A kind of notebook high heat radiation anti-radiation keyboard membrane and preparation method
Technical field
The present invention relates to computer articles fields, and in particular to a kind of notebook high heat radiation anti-radiation keyboard membrane and preparation
Method.
Background technique
The epoch in living space are full of in this current information technology, people increasingly experience the differentiation of consumption electronic product
It is how fast.Before more than 20 years, when PC enters family, the huge of influence that computer lives to people is it
Less than his electronic product, in today of information age, people more and more use computer, and computor-keyboard is undoubtedly people
The important channel contacted with computer, due to the frequent use of computer, some users often allow key because of prolonged typewriting
Mill falls those letters, and keyboard can also turn to be yellow, and the above problem of keyboard of notebook computer is then more serious.
For this purpose, some companies are dedicated to making individual character, fashion, practical notebook periphery accessory.No matter in design or function
Can on penetrate into aesthstic intention, make great efforts to create more preferably product, newest flowing science and technology incorporated to the work and life of people.
Make every effort to that digital life is unusually brilliant, and be then born a variety of keyboard protective films on the market, such as: 1, universal keyboard film: plate
Keyboard membrane, no key mapping fitting, suitable for any notebook of comparable size, the defencive function with high transparency, waterproof and dustproof.
2, transparent keyboard film: the silica gel transparent keyboard film of traditional sense is consistent with the key mapping of keyboard, and concave-convex key mapping perfectly merges,
Defencive function with high transparency, waterproof and dustproof.And some colorful keyboard membranes, but existing keyboard membrane is mostly needle
Waterproof, high function thoroughly are modified, do not made a search to the heat sinking function of computer, especially keyboard dissipates laptop
There are certain inhibitions for heat, are easy to produce laptop caused by heat dissipation difficulty and use exception.And well known computer is
There are radiation, especially keyboard, existing keyboard can't radiation protection.Keyboard is so close from the hand of people, just directly makes to human body
At injury.
Therefore, researching and developing one kind both has preferable waterproof, heat dissipation performance, by the key with preferable radiation protection
Disk film is of great significance, and also complies with the demand of existing market, with good application prospect.
Summary of the invention
For the defects in the prior art, the object of the present invention is to provide a kind of high heat radiation anti-radiation keyboard membranes of notebook
And preparation method, the keyboard membrane not only inherit the waterproof of existing keyboard membrane, high permeability, also have preferable heat dissipation effect and
Excellent shielding property, the normal operation of only computer does not provide guarantee, also provides safety guarantee for computer user,
The radiation bring harm for effectively reducing keyboard, has preferable use value.In addition, described, preparation method is simple,
It is suitble to industrialization promotion production.
The present invention solves technical problem and adopts the following technical scheme that
The present invention relates to a kind of notebook high heat radiation anti-radiation keyboard membranes, including keyboard membrane body layer, are arranged in keyboard
The radiation protective layer of membrane body layer upper surface, and the wear-resisting waterproof layer of radiation protective layer upper surface is set, the keyboard membrane body
Layer lower surface is additionally provided with Electrostatic Absorption layer, passes through adhesive heat bonding between each layer, and the adhesive is epoxide-resin glue
Glutinous agent;
The keyboard membrane body layer be high heat radiator body layer, each component including following parts by weight: polyacrylamide 40~
60 parts, 30~50 parts of polycarbonate, 10~20 parts of modified attapulgite clay, 8~12 parts of nano-titanium dioxide, anti-aging agent 1~3
Part;
The wear-resisting waterproof layer is graphene modified butadiene acrylonitrile rubber hyaline layer, each component including following parts by weight: carboxyl
60~80 parts of nitrile rubber latex, 0.5~2 part of graphene oxide, 2~5 parts of anti-aging agent WL, 5~10 parts of potassium chloride, hydrazine hydrate 8
~12 parts, further include suitable water;
The radiation protective layer be graphene modified PET transparent adhesive tape lamella, each component including following parts by weight: PET 60~
80 parts, 12~16 parts of polyisocyanates, 3~7 parts of nano-titanium dioxide, 0.4~1.2 part of graphene oxide, plasticizer 8~15
Part, 2~5 parts of anti-aging agent;
The Electrostatic Absorption layer is EVA Electrostatic Absorption film.
Preferably, the keyboard membrane body layer includes each component of following parts by weight: 55 parts of polyacrylamide, polycarbonate
40 parts, 18 parts of modified attapulgite clay, 10 parts of nano-titanium dioxide, 2 parts of anti-aging agent.
