CN107313283A - A kind of preparation method of wettable water paper handkerchief - Google Patents
A kind of preparation method of wettable water paper handkerchief Download PDFInfo
- Publication number
- CN107313283A CN107313283A CN201610268627.4A CN201610268627A CN107313283A CN 107313283 A CN107313283 A CN 107313283A CN 201610268627 A CN201610268627 A CN 201610268627A CN 107313283 A CN107313283 A CN 107313283A
- Authority
- CN
- China
- Prior art keywords
- pulp
- concentration
- wood pulp
- paper handkerchief
- wet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation method of wettable water paper handkerchief, add water makes the concentration of softwood pulp and hardwood pulp be adjusted to 5.0 7.0wt% respectively, afterwards size degradation 8 15 minutes;The concentration of softwood pulp is adjusted to 4.0 5.0wt%, fibre cutting and wire-dividing broom purification are carried out in fiberizer;The concentration of adjustment hardwood pulp of adding water carries out fiber to 4.0 5.0wt%, in fluffer and discongested;50 60% softwood pulp and 50 40% hardwood pulp are mixed, adjustment concentration to 3.0 4.0wt%, further cut-out and wire-dividing broom purification are done by fiberizer;Addition wet strength agent and softening agent in mixing wood pulp, adjustment concentration to 2.9 3.1wt%;Mixing wood pulp is diluted to concentration for 0.2 0.25wt% through fan pump, into paper machine, by shaping, squeezes and dry, product is finally made.Paper handkerchief prepared by the present invention wipes the sweat in use, wet tissue can work as after paper scrap, wet water and washcloth is used by not crushing not stay wiping water, while the smoothness raising of the feel of paper handkerchief, using as snug as a bug in a rug.
Description
Technical field
The present invention relates to a kind of preparation method of paper handkerchief, more particularly, to a kind of making side of wettable water paper handkerchief
Method.
Background technology
Common tissue in the market, can only do after use, wet water just very as face tissue, tissue etc.
It is easily broken and can not be continuing with, this routine use given people brings very big inconvenience.Chinese patent CN
2592097Y discloses Multifunctional wet paper napkin, there is one layer of wet-strength paper piece or the water suction scraps of paper, wet-strength paper piece or suction
The upper and lower surface of the water scraps of paper has respectively overlayed at least one layer of wet water paper, constitutes the layer structure of three layers or multilayer build-up,
Infiltration is adsorbed with the wetting agent that plurality of raw materials is formulated on wet-strength paper piece or the water suction scraps of paper.But the paper handkerchief is logical
Cross and use sandwich construction realization can be with wet water, either cost of material or manufacture craft cost all significantly increase
Plus.
The content of the invention
The purpose of the present invention is exactly, in order to overcome the defect that above-mentioned prior art is present, and to provide a kind of wettable water
There is excellent smoothness paper handkerchief preparation method simultaneously.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of preparation method of wettable water paper handkerchief, comprises the following steps:
(1) softwood pulp and hardwood pulp are put into long fine pulper with short fine pulper, adding water respectively
It is 5.0-7.0wt% to adjust wood pulp concentration, and size degradation is pumped into stock tank and short fibre before long fibre is kowtowed and kowtowed respectively after 8-15 minutes
Preceding stock tank;
(2) concentration of softwood pulp, to 4.0-5.0wt%, puts into fiberizer in stock tank before the long fibre of adjustment that adds water is kowtowed
Middle progress fibre cutting and wire-dividing broom purification, are then fed into long fibre and kowtow in rear stock tank;
(3) concentration of hardwood pulp, to 4.0-5.0wt%, puts into fluffer in stock tank before the short fibre of adjustment that adds water is kowtowed
In, carry out fiber and discongest, be then fed into short fibre and kowtow in rear stock tank;
(4) hardwood pulp of 50-60% softwood pulp and 50-40% is pumped into blending chest by weight, plus
Water adjusts concentration to 3.0-4.0wt%, and further cut-out is done to fiber through fiberizer and wire-dividing broom purification is handled, so
Afterwards will mixing wood pulp feeding machine chest;
(5) machine chest mixing wood pulp in addition 25-30kg/t wet strength agent and 0.4-0.6kg/t it is soft
Soft dose, adjustment wood pulp concentration to 2.9-3.1wt%;
(6) mixing wood pulp is diluted to concentration for 0.2-0.25wt% through fan pump, into paper machine, by into
Shape, squeezing and drying, are finally made product.
