CN107382225A - A kind of string imitates bag reason Side fascia and preparation method thereof - Google Patents
A kind of string imitates bag reason Side fascia and preparation method thereof Download PDFInfo
- Publication number
- CN107382225A CN107382225A CN201710698346.7A CN201710698346A CN107382225A CN 107382225 A CN107382225 A CN 107382225A CN 201710698346 A CN201710698346 A CN 201710698346A CN 107382225 A CN107382225 A CN 107382225A
- Authority
- CN
- China
- Prior art keywords
- bed
- string
- following
- parts
- side fascia
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to building material technical field, more particularly to a kind of string to imitate bag reason Side fascia, and it includes the bed of material, the middle bed of material and the following bed of material above；The bed of material and the following bed of material are prepared by including the following raw material above：Quick hardening sulphoaluminate cement, water, string, and additive；The middle bed of material including the following raw material by being prepared：Quick hardening sulphoaluminate cement, water, string, and additive；Alkaline-resisting short glass fiber grid cloth is equipped with the bed of material, the middle bed of material and the following bed of material above；Above bag texture is provided with the outside of the bed of material.In addition, present invention also offers a kind of method for preparing Side fascia.The string of the present invention imitates bag reason Side fascia, and density is low, toughness is high；It is provided with bag texture in the production stage, reduces the extra charge of later stage decoration.Used raw material is cheap and easy to get, reduces the production cost of product.
Description
Technical field
The invention belongs to building material technical field, more particularly to a kind of string to imitate bag reason Side fascia and its preparation
Method.
Background technology
The application of Side fascia makes building seem honest natural and attractive in appearance, can resist various bad weathers, and anti-corrosion
It is fire-retardant, simple installation.No matter in process of production or in Practical, environment is not polluted, and renewable profit
With being preferable environmental-protection decorative material.But existing Side fascia is mostly using quartz sand as aggregate, using low alkali sulphate aluminium cement as glue
Gel material, using alkaline-resisting chopped strand as toughening material, existing Side fascia density is big, and toughness is low, and fragility is big, and not possessing can
Nail, the characteristic that can be sawed, processing installation is not easy to, and cost is higher, is unfavorable for promoting on a large scale.
The content of the invention
(1) technical problems to be solved
The technical problem to be solved in the present invention is to provide a kind of string to imitate bag reason Side fascia, the plate of the Side fascia
Material density is low, and toughness is high, and cost is low, good decorating effect.A kind of effective preparation method of Side fascia is additionally provided simultaneously.
(2) technical scheme
In order to solve the above-mentioned technical problem, the invention provides a kind of string to imitate bag reason Side fascia, and it includes
Precoat, the following bed of material and the middle bed of material above described between the bed of material and the following bed of material, the bed of material, the middle bed of material above
Thickness ratio with the following bed of material is 0.8~1.2：2~2.5：0.8~1.2；
The bed of material and the following bed of material above are prepared by the raw material including following parts by weight：Quick hardening sulphoaluminate water
100 parts of mud, 25~35 parts of water, 6~10 parts of string, and 0.2~0.5 part of additive；
The middle bed of material is prepared by the raw material including following parts by weight：100 parts of quick hardening sulphoaluminate cement, water 35~
40 parts, 15~25 parts of string, and 0.2~0.5 part of additive；
It is described to be equipped with alkaline-resisting short glass fiber grid cloth in the bed of material, the middle bed of material and the following bed of material above；On described
Bag texture is provided with the outside of precoat.
Parts by weight of the present invention are the unit of weights well known in the art such as μ g, mg, g, kg, or are its multiple, such as 1/
100,1/10,10 times, 100 times etc..
Further, the thickness ratio of the bed of material, the middle bed of material and the following bed of material above is 1：2.3：1.
Further, the bed of material and the following bed of material above are prepared by the raw material including following parts by weight：It is fast hard
100 parts of sulphate aluminium cement, 30 parts of water, 8 parts of string, and 0.4 part of additive.
