CN107376630A - A kind of composition by the use of diatomite as carrier and its preparation method and application - Google Patents
A kind of composition by the use of diatomite as carrier and its preparation method and application Download PDFInfo
- Publication number
- CN107376630A CN107376630A CN201710708221.8A CN201710708221A CN107376630A CN 107376630 A CN107376630 A CN 107376630A CN 201710708221 A CN201710708221 A CN 201710708221A CN 107376630 A CN107376630 A CN 107376630A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatomite
- composition
- carrier
- calcium hydroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of composition by the use of diatomite as carrier and its preparation method and application, said composition is made up of diatomite, calcium hydroxide, nano titanium oxide, nano zine oxide, oyster shell whiting, tourmaline powder, vermiculite power, glycoside, lysine, etherification starch, algin, polyethylene glycol, mannitol, glycerine, glucose, manganese dioxide and water.This composition can be not only used for decoration material with the gas of the formaldehyde in adsorption chamber, ammonia and other irritant peculiar smell, it can also be used to sewage disposal, to reduce the content of the harmful substances such as its heavy metal ion, phosphorus, low molecule aldehyde.
Description
Technical field
The present invention relates to building environmental-protection decorative technical field, specifically a kind of composition by the use of diatomite as carrier and
Its preparation method and application.
Background technology
Some harmful substances such as formaldehyde, benzene, dimethylbenzene, trichloro ethylene, ether-ether class, propylene cyanogen, which contain, is attached to many ornament materials
In, it is scattered in for a long time in air in decoration process, causes pernicious gas in room air exceeded, to this environment that hangs up one's hat
Health brings serious threat.In addition, the gas production of many irritant peculiar smell is had in our daily life
It is raw, such as toilet peculiar smell, pet body odor, smoking waste gas, house refuse peculiar smell etc., have a strong impact on daily life quality.I
The formaldehyde that can be allowed in wall material in finishing material, benzene, diformazan are added by the use of diatomite, oyster shell whiting as carrier scavenging material
Excitant gas with foreign flavor in the harmful substances such as benzene, trichloro ethylene, ether-ether class, propylene cyanogen and life is adsorbed in wall, reduces life
The content of pernicious gas in environment living, the living space of a health environment-friendly is built to people.
Contain plurality of heavy metal ion, phosphorus and various harmful inorganic matters and organic matter, such as low point in trade effluent
Sub- aldehyde, directly row can carry out serious threat, it is necessary to which carrying out certain processing can be only achieved sewage to the health care belt of environment and the mankind
The standard of discharge.
Patent CN101574536B discloses a kind of composition of glucoside-containing and preparation method and application, and it is low in removal
There is preferable effect in terms of molecule aldehyde (such as formaldehyde), because the patent is mainly used in interior decoration and cigarette filter, the patent
In sodium thiosulfate when more than 33 DEG C easy heated oxide be decomposed into sodium sulphate and sulfur dioxide, also easily pyrolysis produces ammonium molybdate
Ammonia, secondary pollution is formed, is unfavorable for health.
Therefore it provides a kind of not only can effectively remove formaldehyde, benzene, dimethylbenzene, trichloro ethylene, ether-ether class, propylene cyanogen etc.
Organic pollution, and can effectively remove the composition of the safety and environmental protection of the gas of irritant peculiar smell, non-secondary pollution in living
It is very important.
