CN107384224A - A kind of graphene thermal conductivity UV glue and preparation method thereof - Google Patents
A kind of graphene thermal conductivity UV glue and preparation method thereof Download PDFInfo
- Publication number
- CN107384224A CN107384224A CN201710733216.2A CN201710733216A CN107384224A CN 107384224 A CN107384224 A CN 107384224A CN 201710733216 A CN201710733216 A CN 201710733216A CN 107384224 A CN107384224 A CN 107384224A
- Authority
- CN
- China
- Prior art keywords
- graphene
- thermal conductivity
- glue
- light trigger
- acrylic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to grapheme material field, a kind of graphene thermal conductivity UV glue, including acrylic resin contain 5wt ~ 30wt%;Graphene slurry contains 5wt ~ 50wt%;Acrylic monomers contains 10wt ~ 50wt%;Light trigger contains 0.1wt ~ 5wt%;Auxiliary agent contains 0.5wt ~ 5wt%.In this graphene thermal conductivity UV glue, graphene powder is added in UV solidification glues, the heat conduction demand of existing product can be not only solved, the mechanical strength of UV glue can also be strengthened, so as to improve the cementitiousness of UV solidification glues, and its electric conductivity can be assigned.
Description
Technical field
The present invention relates to grapheme material field, particularly a kind of graphene thermal conductivity UV glue and preparation method thereof.
Background technology
UV solidification glues, it is to use a kind of environment-friendly curing technology(UV solidifies)The product solidified, phase are used extensively
In the encapsulation of medical apparatus, electric equipment products.As electronic product develops toward the direction such as thin, light, small, intelligent, information-based,
Associated with this is that the application such as highly integrated, hypervelocity, high power conversion device is more and more intensive, cause the caloric value of electronic unit into
Scale increases rapidly, and resulting result is exactly that the temperature of electronic chip or junction temperature raise rapidly.This is to UV solidification glues
Performance requirement be consequently increased -- by heat unnecessary in the electronic product in encapsulation transfer out come, i.e., to UV solidification glues requirement
With heat conductivility.And traditional UV solidification glues often do not have heat conductivility, thus, assign the energy that UV solidification glues conduct heat
Power just seems very crucial.
Pure graphene is a kind of Two dimensional Crystallization body of only one atomic thickness, and thickness is about 0.35nm or so, with three-dimensional material
Material is different, and its low dimensional structures can significantly cut down the border radiating of grain boundaries phonon, and assign its special phonon dispersal pattern.Tool
There is the characteristic such as ultra-thin, super firm, superpower electric conductivity and the heat conductivility of superelevation, also have excellent mechanical property concurrently.Commonly
CNT its thermal conductivity factor be about 3000W/mK, and the horizontal thermal conductivity factor of single-layer graphene is up to 5300W/mK or so.
And conventional heat-conducting metal such as silver, copper, gold, aluminium, its thermal conductivity factor also can not show a candle to graphene, respectively 429W/mK, 401W/
MK, 317W/mK and 237W/mK.Excellent heat conduction and mechanical property makes graphene in the great development potentiality of field of heat management, but this
A little performances are all based on microcosmic nanoscale, to form the application also bigger difficulty of macroscopic view.Therefore, by microcosmic graphite
Alkene assembles the material to form macroscopic view, while it will be that graphene scale application is used for heat management to keep or keep its nano effect substantially
The important channel in field.
The content of the invention
To solve the above problems, the present invention provides a kind of graphene thermal conductivity UV glue, have the good capacity of heat transmission and
Mechanical strength and the capacity of heat transmission.
To achieve the above object, the technical solution adopted by the present invention is:A kind of graphene thermal conductivity UV glue, including:
Acrylic resin 5wt ~ 30wt%;
Graphene slurry 5wt ~ 50wt%;
Acrylic monomers 10wt ~ 50wt%;
Light trigger 0.1wt ~ 5wt%;
Auxiliary agent 0.5wt ~ 5wt%.