Further, the middle bed of material is prepared by the raw material including following parts by weight：Quick hardening sulphoaluminate cement 100
Part, 38 parts of water, 20 parts of string, and 0.4 part of additive.
Further, the string is sawdust.
Preferably, the granularity of the sawdust is 60~100 mesh.
Preferably, the quick hardening sulphoaluminate cement is 42.5 labels.
Further, the additive includes the composition of following mass ratio：Water reducer：Retarder：Thickener=18~22：
15~20：1~5.
Further, the alkaline-resisting short glass fiber grid cloth includes the first grid cloth and the second grid set gradually
Cloth, first grid cloth and the second grid cloth are respectively 2 layers and 6 layers, the specification of every layer of first grid cloth for 45~
50g/m2, the specification of every layer of second grid cloth is 160~300g/m2。
Above-mentioned string is prepared present invention also offers one kind and imitates bag reason Side fascia, and it comprises the following steps：
(1) bed of material, the middle bed of material and the following bed of material are mixed and stirred for uniformly according to respective raw material proportioning above will be described；
(2) mat formation the following bed of material：Will after step (1) processing below bed of material material-paving in template, and above
Lay the alkaline-resisting short glass fiber grid cloth；
(3) mat formation the middle bed of material：By the middle bed of material material-paving after step (1) processing in the case where being paved through step (2)
On precoat, and the alkaline-resisting short glass fiber grid cloth is laid above；
(4) mat formation the bed of material above：Will through step (1) processing after above bed of material material-paving paved through step (3)
The middle bed of material on, and the alkaline-resisting short glass fiber grid cloth is laid above, then scribes bag with bag mould and manage；
(5) by respectively through step (2), (3) and (4) pave below the bed of material, the middle bed of material and the bed of material above, use clapper die spotting press
Matched moulds is carried out, then moves into laminating machine, it is compressing under 50~70 DEG C of temperature conditionss and 15~24MPa pressure condition
60~180min；
(6) sheet material after step (5) is compressing is put into curing kilns to be conserved, curing condition is：Temperature 18~
22 DEG C, humidity 87%~93%, after conserving 3 days, produce.
Further, the depth of step (4) the bag reason is not more than 5mm；And/or in step (2)~(4), laying
Through step (1) processing after the bed of material material when, using GRC sprayup processes.
(3) beneficial effect
The above-mentioned technical proposal of the present invention has the advantages that：
The string of the present invention imitates bag reason Side fascia, using string as aggregate, is with quick hardening sulphoaluminate cement
Binder materials, while alkaline-resisting short glass fiber grid cloth is added as toughening material in each bed of material, there is sheet material outer
The physical property and weather resistance of wallboard, while the density of sheet material is reduced, improve the toughness of sheet material；By bag mould or
The bag reason that other texture moulds are scribed, makes outer wall board be provided with bag texture in the production stage, is provided with imitative stone
Effect, avoid extra charge caused by later stage decoration.
The raw material that the present invention uses when preparing Side fascia is material cheap and easy to get, realizes string in Building wood
Application in material, and discarded object can be used, the secondary use to discarded object is realized, greatly reduces being produced into for product
This.The Side fascia of the present invention equally has the advantages that lightweight, insulation, sound insulation possessed by conventional Side fascia.
Embodiment
Embodiments of the present invention are described in further detail with reference to embodiment.Following examples are used to illustrate this
Invention, but can not be used for limiting the scope of the present invention.
Embodiment 1
Present embodiments provide a kind of string imitate bag reason Side fascia, it include above the bed of material, the following bed of material and
The middle bed of material above described between the bed of material and the following bed of material, the thickness point of the bed of material, the middle bed of material and the following bed of material above
Wei not 1mm, 2mm and 1mm；The bed of material and the following bed of material above are prepared by the raw material of following parts by weight：Fast hard sulphur aluminium
Acid salt cement 100kg, water 30kg, string 8kg, and additive 0.4kg；The middle bed of material by following parts by weight raw material
It is prepared：Quick hardening sulphoaluminate cement 100kg, water 38kg, string 20kg, and additive 0.4kg；The upper fabric
Alkaline-resisting short glass fiber grid cloth is equipped with layer, the middle bed of material and the following bed of material；It is described to be provided with bag on the outside of the bed of material above
Texture.