Described softwood pulp is North America softwood pulp, weight in wet base 18-22g, 12-16 ° of SR of beating degree.Described
Hardwood pulp is Brazilian hardwood pulp, weight in wet base 3-4g, 14-17 ° of SR of beating degree.
The energy consumption of fiberizer controls wooden after 90-100kwh/t, fibre cutting and wire-dividing broom purification in step (2)
The weight in wet base 13-16g, 20-25 ° of SR of beating degree of wood pulp are mixed in slurry.
The inter-lobe clearance of fluffer is controlled in 0.25-2.0mm in step (3), discongests and wood is mixed in rear wood pulp
The weight in wet base 2.7-3.2g of slurry, 15-18 ° of SR of beating degree.
The energy consumption of fiberizer controls the wood pulp after 30-35kwh/t, fibre cutting and wire-dividing broom purification in step (4)
The weight in wet base 7-10g, 26-29 ° of SR of beating degree of middle mixing wood pulp.
Described wet strength agent is the reinforced wet strength agents of new wide raw PPE, permanent health wet strength agent FD-2, Suo Lisi are wet
Strong agent 852 etc..Described softening agent is Suo Lisi softening agents TQ1003 etc..
Compared with prior art, the present invention is as a result of long fine as raw material at high proportion, in step (4)
Softwood pulp show that using long fine at high proportion, common facial tissue only needs 28-35%'s long fine., defibrination
Cause interfibrous bond strength increase after machine defibrination so that the obdurability increase of paper handkerchief, fiberizer mainly leads to
Control defibrination power, refining concentration, inlet and outlet pressure etc. is crossed to control defibrination degree.By the machinery of defibrination
Effect, fiber finer cell wall produces displacement and deformation, and P layers and S1 layer segments are abolished, and fiber is cut off, then
Fiber quickly absorbs water swollen, is conducive to the fibrillating of fiber, fiber surface sub-wire and isolates many fine
Fiber, fiber two ends brooming, dissociate many hydroxyls, the specific surface area increase of fiber, under interlayer cohesive force
Drop, fiber becomes soft plastic, so as to effectively increase interfibrous contact area, improves paper strength.
Fluffer mainly rotates the machine that the waterpower to be formed carries out shear action and increment to slurry by the high speed of rotor
Tool is acted on, and is discongested hardwood pulp, the length of fiber does not change substantially.Long fibre is short as skeleton
Fibre, by secondary pulping is passed through again after the fibre mixing of higher proportion length, makes the further fibrillating of fiber as filling,
Interfibrous adhesion is improved, promotes mutually in length and breadth to interweave between fiber, finally manufactures paper with pulp into certain intensity
With the product of flexibility.
Wet strength agent and softening agent are added in preparation process, substantial amounts of wet strength agent can increase the mechanical strength of paper,
Protect the combination between fiber and fiber, prevent swollen and destruction, cation wet strength agent can with it is negatively charged
Fiber attracts each other and kept, and by heating or can be cured after certain time and forms chemical network structure, makes paper
Water swollen can be resisted and there is very high wet strength.Softening agent can improve the flexibility of paper, general to have length
Chain fatty acidic group or containing olefines solvent composition, can strengthen lubricating and reduce interfibrous friction factor, from
And improve the flexibility of paper.Ton paper adds 25-30kg wet strength agents and 0.4-0.6kg softening agent and can not destroyed
Preferably high wet strength and flexibility are obtained under conditions of system balancing so that paper keeps the same of the soft feel of silk
When, has excellent wettable aqueous, and paper handkerchief can equally be used after wet water as wet tissue, does and uses, wet uses all ten
Point convenient, so as to improve, paper feel is smoothness, improves the intensity of paper, add it is wettable aqueous,
Meet people dry with soft and smooth, take good care of tender and lovely skin;It is wet with tough, wipe water and wipe the sweat and is difficult to stay paper scrap, wet water
The requirement of wet tissue or washcloth can also be worked as afterwards.
Embodiment
With reference to specific embodiment, the present invention is described in detail.
