CN107385359A - A kind of stainless steel burglary-resisting window cracking resistance coating material - Google Patents

A kind of stainless steel burglary-resisting window cracking resistance coating material Download PDF

Info

Publication number
CN107385359A
CN107385359A CN201710572895.XA CN201710572895A CN107385359A CN 107385359 A CN107385359 A CN 107385359A CN 201710572895 A CN201710572895 A CN 201710572895A CN 107385359 A CN107385359 A CN 107385359A
Authority
CN
China
Prior art keywords
mass fraction
stainless steel
resisting window
coating material
cracking resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710572895.XA
Other languages
Chinese (zh)
Inventor
胡昌悌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Shuangbao Building Material Co Ltd
Original Assignee
Wuhu Shuangbao Building Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Shuangbao Building Material Co Ltd filed Critical Wuhu Shuangbao Building Material Co Ltd
Priority to CN201710572895.XA priority Critical patent/CN107385359A/en
Publication of CN107385359A publication Critical patent/CN107385359A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of stainless steel burglary-resisting window cracking resistance coating material, and it includes following components by mass fraction：C：0.6~1.2%, B：0.5~1%, Si：0.8~1.3%, Mn：0.8~1.2%, Cr：11~14%, Ti：0.5~0.8%, V：0.4~0.8%, Sc：0.4~0.6%, Sr：0.1~0.3%, Zr：0.3~0.6%, Ni：3~5%, Nb：0.1~0.22%, Ce：0.3~0.5%, La：0.2~0.4%, Y：0.4~0.6%, surplus is Fe and inevitable impurity.A kind of stainless steel burglary-resisting window cracking resistance coating material proposed by the present invention, it has, and splitting resistance is strong with corrosion resistance, difficult for drop-off with ftractureing, beautiful appearance, extends the service life of burglary-resisting window.