In the present embodiment, the quick hardening sulphoaluminate cement is 42.5 labels.The string is sawdust, and sawdust
Granularity is 65 mesh.The additive is made up of the composition of following mass ratio：Water reducer：Retarder：Thickener=10：9：1.It is described
Alkaline-resisting short glass fiber grid cloth includes the first grid cloth and the second grid cloth that set gradually, first grid cloth and the
Two grid cloths are respectively 2 layers and 6 layers, and the specification of every layer of first grid cloth is 47g/m2, every layer of second grid cloth
Specification is 200g/m2。
The present embodiment additionally provides one kind and prepares the imitative bag reason Side fascia of above-mentioned string, and it comprises the following steps：
(1) bed of material, the middle bed of material and the following bed of material are mixed and stirred for uniformly according to respective raw material proportioning above will be described；
(2) mat formation the following bed of material：Will after step (1) processing below bed of material material-paving in template, and above
Lay the alkaline-resisting short glass fiber grid cloth；
(3) mat formation the middle bed of material：By the middle bed of material material-paving after step (1) processing in the case where being paved through step (2)
On precoat, and the alkaline-resisting short glass fiber grid cloth is laid above；
(4) mat formation the bed of material above：Will through step (1) processing after above bed of material material-paving paved through step (3)
The middle bed of material on, and the alkaline-resisting short glass fiber grid cloth is laid above, then scribes bag with bag mould and manage, stone
The depth of texture is 4mm；
(5) by respectively through step (2), (3) and (4) pave below the bed of material, the middle bed of material and the bed of material above, use clapper die spotting press
Matched moulds is carried out, then moves into laminating machine, under 65 DEG C of temperature conditionss and 18MPa pressure condition, compressing 165min；
(6) sheet material after step (5) is compressing is put into curing kilns to be conserved, curing condition is：20 DEG C of temperature,
Humidity 90%, after conserving 3 days, produce.
Wherein, in step (2)~(4), when laying the bed of material material after step (1) processing, it is injected into using GRC
Type technique.
Embodiment 2
Present embodiments provide a kind of string imitate bag reason Side fascia, it include above the bed of material, the following bed of material and
The middle bed of material above described between the bed of material and the following bed of material, the thickness point of the bed of material, the middle bed of material and the following bed of material above
Wei not 0.8mm, 2.3mm and 1.2mm；The bed of material and the following bed of material above are prepared by the raw material of following parts by weight：It hurry up
Hardening sulphoaluminate cement 100kg, water 35kg, string 6kg, and additive 0.2kg；The middle bed of material is by following parts by weight
Raw material be prepared：Quick hardening sulphoaluminate cement 100kg, water 37kg, string 25kg, and additive 0.5kg；It is described
Alkaline-resisting short glass fiber grid cloth is equipped with the bed of material, the middle bed of material and the following bed of material above；It is described to be set above on the outside of the bed of material
There is bag texture.
