CN107385425A - A kind of auto parts remove oil antirust agent - Google Patents
A kind of auto parts remove oil antirust agent Download PDFInfo
- Publication number
- CN107385425A CN107385425A CN201710610521.2A CN201710610521A CN107385425A CN 107385425 A CN107385425 A CN 107385425A CN 201710610521 A CN201710610521 A CN 201710610521A CN 107385425 A CN107385425 A CN 107385425A
- Authority
- CN
- China
- Prior art keywords
- ethanol
- antirust agent
- sodium
- auto parts
- remove oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of auto parts remove oil antirust agent, are made from the following raw materials in parts by weight：Citric acid 56, triethanolamine 46, petroleum sodium sulfonate 45, AEO 34, sodium molybdate 12, ethanol 30 34, ethylene diamine tetra methylene phosphonic acid 23,2 butyl cellosolves 12, ethoxylated trimethylolpropane triacrylate 10 12, EDETATE SODIUM magnesium 12, additive, water 400, a kind of auto parts proposed by the present invention remove oil antirust agent, film can be formed in metal surface, play isolation air, anti-oxidation effect, it can more securely stick antirust agent simultaneously, rust-proof effect is grown, manufacturing cost is low, easy to spread.
Description
Technical field
The invention belongs to auto parts technical field, and in particular to a kind of auto parts remove oil antirust agent.
Background technology
Although traditional hard film rust preventive oil is adapted to long-term rust prevention, film forming is also transparent attractive in appearance, the resin kind of water white transparency
Class is less, unstable also easy oxidation discoloration, it is also necessary to organic solvent dissolves, bring inflammable and explosive danger be also unfavorable for environmental protection and
Health；In general antirust oil uses mineral oil, difficult degradation, and the problem of be used to also bring along oil removing difficulty during short-term rust prevention.Cause
This, comprehensive study performance is more excellent, and the antirust product being more suitable for for different occasion researchs is new direction and become.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of auto parts to remove oil antirust agent, and antirust solution has antirust time
Long, non-volatility acid, the characteristics of being remained without anvil cinder.
To realize above-mentioned technical purpose and the technique effect, the present invention is achieved through the following technical solutions：
A kind of auto parts remove oil antirust agent, are made from the following raw materials in parts by weight：Citric acid 5-6, triethanolamine 4-6,
Petroleum sodium sulfonate 4-5, AEO 3-4, sodium molybdate 1-2, ethanol 30-34, ethylene diamine tetra methylene phosphonic acid 2-3,2-
Butoxy-ethanol 1-2, ethoxylated trimethylolpropane triacrylate 10-12, EDETATE SODIUM magnesium 1-2, additive, water
400。
Preferably, can also be made from the following raw materials in parts by weight：Citric acid 5, triethanolamine 4, oil sulphur
Sour sodium 4, AEO 3, sodium molybdate 1, ethanol 30, ethylene diamine tetra methylene phosphonic acid 2,2- butoxy-ethanol 1, ethoxy
Base trimethylolpropane trimethacrylate 10, EDETATE SODIUM magnesium 1, additive, water 400.
Preferably, can also be made from the following raw materials in parts by weight, citric acid 6, triethanolamine 6, oil sulphur
Sour sodium 5, AEO 4, sodium molybdate 2, ethanol 34, ethylene diamine tetra methylene phosphonic acid 3,2- butoxy-ethanol 2, ethoxy
Base trimethylolpropane trimethacrylate 12, EDETATE SODIUM magnesium 2, additive, water 400.
Preferably, the additive is made from the following raw materials in parts by weight：Sorbitol polyoxyethylene ether 2-3, titanium dioxide
0.2-0.4, sodium tripolyphosphate 3-4, silicate 3-4, methenamine 1.5-3, borax 2.5-3.5, urea 1-3, ammonium persulfate 1-
3rd, deionized water 20-30.
