CN107351344A - The nonmetallic oil pipe preparation method that a kind of oil gas field uses - Google Patents
The nonmetallic oil pipe preparation method that a kind of oil gas field uses Download PDFInfo
- Publication number
- CN107351344A CN107351344A CN201710590329.1A CN201710590329A CN107351344A CN 107351344 A CN107351344 A CN 107351344A CN 201710590329 A CN201710590329 A CN 201710590329A CN 107351344 A CN107351344 A CN 107351344A
- Authority
- CN
- China
- Prior art keywords
- pipe
- box cupling
- layer pipe
- enhancement layer
- finished product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The nonmetallic oil pipe preparation method that a kind of oil gas field uses, including body and box cupling, body and box cupling include refractory layer pipe, middle enhancement layer pipe and anticorrosive coat pipe, refractory layer pipe be molecular weight 150~3,200,000 the heat-proof macromolecule polymer that is polymerized under rigid catalyst of polyethylene or butadiene, middle enhancement layer pipe by resistance to mesohigh glass fibre, enhanced polyester fiber, aramid fiber, polyethylene fibre and netted high-tensile steel wires collectively constitute, anticorrosive coat pipe is polyethylene of the molecular weight 250~4,200,000, the refractory layer bore of body is d and its anticorrosive coat pipe external diameter is D and its length is L, middle enhancement layer bore is equal to refractory layer pipe external diameter and its external diameter is equal to anticorrosive coat bore, L is provided with body anticorrosive coat pipe both ends1Outer cone boss, the L of the length of box cupling >=21And female cone boss is set in its refractory layer pipe, outer cone boss or female cone boss prepare taper pipe thread by screw thread compression molding.
Description
Technical field
The invention belongs to exploitation of oil-gas field equipment technical field, prepared by the nonmetallic oil pipe that especially a kind of oil gas field uses
Method.
Background technology
The oil pipe that oil gas field uses at present is processed into using seamless steel pipe, and oil pipe includes body and box cupling, each body
Between mutually concatenation sealing implemented by the inner cone pipe screw thread at box cupling both ends, easily cause oil pipe abrasion, burn into use
Phenomena such as tube wall incrustation and Taper Pipe screw thread damage, these phenomenons cause frequent well workover, and frequently well workover then reduces production of hydrocarbons
Efficiency, cause the increase of oil-gas mining cost.
Oil pipe is easy to wear, use carries out coating treatment more in its inwall at present for corrosion and tube wall incrustation, due to inboard wall of tube body
Derusting work be difficult to accomplish clean, thorough, cause inside coating adhesive force low, especially the low painting of adhesive force in use
Layer can gradually be peeled off, departed from, and the coating impurity split away off even may also result in holddown, produce new well workover problem.
Also have and install polyethylene liner additional in inboard wall of tube body to solve to wear, corrode and tube wall incrustation, but due to liner material
And install the reasons such as technique additional, liner and the bad factor of body abutment be present, easily produce inner liner and peel off, release, use
The problems such as life-span is unstable.In addition installing liner additional needs and the requirement of processing clean to inner surface of tube body processing high, interior during installation
Lining needs the cumbersome technique such as undergauge, poling, heating, flange, and the manufacturing cost for installing liner additional is high.
The content of the invention
To solve the above problems, the invention provides the nonmetallic oil pipe preparation method that a kind of oil gas field uses, this method
The nonmetallic oil pipe prepared has excellent mechanical property, antiseptic property, anti-wear performance, thermal property, can extensive use
In oil gas field, production cost and maintenance cost are reduced, improves oil gas field production efficiency.