The content of the invention
The present invention is in order to solve the above-mentioned technical problem, there is provided a kind of composition and its preparation by the use of diatomite as carrier
Methods and applications, this composition can effectively remove formaldehyde, low molecule ketone, ammonia, hydrogen cyanide, hydrogen sulfide and other have stimulation
The gas of property peculiar smell, and it is environment friendly and pollution-free.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：A kind of composition by the use of diatomite as carrier,
Count, be made up of following raw material in parts by weight：Diatomite 30-80 parts, calcium hydroxide 10-20 parts, nano titanium oxide 1-10
Part, nano zine oxide 1-15 parts, oyster shell whiting 5-20 parts, tourmaline powder 1-5 parts, vermiculite power 1-10 parts, glycoside 5-10 parts, rely
Propylhomoserin 10-20 parts, starch ether 2-8 parts, algin 1-7 parts, polyethylene glycol 2-10 parts, mannitol 3-15 parts, glycerine 2-3 parts,
500 parts of glucose 1-2 parts, manganese dioxide 0.5-4 parts and water.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.Preferably, the composition is by weight
Number meter, it is made up of following raw material：It is diatomite 40-70 parts, calcium hydroxide 5-15 parts, nano titanium oxide 2-8 parts, nano oxidized
Zinc 2-10 parts, oyster shell whiting 10-15 parts, tourmaline powder 2-3 parts, vermiculite power 2-8 parts, glycoside 6-9 parts, lysine 12-15
Part, etherification starch 4-6 parts, algin 2-5 parts, polyethylene glycol 4-8 parts, mannitol 5-10 parts, glycerine 2-3 parts, glucose 1-
500 parts of 2 parts, manganese dioxide 0.5-4 parts and water.
Preferably, the composition is made up of following raw material fraction meter by weight following raw material：50 parts of diatomite, hydrogen
15 parts of calcium oxide, 5 parts of nano titanium oxide, 10 parts of nano zine oxide, 12 parts of oyster shell whiting, 3 parts of tourmaline powder, 5 parts of vermiculite power,
8 parts of glycoside, 15 parts of lysine, 5 parts of etherification starch, 4 parts of algin, 5 parts of polyethylene glycol, 10 parts of mannitol, glycerine 2
Part, 2 parts of glucose, 2 parts of manganese dioxide and 500 parts of water.
The present invention also provides a kind of preparation method for the composition that carrier is done using diatomite, comprises the following steps：
Count in parts by weight, diatomite is made up of as the composition of carrier following raw material：Diatomite 30-80 parts, hydrogen-oxygen
Change calcium 10-20 parts, nano titanium oxide 1-10 parts, nano zine oxide 1-15 parts, oyster shell whiting 5-20 parts, tourmaline powder 1-5 parts, leech
Stone flour 1-10 parts, glycoside 5-10 parts, lysine 10-20 parts, starch ether 2-8 parts, algin 1-7 parts, polyethylene glycol 2-10
500 parts of part, mannitol 3-15 parts, glycerine 2-3 parts, glucose 1-2 parts, manganese dioxide 0.5-4 parts and water；
Step 1：By nano titanium oxide, nano zine oxide, glycoside, lysine, etherification starch, algin, poly- second
Glycol, mannitol, glycerine, glucose and manganese dioxide are soluble in water, stirring at normal temperature, obtained solution component A；
Step 2：Diatomite, calcium hydroxide, oyster shell whiting, tourmaline powder and vermiculite power are mixed, stirs, obtains B component,
Wherein the weight of calcium hydroxide is the 1/3 of calcium hydroxide gross weight；
Step 3：Step 2 gained B component is added in step 1 gained component A, stirred, be dried to aqueous
Amount is less than 3wt%, and C components are made；
Step 4：Remaining calcium hydroxide is added into step 3 gained C components, stirs, gets product.
The present invention also provides a kind of composition as described above by the use of diatomite as carrier and is removing fitting-up
Material is discharged into the application in the formaldehyde in air, benzene, dimethylbenzene, trichloro ethylene, ether-ether class, propylene cyanogen pernicious gas, and/or
Application in irritant gas with foreign flavor is removed, and/or the application in formaldehyde in indoor air, benzene, ammonia is removed.
The present invention also provides a kind of composition as described above by the use of diatomite as carrier and is removing a huge sum of money in sewage
Belong to the application in ion, phosphorus, low molecule aldehyde.
Compared with prior art, the beneficial effects of the invention are as follows：
The composition by the use of diatomite as carrier of the present invention can effectively remove formaldehyde in finishing material, benzene, two
Excitant gas with foreign flavor in the harmful substances such as toluene, trichloro ethylene, ether-ether class, propylene cyanogen and life, one is built to people
The living space of health environment-friendly；The composition by the use of diatomite as carrier of the present invention can also remove big in trade effluent
Measure heavy metal ion, phosphorus and various harmful inorganic matters and organic matter, such as low molecule aldehyde.
