CN107382166A - Modified epoxy cement floor material - Google Patents
Modified epoxy cement floor material Download PDFInfo
- Publication number
- CN107382166A CN107382166A CN201710644968.1A CN201710644968A CN107382166A CN 107382166 A CN107382166 A CN 107382166A CN 201710644968 A CN201710644968 A CN 201710644968A CN 107382166 A CN107382166 A CN 107382166A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- byk
- weight
- floor material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of modified epoxy cement floor material, is made up of AB components, wherein component A is calculated as by weight：60 80 parts of furfural acetone resin, 60 90 parts of bisphenol A type epoxy resin, 10 20 parts of oyster shell, 0 10 parts of acetonitrile, 5 10 parts of acetone, 0.8 1.0 parts of nano titanium oxide, 10 20 parts of silica flour, 120 180 parts of cement, 50 60 parts of 60 80 mesh quartz sand, 354 0.3 0.5 parts of BYK, 310 0.3 0.8 parts of BYK, 9,076 0.1 0.5 parts of BYK；B component is calculated as by weight：10 15 parts of diethylenetriamines, 26 parts of acetonitrile, 0.5 1.0 parts of sodium carbonate, 0.5 1.0 parts of sodium acid carbonate.The floor material excellent performance, for wear-resisting field factory, parking lot, chemistry, food etc..
Description
Technical field
The invention belongs to floor field, and in particular to a kind of modified epoxy cement floor material.
Background technology
Epoxide terrace is more common industry ground slab, is widely used in the places such as workshop, warehouse, underground garage, still,
Its hardness and wearability are poor, in places such as workshop, parking lot, manufacturing industry because the traveling load of weight is bigger and frequent
Using such as automobile, fork truck, mobile small handcart etc., therefore epoxy floor lacquer coat is also frequently subjected to serious scuffing, caused
Phenomena such as flaking, coming off, have a strong impact on attractive in appearance and service life.Therefore, research and develop a kind of excellent performance, especially hardness it is high and
The good modified epoxy cement floor of wearability is particularly important.
The content of the invention
It is an object of the invention to provide a kind of modified epoxy cement floor material, the floor material has excellent water-fast
Property, oil resistivity, resistance to acids and bases, salt fog resistance, compression strength is good, quick-drying, good leveling property, reduces that crack, impact resistance be good, Yi Wei
Repair, adhesive force is good, hardness is good, the excellent properties such as green, suitable for works such as wear-resisting field factory, parking lot, chemistry, food
Factory.
For achieving the above object, the present invention adopts the following technical scheme that：
A kind of modified epoxy cement floor material, by component A and B component by weight 6:1 composition；Wherein component A is by weight
It is calculated as：Furfural acetone resin 60-80 parts, bisphenol A type epoxy resin 60-90 parts, oyster shell 10-20 parts, acetonitrile 0-10 parts, acetone 5-10
Part, nano titanium oxide 0.8-1.0 parts, silica flour 10-20 parts, cement 120-180 parts, 60-80 mesh quartz sand 50-60 parts,
BYK-354 0.3-0.5 parts, BYK-310 0.3-0.8 parts, BYK-9076 0.1-0.5 parts；B component is calculated as by weight：Two is sub-
Ethyl triamine 10-15 parts, acetonitrile 2-6 parts, sodium carbonate 0.5-1.0 parts, sodium acid carbonate 0.5-1.0 parts.
Preferably, the modified epoxy cement floor material, by component A and B component by weight 6:1 composition；Wherein A groups
Divide and be calculated as by weight：70 parts of furfural acetone resin, 80 parts of bisphenol A type epoxy resin, 15 parts of oyster shell, 5 parts of acetonitrile, 8 parts of acetone, receive
1.0 parts of titanium dioxide of rice, 15 parts of silica flour, 150 parts of cement, 55 parts of 60-80 mesh quartz sand, 0.4 part of BYK-354, BYK-310
0.5 part, 0.3 part of BYK-9076；B component is calculated as by weight：12 parts of diethylenetriamines, 5 parts of acetonitrile, 1.0 parts of sodium carbonate,
1.0 parts of sodium acid carbonate.
A kind of application process of modified epoxy cement floor material as described above, if removing quartz during as interfacial agents
The direct roller coating of sand, which adds graded sand and stone on processed good base concrete layer, during as grinding stone binding material and stirred, is spread out
Paving, if being that direct trowel is coated on the concrete layer handled well as the surface layer directly used, thickness 2-5mm.
The remarkable advantage of the present invention：The present invention modified epoxy cement floor material have excellent wearability, water resistance,
Oil resistivity, resistance to acids and bases, salt fog resistance, compression strength are good, quick-drying, good leveling property, reduce crack, impact resistance it is good, it is easy-maintaining,
Adhesive force is good, hardness is good, the excellent properties such as green.