Preferably, the wear-resisting waterproof layer includes each component of following parts by weight: 70 parts of carboxy nitrile rubber latex, oxidation
1.6 parts of graphene, 4 parts of anti-aging agent WL, 8 parts of potassium chloride, 10 parts of hydrazine hydrate, further include suitable water.
Preferably, the radiation protective layer includes each component of following parts by weight: 70 parts of PET, 13 parts of polyisocyanates, being received
Rice 6 parts of titanium dioxide, 0.9 part of graphene oxide, 12 parts of plasticizer, 3 parts of anti-aging agent.
Preferably, the modified attapulgite clay is that natural attapulgite clay is purified, is acidified, after heat modification
Product.
The invention further relates to a kind of methods prepared such as notebook with high heat radiation anti-radiation keyboard membrane, include the following steps:
(1) preparation of keyboard membrane body layer: weighing polyacrylamide according to the proportion and polycarbonate is added in reaction kettle,
Heating melting, stirs 20~30min, graphene is added into mixture, then anti-aging agent is added in 1~2h of hybrid reaction, stirring
Mix 30~40min;
Into mixture be added modified attapulgite clay, nano-titanium dioxide, be uniformly mixed be placed on revolving speed be 600~
Shearing disperses 10~20min in the cutter of 800 turns/min, under ultrasonic conditions 5~10min of ultrasound, then by mixture
It is placed in film-forming machine and forms a film to get the keyboard membrane body layer;
(2) preparation of wear-resisting waterproof layer material;Carboxy nitrile rubber latex is weighed according to the proportion, by graphene oxide solution
It is added drop-wise in latex, is placed in 40~60min of ultrasound in ultrasonic wave, then mixture is transferred in reaction kettle, hydrazine hydrate is added,
10~15min is stirred, 90~100 DEG C is warming up to, is stirred to react 1~2h;
After reaction, anti-aging agent WL is added into mixture, stirs 5~10min, it is 2 that mixture, which is then placed in PH,
Klorvess Liquid in flocculate, then with 100 DEG C of deionized water clean flocculation after latex, then by latex be put into film-forming machine at
Film is to get the wear-resisting waterproof layer;
(3) PET, polyisocyanates, graphene oxide and plasticising the preparation of radiation protective layer material: are weighed respectively according to the proportion
Agent melting mixing, is stirred to react 30~60min, and mixture is transferred in kneading machine, and nano-titanium dioxide and anti-aging agent is added,
It is kneaded 10~20min, is formed to get the radiation protective layer;
(4) preparation of keyboard membrane: in sequence respectively by wear-resisting waterproof layer, radiation protective layer, keyboard membrane body layer and electrostatic
Adsorption layer arranges from top to bottom, layer by layer between coat adhesive, then layers of material is placed in heat-sealing machine and carries out heat bonding,
Up to the keyboard membrane.
Preferably, in the step (1) modified attapulgite clay the preparation method comprises the following steps:
It takes natural attapulgite to carry out being crushed to 200~300 mesh, 10~20 times of attapulgite quality of water, stirring is added
Mud in suspension is formed, upper suspension 5~10min of centrifugal treating in the centrifuge of 3000~5000 turns/min is taken, vacuum is taken out
Filter;Filter cake is placed in flask, the dilute hydrochloric acid of 2mol/L is added, is stirred at reflux 20~30min in 60~80 DEG C, is filtered by vacuum,
And wash with distilled water to PH be 6~7, obtain filter cake, then filter cake is placed in program in Muffle furnace and is warming up to 600~800 DEG C, then
1~3h of constant temperature calcining, it is 200 mesh that partial size is ground to after cooling.
Preferably, the volume and Concave-convex clay rod mass ratio that the dilute hydrochloric acid is added are 1mL:5g~10g.
Preferably, graphene oxide solution is that the graphene oxide that concentration is 0.1~0.3g/L is water-soluble in the step (2)
Liquid.
Compared with prior art, the present invention have it is following the utility model has the advantages that
(1) the high heat radiation anti-radiation keyboard membrane of notebook of the present invention, not only inherit existing keyboard membrane waterproof,
High permeability also has preferable heat dissipation effect and excellent shielding property, and the normal operation of only computer does not provide guarantee,
It is abnormal to can be avoided the computer work as caused by heat dissipation is difficult, improves the service life of computer and keyboard, while being also electricity
Brain user provides safety guarantee, and effect reduces the radiation bring harm of keyboard, has preferable use value.
