CN107375340A - A kind of hot compress pottery and preparation method thereof - Google Patents
A kind of hot compress pottery and preparation method thereof Download PDFInfo
- Publication number
- CN107375340A CN107375340A CN201710702545.0A CN201710702545A CN107375340A CN 107375340 A CN107375340 A CN 107375340A CN 201710702545 A CN201710702545 A CN 201710702545A CN 107375340 A CN107375340 A CN 107375340A
- Authority
- CN
- China
- Prior art keywords
- hot compress
- pottery
- raw material
- gross mass
- counted
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of hot compress pottery and preparation method thereof, the hot compress pottery includes following composition：Clay, keel, float stone, magnetite and the shell of seaear, counted using the gross mass of raw material as 100wt%, wherein, keel, float stone, magnetite and the shell of seaear weight sum shared by percentage by weight be 4 11wt%.The preparation method is that above-mentioned raw materials are made pottery in 700~1200 DEG C of sintering into hot compress.Hot compress pottery has regulation metabolism, the analgesic and the effect of blood stasis-eliminating and stagnation-dissipating of dispeling cold.
Description
Technical field
The present invention relates to physiotherapy product technical field, more particularly to a kind of hot compress pottery and preparation method thereof.
Background technology
At present, the living standard of people improves constantly, and rhythm of life is constantly accelerated, and causes excessive, insomnia and dreamful sleep of pressure etc.
The generation of Sub-health, hot compress product are becoming increasingly popular, but existing hot compress is produced as a kind of external application physiotherapy product
Product, warm effect is only served, hot application device is water or other heat transfer mediums, and other functional components, physiotherapy effect are not contained in hot application device
Fruit is limited.
The content of the invention
To solve problem above, the invention provides a kind of comprising the active ingredient such as keel, float stone, magnetite and the shell of seaear
A kind of hot compress pottery and preparation method thereof.
Technical scheme is as follows：
The hot compress pottery of the present invention, its raw material includes clay, keel, float stone, magnetite and the shell of seaear, wherein, keel, float stone,
Percentage by weight is 4~11wt% shared by the weight sum of magnetite and the shell of seaear, is counted using the gross mass of raw material as 100wt%.Example
Such as, the content of keel can be 1wt%；The content of float stone can be 3wt%；The content of magnetite can be 3wt%；The shell of seaear
Content can be 2wt%.
Wherein, keel have calmness, hypnosis, anticonvulsant action；Float stone has that clearing lung-heat is fiery, promoting diuresis for stranguria, softening and resolving hard mass it
Effect；Magnetite has the effect of calming the liver, relieving convulsion, hearing-improing and eyesight improving of calming the nerves, gas of receiving are relievingd asthma；The shell of seaear has town liver, improving eyesight, is cured
The effect of ulcer subcutaneous ulcer.
In further embodiment of the present invention, its raw material also includes 1~9wt% clean skin components, with total matter of raw material
Measure and counted for 100wt%.
Herein, clean skin component refers to that the dirts such as the grease in skin can be adsorbed to reach the composition of clean effect.
Clean skin component can be the material that diatomite, seabed mud, stream mud, montmorillonite etc. have loose structure.
In a more preferable scheme, diatomaceous content is suitably more 1~3wt%, with total matter of raw material
Measure and counted for 100wt%, such as：
In a more preferable scheme, the content of seabed mud is suitably more 1~3wt%, with total matter of raw material
Measure and counted for 100wt%.
In a more preferable scheme, the content of stream mud is suitably more 1~3wt%, with total matter of raw material
Measure and counted for 100wt%.
Above-mentioned clay is the composition that can play cementation to be molded, and it is the main component of hot compress pottery.
The content of clay is not particularly limited, such as can be not less than 80wt%, is counted using the gross mass of raw material as 100wt%.
Clay is kaolin, can also be other conventionally forms certainly, as silica, feldspar, fire clay, mullite,
Alumina, magnesia, calcium oxide, barium monoxide and their mixture.Ceramic precursor can be it is powdered, must shape, piece is crystalline or
Other shapes common in the art
The invention also discloses a kind of method for preparing hot compress pottery as described above, by the raw material in 700~1200 DEG C of burnings
Knot forms.
It is understood that the step of also including such as mixing, stirring, shaping obtain green compact before sintering.