Modified epoxy cement floor material can use as various structures layer, green, easy construction, have simultaneously
The superiority of two kinds of epoxy, cement materials, and it is modified both combine improve to a certain extent cement cracking and can not be big
The disadvantage of area construction, also improve it is affected by environment in epoxy material work progress can not normal construction, it is impossible to humidity construction etc.
Disadvantage.
Embodiment
In order that content of the present invention easily facilitates understanding, with reference to embodiment to of the present invention
Technical scheme is described further, but the present invention is not limited only to this.
Embodiment 1
A kind of modified epoxy cement floor material, by component A and B component by weight 6:1 composition；Wherein component A is by weight
It is calculated as：70 parts of furfural acetone resin, 80 parts of bisphenol A type epoxy resin, 15 parts of oyster shell, 5 parts of acetonitrile, 8 parts of acetone, nano titanium oxide
1.0 parts, 15 parts of silica flour, 150 parts of cement, 55 parts of 60-80 mesh quartz sand, 0.4 part of BYK-354,0.5 part of BYK-310, BYK-
9076 0.3 parts；B component is calculated as by weight：12 parts of diethylenetriamines, 5 parts of acetonitrile, 1.0 parts of sodium carbonate, sodium acid carbonate 1.0
Part.
Embodiment 2
A kind of modified epoxy cement floor material, by component A and B component by weight 6:1 composition；Wherein component A is by weight
It is calculated as：60 parts of furfural acetone resin, 60 parts of bisphenol A type epoxy resin, 10 parts of oyster shell, 1 part of acetonitrile, 5 parts of acetone, nano titanium oxide
0.8 part, 10 parts of silica flour, 120 parts of cement, 50 parts of 60-80 mesh quartz sand, 0.3 part of BYK-354,0.3 part of BYK-310, BYK-
9076 0.1 parts；B component is calculated as by weight：10 parts of diethylenetriamines, 2 parts of acetonitrile, 0.5 part of sodium carbonate, sodium acid carbonate 0.5
Part.
Embodiment 3
A kind of modified epoxy cement floor material, by component A and B component by weight 6:1 composition；Wherein component A is by weight
It is calculated as：80 parts of furfural acetone resin, 90 parts of bisphenol A type epoxy resin, 20 parts of oyster shell, 10 parts of acetonitrile, 10 parts of acetone, nanometer titanium dioxide
1.0 parts of titanium, 20 parts of silica flour, 180 parts of cement, 60 parts of 60-80 mesh quartz sand, 0.5 part of BYK-354,0.8 part of BYK-310,
0.5 part of BYK-9076；B component is calculated as by weight：15 parts of diethylenetriamines, 6 parts of acetonitrile, 1.0 parts of sodium carbonate, bicarbonate
1.0 parts of sodium.
Modified epoxy cement floor obtained by embodiment 1-3 is subjected to performance test, it the results are shown in Table 1.
The performance test results of table 1
Presently preferred embodiments of the present invention is the foregoing is only, all equivalent changes done according to scope of the present invention patent are with repairing
Decorations, it should all belong to the covering scope of the present invention.
Claims (3)
- A kind of 1. modified epoxy cement floor material, it is characterised in that：By component A and B component by weight 6:1 composition；Wherein A Component is calculated as by weight：Furfural acetone resin 60-80 parts, bisphenol A type epoxy resin 60-90 parts, oyster shell 10-20 parts, acetonitrile 0- 10 parts, acetone 5-10 parts, nano titanium oxide 0.8-1.0 parts, silica flour 10-20 parts, cement 120-180 parts, 60-80 mesh quartz Sand 50-60 parts, BYK-354 0.3-0.5 parts, BYK-310 0.3-0.8 parts, BYK-9076 0.1-0.5 parts；B component is by weight Part is calculated as：Diethylenetriamines 10-15 parts, acetonitrile 2-6 parts, sodium carbonate 0.5-1.0 parts, sodium acid carbonate 0.5-1.0 parts.
- A kind of 2. modified epoxy cement floor material according to claim 1, it is characterised in that：Pressed by component A and B component Weight is than 6:1 composition；Wherein component A is calculated as by weight：70 parts of furfural acetone resin, 80 parts of bisphenol A type epoxy resin, oyster shell 15 Part, 5 parts of acetonitrile, 8 parts of acetone, 1.0 parts of nano titanium oxide, 15 parts of silica flour, 150 parts of cement, 55 parts of 60-80 mesh quartz sand, 0.4 part of BYK-354,0.5 part of BYK-310,0.3 part of BYK-9076；B component is calculated as by weight：Diethylenetriamines 12 Part, 5 parts of acetonitrile, 1.0 parts of sodium carbonate, 1.0 parts of sodium acid carbonate.
- A kind of 3. application of modified epoxy cement floor material as claimed in claim 1 or 2, it is characterised in that the modification Epoxy cement floor material uses as interfacial agents, grinding stone binding material and surface layer.