For achieving the above object, the present invention adopts the following technical scheme that:
The nonmetallic oil pipe preparation method that a kind of oil gas field uses, nonmetallic oil pipe include body and box cupling, body it is interior
Footpath, external diameter and length dimension are performed by oil gas field standard used in connection with, and box cupling implements Butt sealing, preparation method to two bodys
Using to screw extruder, screw thread moulding press, it is characterized in that:
Body and box cupling include refractory layer pipe, middle enhancement layer pipe and anticorrosive coat pipe, refractory layer pipe and existed by molecular weight
The heat-proof macromolecule polymer composition that 150~3,200,000 polyethylene or butadiene is polymerized under rigid catalyst,
Middle enhancement layer pipe is by the glass fibre of resistance to mesohigh, enhanced polyester fiber, aramid fiber, polyethylene fibre and netted high strength steel
Silk is collectively constituted, and anticorrosive coat pipe is made up of molecular weight in 250~4,200,000 polyethylene;
The refractory layer bore of body is set as d and its anticorrosive coat pipe external diameter is set as D and its length is set as L, middle
The internal diameter of enhancement layer pipe is equal to the external diameter of refractory layer pipe, and the external diameter of middle enhancement layer pipe is equal to the internal diameter of anticorrosive coat pipe, in body
The both ends of anticorrosive coat pipe are L provided with length1Outer cone boss, L1Less than L, each outer cone boss is molded by screw thread
Shaping preparation has outer taper pipe thread;Length >=2L of box cupling1, female cone boss is provided with the refractory layer pipe of box cupling, it is each described
Female cone boss internal diameter is prepared by screw thread compression molding entire body inner cone pipe screw thread, and the nominal bore diameter of inner cone pipe screw thread is equal to outer
The nominal outside diameter of taper pipe thread, by the outer taper pipe threads of adjacent two bodys of the entire body endosiphuncular tube thread connection of box cupling and with this
Analogize;
When preparing body:
1. polyethylene or butadiene and rigid catalyst are placed in high speed agitator, high-speed stirred 3~30 minutes
Discharging obtains heat-proof macromolecule polymer afterwards, is then dried for standby heat-proof macromolecule polymer;
2. middle enhancement layer pipe is cleaned up and preheated 5 minutes at 30~60 DEG C, then in middle enhancement layer pipe
Surfaces externally and internally uniformly coat cool down after binding resin it is standby;
3. by middle enhancement layer pipe sleeve on the design attitude of screw extruder, by screw extruder by heat-proof macromolecule
Polymer is squeezed in the endoporus of middle enhancement layer pipe, is cooled down in mould and is made the wall thickness control of inner tube in 0.6~3.5mm, cooling
Semi-finished product body is prepared by more than L progress excision formings afterwards, the internal diameter of the semi-finished product body should meet the d;
4. the semi-finished product in 3. are enclosed on the design attitude of screw extruder, by screw extruder by polyethylene
Squeeze middle enhancement layer pipe it is cylindrical in, cooling down in mould simultaneously makes the wall thickness control of inner tube press institute after 1.2~5.4mm, cooling
State L progress excision formings and prepare finished product body, the external diameter of the finished product body should meet the D;
Possess it is above-mentioned 1.~2. under the conditions of prepare box cupling when:
5. by middle enhancement layer pipe sleeve on the design attitude of screw extruder, by screw extruder by heat-proof macromolecule
Polymer is squeezed in the endoporus of middle enhancement layer pipe, is cooled down in mould and is made the wall thickness control of inner tube in 0.6~3.5mm, cooling
Semi-finished product box cupling is prepared by more than L progress excision formings afterwards, the internal diameter of the semi-finished product box cupling should be less than the D;
6. the semi-finished product box cupling in 5. is enclosed on the design attitude of screw extruder, will be poly- by screw extruder
Ethene squeeze middle enhancement layer pipe it is cylindrical in, cooling down in mould simultaneously makes the wall thickness control of inner tube after 1.2~5.4mm, cooling
By >=2L1Carry out excision forming and prepare finished product box cupling;
It is L that the finished product body or the finished product box cupling, which are individually placed to prepare both ends on screw thread moulding press,1's
Outer taper pipe thread body or >=2L1Endosiphuncular tube threaded collar joint, it is desirable to body and box cupling are provided with following technical performance:
Long-term hydrostatic strength >=15MPa of body and box cupling;
Tensile strength >=126MPa of body and box cupling and yield strength control at 105~134MPa [25 DEG C];
The heatproof softening point of body and box cupling reaches 150 DEG C;
The density of texture of body and box cupling is controlled in 0.941~1.56g/cm3。
Above-mentioned rigid catalyst is the rigid polymer with binding function group and hole.
Above-mentioned netted high-tensile steel wires are the Wrapping formed network structures of steel wire left-and-right spiral, or steel wire winding shaping
Helicoidal structure.
Due to using technical scheme as described above, the present invention produces following good effect:
1st, the body of oil pipe of the present invention and box cupling its wearability are 4 times of ordinary steel body and box cupling, through measuring and calculating than common
The transfer efficiency of steel tube body and box cupling can improve 20% or so.
