CN107311553A - A kind of architectural waterproof material - Google Patents
A kind of architectural waterproof material Download PDFInfo
- Publication number
- CN107311553A CN107311553A CN201610688260.1A CN201610688260A CN107311553A CN 107311553 A CN107311553 A CN 107311553A CN 201610688260 A CN201610688260 A CN 201610688260A CN 107311553 A CN107311553 A CN 107311553A
- Authority
- CN
- China
- Prior art keywords
- clay
- waterproof material
- petropols
- quartz sand
- synthetic rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Constituted the invention discloses a kind of architectural waterproof material, including following composition:Clay, clay additive, silicate mineral, Petropols, synthetic rubber and quartz sand, and respectively account for weight ratio and be:Clay 60% 70%, clay additive 1% 5%, silicate mineral 5% 8%, Petropols 5% 8%, synthetic rubber 1% 5%, quartz sand 2% 4%.It the advantage is that:The present invention can keep long-term compression strength, and humidity is kept during solidifying.After the completion of freezing period, though because through when dry or solidification cause construction after produce micro cracking, can also absorb water performance its reversible expansion compactness once again, so that micro crackle is expanded into the closely knit waterproof effect for reaching infinite circulating.
Description
Technical field
The present invention relates to building material field, particularly a kind of architectural waterproof material.
Background technology
In existing various waterproof materials, there are the encapsulants such as asphalt series, rubber series, resin system, these category are organic anti-
Water material, such a have and waterproof material placing the temperature change of environment because hardening, decomposing or other factors cause water-proof function
Reduction.Have and waterproof material is without fire line in addition, such a.
Also useful cement class, smectites are used as waterproof material in existing waterproof material.Utilize bentonite water swelling
Property by bentonite directly with powder, the state construction usage of shot-like particle, these waterproof material application properties and keep waterproof for a long time
The aspect of effect two is unable to reach.
The content of the invention
It is an object of the invention to provide a kind of architectural waterproof material steady in a long-term.
The technical solution adopted by the present invention is:
A kind of architectural waterproof material, its innovative point is:Including following composition composition:Clay, clay additive, silicate mineral
Matter, Petropols, synthetic rubber and quartz sand, and respectively account for weight ratio and be:Clay 60%-70%, clay additive 1%-5%, silicic acid
Salt mineral matter 5%-8%, Petropols 5%-8%, synthetic rubber 1%-5%, quartz sand 2%-4%.
Further, calcium chloride 40%-60%, polyacrylamide 15%-25%, alum 8%- in the clay additive
25%。
Further, the silicate mineral includes Portland clinker and portland cement.
Beneficial effects of the present invention are as follows:
The present invention can keep long-term compression strength, and humidity is kept during solidifying.After the completion of freezing period, even if because of warp
When dry or solidification and cause construction after produce micro cracking, can also absorb water once again performance its reversible expansion compactness, from
And micro crackle is expanded into the closely knit waterproof effect for reaching infinite circulating.
Embodiment
Embodiment 1
A kind of architectural waterproof material, its weight ratio is:Clay 60%, clay additive 1%, silicate mineral 5%, Petropols
5%th, synthetic rubber 1%, quartz sand 2%;Calcium chloride 50%, polyacrylamide 20%, alum 16% in clay additive.
Embodiment 2
A kind of architectural waterproof material, its weight ratio is:Clay 70%, clay additive 5%, silicate mineral 8%, Petropols
5%-8%, synthetic rubber 5%, quartz sand 4%;Calcium chloride 50%, polyacrylamide 20%, alum 16% in clay additive.
Embodiment 3
A kind of architectural waterproof material, its weight ratio is:Clay 65%, clay additive 3%, silicate mineral 7%, Petropols
6%th, synthetic rubber 3%, quartz sand 3%;Calcium chloride 50%, polyacrylamide 20%, alum 16% in clay additive.
Described above is the preferred embodiment of the present invention, it is impossible to the interest field of the present invention is limited with this.It should refer to
Go out, for those skilled in the art, technical scheme is modified or equivalent substitution, all
Protection scope of the present invention is not departed from.
Constituted the invention discloses a kind of architectural waterproof material, including following composition:Clay, clay additive, silicate
Mineral matter, Petropols, synthetic rubber and quartz sand, and respectively account for weight ratio and be:Clay 60%-70%, clay additive 1%-5%,
Silicate mineral 5%-8%, Petropols 5%-8%, synthetic rubber 1%-5%, quartz sand 2%-4%.It the advantage is that:Energy of the present invention
Long-term compression strength is enough kept, humidity is kept during solidifying.After the completion of freezing period, though because through when dry or solidify
And micro cracking is produced after causing construction, can also absorb water performance its reversible expansion compactness once again, so that by micro crackle
The closely knit waterproof effect for reaching infinite circulating of expansion.
Claims (3)
1. a kind of architectural waterproof material, it is characterised in that:Including following composition composition:Clay, clay additive, silicate mineral
Matter, Petropols, synthetic rubber and quartz sand, and respectively account for weight ratio and be:Clay 60%-70%, clay additive 1%-5%, silicic acid
Salt mineral matter 5%-8%, Petropols 5%-8%, synthetic rubber 1%-5%, quartz sand 2%-4%.
2. a kind of architectural waterproof material according to claim 1, it is characterised in that:Calcium chloride in the clay additive
40%-60%, polyacrylamide 15%-25%, alum 8%-25%.
3. a kind of architectural waterproof material according to claim 1, it is characterised in that:The silicate mineral includes silicic acid
Salt cement clinker and portland cement.