CN107322719A - A kind of wicker products surface hydrophobicity insect-prevention treatment method - Google Patents
A kind of wicker products surface hydrophobicity insect-prevention treatment method Download PDFInfo
- Publication number
- CN107322719A CN107322719A CN201710571780.9A CN201710571780A CN107322719A CN 107322719 A CN107322719 A CN 107322719A CN 201710571780 A CN201710571780 A CN 201710571780A CN 107322719 A CN107322719 A CN 107322719A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- wicker products
- insect
- wicker
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wicker products surface hydrophobicity insect-prevention treatment method, comprise the following steps：(1) by just woven wicker products, it is put into pretreatment fluid and soaks 2 hours, cleaned after taking-up with clear water, then with 50 60 degrees Celsius of hot blast drying, untill water content is less than 10%；(2) wicker products after air-drying is subjected to surface polishing, removes flash removed, be then coated with subbing, surface coating material is coated again after subbing is parched naturally.The present invention is soaked by pretreatment fluid to wicker products, on the one hand emollescence is played, on the other hand, pretreatment fluid can be penetrated into inside wicker, make wicker products that there is the characteristic of insect prevention antibacterial, further by the coating of subbing and surface coating material, make wicker products surface hydrophobic good, and scratch-resistant.
Description
Technical field
The present invention relates to technical field of agricultural product process, more particularly to a kind of wicker products surface hydrophobicity insect-prevention treatment side
Method.
Background technology
Wicker plaiting article is one of folks of china traditional handicraft product.People are intended only as common daily utility in ancient times, directly
Decades just gradually rise after to 20th century, also the project exported goods and earned foreign currency as selected areas of China gradually.The whole nation has three big
Wicker plaiting article production base, Hubei, Shandong, Anhui (Henan also abounds with wicker plaiting article in addition).
Wicker soft pliable, thickness are well-balanced, color and luster is graceful, by novel design, can be woven into it is various it is simple it is natural,
Handsome in appearance, Portable durable practical art product.Its product includes：Crate (bag), meal basket, food basket (circle, oval), bamboo strainer,
Needlework shallow basket made of wicker or thin bamboo strips, kang mat, reed matting etc..As industry is continued to develop, product is constantly brought forth new ideas, and has more Nover practicals willow attractive in appearance
Product is presented in face of client.
On June 7th, 2008, wicker plaiting article is included in second batch List of National Intangible Cultural Heritage through State Council approved.
Wicker products is easily rotted mouldy, while for a long time not due to its own material feature if often being drenched
Using easily infested.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of wicker products surface hydrophobicity insect-prevention treatment method.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of wicker products surface hydrophobicity insect-prevention treatment method, comprises the following steps：
(1) by just woven wicker products, it is put into pretreatment fluid and soaks 2 hours, is cleaned after taking-up with clear water, then
With 50-60 degrees Celsius of hot blast drying, untill water content is less than 10%；
(2) wicker products after air-drying is subjected to surface polishing, removes flash removed, be then coated with subbing, treat that bottom is applied
Material nature coats surface coating material again after parching；
The pretreatment fluid is made up of the raw material of following parts by weight：250-300 parts of distilled water, 5-8 parts of sodium chloride, ethanol
20-25 parts, 5-10 parts of diethofencarb, 8-15 parts of Siberian cocklebur extract, 5-8 parts of citric acid, 12-15 parts of oxalic acid, 8-10 parts of ammonium acid fluoride,
10-15 parts of carbendazim, 10-12 parts of hundred worms spirit, 30-35 parts of glycerine, 8-10 parts of soybean oil, 25-30 parts of alcohol ether glucoside, polyoxyethylene
10-15 parts of ether, 4-6 parts of hydrogen chloride, 5-8 parts of amphoteric surfactant；
The subbing includes the constituent of following parts by weight：Nanomaterial grade organosilicon-modified styrene-acrylic olefin(e) acid emulsion 10-18
Part, 8-15 parts of polyurethane-modified acrylic acid emulsion, 800 18-25 parts of mesh calcium carbonate, 1500 3-5 parts of mesh talcum powder, rutile titanium white
13-18 parts of powder, 8-10 parts of calcined kaolin, 1-2 parts of grinding auxiliary agent, 4-6 parts of coalescents, 0.1-0.3 parts of nertralizer, defoamer
0.1-0.3 parts, 0.1-0.3 parts of organosilicon wetting agent, 0.1-0.3 parts of polyurethane levelling agent, 0.2-0.5 parts of thickener, bactericide
0.1-0.2 parts, 15-20 parts of deionized water；
The surface coating material includes the constituent of following parts by weight：40-50 parts of HCPE, organic solvent
10-15 parts, 3-5 parts of corrosion-inhibiting pigment, 2-3 parts of defoamer, 2-3 parts of surfactant, 2-3 parts of dimethylbenzene, 3-5 parts of Ludox,
3-5 parts of curing agent, 5-10 parts of chlorinated paraffin, 10-15 parts of deionized water, 5-10 parts of auxiliary agent, 5-10 parts of alumina powder, lead oxide
5-10 parts of powder, 2-5 parts of SiO 2 powder, 2-5 parts of titania powder.