Diatomite, oyster shell whiting in the present invention all have preferable adsorption capacity；Lysine carries carboxyl and amino, amino
It can be reacted with small molecule aldehyde, small molecule ketone, hydrogen cyanide, carboxyl can adsorb ammonia；Glycoside, polyethylene glycol and shallow lake
Powder ether contains substantial amounts of hydroxyl, and PARA FORMALDEHYDE PRILLS(91,95) has preferable adsorption activity, and polyethylene glycol is hygroscopic, manganese dioxide catalysis hydrone
Produce free hydroxyl group, free hydroxyl group can with small organic molecules such as oxidation of formaldehyde, these small organic molecules by nano zine oxide,
Nano titanium oxide, these oxides of calcium hydroxide further aoxidize；Mannitol and glycerine also have substantial amounts of hydroxyl, herein
On the basis of add tourmaline powder and vermiculite power, anion is discharged in the state of having humidity.
The preparation method of composition in the present invention is simple, and easily operation, safety and environmental protection, will not produce secondary pollution.Can
To be widely used in the fields such as coating, wall material, sewage disposal, the content of the harmful substances such as low molecule aldehyde is effectively reduced.
Embodiment
The principles and features of the present invention are described below, and the given examples are served only to explain the present invention, is not intended to limit
Determine the scope of the present invention.
Embodiment 1
The present invention is prepared according to formula as below and ratio, and the composition of carrier is used as by the use of diatomite：Diatomite 6.5g, hydrogen
Calcium oxide 1g, nano titanium oxide 0.5g, nano zine oxide 0.5g, oyster shell whiting 1g, tourmaline powder 0.25g, vermiculite power 0.3g, Portugal
Grape glucoside 0.7g, lysine 0.15g, etherification starch 0.5g, algin 0.2g, polyethylene glycol 0.5g, mannitol 0.5g, glycerine
0.2g, glucose 0.1g, manganese dioxide 0.1g and water 50g.
Embodiment 2
The present invention is prepared according to formula as below and ratio, and the composition of carrier is used as by the use of diatomite：Diatomite 8g, hydrogen-oxygen
Change calcium 2g, nano titanium oxide 0.2g, nano zine oxide 0.2g, oyster shell whiting 0.5g, tourmaline powder 0.2, vermiculite power 0.2, grape
Glucoside 0.5, citric acid 1g, etherification starch 0.3g, algin 0.2g, polyethylene glycol 1g, mannitol 1.5g, glycerine 0.3g, Portugal
Grape sugar 0.2g, manganese dioxide 0.4g and water 50g.
Embodiment 3
The present invention is prepared according to formula as below and ratio, and the composition of carrier is used as by the use of diatomite：Diatomite 7g, hydrogen-oxygen
Change calcium 1.5g, nano titanium oxide 0.5g, nano zine oxide 1g, oyster shell whiting 1g, tourmaline powder 0.3g, vermiculite power 0.5g, grape
Glucoside 1g, citric acid 1.5g, etherification starch 0.5g, algin 0.5g, polyethylene glycol 0.5g, mannitol 0.5g, glycerine 0.3g,
Glucose 0.1g, manganese dioxide 0.2g and water 50g.
Embodiment 4
The present invention is prepared according to formula as below and ratio, and the composition of carrier is used as by the use of diatomite：Diatomite 6g, hydrogen-oxygen
Change calcium 1g, nano titanium oxide 1g, nano zine oxide 0.2g, oyster shell whiting 2g, tourmaline powder 0.1g, vermiculite power 1g, glycoside
0.5g, citric acid 2g, etherification starch 0.2g, algin 0.7g, polyethylene glycol 0.2g, mannitol 1.5g, glycerine 0.2g, Portugal
Grape sugar 0.1g, manganese dioxide 0.4g and water 50g.
