CN107382057A - A kind of corrosion-resistant glass and preparation method thereof - Google Patents
A kind of corrosion-resistant glass and preparation method thereof Download PDFInfo
- Publication number
- CN107382057A CN107382057A CN201710617744.1A CN201710617744A CN107382057A CN 107382057 A CN107382057 A CN 107382057A CN 201710617744 A CN201710617744 A CN 201710617744A CN 107382057 A CN107382057 A CN 107382057A
- Authority
- CN
- China
- Prior art keywords
- parts
- dosage
- glass
- cullet
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of corrosion-resistant glass and preparation method thereof, it is made up of the raw material of following mass fraction：The dosage of quartz sand is 80 100 parts, the dosage of soda ash is 25 32 parts, the dosage of lime stone is 1.5 2.5 parts, the dosage of plant ash is 0.07 0.15 parts, and the dosage of sodium nitrate is 0.01 0.03 parts, and the dosage of saltcake is 0.02 0.04 parts, the dosage of cullet is 0.8 1.2 parts, the advantages of glass obtained by the preparation method of the present invention has corrosion resistance, and stability is good, and service life is long.
Description
Technical field
The present invention relates to a kind of corrosion-resistant glass and preparation method thereof.
Background technology
Glass be fused together by silica and other chemical substances formed (main production raw material is：Soda ash, stone
Lime stone, quartz).Contiguous network structure is formed in melting, viscosity, which gradually increases and hardened, in cooling procedure causes what it was crystallized
Silicates nonmetallic materials.It is widely used in building, for every wind printing opacity, belonging to mixture.Separately some gold have been mixed into it
The oxide or salt of category and show the coloured glass of color, and pass through physics or chemistry method made from tempering glass
Glass etc., is widely used in building, for every wind printing opacity.
Glass contacts with the external world, is influenceed by natural cause, exposes to the weather for a long time, causes glass to corrode, it is difficult to meet people
To the demand of its general performance.
The content of the invention
In view of the drawbacks described above of prior art, it is an object of the invention to provide a kind of corrosion-resistant glass and its making side
Method, there is corrosion resistance, and stability is good, service life length.
The purpose of the present invention realized by such technical scheme, a kind of corrosion-resistant glass, by following mass fraction
Raw material composition：The dosage of quartz sand is 80-100 parts, and the dosage of soda ash is 25-32 parts, and the dosage of lime stone is 1.5-2.5
Part, the dosage of plant ash is 0.07-0.15 parts, and the dosage of sodium nitrate is 0.01-0.03 parts, and the dosage of saltcake is 0.02-0.04
Part, the dosage of cullet is 0.8-1.2 parts.
Further, the cullet remove out impurity, and the cullet are clear glass, and every cullet volume is less than
1m3。
Further, mixed after being soaked 0.5 hour in the cullet immersion hydrofluoric acid solution after filtration and washing with the raw material
Close.
Further, the raw material composition：The dosage of quartz sand is 80 parts, and the dosage of soda ash is 29 parts, the dosage of lime stone
For 2 parts, the dosage of plant ash is 0.1 part, and the dosage of sodium nitrate is 0.02 part, and the dosage of saltcake is 0.03 part, the use of cullet
Measure as 1 part.
A kind of preparation method of corrosion-resistant glass, comprises the following steps：
The first step：Take quartz sand 80-100 parts, soda ash 25-32 parts, lime stone 1.5-2.5 parts, plant ash 0.07-0.15
Part, sodium nitrate 0.01-0.03 parts, saltcake 0.02-0.04 parts, cullet 0.8-1.2 parts are well mixed；
Second step：The mixture of upper step is put into smelting furnace, pressure 100-200Mpa, 500-1000 degrees Celsius of temperature, 1-2
Hour, carry out melting；
3rd step：The bath of glass that top is obtained is poured into prepared mould, is annealed to the demoulding of normal temperature rear mold naturally, is obtained
Glass.
Further, annealing is that glass is placed into lucifuge and ventilation naturally in the 3rd step.
Further, glass will be obtained in the 3rd step should be polished and rounding.
By adopting the above-described technical solution, the present invention has the advantage that：Permanence and corrosion-resistant can be produced
Glass, and service life grow, preparation method is simple, low manufacture cost.
Other advantages, target and the feature of the present invention will be illustrated in the following description to a certain extent, and
And to a certain extent, based on will be apparent to those skilled in the art to investigating hereafter, Huo Zheke
To be instructed from the practice of the present invention.The target and other advantages of the present invention can be wanted by following specification and right
Book is sought to realize and obtain.
Embodiment
With reference to embodiment, the invention will be further described.
Embodiment 1：
A kind of corrosion-resistant glass, is made up of the raw material of following mass fraction：The dosage of quartz sand is 80 parts, the dosage of soda ash
For 29 parts, the dosage of lime stone is 2 parts, and the dosage of plant ash is 0.1 part, and the dosage of sodium nitrate is 0.02 part, the dosage of saltcake
For 0.03 part, the dosage of cullet is 1 part.
The cullet remove out impurity, and the cullet are clear glass, every cullet volume 0.5m3。
Mixed after being soaked 0.5 hour in the cullet immersion hydrofluoric acid solution after filtration and washing with the raw material.
A kind of preparation method of corrosion-resistant glass, comprises the following steps：
The first step：Take 80 parts of quartz sand, 29 parts of soda ash, 2 parts of lime stone, 0.1 part of plant ash, 0.02 part of sodium nitrate, saltcake
0.03 part, 1 part of cullet are well mixed；
Second step：The mixture of upper step is put into smelting furnace, pressure 150Mpa, 800 degrees Celsius of temperature, 1.5 hours, carried out
Melting；
3rd step：The bath of glass that top is obtained is poured into prepared mould, is annealed to the demoulding of normal temperature rear mold naturally, is obtained
Glass.