Preferably, the pretreatment fluid is made up of the raw material of following parts by weight：300 parts of distilled water, 6 parts of sodium chloride, second
23 parts of alcohol, 8 parts of diethofencarb, 12 parts of Siberian cocklebur extract, 6 parts of citric acid, 14 parts of oxalic acid, 9 parts of ammonium acid fluoride, 12 parts of carbendazim, hundred
11 parts of worm spirit, 32 parts of glycerine, 9 parts of soybean oil, 28 parts of alcohol ether glucoside, 12 parts of APEO, 5 parts of hydrogen chloride, amphoteric surface lives
6 parts of agent of property.
Preferably, the subbing includes the constituent of following parts by weight：Nanomaterial grade organosilicon-modified styrene-acrylic olefin(e) acid breast
15 parts of liquid, 10 parts of polyurethane-modified acrylic acid emulsion, 800 20 parts of mesh calcium carbonate, 1,500 5 parts of mesh talcum powder, rutile titanium white powder
15 parts, 8 parts of calcined kaolin, 2 parts of grinding auxiliary agent, 6 parts of coalescents, 0.1 part of nertralizer, 0.2 part of defoamer, organosilicon wetting
0.2 part of agent, 0.3 part of polyurethane levelling agent, 0.4 part of thickener, 0.1 part of bactericide, 17.7 parts of deionized water.
Preferably, the surface coating material includes the constituent of following parts by weight：42 parts of HCPE, You Jirong
15 parts of agent, 5 parts of corrosion-inhibiting pigment, 3 parts of defoamer, 2 parts of surfactant, 2 parts of dimethylbenzene, 3 parts of Ludox, 4 parts of curing agent, chlorine
8 parts of fossil waxes, 15 parts of deionized water, 8 parts of auxiliary agent, 5 parts of alumina powder, 5 parts of lead oxide powder, 3 parts of SiO 2 powder, two
3 parts of titanium dioxide powder.
Beneficial effects of the present invention：The present invention is soaked by pretreatment fluid to wicker products, on the one hand plays softening
Effect, on the other hand, pretreatment fluid can penetrate into inside wicker, wicker products is had the characteristic of insect prevention antibacterial, further pass through
The coating of subbing and surface coating material, makes wicker products surface hydrophobic good, and scratch-resistant, and subbing and surface coating material are adopted
With the formula of science, by force, closure is good for penetration, and film densification is in neat formation, does not ftracture, and swollen, good waterproof performance is not played, and adhesive force is strong,
Extreme hardness, scratch-resistant.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
A kind of wicker products surface hydrophobicity insect-prevention treatment method, comprises the following steps：
(1) by just woven wicker products, it is put into pretreatment fluid and soaks 2 hours, is cleaned after taking-up with clear water, then
With 50 degrees Celsius of hot blast drying, untill water content is less than 10%；
(2) wicker products after air-drying is subjected to surface polishing, removes flash removed, be then coated with subbing, treat that bottom is applied
Material nature coats surface coating material again after parching；
Wherein, the pretreatment fluid is made up of the raw material of following parts by weight：300 parts of distilled water, 6 parts of sodium chloride, ethanol
23 parts, 8 parts of diethofencarb, 12 parts of Siberian cocklebur extract, 6 parts of citric acid, 14 parts of oxalic acid, 9 parts of ammonium acid fluoride, 12 parts of carbendazim, hundred worms
11 parts of spirit, 32 parts of glycerine, 9 parts of soybean oil, 28 parts of alcohol ether glucoside, 12 parts of APEO, 5 parts of hydrogen chloride, amophoteric surface active
6 parts of agent；
Wherein, the subbing includes the constituent of following parts by weight：Nanomaterial grade organosilicon-modified styrene-acrylic olefin(e) acid emulsion
15 parts, 10 parts of polyurethane-modified acrylic acid emulsion, 800 20 parts of mesh calcium carbonate, 1,500 5 parts of mesh talcum powder, rutile titanium white powder 15
Part, 8 parts of calcined kaolin, 2 parts of grinding auxiliary agent, 6 parts of coalescents, 0.1 part of nertralizer, 0.2 part of defoamer, organosilicon wetting agent
0.2 part, 0.3 part of polyurethane levelling agent, 0.4 part of thickener, 0.1 part of bactericide, 17.7 parts of deionized water；
Wherein, the surface coating material includes the constituent of following parts by weight：42 parts of HCPE, organic solvent
15 parts, 5 parts of corrosion-inhibiting pigment, 3 parts of defoamer, 2 parts of surfactant, 2 parts of dimethylbenzene, 3 parts of Ludox, 4 parts of curing agent, chlorination
8 parts of paraffin, 15 parts of deionized water, 8 parts of auxiliary agent, 5 parts of alumina powder, 5 parts of lead oxide powder, 3 parts of SiO 2 powder, dioxy
Change 3 parts of titanium powder.
