CN107311475A - A kind of modification dolomite and preparation method thereof - Google Patents
A kind of modification dolomite and preparation method thereof Download PDFInfo
- Publication number
- CN107311475A CN107311475A CN201710681966.XA CN201710681966A CN107311475A CN 107311475 A CN107311475 A CN 107311475A CN 201710681966 A CN201710681966 A CN 201710681966A CN 107311475 A CN107311475 A CN 107311475A
- Authority
- CN
- China
- Prior art keywords
- light
- dolomite
- burned
- water
- carbon dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides a kind of modification dolomite and preparation method thereof, including light-burned, carbonating, stabilize three phases, modification dolomite prepared by the present invention, crystal structure is loose, porosity is big and even aperture distribution, porosity is not less than 10%, it can reach more than 50 times of corresponding raw ore porosity, for desalination water it is quenched when, the contact area of adjusting material and desalination water is significantly increased, dissolution rate is substantially accelerated, residence time only needs 1~5min just to reach effective regulation to desalinization water water quality, less than 10% of the dolomite raw ore residence time under equal conditions, therefore only desalination water need to be made to flow through the quenched tank equipped with the modification dolomite using the present invention, quenched process need not add medicament, quenched water outlet is in alkalescent, hardness, basicity is moderate, water molecule cluster is small, rich in calcium, magnesium, iron, the beneficial mineral element such as zinc, heavy carbonate rich content.
Description
Technical field
The invention belongs to dolomite preparing technical field, and in particular to a kind of modification dolomite and preparation method thereof.
Background technology
With the development of membrane science technology, counter-infiltration has been increasingly becoming a kind of effective ways for solving world's fresh water crisis.
Counter-infiltration can remove most bacterium, inorganic salts, organic matter etc. in seawater, but not be equal proportion to each ion component in seawater
Ground is removed, Ca2+、Mg2+、SO42-It is high compared with monovalent ion etc. bivalent ions rejection so that the buffer capacity of desalination water is relatively
It is weak.Further, since counter-infiltration can not retain the carbon dioxide in seawater, these carbon dioxide reach production water through membrane module
It can be returned to behind side and HCO is converted into water3-, this will cause desalination by reverse osmosis water to have stronger corrosivity.This spy of desalination water
Property so that transport, storage during calcium carbonate film be difficult on tube wall, bulkhead precipitate so that metallic material corrosion and produce
Raw " red water " phenomenon, meanwhile, microorganism can also grow on tube wall and aggravate piping corrosion.These all will be to water supply cost, use
Family produces a series of influence to the acceptance of desalination water, disinfection efficiency and user's body health etc..Therefore, from piping corrosion
Consider with human body drinking safety, it is necessary to which desalination water water quality is adjusted.
The quenched method of desalination water includes mixing source water blending method, addition medical method and dissolving ore method.It is light in blending method
Change water to be difficult to coordinate with mixing the ratio of source water;When addition medicament is quenched, the easy deliquescence of medicament, not Portable belt, and can be light to seawater
Change water water quality and produce some side effects, for example, add Ca (OH)2When delivery turbidity increase, production water pH may be caused too high, add
Plus NaHCO3When can cause production water it is astringent, influence drink mouthfeel;The raw ores such as dolomite, lime stone, medical stone are directly used in light
When change water is quenched, though tcrude ore Mineral Concentrations are abundant, and it can realize to desalinization water pH, hardness, basicity, calcium-magnesium content
Deng effective regulation, but tcrude ore rate of dissolution is excessively slow, and the residence time of desalination water in a device is long, and quenching and tempering device is excessive.