(2) added with modified in the keyboard membrane body layer of the high heat radiation anti-radiation keyboard membrane of notebook of the present invention
Concave-convex clay rod preferable heat dissipation effect is made it have due to its unique chain layer structure and biggish specific surface area,
And then condition is provided for the high heat dispersion of keyboard membrane.
(3) keyboard membrane of the present invention uses graphene modified butadiene acrylonitrile rubber as wear-resisting waterproof layer, since graphene has
There is lamella conjugated structure, is layering to form fine and close erosion resistant coating, can effectively inhibit infiltration and infiltration of the water to material, thus
So that graphene modified butadiene acrylonitrile rubber layer has preferable water-fast corrosion resistance;Further, since the mechanical property that graphene is excellent
Energy and chemical stability, so that modified polymer has preferable wear-resisting, scratch-resistant mechanical property and chemical stability,
So that the keyboard membrane being prepared has preferable wear-resisting, scratch-resistant mechanical property and chemical stability.
(4) notebook of the present invention uses high heat radiation anti-radiation keyboard membrane to use graphene modified PET material as anti-spoke
Layer is penetrated, since graphene has preferable electromagnet shield effect, so that modified PET material has preferable electromagnetic shielding effect
Fruit can be effectively reduced injury of the keyboard electromagnetic radiation to human body, substantially increase the safety in utilization of keyboard, meet taking human as
This objective.
(5) notebook of the present invention is additionally provided with EVA Electrostatic Absorption layer with high heat radiation anti-radiation keyboard membrane, for no glue
Self-adhesive film, enable keyboard membrane automatic absorbing on the surface of keyboard, prevent keyboard membrane from slipping, have it is easy to use, absorption
Secured feature.
(6) preparation process of the high heat radiation anti-radiation keyboard membrane of notebook of the present invention is simple, mild condition, prepares
Journey object pollutant generates, safety and environmental protection, is suitble to industrialization promotion production.
Specific embodiment
Present invention will be further explained below with reference to specific examples.These embodiments are merely to illustrate the present invention and do not have to
In limiting the scope of the invention.In the following examples, the experimental methods for specific conditions are not specified, usually according to normal condition, such as
The molecular clonings such as Sambrook: laboratory manual (New York:Cold Spring Harbor Laboratory Press,
1989) condition described in, or according to the normal condition proposed by manufacturer.
Embodiment 1:
A kind of notebook of the preferred embodiment of the present invention high heat radiation anti-radiation keyboard membrane and preparation method;
The notebook high heat radiation anti-radiation keyboard membrane, including keyboard membrane body layer are arranged in keyboard membrane body layer
The radiation protective layer on surface, and the wear-resisting waterproof layer of radiation protective layer upper surface is set, keyboard membrane body layer lower surface is also
It is provided with Electrostatic Absorption layer, passes through adhesive heat bonding between each layer, the adhesive is epoxy resin adhesive;
The keyboard membrane body layer be high heat radiator body layer, each component including following parts by weight: 55 parts of polyacrylamide,
40 parts of polycarbonate, 18 parts of modified attapulgite clay, 10 parts of nano-titanium dioxide, 2 parts of anti-aging agent;
The wear-resisting waterproof layer is graphene modified butadiene acrylonitrile rubber hyaline layer, each component including following parts by weight: carboxyl
70 parts of nitrile rubber latex, 1.6 parts of graphene oxide, 4 parts of anti-aging agent WL, 8 parts of potassium chloride, 10 parts of hydrazine hydrate, further include appropriate
Water;
The radiation protective layer is graphene modified PET transparent adhesive tape lamella, each component including following parts by weight: PET 70
Part, 13 parts of polyisocyanates, 6 parts of nano-titanium dioxide, 0.9 part of graphene oxide, 12 parts of plasticizer, 3 parts of anti-aging agent;
The Electrostatic Absorption layer is EVA Electrostatic Absorption film, selects this Electrostatic Absorption film to be because EVA Electrostatic Absorption film is nothing
The self-adhesive film of glue, enable to keyboard membrane can automatic absorbing on the surface of keyboard, prevent keyboard membrane from slipping, have user
Just, secured feature is adsorbed.