Annealing is that glass is placed into lucifuge and ventilation naturally in 3rd step.
Glass will be obtained in 3rd step should be polished and rounding.
Embodiment 2
A kind of corrosion-resistant glass, is made up of the raw material of following mass fraction：The dosage of quartz sand is 90 parts, the dosage of soda ash
For 25 parts, the dosage of lime stone is 1.5 parts, and the dosage of plant ash is 0.07 part, and the dosage of sodium nitrate is 0.01 part, the use of saltcake
Measure as 0.02 part, the dosage of cullet is 0.8 part.
The cullet remove out impurity, and the cullet are clear glass, every cullet volume 0.5m3。
Mixed after being soaked 0.5 hour in the cullet immersion hydrofluoric acid solution after filtration and washing with the raw material.
A kind of preparation method of corrosion-resistant glass, comprises the following steps：
The first step：Take 90 parts of quartz sand, 25 parts of soda ash, 1.5 parts of lime stone, 0.07 part of plant ash, 0.01 part of sodium nitrate, awns
0.02 part of nitre, 0.8 part of cullet are well mixed；
Second step：The mixture of upper step is put into smelting furnace, pressure 100Mpa, 500 degrees Celsius of temperature, 1 hour, melted
Refining；
3rd step：The bath of glass that top is obtained is poured into prepared mould, is annealed to the demoulding of normal temperature rear mold naturally, is obtained
Glass.
Annealing is that glass is placed into lucifuge and ventilation naturally in 3rd step.
Glass will be obtained in 3rd step should be polished and rounding.
Embodiment 3
A kind of corrosion-resistant glass, is made up of the raw material of following mass fraction：The dosage of quartz sand is 100 parts, the use of soda ash
Measure as 32 parts, the dosage of lime stone is 2.5 parts, and the dosage of plant ash is 0.15 part, and the dosage of sodium nitrate is 0.03 part, saltcake
Dosage is 0.04 part, and the dosage of cullet is 1.2 parts.
The cullet remove out impurity, and the cullet are clear glass, every cullet volume 0.5m3。
Mixed after being soaked 0.5 hour in the cullet immersion hydrofluoric acid solution after filtration and washing with the raw material.
A kind of preparation method of corrosion-resistant glass, comprises the following steps：
The first step：Take 100 parts of quartz sand, 32 parts of soda ash, 2.5 parts of lime stone, 0.15 part of plant ash, 0.03 part of sodium nitrate,
0.04 part of saltcake, 1.2 parts of cullet are well mixed；
Second step：The mixture of upper step is put into smelting furnace, pressure 200Mpa, 1000 degrees Celsius of temperature, 2 hours, carried out
Melting；
3rd step：The bath of glass that top is obtained is poured into prepared mould, is annealed to the demoulding of normal temperature rear mold naturally, is obtained
Glass.
Annealing is that glass is placed into lucifuge and ventilation naturally in 3rd step.
Glass will be obtained in 3rd step should be polished and rounding.
The glass that the present embodiment 1 obtains has decay resistance and stably, service life length.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the skill of the present invention
Art scheme is modified or equivalent substitution, and without departing from the objective and scope of the technical program, it all should cover in the present invention
Right among.
Claims (7)
- A kind of 1. corrosion-resistant glass, it is characterised in that：It is made up of the raw material of following mass fraction：The dosage of quartz sand is 80-100 Part, the dosage of soda ash is 25-32 parts, and the dosage of lime stone is 1.5-2.5 parts, and the dosage of plant ash is 0.07-0.15 parts, nitric acid The dosage of sodium is 0.01-0.03 parts, and the dosage of saltcake is 0.02-0.04 parts, and the dosage of cullet is 0.8-1.2 parts.
- 2. corrosion-resistant glass as claimed in claim 1, it is characterised in that：The cullet remove out impurity, and the cullet are Clear glass, every cullet volume are less than 1m3。
- 3. corrosion-resistant glass as claimed in claim 1, it is characterised in that：The cullet immerse in hydrofluoric acid solution and soaked Mixed after 0.5 hour after filtration and washing with the raw material.
- 4. corrosion-resistant glass as claimed in claim 1, it is characterised in that：The raw material composition：The dosage of quartz sand is 80 parts, The dosage of soda ash is 29 parts, and the dosage of lime stone is 2 parts, and the dosage of plant ash is 0.1 part, and the dosage of sodium nitrate is 0.02 part, The dosage of saltcake is 0.03 part, and the dosage of cullet is 1 part.
- A kind of 5. preparation method of corrosion-resistant glass, it is characterised in that：Comprise the following steps：The first step：Take quartz sand 80-100 parts, soda ash 25-32 parts, lime stone 1.5-2.5 parts, plant ash 0.07-0.15 parts, nitre Sour sodium 0.01-0.03 parts, saltcake 0.02-0.04 parts, cullet 0.8-1.2 parts are well mixed；Second step：The mixture of upper step is put into smelting furnace, pressure 100-200Mpa, 500-1000 degrees Celsius of temperature, 1-2 is small When, carry out melting；3rd step：The bath of glass that top is obtained is poured into prepared mould, is annealed to the demoulding of normal temperature rear mold naturally, is obtained glass Glass.
- 6. the preparation method of corrosion-resistant glass as claimed in claim 5, it is characterised in that：Annealing is naturally in 3rd step Glass is placed into lucifuge and ventilation.
- 7. the preparation method of corrosion-resistant glass as claimed in claim 5, it is characterised in that：Glass will be obtained in 3rd step It should be polished and rounding.