The mode of sintering can use known form, can be once sintered, double sintering etc..
The shape of hot compress pottery does not limit, and can be a shape or sheet etc., according to selected by the application scenario of reality.
In the hot compress pottery disclosed in this invention, it directly can be applied on skin, such as can first be placed in the hot water
To predetermined temperature, then the skin of human body is fitted in hot compress.
The invention also discloses a kind of hot compress bag, it includes bag body and is filled in internal as described above sintered of the bag
The hot compress pottery formed.
Beneficial effects of the present invention are as follows：
The present invention is by adding keel, float stone, hot compress is made pottery made from magnetite and the shell of seaear, has regulation metabolism, drives
The effect of cold analgesic and blood stasis-eliminating and stagnation-dissipating.By the combination of several active ingredients, hot compress of the invention pottery can be by internal pathogenic QI in the body, cold
Aspiration comes out, at the same can relaxed muscle, expand capillary, increase sweat gland secretion, stimulate circulation, improve body new old generation
The speed thanked.
On the other hand, hot compress of the invention pottery has promoting flow of qi by warming channel, anti-inflammatory cold dispelling, lenitive effect.For the soreness of waist
Backache, arthritis, chronic gastralgia, diarrhoea, neuralgia, chilly disease has effective.
Embodiment
Further to illustrate the technological means and its effect of the invention taken, below in conjunction with being preferable to carry out for the present invention
Example is described in detail.
Embodiment 1
Step 1: proportioning raw material：A kind of hot compress pottery, is counted using the gross mass of raw material as 100wt%, its by following component original
Material composition：86wt% kaolin, 4wt% keel, 2wt% float stones, 1wt% magnetites, the 2wt% shells of seaear, 1wt% diatomite,
3wt% streams mud and 1wt% seabeds mud.Gross mass is 200g.
Step 2: the raw material of said ratio is well mixed, adds 10ml water, stir.
Step 3: blended raw material is molded with mould, blank is obtained.
24h is sintered at 800 DEG C Step 4: above-mentioned blank is placed in sintering oven, obtains hot compress pottery.Hot compress pottery is length
Cylinder.
In use, hot compress pottery is placed in micro-wave oven, high fire heating 2 minutes, takes out and do not locate freely after subject's body
Kept for 15-25 minutes.
Embodiment 2
Step 1: proportioning raw material：A kind of hot compress pottery, is counted using the gross mass of raw material as 100g, its by following component raw material
Composition：80g kaolin, 2g keel, 3g float stones, 5g magnetites, the 1g shells of seaear, 1g diatomite, 4g streams Ni He4g seabeds mud.
Step 2: the raw material of said ratio is well mixed, 8ml water is added, is stirred.
Step 3: blended raw material is granulated, graininess blank is obtained.
20h is sintered at 700 DEG C Step 4: above-mentioned graininess blank is placed in sintering oven, obtains graininess haydite.
Embodiment 3
Step 1: proportioning raw material：A kind of hot compress pottery, is counted using the gross mass of raw material as 100wt%, its by following component original
Material composition：83wt% kaolin, 3wt% keel, 1wt% float stones, 4wt% magnetites, the 1wt% shells of seaear, 3wt% diatomite,
1wt% streams mud and 4wt% seabeds mud.Gross mass is 300g.
Step 2: the raw material of said ratio is well mixed.Add 25ml water.
Step 3: blended raw material is molded with mould, blank is obtained.
Sintered Step 4: above-mentioned blank is placed in sintering oven at 920 DEG C, obtain hot compress pottery.The hot compress of the present embodiment
Make pottery as similar to spherical.
Embodiment 4
Step 1: proportioning raw material：A kind of hot compress pottery, is counted using the gross mass of raw material as 100wt%, its by following component original
Material composition：85wt% kaolin, 3wt% keel, 2wt% float stones, 2wt% magnetites, the 1wt% shells of seaear, 2wt% diatomite,
3wt% streams mud and 2wt% seabeds mud, gross mass 200g.
Step 2: the raw material of said ratio is well mixed, add a small amount of water, stir.
Step 3: blended raw material is molded sheet blank with mould.
Sintered Step 4: above-mentioned blank is placed in sintering oven at 1180 DEG C, obtain hot compress pottery piece.