The modified attapulgite clay is the product after purified natural attapulgite clay, acidification, heat modification.Make
It is to make it have preferable heat dissipation because of its unique chain layer structure and biggish specific surface area with such Concave-convex clay rod
Effect, and then condition is provided for the high heat dispersion of keyboard membrane.
It is of the present invention to prepare the notebook method of high heat radiation anti-radiation keyboard membrane, include the following steps:
(1) preparation of keyboard membrane body layer: weighing polyacrylamide according to the proportion and polycarbonate is added in reaction kettle,
Heating melting, stirs 30min, graphene is added into mixture, then hybrid reaction 2h is added anti-aging agent, is stirred
30min;
Modified attapulgite clay, nano-titanium dioxide are added into mixture, being uniformly mixed and being placed on revolving speed is 800
Turn/cutter of min in shearing dispersion 15min, ultrasound 10min, is then placed in film-forming machine for mixture under ultrasonic conditions
Middle film forming is to get the keyboard membrane body layer;
(2) preparation of wear-resisting waterproof layer material;Carboxy nitrile rubber latex is weighed according to the proportion, is 0.2g/L's by concentration
Graphene oxide water solution is added drop-wise in latex, is placed in ultrasound 50min in ultrasonic wave, mixture is then transferred to reaction kettle
In, hydrazine hydrate is added, stirs 10min, is warming up to 90~100 DEG C, is stirred to react 1h;
After reaction, anti-aging agent WL is added into mixture, stirs 10min, mixture is then placed in the chlorine that PH is 2
Change and flocculate in potassium solution, then cleans the latex after flocculating with 100 DEG C of deionized water, then latex is put into film-forming machine and is formed a film,
Up to the wear-resisting waterproof layer;
(3) PET, polyisocyanates, graphene oxide and plasticising the preparation of radiation protective layer material: are weighed respectively according to the proportion
Agent melting mixing, is stirred to react 50min, and mixture is transferred in kneading machine, and nano-titanium dioxide and anti-aging agent is added, and is kneaded
20min forms to get the radiation protective layer;
(4) preparation of keyboard membrane: in sequence respectively by wear-resisting waterproof layer, radiation protective layer, keyboard membrane body layer and electrostatic
Adsorption layer arranges from top to bottom, layer by layer between coat adhesive, then layers of material is placed in heat-sealing machine and carries out heat bonding,
Up to the keyboard membrane.
In step (1) modified attapulgite clay the preparation method comprises the following steps:
It takes natural attapulgite to carry out being crushed to 200~300 mesh, 16 times of attapulgite quality of water is added, stirring is formed
Mud in suspension takes upper suspension centrifugal treating 10min in the centrifuge of 4000 turns/min, vacuum filtration;Filter cake is placed in
In flask, the dilute hydrochloric acid of 2mol/L is added, wherein the volume that the dilute hydrochloric acid is added is with Concave-convex clay rod mass ratio
Then 1mL:6g is stirred at reflux 30min in 60~80 DEG C, vacuum filtration, and is wash with distilled water 6~7 to PH, obtains filter cake,
Filter cake is placed in program in Muffle furnace again and is warming up to 800 DEG C, then constant temperature calcining 2h, be ground to after cooling partial size be 200 mesh i.e.
It can.
Embodiment 2:
A kind of notebook of the preferred embodiment of the present invention high heat radiation anti-radiation keyboard membrane and preparation method;
The notebook high heat radiation anti-radiation keyboard membrane, including keyboard membrane body layer are arranged in keyboard membrane body layer
The radiation protective layer on surface, and the wear-resisting waterproof layer of radiation protective layer upper surface is set, keyboard membrane body layer lower surface is also
It is provided with Electrostatic Absorption layer, passes through adhesive heat bonding between each layer, the adhesive is epoxy resin adhesive;
The keyboard membrane body layer be high heat radiator body layer, each component including following parts by weight: 40 parts of polyacrylamide,
30 parts of polycarbonate, 10 parts of modified attapulgite clay, 8 parts of nano-titanium dioxide, 1 part of anti-aging agent;
The wear-resisting waterproof layer is graphene modified butadiene acrylonitrile rubber hyaline layer, each component including following parts by weight: carboxyl
60 parts of nitrile rubber latex, 0.5 part of graphene oxide, 2 parts of anti-aging agent WL, 5 parts of potassium chloride, 8 parts of hydrazine hydrate, further include appropriate
Water;
The radiation protective layer is graphene modified PET transparent adhesive tape lamella, each component including following parts by weight: PET 60
Part, 12 parts of polyisocyanates, 3 parts of nano-titanium dioxide, 0.4 part of graphene oxide, 8 parts of plasticizer, 2 parts of anti-aging agent;
The Electrostatic Absorption layer is EVA Electrostatic Absorption film.
