CN107385550A - A kind of antibacterial automobile interior carpet material and preparation method thereof - Google Patents
A kind of antibacterial automobile interior carpet material and preparation method thereof Download PDFInfo
- Publication number
- CN107385550A CN107385550A CN201710689732.XA CN201710689732A CN107385550A CN 107385550 A CN107385550 A CN 107385550A CN 201710689732 A CN201710689732 A CN 201710689732A CN 107385550 A CN107385550 A CN 107385550A
- Authority
- CN
- China
- Prior art keywords
- pellet
- parts
- antibacterial
- extruder
- automobile interior
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of antibacterial automobile interior carpet material and preparation method thereof, it is prepared by the raw material of following mass parts, 50 80 parts of titanium dioxide powder, 25 parts of nano-graphene, 10 50 parts of pellet.Preparation method comprises the following steps：(1) it is put into after mixing titanium dioxide powder, nano-graphene and pellet in extruder, simultaneously pelletizing obtains antibacterial matrices to extrusion at being 150 DEG C 250 DEG C in the operating temperature of extruder；(2) antibacterial matrices prepared in step (1) are added in pellet, it is put into after mixing in extruder, wherein in compound the weight/mass percentage composition of antibacterial matrices be 5 20%, surplus be pellet, extruded at being 150 DEG C 200 DEG C in extruder operating temperature and be spun into long filament or chopped fiber by spinning equipment.Vehicle internal decoration carpet fibrous material prepared by the preparation method of the present invention has the function that antibacterial, while manufacture craft is simple, is adapted to industrialized production.
Description
Technical field
The invention belongs to automotive trim product technical field, and in particular to a kind of antibacterial automobile interior carpet material and its preparation
Method.
Background technology
Vehicle internal decoration carpet common at present directly (is commonly called as using PA (being commonly called as nylon), PP (being commonly called as polypropylene fibre), PET mostly
Terylene) fibrous material weaving, i.e. nylon, polypropylene fibre, polyester fiber directly weaved into automotive trim carpet without modified, these
Although vehicle internal decoration carpet has the functions such as antifouling, dust suction, use for a long time, due to being drawn badly in automobile, temperature humidity
It is not easily controlled, the easy mould growth of vehicle internal decoration carpet, the length of time one will influence to drive the health with passenger.
The content of the invention
To solve the above problems, it is an object of the invention to provide a kind of antibacterial automobile interior carpet material and its preparation side
Method, specific technical scheme are：
A kind of antibacterial automobile interior carpet material, is prepared by the raw material of following mass parts, titanium dioxide powder 50-80
Part, nano-graphene 2-5 parts, pellet 10-50 parts.
Preferably, a kind of antibacterial automobile interior carpet material of the present invention, by the raw material preparation of following mass parts
Into, 60 parts of titanium dioxide powder, 3 parts of nano-graphene, 30 parts of pellet.
Preferably, the pellet is polyethylene terephthalate.
A kind of preparation method of antibacterial automobile interior carpet material of the present invention, comprises the following steps：
(1) it is put into after mixing titanium dioxide powder, nano-graphene and pellet in extruder, in the operating temperature of extruder
For extrusion at 150 DEG C -250 DEG C and pelletizing obtains antibacterial matrices；
(2) antibacterial matrices prepared in step (1) are added in pellet, are put into after mixing in extruder, wherein mixing
In material the weight/mass percentage composition of antibacterial matrices be 5-20%, surplus be pellet, extruder operating temperature be 150 DEG C -200 DEG C at
Extrude and pass through spinning equipment and be spun into long filament or chopped fiber.
Beneficial effect：The invention provides a kind of antibacterial automobile interior carpet material and preparation method thereof, system of the invention
Vehicle internal decoration carpet fibrous material prepared by Preparation Method has the function that antibacterial, while manufacture craft is simple, is adapted to industrial metaplasia
Production；The vehicle internal decoration carpet produced using the fibrous material of the present invention has the advantages of antibacterial, economical and practical.
Embodiment
The invention will now be further described with reference to specific embodiments, and following examples are only the optimal implementation of the present invention
Example, any restrictions are not formed to the scope of the present invention.It will be understood by those skilled in the art that without departing from the present invention's
The details and form of technical solution of the present invention can be modified or replaced under spirit and scope, but these modifications and replacement are equal
Fall within the scope of protection of the present invention.
Embodiment 1
Preferably, a kind of antibacterial automobile interior carpet material of the present invention, by the raw material preparation of following mass parts
Into, 60 parts of titanium dioxide powder, 3 parts of nano-graphene, 30 parts of pellet.
Preferably, the pellet is polyethylene terephthalate.
