CN1073624A

CN1073624A - Ceramic aggregate terrazzo and production method thereof

Info

Publication number: CN1073624A
Application number: CN 92114917
Authority: CN
Inventors: 王兴飞
Original assignee: Individual
Current assignee: Individual
Priority date: 1992-12-28
Filing date: 1992-12-28
Publication date: 1993-06-30

Abstract

The present invention is ceramic aggregate terrazzo and production method thereof, belongs to building and ornament materials.Be made up of underlying material and capstock, wherein capstock is aggregate with the pottery, is mixed with coloured cement, ballast, and bottom is made up of ordinary cement, sand, rubble.At first make surface layer material plate with capstock, after leaving standstill, go up underlying material again, maintenance then, corase grind, fine grinding, light maintenance get product.The present invention is mainly used in the flooring and decorates, and its advantage is, than lithotome rich color, and the degree of monochromaticity height, the intensity height, the comparable lithotome attenuate 1/3 of surface thickness, intensity increases about 10%, have specific decorative effect, and cost is low.

Description

Ceramic aggregate terrazzo and production method thereof

The invention belongs to building and ornament materials.

At present, the terrazzo kind is a lot, and the surface layer aggregate is with griotte, limestone and dolomite are main, decorate the shallow variation of color depth and form naturally, but also there is deficiency in lithotome aspect color, the one, degree of monochromaticity is not high, as: a large amount of at present dolomites that use, be commonly called as white quarrel stone, with＜chromatogram〉(annotate: Mapping Press's front page in 1987) listed color lump contrasts a book, during its color is formed, palm fibre accounts for 10%, and orchid accounts for 5%, so whiteness is undesirable; The 2nd, lack partial color, as: bright cyan (vividblue) avy blue (deepblue), also do not find so far in the lithotome.

The present invention is the terrazzo facing aggregate with the pottery, and underlying material is the light water grinding stone roughly the same, and its advantage is: the one, and rich color has plurality of color such as the unexistent bright cyan of lithotome, avy blue; The 2nd, the degree of monochromaticity height, as: during ceramic whiteware sheet color is formed, have only to deceive to account for 5%, whiteness is apparently higher than lithotome; The 3rd, the intensity height causes the comparable lithotome attenuate 1/3 of terrazzo facing, and intensity increases about 10%.Therefore, be the terrazzo of aggregate with the pottery, have specific decorative effect, cost is low simultaneously, has social benefit well.

Pottery derives from a large amount of waste product things such as ceramic producer, after reclaiming, screening cleaning, is processed into 2～20 millimeters indefinite moulding mixture, can use.

Ceramic aggregate terrazzo lining percentage by weight sees Table one:

Table one

Component	Coloured cement	Pottery	Ballast or stone flour
				W％	15～30	20～80	0～60

Can add as required pigment a little, be generally 0～8% of coloured cement.

Manufacture technology of the present invention is: earlier with lining proportioning apolegamy in accordance with regulations, be mixed, and stir, make surface layer material plate with an amount of hydration material, left standstill 15～40 minutes, go up underlying material again, natural curing more than 20 hours then, demoulding, water curing is 150～180 hours again, take out corase grind, fine grinding, polishing, light maintenance promptly get ceramic aggregate terrazzo.

Embodiment:

The underlying material percentage by weight sees Table two

Table two

Component	Ordinary cement	Rough sand	Rubble
				W％	25	37.5	37.5

The capstock percentage by weight sees Table three

Table three

Component		Coloured cement	Pottery	Ballast or stone flour	Σ
						W％	Scheme one	25	50	25	100
Scheme two	20	70	10	100

Press table three scheme one, select whiteware, white cement, the stone that is cut in vain for use, do not add any pigment, add an amount of hydration material and stir, make surface layer material plate, thick 6 millimeters.

Scheme two, select bright cyan pottery, white cement, albarium for use, add a little bright blue or green pigment, add an amount of hydration material and stir, make the lining plate, thick 6 millimeters.After surface layer material plate is made, left standstill 25 minutes, press table two proportioning, add an amount of hydration material and stir last underlying material, thick 10 millimeters, natural curing is 25 hours then, the demoulding, and the maintenance of water logging bubble is 170 hours again, take out corase grind, fine grinding, polishing, light maintenance, promptly obtain white, bright blue or green two kinds of ceramic aggregate terrazzos respectively.

Claims

1, ceramic aggregate terrazzo is made up of underlying material and capstock, and underlying material is the light water grinding stone roughly the same, and capstock is made up of coloured cement, ballast or stone flour, pigment etc., it is characterized in that: capstock is aggregate with the pottery.

According to the described ceramic aggregate terrazzo of claim 1, it is characterized in that 2, the percentage by weight of capstock is coloured cement 15～30%, pottery 20～80%, ballast or stone flour 0～60%.

According to claim 1 or 2 described ceramic terrazzos, it is characterized in that 3, the percentage by weight of capstock is coloured cement 25%, pottery 50%, rock ballast 25%.

According to claim 1 or 2 described ceramic terrazzos, it is characterized in that 4, the percentage by weight of capstock is coloured cement 20%, pottery 70%, stone flour 10%.