2nd, the heat-proof macromolecule that refractory layer pipe is polymerized by polyethylene or butadiene under rigid catalyst gathers
Compound, the heat resistance of body and box cupling can be significantly improved.
3rd, the body of oil pipe of the present invention and box cupling density are only 1/5th or so of ordinary steel body and box cupling density, but
Coefficient of friction is only 1/6th or so of ordinary steel body and box cupling.
4th, the outer taper pipe thread of body and the inner cone pipe screw thread of box cupling meet relevant criterion, do not change the existing work of oil gas field
Industry technique.
5th, preparation method of the invention is simple, easy to operate, equipment investment is small, is easy to large-scale production, can save big dimension
Material, mitigate the manipulation strength of oil gas field worker, be useful in very much oil gas field and promote the use of.
Brief description of the drawings
Fig. 1 is the axial diagrammatic cross-sectional view of the present invention.
Fig. 2 is the radial direction diagrammatic cross-sectional view of body of the present invention.
In above-mentioned figure:1- bodys;1.1- refractory layer pipes;Enhancement layer pipe among 1.2-;1.3- anticorrosive coat pipes;2- box cuplings.
Embodiment
The present invention is the nonmetallic oil pipe preparation method that a kind of oil gas field uses, and the nonmetallic oil pipe that oil gas field uses includes
Body and box cupling, body and box cupling are the inseparable entirety of oil pipe, and only nonmetallic body and nonmetallic box cupling could be formed
Nonmetallic oil pipe, this is also that body and box cupling are combined into one one of the reasons why stating altogether by the present invention.
The preparation method of the present invention uses screw extruder, screw thread moulding press, and screw extruder and screw thread moulding press are equal
For conventional equipment and commercially available.
With reference to Fig. 1-2, nonmetallic oil pipe of the invention includes body 1 and box cupling 2, internal diameter, external diameter and the length ruler of body 1
Very little to be performed by oil gas field standard used in connection with, box cupling 2 implements Butt sealing to two bodys.Body 1 and box cupling 2 include resistance to
Thermosphere pipe 1.1, middle enhancement layer pipe 1.2 and anticorrosive coat pipe 1.3, refractory layer pipe 1.1 is by poly- second of the molecular weight 150~3,200,000
The heat-proof macromolecule polymer composition that alkene or butadiene are polymerized under rigid catalyst, the rigid catalyst are
Rigid polymer with binding function group and hole.Glass fibre, enhanced polyester of the middle enhancement layer pipe 1.2 by resistance to mesohigh
Fiber, aramid fiber, polyethylene fibre and netted high-tensile steel wires collectively constitute, and the netted high-tensile steel wires are steel wire left-and-right spirals
Wrapping formed network structure, or the helicoidal structure of steel wire winding shaping.Anticorrosive coat pipe 1.3 is by molecular weight 250~420
Ten thousand polyethylene composition.Refractory layer pipe 1.1, middle enhancement layer pipe 1.2 and anticorrosive coat pipe 1.3 form integral structure, although its
Intensity index is slightly below metal oil conduit, but it combines fine and close, firmly, is not in layering and peeling and in light weight, complete
The use of full up sufficient oil gas field.
Utilize ultra-high molecular weight polyethylene or the butadiene material such as have good anti-corrosion, wear-resisting, self-lubricating, surface smooth
Expect characteristic, can solve the problems such as abrasion, corrosion and scaling of nonmetallic oil pipe, improve resistance to compression and the pull resistance of nonmetallic oil pipe
Energy.
The internal diameter of refractory layer pipe 1.1 of body 1 is set as d and its external diameter of anticorrosive coat pipe 1.3 is set as D and its length is set as
L, preferable body refers to outer diameter D=φ 73mm and it refers to internal diameter d=φ 62mm.The internal diameter of middle enhancement layer pipe 1.2 is equal to
The external diameter of refractory layer pipe 1.1, the external diameter of middle enhancement layer pipe 1.2 is equal to the internal diameter of anticorrosive coat pipe 1.3, in the anticorrosive coat pipe of body 1
1.3 both ends are L provided with length1Outer cone boss, L1Less than L, each outer cone boss passes through screw thread compression molding system
Have outer taper pipe thread.