Description

A kind of stainless steel burglary-resisting window cracking resistance coating material
Technical field
The present invention relates to coating material technical field, more particularly to a kind of stainless steel burglary-resisting window cracking resistance coating material.
Background technology
Coating, which refers to be attached on a certain matrix material, plays certain special role, and has certain combine by force with matrix material The layer material of degree, it can overcome certain defect of matrix material, improve its surface characteristic, as optical characteristics, electrology characteristic, Resistant to corrosion and burn into wear resistance and raising mechanical strength etc..Burglary-resisting window is easily made because its working environment is complicated to its surface Into cracking and corrosion, the reduction of its performance is caused, influences its outward appearance, so needing development is a kind of to have cracking resistance and corrosion resistance strong Metal coating, for improving the overall performance of burglary-resisting window, extend the service life of burglary-resisting window.
The content of the invention
Based on technical problem existing for background technology, the present invention proposes a kind of stainless steel burglary-resisting window cracking resistance coating material Material, it has, and splitting resistance is strong with corrosion resistance, while big with burglary-resisting window metallic matrix bond strength, difficult for drop-off with ftractureing, Beautiful appearance, effectively extend the service life of burglary-resisting window.
A kind of stainless steel burglary-resisting window cracking resistance coating material proposed by the present invention, it is included with the following group by mass fraction Point：C：0.6~1.2%, B：0.5~1%, Si：0.8~1.3%, Mn：0.8~1.2%, Cr：11~14%, Ti：1.5~ 2.2%th, V：0.6~1.2%, Sc：0.4~0.6%, Sr：0.1~0.3%, Zr：0.3~0.6%, Ni：3~5%, Nb： 0.25~0.4%, Ce：0.3~0.5%, La：0.2~0.4%, Y：0.4~0.6%, surplus be Fe and inevitably it is miscellaneous Matter.
In specific embodiment, C mass fraction can also be 0.7%, 0.8%, 0.9%, 1%, 1.1%, B quality point Number can also be 0.6%, 0.7%, 0.75%, 0.8%, 0.9%, Si mass fraction can also be 0.9%, 1%, 1.1%, 1.15%th, 1.2%, Mn mass fraction can also be 0.9%, 0.95%, 1%, 1.1%, 1.15%, Cr mass fraction also Can be 11.5%, 12%, 12.5%, 13%, 13.5%, Ti mass fraction can also be 1.6%, 1.7%, 1.8%, 2%th, 2.1%, V mass fraction can also can also be for 0.7%, 0.8%, 0.9%, 1%, 1.1%, Sc mass fraction 0.44%th, 0.48%, 0.5%, 0.52%, 0.55%, 0.58%, Sr mass fraction can also be 0.14%, 0.18%, 0.2%th, 0.22%, 0.25%, 0.28%, Zr mass fraction can also be 0.35%, 0.4%, 0.45%, 0.5%, 0.55%, Ni mass fraction can also may be used also for 3.2%, 3.5%, 4%, 4.2%, 4.5%, 4.8%, Nb mass fraction Think 0.28%, 0.3%, 0.33%, 0.35%, 0.38%, Ce mass fraction can also be 0.32%, 0.35%, 0.38%th, 0.42%, 0.45%, 0.48%, La mass fraction can also be 0.24%, 0.28%, 0.32%, 0.35%, 0.38%, Y mass fraction can also be 0.44%, 0.48%, 0.52%, 0.55%, 0.58%, and surplus is Fe and can not kept away The impurity exempted from.
Preferably, it includes following components by mass fraction：C：0.7~1.1%, B：0.65~0.9%, Si：0.9~ 1.2%th, Mn：0.9~1.1%, Cr：11.5~13.5%, Ti：1.6~2%, V：0.7~1%, Sc：0.45~0.55%, Sr：0.15~0.25%, Zr：0.35~0.55%, Ni：3.5~4.5%, Nb：0.3~0.35%, Ce：0.35~0.45%, La：0.25~0.35%, Y：0.45~0.55%, surplus is Fe and inevitable impurity.
Preferably, it includes following components by mass fraction：C：0.9%th, B：0.8%th, Si：1%th, Mn：1%th, Cr： 12.5%th, Ti：1.8%th, V：0.85%th, Sc：0.55%th, Sr：0.2%th, Zr：0.455%th, Ni：4%th, Nb：0.33%th, Ce： 0.45%th, La：0.3%th, Y：0.5%, surplus is Fe and inevitable impurity.
Preferably, V, Nb, Ti mass fraction meet relationship below：2.7%≤wV+wNb+wTi≤ 3.2%；Wherein, wV For V mass fraction, wNbFor Nb mass fraction, wTiFor Ti mass fraction.
Preferably, C, B, Nb mass fraction meet relationship below：wC=wB+wNb- k, wherein, wCFor C quality point Number, wBFor B mass fraction, wNbFor Nb mass fraction, k=0.15~0.25%.
By optimization of C/C composites in the present invention, the content of each component is controlled so that coating of the present invention has good corrosion-resistant Property, splitting resistance, heat resistance and creep resistance, while also have that hardness is big, good toughness, with stainless steel burglary-resisting window metallic matrix Bond strength is big, the service life difficult for drop-off with cracking, effectively extension stainless steel burglary-resisting window；By controlling B, Zr, Sc, C, Nb Content, V, Nb, Ti and C, B, Nb is met certain functional relation, show good deoxidation dehydrogenation effect, generation Strong carbide Dispersed precipitate is in metal coating, raising nucleation rate, effective thinning microstructure crystal grain, improves the knot of tissue of metal coating Structure, hardness, intensity, toughness, wearability, the corrosion resistance of metal coating are improved, and improve coating and stainless steel burglary-resisting window metal The bond strength of matrix；By controlling the content of rare element, porosity is reduced, effectively refines and improves each nascent in coating The size and distribution of carbide and hardening constituent, improve the overall performance of coating.A kind of stainless steel stainless steel proposed by the present invention is prevented Steal window cracking resistance coating material, it has, and splitting resistance is strong with corrosion resistance, at the same with stainless steel burglary-resisting window metallic matrix knot It is big to close intensity, the service life difficult for drop-off with cracking, effectively extension stainless steel burglary-resisting window.
Embodiment
Below, technical scheme is described in detail by specific embodiment.
Embodiment 1
A kind of stainless steel burglary-resisting window cracking resistance coating material proposed by the present invention, it is included with the following group by mass fraction Point：C：0.6%th, B：1%th, Si：0.8%th, Mn：1.2%th, Cr：11%th, Ti：2.2%th, V：0.6%th, Sc：.6%, Sr：0.1%th, Zr：0.6%th, Ni：3%th, Nb：0.22%th, Ce：0.3%th, La：0.4%th, Y：0.4%, surplus is Fe and inevitable impurity.
Embodiment 2
A kind of stainless steel burglary-resisting window cracking resistance coating material proposed by the present invention, it is included with the following group by mass fraction Point：C：1.2%th, B：0.5%th, Si：1.3%th, Mn：0.8%th, Cr：14%th, Ti：1.5%th, V：1.2%th, Sc：0.4%th, Sr： 0.3%th, Zr：0.3%th, Ni：5%th, Nb：0.1%th, Ce：0.5%th, La：0.2%th, Y：0.6%, surplus is for Fe and inevitably Impurity.
Embodiment 3
A kind of stainless steel burglary-resisting window cracking resistance coating material proposed by the present invention, it is included with the following group by mass fraction Point：C：0.9%th, B：0.8%th, Si：1%th, Mn：1%th, Cr：12.5%th, Ti：1.8%th, V：0.85%th, Sc：0.55%th, Sr： 0.2%th, Zr：0.455%th, Ni：4%th, Nb：0.16%th, Ce：0.45%th, La：0.3%th, Y：0.5%, surplus is Fe and can not kept away The impurity exempted from.
Embodiment 4
A kind of stainless steel burglary-resisting window cracking resistance coating material proposed by the present invention, it is included with the following group by mass fraction Point：C：0.7%th, B：0.9%th, Si：0.9%th, Mn：1.1%th, Cr：11.5%th, Ti：2%th, V：0.7%th, Sc：0.55%th, Sr： 0.15%th, Zr：0.55%th, Ni：3.5%th, Nb：0.2%th, Ce：0.35%th, La：0.35%th, Y：0.455%, surplus is for Fe and not Evitable impurity.
Embodiment 5
A kind of stainless steel burglary-resisting window cracking resistance coating material proposed by the present invention, it is included with the following group by mass fraction Point：C：1.1%th, B：0.65%th, Si：1.2%th, Mn：0.9%th, Cr：13.5%th, Ti：1.6%th, V：0.7%th, Sc：0.45%th, Sr：~0.25%, Zr：0.35%th, Ni：4.5%th, Nb：0.12、Ce：0.45%th, La：0.25%th, Y：0.55%, surplus Fe And inevitable impurity.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto, Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.