In the present embodiment, the quick hardening sulphoaluminate cement is 42.5 labels.The string is sawdust, and sawdust
Granularity is 80 mesh.The additive is made up of the composition of following mass ratio：Water reducer：Retarder：Thickener=9：8：2.It is described
Alkaline-resisting short glass fiber grid cloth includes the first grid cloth and the second grid cloth that set gradually, first grid cloth and the
Two grid cloths are respectively 2 layers and 6 layers, the specification 48g/m of every layer of first grid cloth2, the rule of every layer of second grid cloth
Lattice are 165g/m2。
The present embodiment additionally provides one kind and prepares the imitative bag reason Side fascia of above-mentioned string, and it comprises the following steps：
(1) bed of material, the middle bed of material and the following bed of material are mixed and stirred for uniformly according to respective raw material proportioning above will be described；
(2) mat formation the following bed of material：Will after step (1) processing below bed of material material-paving in template, and above
Lay the alkaline-resisting short glass fiber grid cloth；
(3) mat formation the middle bed of material：By the middle bed of material material-paving after step (1) processing in the case where being paved through step (2)
On precoat, and the alkaline-resisting short glass fiber grid cloth is laid above；
(4) mat formation the bed of material above：Will through step (1) processing after above bed of material material-paving paved through step (3)
The middle bed of material on, and the alkaline-resisting short glass fiber grid cloth is laid above, then scribes bag with bag mould and manage, stone
The depth of texture is 5mm；
(5) by respectively through step (2), (3) and (4) pave below the bed of material, the middle bed of material and the bed of material above, use clapper die spotting press
Matched moulds is carried out, then moves into laminating machine, under 70 DEG C of temperature conditionss and 22MPa pressure condition, compressing 75min；
(6) sheet material after step (5) is compressing is put into curing kilns to be conserved, curing condition is：18 DEG C of temperature,
Humidity 93%, after conserving 3 days, produce.
Wherein, in step (2)~(4), when laying the bed of material material after step (1) processing, it is injected into using GRC
Type technique.
Embodiment 3
Present embodiments provide a kind of string imitate bag reason Side fascia, it include above the bed of material, the following bed of material and
The middle bed of material above described between the bed of material and the following bed of material, the thickness point of the bed of material, the middle bed of material and the following bed of material above
Wei not 1.2mm, 2.5mm and 0.8mm；The bed of material and the following bed of material above are prepared by the raw material of following parts by weight：It hurry up
Hardening sulphoaluminate cement 100kg, water 25kg, string 10kg, and additive 0.5kg；The middle bed of material is by following weight
The raw material of part is prepared：Quick hardening sulphoaluminate cement 100kg, water 36kg, string 24kg, and additive 0.3kg；Institute
State and be equipped with alkaline-resisting short glass fiber grid cloth in the bed of material, the middle bed of material and the following bed of material above；The bed of material outside above
Provided with bag texture.
In the present embodiment, the quick hardening sulphoaluminate cement is 42.5 labels.The string is sawdust, and sawdust
Granularity is 100 mesh.The additive is made up of the composition of following mass ratio：Water reducer：Retarder：Thickener=9：10：2.Institute
Stating alkaline-resisting short glass fiber grid cloth includes the first grid cloth and the second grid cloth that set gradually, first grid cloth and
Second grid cloth is respectively 2 layers and 6 layers, the specification 48g/m of every layer of first grid cloth2, every layer of second grid cloth
Specification is 290g/m2。
Test example 1
To verify that string of the present invention imitates the performance that bag manages Side fascia, spy provides the test example.This test example
A kind of imitative bag reason Side fascia and preparation method thereof is provided, this test example differs only in embodiment 1：Replaced with quartz sand
The string changed in embodiment 1.
Performance detection is carried out respectively to the Side fascia of embodiment 1~3 and the test example according to conventional technical means, drawn
Related performance indicators are as shown in table 1：
Table 1：The performance of each Side fascia
In summary, Side fascia density of the invention is smaller, and the quality of unit area is smaller, that is, conducts oneself with dignity smaller；It is and tough
Property and heat-insulating property are more preferable.
Embodiments of the invention provide for the sake of example and description, and are not exhaustively or by this to send out
It is bright to be limited to disclosed form.Many modifications and variations are obvious for the ordinary skill in the art.Choosing
Select and describe embodiment and be to more preferably illustrate the principle and practical application of the present invention, and make one of ordinary skill in the art
It will be appreciated that the present invention is so as to designing the various embodiments with various modifications suitable for special-purpose.