The length of box cupling is more than 2L1, female cone boss is provided with the refractory layer pipe 1.1 of box cupling 2, each female cone is convex
Platform internal diameter is prepared by screw thread compression molding entire body inner cone pipe screw thread, and the nominal bore diameter of inner cone pipe screw thread is equal to outer taper pipe thread
Nominal outside diameter, pass through outer taper pipe thread of entire body endosiphuncular tube two bodys of thread connection of box cupling and so on.Box cupling can
Depending on above-mentioned preferable body size, the outside dimension of box cupling is defined by not interfered with existing sleeve pipe, oil well pump.
The present invention is when preparing body:
1. polyethylene and butadiene and rigid catalyst are placed in high speed agitator, high-speed stirred is after 3~30 minutes
Discharging obtains heat-proof macromolecule polymer, is then dried for standby heat-proof macromolecule polymer.
2. middle enhancement layer pipe is cleaned up and preheated 5 minutes at 30~60 DEG C, then in middle enhancement layer pipe
Surfaces externally and internally uniformly coat cool down after binding resin it is standby.
3. by middle enhancement layer pipe sleeve on the design attitude of screw extruder, by screw extruder by heat-proof macromolecule
Polymer is squeezed in the endoporus of middle enhancement layer pipe, is cooled down in mould and is made the wall thickness control of inner tube in 0.6~3.5mm, cooling
Semi-finished product body is prepared by more than L progress excision formings afterwards, the internal diameter of the semi-finished product body should meet the d.
4. the semi-finished product in 3. are enclosed on the design attitude of screw extruder, by screw extruder by polyethylene
Squeeze middle enhancement layer pipe it is cylindrical in, cooling down in mould simultaneously makes the wall thickness control of inner tube press institute after 1.2~5.4mm, cooling
State L progress excision formings and prepare finished product body, the external diameter of the finished product body should meet the D.Chilling temperature presses spiral shell in mould
Bar extruder conventional arrangement.
Possess it is above-mentioned 1.~2. under the conditions of prepare box cupling when:
5. by middle enhancement layer pipe sleeve on the design attitude of screw extruder, by screw extruder by heat-proof macromolecule
Polymer is squeezed in the endoporus of middle enhancement layer pipe, is cooled down in mould and is made the wall thickness control of inner tube in 0.6~3.5mm, cooling
Semi-finished product box cupling is prepared by more than L progress excision formings afterwards, the internal diameter of the semi-finished product box cupling should be less than the D.
6. the semi-finished product box cupling in 5. is enclosed on the design attitude of screw extruder, will be poly- by screw extruder
Ethene squeeze middle enhancement layer pipe it is cylindrical in, cooling down in mould simultaneously makes the wall thickness control of inner tube after 1.2~5.4mm, cooling
By >=2L1Carry out excision forming and prepare finished product box cupling.
Actually the preparation process of finished product box cupling is as indicated in finished product body, and only the inside/outside diameter size of finished product box cupling is big
In the inside/outside diameter size of finished product body, other relative dimensions such as inner cone pipe screw thread are carried out in the following manner.
It is L that the finished product body or the finished product box cupling, which are individually placed to prepare both ends on screw thread moulding press,1's
Outer taper pipe thread body or >=2L1Endosiphuncular tube threaded collar joint, it is desirable to body and box cupling are provided with following technical performance:
Long-term hydrostatic strength >=15MPa of body and box cupling;
Tensile strength >=126MPa of body and box cupling and yield strength control at 105~134MPa [25 DEG C];
The heatproof softening point of body and box cupling reaches 150 DEG C;
The density of texture of body and box cupling is controlled in 0.941~1.56g/cm3。
The present invention is in preparation process:Ultrasonic scanning device, rice remeasurement control dress are provided with its each production line
Put, the wall thickness monitoring full-automatic computer control system such as controller, and dynamic control carried out to body and box cupling in preparation process,
To ensure the quality of production of nonmetallic oil pipe.
