing.
Optionally, the sand paper that the bruting process uses is sand paper more than 500 mesh.
Optionally, the soldering method of the metal mesh belt also includes a polishing process, to the gold after welding or after polishing
Category guipure is polished.
Compared to prior art, the soldering method of metal mesh belt of the invention, due to being that solder joint reddens in welding
Process be passed through inert gas, therefore air can be blown away, butt welding point surface is protected, and avoids solder joint oxidation blackening,
Butt welding point is finely polished, and can remove the burr of pad surface, the metal mesh belt after welding is polished so that place
Metal mesh belt after reason has more glossiness.
【Brief description of the drawings】
Fig. 1 is schematically shown as the metal mesh belt schematic diagram of the welding method production of prior art.
Fig. 2 is schematically shown as the metal mesh belt schematic diagram after the soldering method processing of metal mesh belt of the present invention.
【Embodiment】
In order to achieve the above object, the soldering method of metal mesh belt of the invention, this method is using argon arc welding to phase
Adjacent helical end welding, the process that solder joint reddens in welding are passed through inert gas.
Referring to Fig. 2, the metal mesh belt that Fig. 2 is schematically shown as after the soldering method processing of metal mesh belt of the present invention shows
It is intended to.
The soldering method of the metal mesh belt of the present invention, due to being that the process that solder joint reddens in welding is passed through indifferent gas
Body, therefore air can be blown away, the surface of butt welding point 201 is protected, and is avoided solder joint 201 and is aoxidized blackening.
Wherein, the inert gas is argon gas.
Wherein, the mode that is passed through of the inert gas is blown on the surface of the solder joint 201, can avoid or reduce welding
During air and solder joint 201 touch opportunity, reduce the surface oxidation of solder joint 201.
Wherein, the inert gas is passed through before the blackening of solder joint 201, experiments verify that, blackening can be greatly reduced
Probability.
Wherein, the inert gas is passed through when -5 seconds 0.5 second after solder joint 201 reddens, and by verifying repeatedly, this is one
It is individual good to be passed through opportunity.
Wherein, the soldering method of the metal mesh belt also includes a polishing operation, it is however generally that, at the above method
The less burr in surface after reason, if burr be present, the surface of solder joint 201 after welding is polished, butt welding point 201 is finely beaten
Mill, the burr on the surface of solder joint 201 can be removed.
Wherein, it is demonstrated experimentally that the sand paper that uses of the bruting process has better effects for sand paper more than 500 mesh, and
It will not make it that solder joint 201 is impaired.
Wherein, the soldering method of the metal mesh belt also includes a polishing process, to the metal after welding or after polishing
Guipure 200 is polished, due to being polished to the metal mesh belt 200 after welding so that the metal mesh belt 200 after processing has more
Glossiness.
It is noted that the invention is not restricted to above-mentioned embodiment, any person skilled in the art is based on this hair
Any simple modification, equivalent change and modification that bright technical scheme is made to above-described embodiment, both fall within the protection model of the present invention
In enclosing.
Claims (9)
1. a kind of soldering method of metal mesh belt, it is characterised in that this method is welded using argon arc welding to adjacent helical end
Connect, the process that solder joint reddens in welding is passed through inert gas.
2. the soldering method of metal mesh belt according to claim 1, it is characterised in that the inert gas is argon
Gas.
3. the soldering method of metal mesh belt according to claim 1, it is characterised in that the inert gas is passed through
Mode is blown on the surface of the solder joint.
4. the soldering method of metal mesh belt according to claim 1, it is characterised in that the inert gas is to weld
It is passed through before point blackening.
5. the soldering method of metal mesh belt according to claim 1, it is characterised in that the inert gas is to weld
It is passed through when putting after reddening -5 seconds 0.5 second.
6. the soldering method of the metal mesh belt according to any one of claim 1-5, it is characterised in that the wire netting
The soldering method of band also includes a polishing process, and the metal mesh belt after welding is polished.
7. the soldering method of the metal mesh belt according to any one of claim 1-5, it is characterised in that the wire netting
The soldering method of band also includes a polishing operation, and the pad surface after welding is polished.
8. the soldering method of metal mesh belt according to claim 7, it is characterised in that what the bruting process used
Sand paper is sand paper more than 500 mesh.
9. the soldering method of metal mesh belt according to claim 8, it is characterised in that the weld of the metal mesh belt
Reason method also includes a polishing process, and the metal mesh belt after polishing is polished.