CN107383925A - A kind of preparation method of enhanced environment-friendlyinsulation insulation material - Google Patents
A kind of preparation method of enhanced environment-friendlyinsulation insulation material Download PDFInfo
- Publication number
- CN107383925A CN107383925A CN201710823444.9A CN201710823444A CN107383925A CN 107383925 A CN107383925 A CN 107383925A CN 201710823444 A CN201710823444 A CN 201710823444A CN 107383925 A CN107383925 A CN 107383925A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- area
- preparation
- insulation material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation method of enhanced environment-friendlyinsulation insulation material, the enhanced environment-friendlyinsulation insulation material is made up of the component of following parts by weight:6 10 parts of 80 120 parts of 6 resins of HRB, 20 40 parts of alkali-free glass fibre silk, 8 12 parts of polypropylene fibre, 46 parts of solubilizer, 16 24 parts of nano-stephanoporate silicon dioxide, 5 15 parts of dimethicone and antioxidant.The advantage of the invention is that:By the preparation method of the enhanced environment-friendlyinsulation insulation material of the present invention, the insulating materials mechanical strength prepared is high, heat-resist, has good resistance to sparking energy, is a kind of environment-friendlyinsulation insulation material of excellent combination property.
Description
Technical field
The present invention relates to insulating materials technical field, more particularly to a kind of preparation method of enhanced environment-friendlyinsulation insulation material.
Background technology
Polyester due to its excellent molding processibility, electrical insulating property and heat resistance be widely used in electronics, electrical equipment and
The industries such as household electrical appliances.In recent years, with highest attention of the society to environmental problem, the environmentally friendly poly terephthalic acid in polyester
Butanediol ester(PBT)It is widely used in insulating material field.Electric field is often referred to high temperature, hyperbaric environment, and common
Because mechanical strength, heat resistance and dielectric properties are not good enough electrical breakdown easily occurs in above-mentioned environment for PBT material.
The content of the invention
The technical problem to be solved in the present invention is to provide it is a kind of disclosure satisfy that high temperature, hyperbaric environment requirement it is enhanced
The preparation method of environment-friendlyinsulation insulation material.
In order to solve the above technical problems, the technical scheme is that:A kind of preparation side of enhanced environment-friendlyinsulation insulation material
Method, its innovative point are:The preparation method comprises the following steps:
(1)Each raw material for standby is accurately weighed by weight ratio:HRB-6 resin 80-120 parts, alkali-free glass fibre silk 20-40
Part, polypropylene fibre 8-12 parts, solubilizer 4-6 parts, nano-stephanoporate silicon dioxide 16-24 parts, dimethicone 5-15 parts and anti-
Oxygen agent 6-10 parts;
(2)HRB-6 resins, solubilizer, nano-stephanoporate silicon dioxide and antioxidant are sequentially added in banbury, with 100 turns/
Min rotating speed is stirred 20min, and banbury then is warming up into 190 DEG C, and nothing is sequentially added from loading hopper while stirring
Alkali containing glass fibre silk, polypropylene fibre and dimethicone, 10~20min of banburying, compound is set all to mix, after cooling down
Discharging, and cut into fine grained chippings;
(3)By step(2)The injection machine injection molding of the fine grained chippings of middle preparation, Shooting Technique condition are:One 190 DEG C of area's temperature,
Two 220 DEG C of area's temperature, three 220 DEG C of area's temperature, four 220 DEG C of area's temperature, five 200 DEG C of area's temperature, injection pressure 10MPa, during pressurize
Between 5min.
The advantage of the invention is that:By the preparation method of the enhanced environment-friendlyinsulation insulation material of the present invention, the insulation prepared
Mechanics of materials intensity is high, heat-resist, has good resistance to sparking energy, is a kind of environmentally friendly insulation material of excellent combination property
Material.
Embodiment
The following examples can make professional and technical personnel that the present invention be more fully understood, but therefore not send out this
It is bright to be limited among described scope of embodiments.
Embodiment 1
The preparation method of the enhanced environment-friendlyinsulation insulation material of the present embodiment, the preparation method comprise the following steps:
(1)Each raw material for standby is accurately weighed by weight ratio:80 parts of HRB-6 resins, 20 parts of alkali-free glass fibre silk, polypropylene
6 parts of 8 parts of fiber, 4 parts of solubilizer, 16 parts of nano-stephanoporate silicon dioxide, 5 parts of dimethicone and antioxidant;
(2)HRB-6 resins, solubilizer, nano-stephanoporate silicon dioxide and antioxidant are sequentially added in banbury, with 100 turns/
Min rotating speed is stirred 20min, and banbury then is warming up into 190 DEG C, and nothing is sequentially added from loading hopper while stirring
Alkali containing glass fibre silk, polypropylene fibre and dimethicone, banburying 10min, compound is all mixed, go out after cooling down
Material, and cut into fine grained chippings;
(3)By step(2)The injection machine injection molding of the fine grained chippings of middle preparation, Shooting Technique condition are:One 190 DEG C of area's temperature,
Two 220 DEG C of area's temperature, three 220 DEG C of area's temperature, four 220 DEG C of area's temperature, five 200 DEG C of area's temperature, injection pressure 10MPa, during pressurize
Between 5min.