Embodiment 2
A kind of wicker products surface hydrophobicity insect-prevention treatment method, comprises the following steps：
(1) by just woven wicker products, it is put into pretreatment fluid and soaks 2 hours, is cleaned after taking-up with clear water, then
With 50 degrees Celsius of hot blast drying, untill water content is less than 10%；
(2) wicker products after air-drying is subjected to surface polishing, removes flash removed, be then coated with subbing, treat that bottom is applied
Material nature coats surface coating material again after parching；
Wherein, the pretreatment fluid is made up of the raw material of following parts by weight：250 parts of distilled water, 5 parts of sodium chloride, ethanol
25 parts, 7 parts of diethofencarb, 11 parts of Siberian cocklebur extract, 7 parts of citric acid, 15 parts of oxalic acid, 9 parts of ammonium acid fluoride, 13 parts of carbendazim, hundred worms
12 parts of spirit, 33 parts of glycerine, 9 parts of soybean oil, 26 parts of alcohol ether glucoside, 12 parts of APEO, 5 parts of hydrogen chloride, amophoteric surface active
6 parts of agent；
Wherein, the subbing includes the constituent of following parts by weight：Nanomaterial grade organosilicon-modified styrene-acrylic olefin(e) acid emulsion
16 parts, 14 parts of polyurethane-modified acrylic acid emulsion, 800 22 parts of mesh calcium carbonate, 1,500 4 parts of mesh talcum powder, rutile titanium white powder 14
Part, 8 parts of calcined kaolin, 1 part of grinding auxiliary agent, 5 parts of coalescents, 0.1 part of nertralizer, 0.3 part of defoamer, organosilicon wetting agent
0.3 part, 0.2 part of polyurethane levelling agent, 0.2 part of thickener, 0.15 part of bactericide, 18 parts of deionized water；
Wherein, the surface coating material includes the constituent of following parts by weight：48 parts of HCPE, organic solvent
10 parts, 5 parts of corrosion-inhibiting pigment, 2 parts of defoamer, 3 parts of surfactant, 2.5 parts of dimethylbenzene, 3 parts of Ludox, 4 parts of curing agent, chlorine
8 parts of fossil waxes, 11 parts of deionized water, 8 parts of auxiliary agent, 6 parts of alumina powder, 6 parts of lead oxide powder, 3 parts of SiO 2 powder, two
3 parts of titanium dioxide powder.
The embodiment of the present invention is contrasted as follows compared with common wicker products surface treatment method：(10 points of full marks)
The present invention is soaked by pretreatment fluid to wicker products, on the one hand plays emollescence, on the other hand, pre- place
Reason liquid can be penetrated into inside wicker, wicker products is had the characteristic of insect prevention antibacterial, further passed through subbing and surface coating material
Coating, make wicker products surface hydrophobic good, and scratch-resistant, subbing and surface coating material use the formula of science, infiltration
Power is strong, and closure is good, and film densification is in neat formation, does not ftracture, and swollen, good waterproof performance is not played, and adhesive force is strong, extreme hardness, scratch-resistant.
The general principle and principal character of the present invention has been shown and described above.It should be understood by those skilled in the art that,
The present invention is not limited to the above embodiments, merely illustrating the principles of the invention described in above-described embodiment and specification,
Without departing from the spirit and scope, various changes and modifications of the present invention are possible, and these changes and improvements all fall
Enter in scope of the claimed invention.The scope of the present invention is defined by the appended claims and its equivalents.