As preferable, the acrylic resin be the epoxy modified acrylic resin that viscosity is 50 ~ 2,000 mm2/s,
One kind or its mixing in polyurethane acrylic resin or pure acrylic resin.
As preferable, the graphene slurry is the resin for being mixed with graphene powder, wherein resin graphene powder
Pattern can be spherical, sheet.
As preferable, the acrylic monomers be methyl methacrylate, three contracting tripropylene glycol diacrylate monomers,
Third oxygen ethyl propylene acid ester monomer, one kind of two contracting omega-diol diacrylates or its mixing.
As preferable, the light trigger is one kind of light trigger 184, light trigger 819 or light trigger 1173
Or its mixing.
A kind of preparation method of graphene thermal conductivity UV glue, by upper acrylic resin, graphene slurry, acrylic acid list
Body, light trigger and auxiliary agent are weighed in ratio respectively, and acrylic monomers, auxiliary agent first are added into inquisition room agitator or ball milling instrument
In be well mixed, then add graphene slurry, mix 0.5 ~ 1h;Then acrylic resin, stir about 1h are added;Add afterwards
Light trigger, mix 1h;Ground and mixed three to five times in three-roll grinder, gained mixture is in vacuum(-0.1MPa)Under
1h is vented, produces graphene thermal conductivity UV glue.
Using the beneficial effects of the invention are as follows:In this graphene thermal conductivity UV glue, graphene powder addition UV is consolidated
Change in glue, can not only solve the heat conduction demand of existing product, the mechanical strength of UV glue can also be strengthened, so as to improve UV solidifications
The cementitiousness of glue, and its electric conductivity can be assigned.
Embodiment
The present invention is described in detail below.
A kind of graphene thermal conductivity UV glue, including acrylic resin contain 5wt ~ 30wt%;Graphene slurry contain 5wt ~
50wt%;Acrylic monomers contains 10wt ~ 50wt%;Light trigger contains 0.1wt ~ 5wt%;Auxiliary agent contains 0.5wt ~ 5wt%.At this
In graphene thermal conductivity UV glue, graphene powder is added in UV solidification glues, the heat conduction that can not only solve existing product needs
Ask, the mechanical strength of UV glue can also be strengthened, so as to improve the cementitiousness of UV solidification glues, and its electric conductivity can be assigned
Energy.
Acrylic resin is base frame thing, and viscosity is 50 ~ 2,000 mm2/s epoxy modified acrylic resin, poly- ammonia
One or more of mixtures in ester acrylic resin or pure acrylic resin.
Graphene slurry, it acts on the graphene powder for being to make different-shape and is easier, increase graphene affine with resin
Powder is evenly distributed in resin, so as to be added in heat conduction elargol increase the heat conductivility of heat conduction elargol, electric conductivity and
Strengthen its mechanical strength, solid content is 1 ~ 50wt%, selects suitable solid content as needed.The pattern of graphene powder can be with
It is spherical, sheet or other shapes that may be present.
Acrylic monomers is the crosslinking agent being crosslinked with base frame thing, is generally available methyl methacrylate(MMA)、
Three contracting tripropylene glycol diacrylate monomers(TPGDA), the third oxygen ethyl propylene acid ester monomer(NPGDA), the propylene of two contracting glycol two
Acid ester monomer(TMPTA)Deng can be a kind of or several mixtures.
Light trigger is catalyst, under the light action of ultra-violet (UV) band or near ultraviolet band, triggers acrylic resin to enter with monomer
The compound of row crosslinking curing, typically using light trigger 184,819,1173 etc., one kind can be used, several can also be mixed
Use.
Auxiliary agent is organic additive, increases the affinity of graphene slurry and acrylic resin, and the entirety for reducing UV glue is glued
Denseness.