Embodiment 5
The present invention is prepared according to formula as below and ratio, and the composition of carrier is used as by the use of diatomite：Diatomite 5g, hydrogen-oxygen
Change calcium 1.5g, nano titanium oxide 0.5g, nano zine oxide 1g, oyster shell whiting 1.2g, tourmaline powder 0.3g, vermiculite power 0.5g, Portugal
Grape glucoside 0.8g, citric acid 1.5g, etherification starch 0.5g, algin 0.4g, polyethylene glycol 0.5g, mannitol 1g, glycerine
0.2g, glucose 0.2g, manganese dioxide 0.2g and water 50g.
Embodiment 6
The present invention is prepared according to formula as below and ratio, and the composition of carrier is used as by the use of diatomite：Diatomite 4g, hydrogen-oxygen
Change calcium 1.5g, nano titanium oxide 0.5g, nano zine oxide 0.7g, oyster shell whiting 1g, tourmaline powder 0.3g, vermiculite power 0.2g, Portugal
Grape glucoside 0.8g, citric acid 1.6g, etherification starch 0.5g, algin 0.5g, polyethylene glycol 0.3g, mannitol 1g, glycerine
0.2g, glucose 0.15g, manganese dioxide 0.25g and water 50g.
The preparation method of above-mentioned composition is with reference to as follows：
Step 1：By nano titanium oxide, nano zine oxide, glycoside, lysine, etherification starch, algin, poly- second
Glycol, mannitol, glycerine, glucose and manganese dioxide are soluble in water, stirring at normal temperature, obtained solution component A；
Step 2：Diatomite, calcium hydroxide, oyster shell whiting, tourmaline powder and vermiculite power are mixed, stirs, obtains B component；
Step 3：Step 2 gained B component is added in step 1 gained component A, stirred, be dried to aqueous
Amount is less than 3wt%, and C components are made；
Step 4：Calcium hydroxide is added into step 3 gained C components, stirs, gets product.
Composition prepared by 1-6 of the embodiment of the present invention stirs, and is applied to ground or wall is used to remove finishing
Ornament materials is discharged into formaldehyde, benzene, dimethylbenzene, trichloro ethylene, ether-ether class, propylene cyanogen or other irritant peculiar smell in air
Gas (peculiar smell that such as toilet distributes, pet body odor, ammonia), within one day, the clearance rate of formaldehyde is all higher than 95%, benzene
Clearance rate be all higher than 87%, the clearance rate of dimethylbenzene is all higher than 89%, and the clearance rate of trichloro ethylene is all higher than 69%, ether-ether class
Clearance rate be all higher than 50%, the clearance rate of propylene cyanogen is all higher than 75%；For the peculiar smell of toilet, can in 30 minutes base
This elimination, the clearance rate of ammonia are all higher than 85%.
Composition prepared by 1-6 of the embodiment of the present invention stirs, and is directly used in sewage disposal, heavy metal ion
Clearance rate is all higher than 89%, and the clearance rate of phosphorus is all higher than 70%, and the clearance rate of low molecule aldehyde is more than 99%.
In summary, the diatomite in the present invention, oyster shell whiting all have preferable adsorption capacity；Lysine with carboxyl and
Amino, amino can be reacted with small molecule aldehyde, small molecule ketone, hydrogen cyanide, and carboxyl can adsorb ammonia；Glycoside, gather
Ethylene glycol and starch ether contain substantial amounts of hydroxyl, and PARA FORMALDEHYDE PRILLS(91,95) has preferable adsorption activity, and polyethylene glycol is hygroscopic, manganese dioxide
It is catalyzed hydrone and produces free hydroxyl group, free hydroxyl group can be with small organic molecules such as oxidation of formaldehyde, these small organic molecule quilts
Nano zine oxide, nano titanium oxide, these oxides of calcium hydroxide further aoxidize；Mannitol and glycerine also have a large amount of
Hydroxyl, add tourmaline powder and vermiculite power on this basis, anion discharged in the state of having humidity.The present invention side of effecting a permanent cure
Method is simple to operation, and cost is cheap, will not produce secondary pollution, and low molecule aldehyde, ketone can be reduced in gas, liquid, can be with
It is directly appended in finishing and ornament materials；Heavy metal ion, phosphorus and small molecule aldehyde are removed in sewage disposal also to be had well
Using.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (6)
1. a kind of composition by the use of diatomite as carrier, it is characterised in that count, be made up of following raw material in parts by weight：
Diatomite 30-80 parts, calcium hydroxide 10-20 parts, nano titanium oxide 1-10 parts, nano zine oxide 1-15 parts, oyster shell whiting 5-20
Part, tourmaline powder 1-5 parts, vermiculite power 1-10 parts, glycoside 5-10 parts, lysine 10-20 parts, starch ether 2-8 parts, algin
1-7 parts, polyethylene glycol 2-10 parts, mannitol 3-15 parts, glycerine 2-3 parts, glucose 1-2 parts, manganese dioxide 0.5-4 parts and water
500 parts.