Claims (5)

1. a kind of stainless steel burglary-resisting window cracking resistance coating material, it is characterised in that it includes following components by mass fraction：C： 0.6~1.2%, B：0.5~1%, Si：0.8~1.3%, Mn：0.8~1.2%, Cr：11~14%, Ti：1.5~2.2%, V：0.6~1.2%, Sc：0.4~0.6%, Sr：0.1~0.3%, Zr：0.3~0.6%, Ni：3~5%, Nb：0.25~ 0.4%th, Ce：0.3~0.5%, La：0.2~0.4%, Y：0.4~0.6%, surplus is Fe and inevitable impurity.
2. stainless steel burglary-resisting window cracking resistance coating material according to claim 1, it is characterised in that it presses mass fraction bag Include following components：C：0.7~1.1%, B：0.65~0.9%, Si：0.9~1.2%, Mn：0.9~1.1%, Cr：11.5~ 13.5%th, Ti：1.6~2%, V：0.7~1%, Sc：0.45~0.55%, Sr：0.15~0.25%, Zr：0.35~ 0.55%th, Ni：3.5~4.5%, Nb：0.3~0.35%, Ce：0.35~0.45%, La：0.25~0.35%, Y：0.45~ 0.55%, surplus is Fe and inevitable impurity.
3. stainless steel burglary-resisting window cracking resistance coating material according to claim 1, it is characterised in that it presses mass fraction bag Include following components：C：0.9%th, B：0.8%th, Si：1%th, Mn：1%th, Cr：12.5%th, Ti：1.8%th, V：0.85%th, Sc： 0.55%th, Sr：0.2%th, Zr：0.455%th, Ni：4%th, Nb：0.33%th, Ce：0.45%th, La：0.3%th, Y：0.5%, surplus is Fe and inevitable impurity.
4. stainless steel burglary-resisting window cracking resistance coating material according to claim 1 or claim 2, it is characterised in that V, Nb, Ti matter Amount fraction meets relationship below：2.7%≤wV+wNb+wTi≤ 3.2%；Wherein, wVFor V mass fraction, wNbFor Nb quality Fraction, wTiFor Ti mass fraction.
5. stainless steel burglary-resisting window cracking resistance coating material according to claim 1 or claim 2, it is characterised in that C, B, Nb matter Amount fraction meets relationship below：wC=wB+wNb- k, wherein, wCFor C mass fraction, wBFor B mass fraction, wNbFor Nb's Mass fraction, k=0.15~0.25%.
CN201710572895.XA 2017-07-13 2017-07-13 A kind of stainless steel burglary-resisting window cracking resistance coating material Pending CN107385359A (en)