The modified attapulgite clay is the product after purified natural attapulgite clay, acidification, heat modification.
It is of the present invention to prepare the notebook method of high heat radiation anti-radiation keyboard membrane, include the following steps:
(1) preparation of keyboard membrane body layer: weighing polyacrylamide according to the proportion and polycarbonate is added in reaction kettle,
Heating melting, stirs 20min, graphene is added into mixture, then hybrid reaction 1h is added anti-aging agent, is stirred
30min;
Modified attapulgite clay, nano-titanium dioxide are added into mixture, being uniformly mixed and being placed on revolving speed is 600
Turn/cutter of min in shearing dispersion 20min, mixture, is then placed in film-forming machine by ultrasound 5min under ultrasonic conditions
Film forming is to get the keyboard membrane body layer;
(2) preparation of wear-resisting waterproof layer material;Carboxy nitrile rubber latex is weighed according to the proportion, is 0.1g/L's by concentration
Graphene oxide water solution is added drop-wise in latex, is placed in ultrasound 40min in ultrasonic wave, mixture is then transferred to reaction kettle
In, hydrazine hydrate is added, stirs 10min, is warming up to 90 DEG C, is stirred to react 2h;
After reaction, anti-aging agent WL is added into mixture, stirs 5min, mixture is then placed in the chlorine that PH is 2
Change and flocculate in potassium solution, then cleans the latex after flocculating with 100 DEG C of deionized water, then latex is put into film-forming machine and is formed a film,
Up to the wear-resisting waterproof layer;
(3) PET, polyisocyanates, graphene oxide and plasticising the preparation of radiation protective layer material: are weighed respectively according to the proportion
Agent melting mixing, is stirred to react 30min, and mixture is transferred in kneading machine, and nano-titanium dioxide and anti-aging agent is added, and is kneaded
10min forms to get the radiation protective layer;
(4) preparation of keyboard membrane: in sequence respectively by wear-resisting waterproof layer, radiation protective layer, keyboard membrane body layer and electrostatic
Adsorption layer arranges from top to bottom, layer by layer between coat adhesive, then layers of material is placed in heat-sealing machine and carries out heat bonding,
Up to the keyboard membrane.
In step (1) modified attapulgite clay the preparation method comprises the following steps:
It takes natural attapulgite to carry out being crushed to 200~300 mesh, 10 times of attapulgite quality of water is added, stirring is formed
Mud in suspension takes upper suspension centrifugal treating 10min in the centrifuge of 3000 turns/min, vacuum filtration;Filter cake is placed in
In flask, the dilute hydrochloric acid of 2mol/L is added, wherein the volume that the dilute hydrochloric acid is added is with Concave-convex clay rod mass ratio
Then 1mL:5g is stirred at reflux 30min in 60 DEG C, vacuum filtration, and is wash with distilled water 6~7 to PH, obtains filter cake, then will
Filter cake is placed in program in Muffle furnace and is warming up to 600 DEG C, then constant temperature calcining 3h, and it is 200 mesh that partial size is ground to after cooling.
Embodiment 3:
A kind of notebook of the preferred embodiment of the present invention high heat radiation anti-radiation keyboard membrane and preparation method;
The notebook high heat radiation anti-radiation keyboard membrane, including keyboard membrane body layer are arranged in keyboard membrane body layer
The radiation protective layer on surface, and the wear-resisting waterproof layer of radiation protective layer upper surface is set, keyboard membrane body layer lower surface is also
It is provided with Electrostatic Absorption layer, passes through adhesive heat bonding between each layer, the adhesive is epoxy resin adhesive;
The keyboard membrane body layer be high heat radiator body layer, each component including following parts by weight: 60 parts of polyacrylamide,
50 parts of polycarbonate, 20 parts of modified attapulgite clay, 12 parts of nano-titanium dioxide, 3 parts of anti-aging agent;
The wear-resisting waterproof layer is graphene modified butadiene acrylonitrile rubber hyaline layer, each component including following parts by weight: carboxyl
80 parts of nitrile rubber latex, 2 parts of graphene oxide, 5 parts of anti-aging agent WL, 10 parts of potassium chloride, 12 parts of hydrazine hydrate, further include appropriate
Water;
The radiation protective layer is graphene modified PET transparent adhesive tape lamella, each component including following parts by weight: PET 80
Part, 16 parts of polyisocyanates, 7 parts of nano-titanium dioxide, 1.2 parts of graphene oxide, 15 parts of plasticizer, 5 parts of anti-aging agent;
The Electrostatic Absorption layer is EVA Electrostatic Absorption film.