Embodiment 1
A kind of preparation method of wettable water paper handkerchief, is prepared using following steps:
(1) by 1610 kilograms of North America softwood pulp, Brazilian 1750 kilograms of hardwood pulp put into respectively it is long,
In short fine pulper, North America softwood pulp, weight in wet base 18g, 12 ° of SR of beating degree, Brazilian hardwood pulp, weight in wet base
3g, 14 ° of SR of beating degree.The adjustment concentration that adds water is to carry out size degradation after 5.5wt%, beating time 10 minutes,
It is pumped into long and short fibre respectively afterwards and kowtows preceding stock tank;
(2) concentration of stock tank Middle and North America softwood pulp before long fibre is kowtowed is adjusted to 4.5wt%, into fiberizer,
It is 95kwh/t to control refining energy consumption, fibre cutting and wire-dividing broom purification is carried out, after fibre cutting and wire-dividing broom purification
Weight in wet base 13g, 20 ° of SR of beating degree of wood pulp are mixed in wood pulp, rear stock tank are kowtowed into long fibre afterwards;
(3) concentration of Brazilian hardwood pulp in stock tank before short fibre is kowtowed is adjusted to 4.5wt%, by fluffer,
The inter-lobe clearance for controlling fluffer is 1.0mm, carries out fiber and discongests, discongests and the wet of wood pulp is mixed in rear wood pulp
Weight 2.7g, 15 ° of SR of beating degree, kowtow rear stock tank into short fibre afterwards;
(4) mixed in the ratio of North America softwood pulp 55% and Brazilian hardwood pulp 45%, be pumped into mixing slurry
Pond, the concentration for the adjustment mixing wood pulp that adds water is done further cut-out to fiber by fiberizer and divided to 3.5wt%
Silk brooming processing, mixes weight in wet base 7g, 26 ° of SR of beating degree of wood pulp in wood pulp after fibre cutting and wire-dividing broom purification,
It is 30kwh/t to control refining energy consumption, afterwards into machine chest;
(5) the 28kg/t new wide raw reinforced wet strength agents of PPE are added in the mixing wood pulp that machine chest comes out
And 0.5kg/t Suo Lisi softening agent TQ1003, adjustment concentration to 3.0wt%;
(6) mixing wood pulp is diluted to concentration for 0.23wt% through fan pump, into paper machine, by shaping,
After squeezing and drying, product is finally made.
Embodiment 2
A kind of preparation method of wettable water paper handkerchief, is prepared using following steps:
(1) 1500 kilograms of North America softwood pulps and 1500 kilograms of Brazilian hardwood pulps are put into long fibre respectively
In pulper and short fine pulper, North America softwood pulp, weight in wet base 20g, 13 ° of SR of beating degree, Brazilian leaf wood
Slurry, weight in wet base 3g, 15 ° of SR of beating degree.Adding water makes the concentration of wood pulp be adjusted to 5.0wt%, afterwards size degradation 8
Minute, stock tank and short fibre before long fibre is kowtowed then are pumped into respectively kowtows preceding stock tank;
(2) concentration of stock tank Middle and North America softwood pulp is put into afterwards to 4.0wt% before the long fibre of adjustment that adds water is kowtowed
In first fiberizer, fibre cutting and wire-dividing broom purification are carried out, is mixed after fibre cutting and wire-dividing broom purification in wood pulp
The weight in wet base 14g of wood pulp, 22 ° of SR of beating degree, is then fed into long fibre and kowtows in rear stock tank, the energy of the first fiberizer
Consumption control is in 90kwh/t;
(3) concentration of Brazilian hardwood pulp, to 4.0wt%, is put into afterwards in stock tank before the short fibre of adjustment that adds water is kowtowed
In fluffer, carry out fiber and discongest, discongest weight in wet base 2.8g, 16 ° of SR of beating degree that wood pulp is mixed in rear wood pulp,
It is then fed into short fibre to kowtow in rear stock tank, the inter-lobe clearance of fluffer is controlled in 0.25mm;
(4) 57% North America softwood pulp and 43% Brazilian hardwood pulp are pumped into blending chest, added water
Concentration is adjusted to 3.0wt%, fiber is done at further cut-out and wire-dividing broom purification by the second fiberizer afterwards
Reason, mixes weight in wet base 8g, 27 ° of SR of beating degree of wood pulp in wood pulp after fibre cutting and wire-dividing broom purification, then will
Wood pulp feeding machine chest is mixed, the energy consumption of the second fiberizer is controlled in 30kwh/t;
(5) 25kg/t permanent health wet strength agent FD-2 and 0.4kg/t is added in the mixing wood pulp of machine chest
Suo Lisi softening agent TQ1003, adjustment concentration is to 2.9wt%.
(6) mixing wood pulp is diluted to concentration for 0.2wt% through fan pump, into paper machine, by shaping,
Squeeze and dry, product is finally made.