Claims (3)
1. the nonmetallic oil pipe preparation method that a kind of oil gas field uses, nonmetallic oil pipe includes body and box cupling, the internal diameter of body,
External diameter and length dimension are performed by oil gas field standard used in connection with, and box cupling implements Butt sealing to two bodys, and preparation method makes
Screw extruder, screw thread moulding press are used, it is characterized in that:
Body (1) and box cupling (2) include refractory layer pipe (1.1), middle enhancement layer pipe (1.2) and anticorrosive coat pipe (1.3), resistance to
Thermosphere pipe by molecular weight 150~3,200,000 polyethylene or butadiene be polymerized under rigid catalyst it is heat-resisting
High molecular polymer forms, and middle enhancement layer pipe is by the glass fibre of resistance to mesohigh, enhanced polyester fiber, aramid fiber, polyethylene
Fiber and netted high-tensile steel wires are collectively constituted, and anticorrosive coat pipe is made up of molecular weight in 250~4,200,000 polyethylene;
The refractory layer bore of body is set as d and its anticorrosive coat pipe external diameter is set as D and its length is set as L, and centre is strengthened
The internal diameter of layer pipe is equal to the external diameter of refractory layer pipe, and the external diameter of middle enhancement layer pipe is equal to the internal diameter of anticorrosive coat pipe, in body anti-corrosion
The both ends of layer pipe are L provided with length1Outer cone boss, L1Less than L, each outer cone boss passes through screw thread compression molding
Preparation has outer taper pipe thread;Length >=2L of box cupling1, female cone boss is provided with the refractory layer pipe of box cupling, each inner circle
Cone boss internal diameter is prepared by screw thread compression molding entire body inner cone pipe screw thread, and the nominal bore diameter of inner cone pipe screw thread is equal to outer Taper Pipe
The nominal outside diameter of screw thread, by the outer taper pipe threads of adjacent two bodys of the entire body endosiphuncular tube thread connection of box cupling and with such
Push away;
When preparing body:
1. polyethylene or butadiene and rigid catalyst are placed in high speed agitator, high-speed stirred goes out after 3~30 minutes
Material obtains heat-proof macromolecule polymer, is then dried for standby heat-proof macromolecule polymer;
2. middle enhancement layer pipe is cleaned up and preheated 5 minutes at 30~60 DEG C, then inside and outside middle enhancement layer pipe
Surface uniformly coat cool down after binding resin it is standby;
3. by middle enhancement layer pipe sleeve on the design attitude of screw extruder, heat-proof macromolecule is polymerize by screw extruder
Thing is squeezed in the endoporus of middle enhancement layer pipe, is cooled down in mould and the wall thickness control of inner tube is pressed after 0.6~3.5mm, cooling
Excision forming is carried out more than the L and prepares semi-finished product body, and the internal diameter of the semi-finished product body should meet the d;
4. the semi-finished product in 3. are enclosed on the design attitude of screw extruder, polyethylene is squeezed by screw extruder
Middle enhancement layer pipe it is cylindrical in, cooling down in mould simultaneously makes the wall thickness control of inner tube enter after 1.2~5.4mm, cooling by the L
Row excision forming prepares finished product body, and the external diameter of the finished product body should meet the D;
Possess it is above-mentioned 1.~2. under the conditions of prepare box cupling when:
5. by middle enhancement layer pipe sleeve on the design attitude of screw extruder, heat-proof macromolecule is polymerize by screw extruder
Thing is squeezed in the endoporus of middle enhancement layer pipe, is cooled down in mould and the wall thickness control of inner tube is pressed after 0.6~3.5mm, cooling
Excision forming is carried out more than the L and prepares semi-finished product box cupling, and the internal diameter of the semi-finished product box cupling should be less than the D;
6. the semi-finished product box cupling in 5. is enclosed on the design attitude of screw extruder, by screw extruder by polyethylene
Squeeze middle enhancement layer pipe it is cylindrical in, cool down in mould and make the wall thickness control of inner tube after 1.2~5.4mm, cooling by >=
2L1Carry out excision forming and prepare finished product box cupling;
It is L that the finished product body or the finished product box cupling, which are individually placed to prepare both ends on screw thread moulding press,1Outer Taper Pipe
Screw-thread pipe body or >=2L1Endosiphuncular tube threaded collar joint, it is desirable to body and box cupling are provided with following technical performance:
Long-term hydrostatic strength >=15MPa of body and box cupling;
Tensile strength >=126MPa of body and box cupling and yield strength control at 105~134MPa [25 DEG C];
The heatproof softening point of body and box cupling reaches 150 DEG C;
The density of texture of body and box cupling is controlled in 0.941~1.56g/cm3。
2. the nonmetallic oil pipe preparation method that a kind of oil gas field uses according to claim 1, it is characterized in that:Rigid catalyst
It is the rigid polymer with binding function group and hole.
3. the nonmetallic oil pipe preparation method that a kind of oil gas field uses according to claim 1, it is characterized in that:Netted high intensity
Steel wire is the Wrapping formed network structure of steel wire left-and-right spiral, or the helicoidal structure of steel wire winding shaping.