If using H2SO4Or CO2Reduce inlet flow-patterm and accelerate ore rate of dissolution, water outlet pH can be made in acidity, need dosing to carry out pH regulations, and
H2SO4With CO2Not portable, storage inconvenience greatly limit its application in ship desalination water is quenched
The content of the invention
To solve the above problems, it is an object of the invention to provide a kind of modification dolomite and preparation method thereof, specifically
Technical scheme is:A kind of modification dolomite and preparation method thereof, comprises the following steps:
(1) it is light-burned:By raw material of dolomite raw ore, progress is light-burned, and light roasting temperature is 500~1200 DEG C, and the light-burned time is 3-
6h, is passed through carbon dioxide during light-burned, and light-burned stage heating rate is 5~10 DEG C/min, light-burned carbon dioxide in process
Inside effusion, dolomite and surface forms uniform hole, and dolomite decomposition is calcium carbonate, calcium oxide and magnesia;
(2) it is carbonated:Product of the step 1 after light-burned is carbonated using wet method, carbonation is passed through vapor
With carbon dioxide, calcium oxide, oxidation reactive magnesium generation hydroxide of the vapor with the formation of light-burned stage, then with carbon dioxide
Reaction generation carbonate, heavy carbonate;Described vapor accounts for the 30~50% of mixed gas volume, and carbonation temperature is 50~
150 DEG C, carbonation time is 1~5h;
(3) stabilize:Product after carbonating is stabilized in carbon dioxide atmosphere, stabilization temperature is 100
~150 DEG C, the stabilisation time is 2-4h.
Further, the porosity of the modification dolomite is not less than 10%.
Further, the particle diameter of the dolomite raw ore used is 5~10mm.
Modification dolomite prepared by method of the present invention.
Beneficial effect:The invention provides modification white clouds prepared by a kind of modification dolomite and preparation method thereof, the present invention
Stone, crystal structure is loose, and porosity is big and even aperture distribution, and porosity is not less than 10%, can reach corresponding raw ore porosity
More than 50 times, for desalination water it is quenched when, the contact area of adjusting material and desalination water is significantly increased, and dissolution rate substantially adds
It hurry up, the residence time only needs 1~5min just to reach effective regulation to desalinization water water quality, less than white clouds under equal conditions
The 10% of stone raw ore residence time, therefore only desalination water need to be made to flow through equipped with the quenched of the modification dolomite using this patent
Tank, quenched process need not add medicament, and quenched water outlet is in alkalescent, and hardness, basicity are moderate, and water molecule cluster is small, rich in calcium,
The beneficial mineral element such as magnesium, iron, zinc, heavy carbonate rich content.
Embodiment
The invention will now be further described with reference to specific embodiments, and following examples are only the optimal implementation of the present invention
Example, does not constitute any limitation to the scope of the present invention.It will be understood by those skilled in the art that without departing from the present invention's
The details and form of technical solution of the present invention can be modified or replaced under spirit and scope, but these modifications and replacement are equal
Fall within the scope of protection of the present invention.
Embodiment 1
A kind of modification dolomite and preparation method thereof, comprises the following steps:
(1) it is light-burned:By raw material of dolomite raw ore, progress is light-burned, and light roasting temperature is 800 DEG C, and the light-burned time is 5h, light
Carbon dioxide is passed through during burning, light-burned stage heating rate is 8 DEG C/min, light-burned carbon dioxide in process effusion, dolomite
Internal and surface forms uniform hole, and dolomite decomposition is calcium carbonate, calcium oxide and magnesia;
(2) it is carbonated:Product of the step 1 after light-burned is carbonated using wet method, carbonation is passed through vapor
With carbon dioxide, calcium oxide, oxidation reactive magnesium generation hydroxide of the vapor with the formation of light-burned stage, then with carbon dioxide
Reaction generation carbonate, heavy carbonate;Described vapor accounts for the 40% of mixed gas volume, and carbonation temperature is 100 DEG C, carbon
Acidificatoin time is 3h;
(3) stabilize:Product after carbonating is stabilized in carbon dioxide atmosphere, stabilization temperature is 120
DEG C, the stabilisation time is 2-4h.
Further, the porosity of the modification dolomite is not less than 10%.
Further, the particle diameter of the dolomite raw ore used is 8mm.
Modification dolomite prepared by method of the present invention.