Embodiment 3
A kind of preparation method of wettable water paper handkerchief, is prepared using following steps:
(1) 1400 kilograms of North America softwood pulps and 1600 kilograms of Brazilian hardwood pulps are put into long fibre respectively
In pulper and short fine pulper, North America softwood pulp, weight in wet base 21g, 15 ° of SR of beating degree, Brazilian leaf wood
Slurry, weight in wet base 4g, 16 ° of SR of beating degree.Adding water makes the concentration of wood pulp be adjusted to 6.0wt%, afterwards size degradation 12
Minute, stock tank and short fibre before long fibre is kowtowed then are pumped into respectively kowtows preceding stock tank;
(2) concentration of stock tank Middle and North America softwood pulp is put into afterwards to 4.5wt% before the long fibre of adjustment that adds water is kowtowed
In first fiberizer, fibre cutting and wire-dividing broom purification are carried out, is mixed after fibre cutting and wire-dividing broom purification in wood pulp
The weight in wet base 15g of wood pulp, 24 ° of SR of beating degree, is then fed into long fibre and kowtows in rear stock tank, the energy of the first fiberizer
Consumption control is in 95kwh/t;
(3) concentration of Brazilian hardwood pulp, to 4.5wt%, is put into afterwards in stock tank before the short fibre of adjustment that adds water is kowtowed
In fluffer, carry out fiber and discongest, discongest weight in wet base 3.2g, 17 ° of SR of beating degree that wood pulp is mixed in rear wood pulp,
It is then fed into short fibre to kowtow in rear stock tank, the inter-lobe clearance of fluffer is controlled in 1.0mm;
(4) 55% North America softwood pulp and 45% Brazilian hardwood pulp are pumped into blending chest, added water
Concentration is adjusted to 3.5wt%, fiber is done at further cut-out and wire-dividing broom purification by the second fiberizer afterwards
Reason, mixes weight in wet base 9g, 28 ° of SR of beating degree of wood pulp in wood pulp after fibre cutting and wire-dividing broom purification, then will
Wood pulp feeding machine chest is mixed, the energy consumption of the second fiberizer is controlled in 32.5kwh/t;
(5) 27.5kg/t Suo Lisi wet strength agents 852 and 0.5kg/t is added in the mixing wood pulp of machine chest
Suo Lisi softening agent TQ1003, adjustment concentration is to 3.0wt%.
(6) mixing wood pulp is diluted to concentration for 0.22wt% through fan pump, into paper machine, by shaping,
Squeeze and dry, product is finally made.
Embodiment 4
A kind of preparation method of wettable water paper handkerchief, is prepared using following steps:
(1) 1600 kilograms of North America softwood pulps and 1800 kilograms of Brazilian hardwood pulps are put into long fibre respectively
In pulper and short fine pulper, North America softwood pulp, weight in wet base 22g, 16 ° of SR of beating degree, Brazilian leaf wood
Slurry, weight in wet base 4g, 17 ° of SR of beating degree.Adding water makes the concentration of wood pulp be adjusted to 7.0wt%, afterwards size degradation 15
Minute, stock tank and short fibre before long fibre is kowtowed then are pumped into respectively kowtows preceding stock tank;
(2) concentration of stock tank Middle and North America softwood pulp is put into afterwards to 5.0wt% before the long fibre of adjustment that adds water is kowtowed
In first fiberizer, fibre cutting and wire-dividing broom purification are carried out, is mixed after fibre cutting and wire-dividing broom purification in wood pulp
The weight in wet base 16g of wood pulp, 25 ° of SR of beating degree, is then fed into long fibre and kowtows in rear stock tank, the energy of the first fiberizer
Consumption control is in 100kwh/t;
(3) concentration of Brazilian hardwood pulp, to 5.0wt%, is put into afterwards in stock tank before the short fibre of adjustment that adds water is kowtowed
In fluffer, carry out fiber and discongest, discongest weight in wet base 3.2g, 18 ° of SR of beating degree that wood pulp is mixed in rear wood pulp,
It is then fed into short fibre to kowtow in rear stock tank, the inter-lobe clearance of fluffer is controlled in 2.0mm;
(4) 60% North America softwood pulp and 40% Brazilian hardwood pulp are pumped into blending chest, added water
Concentration is adjusted to 4.0wt%, fiber is done at further cut-out and wire-dividing broom purification by the second fiberizer afterwards
Reason, mixes weight in wet base 10g, 29 ° of SR of beating degree of wood pulp, then in wood pulp after fibre cutting and wire-dividing broom purification
Mixing wood pulp is sent into machine chest, the energy consumption of the second fiberizer is controlled in 35kwh/t;
(5) 30kg/t Suo Lisi wet strength agents 852 and 0.6kg/t is added in the mixing wood pulp of machine chest
Suo Lisi softening agent TQ1003, adjustment concentration is to 3.1wt%.