The modified attapulgite clay is the product after purified natural attapulgite clay, acidification, heat modification.
It is of the present invention to prepare the notebook method of high heat radiation anti-radiation keyboard membrane, include the following steps:
(1) preparation of keyboard membrane body layer: weighing polyacrylamide according to the proportion and polycarbonate is added in reaction kettle,
Heating melting, stirs 30min, graphene is added into mixture, then hybrid reaction 2h is added anti-aging agent, is stirred
40min;
Modified attapulgite clay, nano-titanium dioxide are added into mixture, being uniformly mixed and being placed on revolving speed is 800
Turn/cutter of min in shearing dispersion 10min, ultrasound 10min, is then placed in film-forming machine for mixture under ultrasonic conditions
Middle film forming is to get the keyboard membrane body layer;
(2) preparation of wear-resisting waterproof layer material;Carboxy nitrile rubber latex is weighed according to the proportion, is 0.3g/L's by concentration
Graphene oxide water solution is added drop-wise in latex, is placed in ultrasound 60min in ultrasonic wave, mixture is then transferred to reaction kettle
In, hydrazine hydrate is added, stirs 15min, is warming up to 100 DEG C, is stirred to react 1h;
After reaction, anti-aging agent WL is added into mixture, stirs 10min, mixture is then placed in the chlorine that PH is 2
Change and flocculate in potassium solution, then cleans the latex after flocculating with 100 DEG C of deionized water, then latex is put into film-forming machine and is formed a film,
Up to the wear-resisting waterproof layer;
(3) PET, polyisocyanates, graphene oxide and plasticising the preparation of radiation protective layer material: are weighed respectively according to the proportion
Agent melting mixing, is stirred to react 60min, and mixture is transferred in kneading machine, and nano-titanium dioxide and anti-aging agent is added, and is kneaded
20min forms to get the radiation protective layer;
(4) preparation of keyboard membrane: in sequence respectively by wear-resisting waterproof layer, radiation protective layer, keyboard membrane body layer and electrostatic
Adsorption layer arranges from top to bottom, layer by layer between coat adhesive, then layers of material is placed in heat-sealing machine and carries out heat bonding,
Up to the keyboard membrane.
In step (1) modified attapulgite clay the preparation method comprises the following steps:
It takes natural attapulgite to carry out being crushed to 200~300 mesh, 20 times of attapulgite quality of water is added, stirring is formed
Mud in suspension takes upper suspension centrifugal treating 5min in the centrifuge of 5000 turns/min, vacuum filtration;Filter cake is placed in burning
In bottle, the dilute hydrochloric acid of 2mol/L is added, wherein the volume that the dilute hydrochloric acid is added is with Concave-convex clay rod mass ratio
Then 1mL:10g is stirred at reflux 30min in 60~80 DEG C, vacuum filtration, and is wash with distilled water 6~7 to PH, obtains filter cake,
Filter cake is placed in program in Muffle furnace again and is warming up to 800 DEG C, then constant temperature calcining 1h, be ground to after cooling partial size be 200 mesh i.e.
It can.
In conclusion the high heat radiation anti-radiation keyboard membrane of notebook of the present invention, not only inherits existing keyboard membrane
Waterproof, high permeability, also have preferable heat dissipation effect and excellent shielding property, not only computer normal operation provide
It ensures, it is abnormal to can be avoided the computer work as caused by heat dissipation is difficult, improves the service life of computer and keyboard, simultaneously
Safety guarantee also is provided for computer user, effect reduces the radiation bring harm of keyboard, has preferable use value.
The preparation process of the high heat radiation anti-radiation keyboard membrane of notebook of the present invention is simple, mild condition, preparation process object pollutant
It generates, safety and environmental protection, is suitble to industrialization promotion production.
Specific embodiments of the present invention are described above.It is to be appreciated that the invention is not limited to above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring substantive content of the invention.