A kind of preparation method of antibacterial automobile interior carpet material of the present invention, comprises the following steps：
(1) it is put into after mixing titanium dioxide powder, nano-graphene and pellet in extruder, in the operating temperature of extruder
For extrusion at 200 DEG C and pelletizing obtains antibacterial matrices；
(2) antibacterial matrices prepared in step (1) are added in pellet, are put into after mixing in extruder, wherein mixing
In material the weight/mass percentage composition of antibacterial matrices be 10%, surplus be pellet, extrude and pass through at being 180 DEG C in extruder operating temperature
Cross spinning equipment and be spun into long filament or chopped fiber.
Embodiment 2
A kind of antibacterial automobile interior carpet material, is prepared by the raw material of following mass parts, 50 parts of titanium dioxide powder, is received
2 parts of graphene of rice, 10 parts of pellet.
Preferably, the pellet is polyethylene terephthalate.
A kind of preparation method of antibacterial automobile interior carpet material of the present invention, comprises the following steps：
(1) it is put into after mixing titanium dioxide powder, nano-graphene and pellet in extruder, in the operating temperature of extruder
For extrusion at 150 DEG C and pelletizing obtains antibacterial matrices；
(2) antibacterial matrices prepared in step (1) are added in pellet, are put into after mixing in extruder, wherein mixing
In material the weight/mass percentage composition of antibacterial matrices be 5-20%, surplus be pellet, extruder operating temperature be 150 DEG C at extrude simultaneously
Long filament or chopped fiber are spun into by spinning equipment.
Embodiment 3
A kind of antibacterial automobile interior carpet material, is prepared by the raw material of following mass parts, 80 parts of titanium dioxide powder, is received
5 parts of graphene of rice, 50 parts of pellet.
Preferably, the pellet is polyethylene terephthalate.
A kind of preparation method of antibacterial automobile interior carpet material of the present invention, comprises the following steps：
(1) it is put into after mixing titanium dioxide powder, nano-graphene and pellet in extruder, in the operating temperature of extruder
For extrusion at 250 DEG C and pelletizing obtains antibacterial matrices；
(2) antibacterial matrices prepared in step (1) are added in pellet, are put into after mixing in extruder, wherein mixing
In material the weight/mass percentage composition of antibacterial matrices be 5-20%, surplus be pellet, extruder operating temperature be 200 DEG C at extrude simultaneously
Long filament or chopped fiber are spun into by spinning equipment.
Embodiment 4
A kind of antibacterial automobile interior carpet material, is prepared by the raw material of following mass parts, 65 parts of titanium dioxide powder, is received
4 parts of graphene of rice, 25 parts of pellet.
Preferably, the pellet is polyethylene terephthalate.
A kind of preparation method of antibacterial automobile interior carpet material of the present invention, comprises the following steps：
(1) it is put into after mixing titanium dioxide powder, nano-graphene and pellet in extruder, in the operating temperature of extruder
For extrusion at 220 DEG C and pelletizing obtains antibacterial matrices；
(2) antibacterial matrices prepared in step (1) are added in pellet, are put into after mixing in extruder, wherein mixing
In material the weight/mass percentage composition of antibacterial matrices be 18%, surplus be pellet, extrude and pass through at being 175 DEG C in extruder operating temperature
Cross spinning equipment and be spun into long filament or chopped fiber.
Claims (4)
1. a kind of antibacterial automobile interior carpet material, it is characterised in that be prepared by the raw material of following mass parts, titanium dioxide
Powder 50-80 parts, nano-graphene 2-5 parts, pellet 10-50 parts.
2. a kind of antibacterial automobile interior carpet material according to claim 1, it is characterised in that by the original of following mass parts
Material is prepared, 60 parts of titanium dioxide powder, 3 parts of nano-graphene, 30 parts of pellet.
3. a kind of antibacterial automobile interior carpet material according to claim 1 or 2, it is characterised in that the pellet is poly-
Ethylene glycol terephthalate.
4. the preparation method of the antibacterial automobile interior carpet material described in a kind of claim 1, it is characterised in that including following step
Suddenly：
(1) it is put into after mixing titanium dioxide powder, nano-graphene and pellet in extruder, is in the operating temperature of extruder
Simultaneously pelletizing obtains antibacterial matrices to extrusion at 150 DEG C -250 DEG C；
(2) antibacterial matrices prepared in step (1) are added in pellet, are put into after mixing in extruder, wherein in compound
The weight/mass percentage composition of antibacterial matrices is 5-20%, surplus is pellet, is extruded at being 150 DEG C -200 DEG C in extruder operating temperature
And it is spun into long filament or chopped fiber by spinning equipment.