Embodiment 2
A kind of modification dolomite and preparation method thereof, comprises the following steps:
(1) it is light-burned:By raw material of dolomite raw ore, progress is light-burned, and light roasting temperature is 500 DEG C, and the light-burned time is 3h, light
Carbon dioxide is passed through during burning, light-burned stage heating rate is 5 DEG C/min, light-burned carbon dioxide in process effusion, dolomite
Internal and surface forms uniform hole, and dolomite decomposition is calcium carbonate, calcium oxide and magnesia;
(2) it is carbonated:Product of the step 1 after light-burned is carbonated using wet method, carbonation is passed through vapor
With carbon dioxide, calcium oxide, oxidation reactive magnesium generation hydroxide of the vapor with the formation of light-burned stage, then with carbon dioxide
Reaction generation carbonate, heavy carbonate;Described vapor accounts for the 30%~50% of mixed gas volume, and carbonation temperature is 50
DEG C, carbonation time is 1h;
(3) stabilize:Product after carbonating is stabilized in carbon dioxide atmosphere, stabilization temperature is 100
DEG C, the stabilisation time is 2h.
Further, the porosity of the modification dolomite is not less than 10%.
Further, the particle diameter of the dolomite raw ore used is 5mm.
Modification dolomite prepared by method of the present invention.
Embodiment 3
A kind of modification dolomite and preparation method thereof, comprises the following steps:
(1) it is light-burned:By raw material of dolomite raw ore, progress is light-burned, and light roasting temperature is 1200 DEG C, and the light-burned time is 6h, light
Carbon dioxide is passed through during burning, light-burned stage heating rate is 10 DEG C/min, light-burned carbon dioxide in process effusion, dolomite
Internal and surface forms uniform hole, and dolomite decomposition is calcium carbonate, calcium oxide and magnesia;
(2) it is carbonated:Product of the step 1 after light-burned is carbonated using wet method, carbonation is passed through vapor
With carbon dioxide, calcium oxide, oxidation reactive magnesium generation hydroxide of the vapor with the formation of light-burned stage, then with carbon dioxide
Reaction generation carbonate, heavy carbonate;Described vapor accounts for the 50% of mixed gas volume, and carbonation temperature is 150 DEG C, carbon
Acidificatoin time is 1h~5h;
(3) stabilize:Product after carbonating is stabilized in carbon dioxide atmosphere, stabilization temperature is 150
DEG C, the stabilisation time is 4h.
Further, the porosity of the modification dolomite is not less than 10%.
Further, the particle diameter of the dolomite raw ore used is 10mm.
Modification dolomite prepared by method of the present invention.
Claims (4)
1. a kind of modification dolomite and preparation method thereof, it is characterised in that comprise the following steps:
(1) it is light-burned:By raw material of dolomite raw ore, progress is light-burned, and light roasting temperature is 500~1200 DEG C, and the light-burned time is 3-6h,
Carbon dioxide is passed through during light-burned, light-burned stage heating rate is 5~10 DEG C/min, light-burned carbon dioxide in process ease
Go out, inside dolomite and surface forms uniform hole, dolomite decomposition is calcium carbonate, calcium oxide and magnesia;
(2) it is carbonated:Product of the step 1 after light-burned is carbonated using wet method, carbonation is passed through vapor and two
Carbonoxide, calcium oxide, oxidation reactive magnesium generation hydroxide of the vapor with the formation of light-burned stage, then with carbon dioxide reaction
Generate carbonate, heavy carbonate;Described vapor accounts for the 30~50% of mixed gas volume, and carbonation temperature is 50~150
DEG C, carbonation time is 1~5h;
(3) stabilize:Product after carbonating is stabilized in carbon dioxide atmosphere, stabilization temperature is 100~150
DEG C, the stabilisation time is 2-4h.
2. a kind of modification dolomite according to claim 1 and preparation method thereof, it is characterised in that the modification dolomite
Porosity be not less than 10%.
3. a kind of modification dolomite according to claim 1 and preparation method thereof, it is characterised in that the white clouds of the use
The particle diameter of stone raw ore is 5~10mm.
4. modification dolomite prepared by the method described in claim 1.