Claims (10)
1. a kind of string imitates bag reason Side fascia, it is characterised in that including the bed of material above, the following bed of material and located at described
The middle bed of material between the bed of material and the following bed of material above, the thickness ratio of the bed of material, the middle bed of material and the following bed of material above for 0.8~
1.2：2~2.5：0.8~1.2；
The bed of material and the following bed of material above are prepared by the raw material including following parts by weight：Quick hardening sulphoaluminate cement
100 parts, 25~35 parts of water, 6~10 parts of string, and 0.2~0.5 part of additive；
The middle bed of material is prepared by the raw material including following parts by weight：100 parts of quick hardening sulphoaluminate cement, water 35~40
Part, 15~25 parts of string, and 0.2~0.5 part of additive；
It is described to be equipped with alkaline-resisting short glass fiber grid cloth in the bed of material, the middle bed of material and the following bed of material above；The upper fabric
Layer outside is provided with bag texture.
2. string according to claim 1 imitates bag reason Side fascia, it is characterised in that the bed of material, the middle material above
The thickness ratio of layer and the following bed of material is 1：2.3：1.
3. string according to claim 1 imitates bag reason Side fascia, it is characterised in that the bed of material and following above
The bed of material is prepared by the raw material including following parts by weight：100 parts of quick hardening sulphoaluminate cement, 30 parts of water, string 8
Part, and 0.4 part of additive.
4. string according to claim 1 imitates bag reason Side fascia, it is characterised in that the middle bed of material is by including such as
The raw material of lower parts by weight is prepared：100 parts of quick hardening sulphoaluminate cement, 38 parts of water, 20 parts of string, and additive
0.4 part.
5. the string according to any one of Claims 1 to 4 imitates bag reason Side fascia, it is characterised in that the plant
Fiber is sawdust.
6. string according to claim 5 imitates bag reason Side fascia, it is characterised in that the granularity of the sawdust is 60
~100 mesh.
7. the string according to any one of Claims 1 to 4 imitates bag reason Side fascia, it is characterised in that described additional
Agent includes the composition of following mass ratio：Water reducer：Retarder：Thickener=18~22：15~20：1~5.
8. the string according to any one of Claims 1 to 4 imitates bag reason Side fascia, it is characterised in that described alkaline-resisting
Short glass fiber grid cloth includes the first grid cloth and the second grid cloth set gradually, first grid cloth and the second net
Ge Bu is respectively 2 layers and 6 layers, and the specification of every layer of first grid cloth is 45~50g/m2, every layer of second grid cloth
Specification is 160~300g/m2。
9. a kind of string prepared described in any one of claim 1~8 imitates bag reason Side fascia, it is characterised in that including
Following steps：
(1) bed of material, the middle bed of material and the following bed of material are mixed and stirred for uniformly according to respective raw material proportioning above will be described；
(2) mat formation the following bed of material：Will through step (1) processing after below bed of material material-paving laid in template, and above
The alkaline-resisting short glass fiber grid cloth；
(3) mat formation the middle bed of material：Middle bed of material material-paving after step (1) processing is expected below being paved through step (2)
On layer, and the alkaline-resisting short glass fiber grid cloth is laid above；
(4) mat formation the bed of material above：Will through step (1) processing after above bed of material material-paving in being paved through step (3)
On the bed of material, and the alkaline-resisting short glass fiber grid cloth is laid above, then scribe bag with bag mould and manage；
(5) by respectively through step (2), (3) and (4) pave below the bed of material, the middle bed of material and the bed of material above, carried out with clapper die spotting press
Matched moulds, laminating machine is then moved into, under 50~70 DEG C of temperature conditionss and 15~24MPa pressure condition, compressing 60~
180min；
(6) sheet material after step (5) is compressing is put into curing kilns to be conserved, curing condition is：18~22 DEG C of temperature,
Humidity 87%~93%, after conserving 3 days, produce.
10. preparation method according to claim 9, it is characterised in that the depth of step (4) the bag reason is not more than
5mm；And/or in step (2)~(4), when laying the bed of material material after step (1) processing, using GRC injection moldings
Technique.