(6) mixing wood pulp is diluted to concentration for 0.25wt% through fan pump, into paper machine, by shaping,
Squeeze and dry, product is finally made.
The product that embodiment 1,2 is prepared and pair of the common soft performance parameter for taking out facial tissue and tissue
Than as shown in the table.
Compared by above-mentioned as can be seen that the application improves that paper feel is smoothness, improve the strong of paper
Degree, is added wettable aqueous.
Claims (8)
1. a kind of preparation method of wettable water paper handkerchief, it is characterised in that this method comprises the following steps:
(1) softwood pulp and hardwood pulp are put into long fine pulper with short fine pulper, adding water respectively
It is 5.0-7.0wt% to adjust wood pulp concentration, and size degradation is pumped into stock tank and short fibre before long fibre is kowtowed and kowtowed respectively after 8-15 minutes
Preceding stock tank;
(2) concentration of softwood pulp, to 4.0-5.0wt%, puts into fiberizer in stock tank before the long fibre of adjustment that adds water is kowtowed
Middle progress fibre cutting and wire-dividing broom purification, are then fed into long fibre and kowtow in rear stock tank;
(3) concentration of hardwood pulp, to 4.0-5.0wt%, puts into fluffer in stock tank before the short fibre of adjustment that adds water is kowtowed
In, carry out fiber and discongest, be then fed into short fibre and kowtow in rear stock tank;
(4) hardwood pulp of 50-60% softwood pulp and 50-40% is pumped into blending chest by weight, plus
Water adjusts concentration to 3.0-4.0wt%, and further cut-out is done to fiber through fiberizer and wire-dividing broom purification is handled, so
Afterwards will mixing wood pulp feeding machine chest;
(5) machine chest mixing wood pulp in addition 25-30kg/t wet strength agent and 0.4-0.6kg/t it is soft
Soft dose, adjustment wood pulp concentration to 2.9-3.1wt%;
(6) mixing wood pulp is diluted to concentration for 0.2-0.25wt% through fan pump, into paper machine, by into
Shape, squeezing and drying, are finally made product.
2. a kind of preparation method of wettable water paper handkerchief according to claim 1, it is characterised in that institute
The softwood pulp stated is North America softwood pulp, weight in wet base 18-22g, 12-16 ° of SR of beating degree.
3. a kind of preparation method of wettable water paper handkerchief according to claim 1, it is characterised in that institute
The hardwood pulp stated is Brazilian hardwood pulp, weight in wet base 3-4g, 14-17 ° of SR of beating degree.
4. a kind of preparation method of wettable water paper handkerchief according to claim 1, it is characterised in that step
Suddenly the energy consumption of fiberizer controls to mix in wood pulp after 90-100kwh/t, fibre cutting and wire-dividing broom purification in (2)
Close the weight in wet base 13-16g, 20-25 ° of SR of beating degree of wood pulp.
5. a kind of preparation method of wettable water paper handkerchief according to claim 1, it is characterised in that step
Suddenly the inter-lobe clearance control of fluffer, in 0.25-2.0mm, is discongested and the wet of wood pulp is mixed in rear wood pulp in (3)
Weight 2.7-3.2g, 15-18 ° of SR of beating degree.
6. a kind of preparation method of wettable water paper handkerchief according to claim 1, it is characterised in that step
Suddenly the energy consumption of fiberizer controls to mix in wood pulp after 30-35kwh/t, fibre cutting and wire-dividing broom purification in (4)
The weight in wet base 7-10g of wood pulp, 26-29 ° of SR of beating degree.
7. a kind of preparation method of wettable water paper handkerchief according to claim 1, it is characterised in that institute
The wet strength agent stated is the reinforced wet strength agents of new extensively raw PPE, Suo Lisi wet strength agents 852 or perseverance health wet strength agent FD-2.
8. a kind of preparation method of wettable water paper handkerchief according to claim 1, it is characterised in that institute
The softening agent stated is Suo Lisi softening agents TQ1003.