Claims (4)
1. a kind of wicker products surface hydrophobicity insect-prevention treatment method, it is characterised in that comprise the following steps：
(1) by just woven wicker products, it is put into pretreatment fluid and soaks 2 hours, is cleaned after taking-up with clear water, Ran Houyong
50-60 degrees Celsius of hot blast drying, untill water content is less than 10%；
(2) wicker products after air-drying is subjected to surface polishing, removes flash removed, be then coated with subbing, treat subbing certainly
Surface coating material is coated again after so parching；
The pretreatment fluid is made up of the raw material of following parts by weight：250-300 parts of distilled water, 5-8 parts of sodium chloride, ethanol 20-
25 parts, 5-10 parts of diethofencarb, 8-15 parts of Siberian cocklebur extract, 5-8 parts of citric acid, 12-15 parts of oxalic acid, 8-10 parts of ammonium acid fluoride is more
10-15 parts of bacterium spirit, 10-12 parts of hundred worms spirit, 30-35 parts of glycerine, 8-10 parts of soybean oil, 25-30 parts of alcohol ether glucoside, APEO
10-15 parts, 4-6 parts of hydrogen chloride, 5-8 parts of amphoteric surfactant；
The subbing includes the constituent of following parts by weight：10-18 parts of nanomaterial grade organosilicon-modified styrene-acrylic olefin(e) acid emulsion, gathers
8-15 parts of urethane modified acrylate emulsion, 800 18-25 parts of mesh calcium carbonate, 1500 3-5 parts of mesh talcum powder, rutile titanium white powder 13-
18 parts, 8-10 parts of calcined kaolin, 1-2 parts of grinding auxiliary agent, 4-6 parts of coalescents, 0.1-0.3 parts of nertralizer, defoamer 0.1-
0.3 part, 0.1-0.3 parts of organosilicon wetting agent, 0.1-0.3 parts of polyurethane levelling agent, 0.2-0.5 parts of thickener, bactericide 0.1-
0.2 part, 15-20 parts of deionized water；
The surface coating material includes the constituent of following parts by weight：40-50 parts of HCPE, organic solvent 10-15
Part, 3-5 parts of corrosion-inhibiting pigment, 2-3 parts of defoamer, 2-3 parts of surfactant, 2-3 parts of dimethylbenzene, 3-5 parts of Ludox, curing agent
3-5 parts, 5-10 parts of chlorinated paraffin, 10-15 parts of deionized water, 5-10 parts of auxiliary agent, 5-10 parts of alumina powder, lead oxide powder 5-
10 parts, 2-5 parts of SiO 2 powder, 2-5 parts of titania powder.
2. a kind of wicker products surface hydrophobicity insect-prevention treatment method according to claim 1, it is characterised in that the pre- place
Reason liquid is made up of the raw material of following parts by weight：300 parts of distilled water, 6 parts of sodium chloride, 23 parts of ethanol, 8 parts of diethofencarb, Siberian cocklebur carries
Take 12 parts of thing, 6 parts of citric acid, 14 parts of oxalic acid, 9 parts of ammonium acid fluoride, 12 parts of carbendazim, 11 parts of hundred worms spirit, 32 parts of glycerine, soybean oil
9 parts, 28 parts of alcohol ether glucoside, 12 parts of APEO, 5 parts of hydrogen chloride, 6 parts of amphoteric surfactant.
3. a kind of wicker products surface hydrophobicity insect-prevention treatment method according to claim 1, it is characterised in that the bottom
Coating includes the constituent of following parts by weight：15 parts of nanomaterial grade organosilicon-modified styrene-acrylic olefin(e) acid emulsion, polyurethane-modified acrylic acid
10 parts of emulsion, 800 20 parts of mesh calcium carbonate, 1,500 5 parts of mesh talcum powder, 15 parts of rutile titanium white powder, 8 parts of calcined kaolin, polishing
2 parts of auxiliary agent, 6 parts of coalescents, 0.1 part of nertralizer, 0.2 part of defoamer, 0.2 part of organosilicon wetting agent, polyurethane levelling agent 0.3
Part, 0.4 part of thickener, 0.1 part of bactericide, 17.7 parts of deionized water.
4. a kind of wicker products surface hydrophobicity insect-prevention treatment method according to claim 1, it is characterised in that the top layer
Coating includes the constituent of following parts by weight：42 parts of HCPE, 15 parts of organic solvent, 5 parts of corrosion-inhibiting pigment disappears
3 parts of infusion, 2 parts of surfactant, 2 parts of dimethylbenzene, 3 parts of Ludox, 4 parts of curing agent, 8 parts of chlorinated paraffin, 15 parts of deionized water,
8 parts of auxiliary agent, 5 parts of alumina powder, 5 parts of lead oxide powder, 3 parts of SiO 2 powder, 3 parts of titania powder.