Embodiment 5
Step 1: proportioning raw material：A kind of hot compress pottery, is counted using the gross mass of raw material as 100wt%, its by following component original
Material composition：88wt% kaolin, 2wt% keel, 1wt% float stones, 1wt% magnetites, the 3wt% shells of seaear, 2wt% diatomite,
1wt% streams mud and 2wt% seabeds mud.Gross mass is 100g.
Step 2: the raw material of said ratio is well mixed, adds a small amount of water, stir.
Step 3: blended raw material is granulated.
Sintered Step 4: above-mentioned granulation blank is placed in sintering oven at 830 DEG C, obtain graininess hot compress pottery.
The sintered graininess hot compress pottery formed, can be loaded in the bag body of hot compress bag and obtain one kind with graininess hot compress pottery
New hot compress bag product；The sintered sheet hot compress pottery formed can directly soak hot water and directly use, and can also be loaded on certainly
In hot compress bag, a kind of new hot compress bag product with sheet hot compress pottery is obtained.
Theory of traditional Chinese medical science thinks that many illnesss of human body are all relevant with cold air, therefore it is first as healthcare field how to dispel cold air
The factor first considered, technical scheme employ keel, float stone, magnetite and hot compress made from the shell of seaear and made pottery, using
When first heated, then spread on affected part, there is remarkable result for analgesic of dispeling cold.
Using hot compress as described above make pottery hot compress fictile application method be：
For insomnia and dreamful sleep, palpitaition, patient, by equipped with the hot compress make pottery particle hot compress bag directly spread on forehead portion, often
It once, can reach calm the nerves, calm nerves pressure and gas of receiving are relievingd asthma makees effect；
For the grieved patient that swells and ache, the hot compress bag equipped with hot compress pottery particle is spread at swelling and pain, 15min-30min/ times,
Play activating blood circulation and reducing swelling and analgesic efficacy.
For trembled with fear person, the effect dispeled cold of being dried using the hot compress pottery progress hot compress of the present invention is also more apparent.For example, to pain
Wind patient, the hot compress bag equipped with hot compress pottery particle can be used to be put in knee, have alleviation to disappear bitterly, analgesic activity, make for a long time
With unobstructed blood, rheumatism symptom, which has, to be alleviated.
Clinical test is proved, the hot compress fictile is included into hot compress bag and hot compress pottery piece, female is pasted under tepid state
Property the disease such as belly, the menorrhalgia caused for treating deficient cold, uterine bleeding, pregnant woman are caught cold, abdominal pain pain and fetal irritability have
It is obvious to improve effect；Hot compress Tao Pin is included into hot compress bag and hot compress plate, male's belly is pasted on, to emission and spermatorrhea, uterine bleeding
Improved significantly effect with inferior tool.
It is described above, for the person of ordinary skill of the art, can be with technique according to the invention scheme and technology
Other various corresponding changes and deformation are made in design, and all these changes and deformation should all belong to the claims in the present invention
Protection domain.
Claims (8)
1. a kind of hot compress pottery, comprising clay, keel, float stone, magnetite and the shell of seaear, wherein, the keel, float stone, magnetite and stone
Percentage by weight is 4~11wt% shared by the weight sum of Cassia, is counted using the gross mass of raw material as 100wt%.
2. hot compress pottery according to claim 1, it is characterised in that the clean skin component also comprising 1~9wt%, with raw material
Gross mass is counted for 100wt%.
3. hot compress pottery according to claim 2, it is characterised in that the clean skin component includes diatomite, the diatomite
Content is 1~3wt%, is counted using the gross mass of raw material as 100wt%.
4. hot compress pottery according to claim 2, it is characterised in that the clean skin component also includes seabed mud, the seabed
Cement content is 1~3wt%, is counted using the gross mass of raw material as 100wt%.
5. hot compress pottery according to claim 2, it is characterised in that the clean skin component also includes stream mud, the stream
Cement content is 1~3wt%, is counted using the gross mass of raw material as 100wt%.
6. hot compress pottery according to claim 1, it is characterised in that the content of the clay is not less than 80wt%, with raw material
Gross mass be 100wt% meter.
7. hot compress pottery according to claim 1, it is characterised in that the clay is kaolin.
8. a kind of prepare the method made pottery such as hot compress according to any one of claims 1 to 7, it is characterised in that by the raw material
Formed in 700~1200 DEG C of sintering.