The beneficial effects of the present invention are：Film can be formed in metal surface, play isolation air, anti-oxidation effect,
Antirust agent can more securely be sticked simultaneously, rust-proof effect length, manufacturing cost is low, easy to spread.
Embodiment
Embodiment:A kind of auto parts remove oil antirust agent, are made from the following raw materials in parts by weight：Citric acid 5-6, three ethanol
Amine 4-6, petroleum sodium sulfonate 4-5, AEO 3-4, sodium molybdate 1-2, ethanol 30-34, ethylene diamine tetra methylene phosphonic acid
2-3,2- butoxy-ethanol 1-2, ethoxylated trimethylolpropane triacrylate 10-12, EDETATE SODIUM magnesium 1-2, addition
Agent, water 400.
Preferably, can also be made from the following raw materials in parts by weight：Citric acid 5, triethanolamine 4, oil sulphur
Sour sodium 4, AEO 3, sodium molybdate 1, ethanol 30, ethylene diamine tetra methylene phosphonic acid 2,2- butoxy-ethanol 1, ethoxy
Base trimethylolpropane trimethacrylate 10, EDETATE SODIUM magnesium 1, additive, water 400.
Preferably, can also be made from the following raw materials in parts by weight, citric acid 6, triethanolamine 6, oil sulphur
Sour sodium 5, AEO 4, sodium molybdate 2, ethanol 34, ethylene diamine tetra methylene phosphonic acid 3,2- butoxy-ethanol 2, ethoxy
Base trimethylolpropane trimethacrylate 12, EDETATE SODIUM magnesium 2, additive, water 400.
Preferably, the additive is made from the following raw materials in parts by weight：Sorbitol polyoxyethylene ether 2-3, titanium dioxide
0.2-0.4, sodium tripolyphosphate 3-4, silicate 3-4, methenamine 1.5-3, borax 2.5-3.5, urea 1-3, ammonium persulfate 1-
3rd, deionized water 20-30.
Described above is only the preferred application implementation mode of the present invention, it is noted that for the common skill of the art
For art personnel, without departing from the technical principles of the invention, some improvement can also be made.
Claims (4)
1. a kind of auto parts remove oil antirust agent, it is characterised in that：It is made from the following raw materials in parts by weight, citric acid 5-6, three second
Hydramine 4-6, petroleum sodium sulfonate 4-5, AEO 3-4, sodium molybdate 1-2, ethanol 30-34, ethylenediamine tetraacetic methene phosphine
Sour 2-3,2- butoxy-ethanol 1-2, ethoxylated trimethylolpropane triacrylate 10-12, EDETATE SODIUM magnesium 1-2, addition
Agent, water 400.
2. auto parts according to claim 1 remove oil antirust agent, it is characterised in that：By the raw material system of following parts by weight
Into citric acid 5, triethanolamine 4, petroleum sodium sulfonate 4, AEO 3, sodium molybdate 1, ethanol 30, ethylenediamine tetramethyl
Pitch phosphonic acids 2,2- butoxy-ethanol 1, ethoxylated trimethylolpropane triacrylate 10, EDETATE SODIUM magnesium 1, additive, water
400。
3. auto parts according to claim 1 remove oil antirust agent, it is characterised in that：By the raw material system of following parts by weight
Into citric acid 6, triethanolamine 6, petroleum sodium sulfonate 5, AEO 4, sodium molybdate 2, ethanol 34, ethylenediamine tetramethyl
Pitch phosphonic acids 3,2- butoxy-ethanol 2, ethoxylated trimethylolpropane triacrylate 12, EDETATE SODIUM magnesium 2, additive, water
400。
4. the auto parts according to right will remove 1-3 remove oil antirust agent, it is characterised in that：The additive is by following weight
The raw material of part is made, sorbitol polyoxyethylene ether 2-3, titanium dioxide 0.2-0.4, sodium tripolyphosphate 3-4, silicate 3-4, Wu Luo
Tropine 1.5-3, borax 2.5-3.5, urea 1-3, ammonium persulfate 1-3, deionized water 20-30.