Embodiment 2
The preparation method of the enhanced environment-friendlyinsulation insulation material of the present embodiment, the preparation method comprise the following steps:
(1)Each raw material for standby is accurately weighed by weight ratio:120 parts of HRB-6 resins, 40 parts of alkali-free glass fibre silk, poly- third
10 parts of 12 parts of alkene fiber, 6 parts of solubilizer, 24 parts of nano-stephanoporate silicon dioxide, 15 parts of dimethicone and antioxidant;
(2)HRB-6 resins, solubilizer, nano-stephanoporate silicon dioxide and antioxidant are sequentially added in banbury, with 100 turns/
Min rotating speed is stirred 20min, and banbury then is warming up into 190 DEG C, and nothing is sequentially added from loading hopper while stirring
Alkali containing glass fibre silk, polypropylene fibre and dimethicone, banburying 20min, compound is all mixed, go out after cooling down
Material, and cut into fine grained chippings;
(3)By step(2)The injection machine injection molding of the fine grained chippings of middle preparation, Shooting Technique condition are:One 190 DEG C of area's temperature,
Two 220 DEG C of area's temperature, three 220 DEG C of area's temperature, four 220 DEG C of area's temperature, five 200 DEG C of area's temperature, injection pressure 10MPa, during pressurize
Between 5min.
Embodiment 3
The preparation method of the enhanced environment-friendlyinsulation insulation material of the present embodiment, the preparation method comprise the following steps:
(1)Each raw material for standby is accurately weighed by weight ratio:100 parts of HRB-6 resins, 30 parts of alkali-free glass fibre silk, poly- third
8 parts of 10 parts of alkene fiber, 5 parts of solubilizer, 20 parts of nano-stephanoporate silicon dioxide, 10 parts of dimethicone and antioxidant;
(2)HRB-6 resins, solubilizer, nano-stephanoporate silicon dioxide and antioxidant are sequentially added in banbury, with 100 turns/
Min rotating speed is stirred 20min, and banbury then is warming up into 190 DEG C, and nothing is sequentially added from loading hopper while stirring
Alkali containing glass fibre silk, polypropylene fibre and dimethicone, banburying 15min, compound is all mixed, go out after cooling down
Material, and cut into fine grained chippings;
(3)By step(2)The injection machine injection molding of the fine grained chippings of middle preparation, Shooting Technique condition are:One 190 DEG C of area's temperature,
Two 220 DEG C of area's temperature, three 220 DEG C of area's temperature, four 220 DEG C of area's temperature, five 200 DEG C of area's temperature, injection pressure 10MPa, during pressurize
Between 5min.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The skill of the industry
For art personnel it should be appreciated that the present invention is not limited to the above embodiments, described in above-described embodiment and specification is explanation
The principle of the present invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these
Changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and
Its equivalent thereof.
Claims (1)
- A kind of 1. preparation method of enhanced environment-friendlyinsulation insulation material, it is characterised in that:The preparation method comprises the following steps:(1)Each raw material for standby is accurately weighed by weight ratio:HRB-6 resin 80-120 parts, alkali-free glass fibre silk 20-40 Part, polypropylene fibre 8-12 parts, solubilizer 4-6 parts, nano-stephanoporate silicon dioxide 16-24 parts, dimethicone 5-15 parts and anti- Oxygen agent 6-10 parts;(2)HRB-6 resins, solubilizer, nano-stephanoporate silicon dioxide and antioxidant are sequentially added in banbury, with 100 turns/ Min rotating speed is stirred 20min, and banbury then is warming up into 190 DEG C, and nothing is sequentially added from loading hopper while stirring Alkali containing glass fibre silk, polypropylene fibre and dimethicone, 10~20min of banburying, compound is set all to mix, after cooling down Discharging, and cut into fine grained chippings;(3)By step(2)The injection machine injection molding of the fine grained chippings of middle preparation, Shooting Technique condition are:One 190 DEG C of area's temperature, Two 220 DEG C of area's temperature, three 220 DEG C of area's temperature, four 220 DEG C of area's temperature, five 200 DEG C of area's temperature, injection pressure 10MPa, during pressurize Between 5min.