A kind of 2. composition by the use of diatomite as carrier according to claim 1, it is characterised in that fraction by weight
Meter, is made up of following raw material：Diatomite 40-70 parts, calcium hydroxide 5-15 parts, nano titanium oxide 2-8 parts, nano zine oxide 2-
10 parts, oyster shell whiting 10-15 parts, tourmaline powder 2-3 parts, vermiculite power 2-8 parts, glycoside 6-9 parts, lysine 12-15 parts, etherificate
Starch 4-6 parts, algin 2-5 parts, polyethylene glycol 4-8 parts, mannitol 5-10 parts, glycerine 2-3 parts, glucose 1-2 parts, dioxy
Change 500 parts of manganese 0.5-4 parts and water.
A kind of 3. composition by the use of diatomite as carrier according to claim 2, it is characterised in that fraction by weight
Meter, is made up of following raw material：50 parts of diatomite, 15 parts of calcium hydroxide, 5 parts of nano titanium oxide, 10 parts of nano zine oxide, shell
It is 12 parts of powder, 3 parts of tourmaline powder, 5 parts of vermiculite power, 8 parts of glycoside, 15 parts of lysine, 5 parts of etherification starch, 4 parts of algin, poly-
500 parts of 5 parts of ethylene glycol, 10 parts of mannitol, 2 parts of glycerine, 2 parts of glucose, 2 parts of manganese dioxide and water.
4. a kind of preparation method by the use of diatomite as the composition of carrier, it is characterised in that comprise the following steps:
Count in parts by weight, diatomite is made up of as the composition of carrier following raw material：Diatomite 30-80 parts, calcium hydroxide
10-20 parts, nano titanium oxide 1-10 parts, nano zine oxide 1-15 parts, oyster shell whiting 5-20 parts, tourmaline powder 1-5 parts, vermiculite power
It is 1-10 parts, glycoside 5-10 parts, lysine 10-20 parts, starch ether 2-8 parts, algin 1-7 parts, polyethylene glycol 2-10 parts, sweet
Reveal 500 parts of alcohol 3-15 parts, glycerine 2-3 parts, glucose 1-2 parts, manganese dioxide 0.5-4 parts and water；
Step 1：By nano titanium oxide, nano zine oxide, glycoside, lysine, etherification starch, algin, polyethylene glycol,
Mannitol, glycerine, glucose and manganese dioxide are soluble in water, stirring at normal temperature, obtained solution component A；
Step 2：Diatomite, calcium hydroxide, oyster shell whiting, tourmaline powder and vermiculite power are mixed, stirs, obtains B component, wherein
The weight of calcium hydroxide is the 1/3 of calcium hydroxide gross weight；
Step 3：Step 2 gained B component is added in step 1 gained component A, stirred, carries out being dried to water content low
In 3wt%, C components are made；
Step 4：Remaining calcium hydroxide is added into step 3 gained C components, stirs, gets product.
5. a kind of a kind of composition by the use of diatomite as carrier as described in claim any one of 1-3 is removing finishing dress
Exterior material is discharged into the application in the formaldehyde in air, benzene, dimethylbenzene, trichloro ethylene, ether-ether class, propylene cyanogen pernicious gas, and/
Or the application in irritant gas with foreign flavor is removed, and/or the application in formaldehyde in indoor air, benzene, ammonia is removed.
6. a kind of a kind of composition by the use of diatomite as carrier as described in claim any one of 1-3 is removing weight in sewage
Application in metal ion, phosphorus, low molecule aldehyde.