In one embodiment, acrylic resin A:Epoxy modified acrylic resin(Liquid)MR7307.Graphene slurry
B:Graphene content:30wt%.Acrylic monomers C:Methyl methacrylate(MMA).Light trigger D:Changzhou space honor chemical industry is limited
Company, 819.Auxiliary agent E:Dodecyltrimethoxysilane, C12H25Si (OCH3) 3, JH-N3112.
A kind of preparation method of graphene thermal conductivity UV glue, by upper acrylic resin, graphene slurry, acrylic acid list
Body, light trigger and auxiliary agent are weighed in ratio respectively, and acrylic monomers, auxiliary agent first are added into inquisition room agitator or ball milling instrument
In be well mixed, then add graphene slurry, mix 0.5 ~ 1h;Then acrylic resin, stir about 1h are added;Add afterwards
Light trigger, mix 1h;Ground and mixed three to five times in three-roll grinder, gained mixture is in vacuum(-0.1MPa)Under
1h is vented, produces graphene thermal conductivity UV glue.
It is below the method for test this graphene thermal conductivity UV glue.
Method of testing:(Graphene thermal conductivity UV glue solidifies 30s under UV light, then test performance)
1. the test of thermal conductivity factor, is tested using LFA-467.
2. thermo-resistance measurement, tested using LFA-467.
3. resistivity measurement, tested using resistivity tester FT-300A1.
4. tensile strength is tested, tested using tensilon YN-ACH-C.
Table 1:
Wherein, component A is acrylic resin, and component B is graphene slurry, and component C is acrylic monomers, and component D is light-initiated
Agent, component E are auxiliary agent.
Above content is only presently preferred embodiments of the present invention, for one of ordinary skill in the art, according to the present invention's
Thought, in specific embodiments and applications can be so that many changes may be made, as long as these changes are without departing from the structure of the present invention
Think, belong to protection scope of the present invention.
Claims (6)
- A kind of 1. graphene thermal conductivity UV glue, it is characterised in that:IncludingAcrylic resin 5wt ~ 30wt%;Graphene slurry 5wt ~ 50wt%;Acrylic monomers 10wt ~ 50wt%;Light trigger 0.1wt ~ 5wt%;Auxiliary agent 0.5wt ~ 5wt%.
- 2. graphene thermal conductivity UV glue according to claim 1, it is characterised in that:The acrylic resin is that viscosity is 50 ~ 2,000 mm2/s epoxy modified acrylic resin, polyurethane acrylic resin or one kind in pure acrylic resin or its Mixing.
- 3. graphene thermal conductivity UV glue according to claim 1, it is characterised in that:The graphene slurry is to be mixed with The resin of graphene powder, the wherein pattern of resin graphene powder can be spherical, sheets.
- 4. graphene thermal conductivity UV glue according to claim 1, it is characterised in that:The acrylic monomers is methyl-prop E pioic acid methyl ester, three contracting tripropylene glycol diacrylate monomers, the third oxygen ethyl propylene acid ester monomer, two contracting omega-diol diacrylates A kind of or its mixing.
- 5. graphene thermal conductivity UV glue according to claim 1, it is characterised in that:The light trigger is light trigger 184th, light trigger 819 or one kind of light trigger 1173 or its mixing.
- A kind of 6. preparation method of graphene thermal conductivity UV glue, it is characterised in that:By the acrylic resin in claim 1, Graphene slurry, acrylic monomers, light trigger and auxiliary agent are weighed in ratio respectively, first add acrylic monomers, auxiliary agent It is well mixed in inquisition room agitator or ball milling instrument, then adds graphene slurry, mixes 0.5 ~ 1h;Then acrylic acid tree is added Fat, stir about 1h;Light trigger is added afterwards, mixes 1h;Ground and mixed three to five times in three-roll grinder, gained mixing Thing is in vacuum(-0.1MPa)Lower exhaust 1h, produce graphene thermal conductivity UV glue.