CN107345054A - A kind of inorganic particulate strengthens PC/PET alloys - Google Patents
A kind of inorganic particulate strengthens PC/PET alloys Download PDFInfo
- Publication number
- CN107345054A CN107345054A CN201710782652.9A CN201710782652A CN107345054A CN 107345054 A CN107345054 A CN 107345054A CN 201710782652 A CN201710782652 A CN 201710782652A CN 107345054 A CN107345054 A CN 107345054A
- Authority
- CN
- China
- Prior art keywords
- pet
- inorganic particulate
- alloys
- raw material
- good
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of inorganic particulate enhancing PC/PET alloys of the present invention, its raw material and raw material weight percentage composition are as follows:PC 40 50%;Inorganic particulate 0.1 1%;Boron nitride 0.1 3%;Lanthana 0.1 3%;Polytetrafluoroethylene (PTFE) 0.1 3%;PET 40 60%.The beneficial effects of the invention are as follows, compared with prior art, inorganic particulate provided by the invention strengthens PC/PET alloys, not only with PC and PET each the advantages of, it compensate for the defects of one-component performance, but also having the characteristics that intensity is high, rigidity is good, heat-and corrosion-resistant function admirable, good weatherability, electrical property and processing characteristics are excellent, its cost is also low, thus has good application prospect in fields such as auto industry, electronic apparatus, component of machine, buildings.
Description
Technical field
The present invention relates to technical field of polymer materials, specifically a kind of inorganic particulate enhancing PC/PET alloys.
Background technology
Makrolon (PC) is the engineering plastics of excellent performance, have impact strength height, creep resistant, good stability of the dimension,
The advantages that heat-resisting, transparent, dielectric properties are excellent, but PC melt viscosity is big, poor fluidity, poor solvent resistance, particularly pair
The poor resistance of organic solvent and alkaline medicine, stress cracking and swelling easily occur under solvent and alkaline environment, and to lacking
Mouth is sensitive.Polyethylene terephthalate (PET) is a kind of translucent crystalline thermoplastic polyester, has high-fire resistance, tough
Property, fatigue durability, self-lubricating, low-friction coefficient, weatherability still keep various physical property (including electrical property) in wet environment,
Heat-proof water, bases, acids, oils, it can crystallize rapidly under low temperature, good forming ability, but PET notch impact strength is low, and
Easily corroded by halogenated hydrocarbon, hydrolytic resistance is poor, and molding shrinkage is big.PC and PET are blended, both with PC rigidity and heat resistance, again
Solvent resistance with PET.However, because PET is crystalline polymer, PC is non-crystalline polymer, and PC/PET alloys belong to allusion quotation
The amorphous of type/crystallization co-mixing system, and the PC/PET alloys of in the market also exist intensity it is not good enough and both blending influence mechanics
The problem of performance etc..
The content of the invention
To solve above-mentioned existing technical problem, the present invention uses following scheme:
A kind of inorganic particulate strengthens PC/PET alloys, and its raw material and raw material weight percentage composition are as follows:
PC40-50%;
Inorganic particulate 0.1-1%;
Boron nitride 0.1-3%;
Lanthana 0.1-3%;
Polytetrafluoroethylene (PTFE) 0.1-3%;
PET 40-60%.
The invention has the advantages that compared with prior art, inorganic particulate provided by the invention strengthens PC/PET alloys,
Not only with PC and PET each the advantages of, compensate for the defects of one-component performance, but also with intensity is high, rigidity
The features such as good, heat-and corrosion-resistant function admirable, good weatherability, excellent electrical property and processing characteristics, its cost is also low, thus in vapour
The fields such as turner industry, electronic apparatus, component of machine, building have good application prospect.
Embodiment
The present invention is described in detail below in conjunction with specific embodiment, herein illustrative examples and explanation of the invention
For explaining the present invention, but it is not as a limitation of the invention.
Embodiment
A kind of inorganic particulate enhancing PC/PET alloys of the present invention, its raw material and raw material weight percentage composition are as follows:
PC45%, inorganic particulate 0.5%, boron nitride 0.5%, lanthana 1%, polytetrafluoroethylene (PTFE) 2%, PET 51%.
The above-described embodiments merely illustrate the principles and effects of the present invention, not for the limitation present invention.It is any ripe
Know the personage of this technology all can carry out modifications and changes under the spirit and scope without prejudice to the present invention to above-described embodiment.Cause
This, those of ordinary skill in the art is complete without departing from disclosed spirit and institute under technological thought such as
Into all equivalent modifications or change, should by the present invention claim be covered.
Claims (1)
1. a kind of inorganic particulate strengthens PC/PET alloys, it is characterised in that its raw material and raw material weight percentage composition are as follows:
PC 40-50%;
Inorganic particulate 0.1-1%;
Boron nitride 0.1-3%;
Lanthana 0.1-3%;
Polytetrafluoroethylene (PTFE) 0.1-3%;
PET 40-60%.