CN107300508B - A kind of testing machine of metal material impact resistance corrosive wear - Google Patents

A kind of testing machine of metal material impact resistance corrosive wear Download PDF

Info

Publication number
CN107300508B
CN107300508B CN201710591771.6A CN201710591771A CN107300508B CN 107300508 B CN107300508 B CN 107300508B CN 201710591771 A CN201710591771 A CN 201710591771A CN 107300508 B CN107300508 B CN 107300508B
Authority
CN
China
Prior art keywords
electrode
main shaft
corrosive wear
testing machine
metal material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201710591771.6A
Other languages
Chinese (zh)
Other versions
CN107300508A (en
Inventor
涂小慧
张鹏
邓淑玲
林志丹
李卫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jinan University
Original Assignee
Jinan University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jinan University filed Critical Jinan University
Priority to CN201710591771.6A priority Critical patent/CN107300508B/en
Publication of CN107300508A publication Critical patent/CN107300508A/en
Application granted granted Critical
Publication of CN107300508B publication Critical patent/CN107300508B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to a kind of testing machines of metal material impact resistance corrosive wear, including experimental situation analog portion and electrochemistry microcomputer measuring and controlling part, experimental situation analog portion includes block stamp, main shaft and corrosive wear slot, one end of main shaft connects driving device, the other end of main shaft protrudes into corrosive wear slot, the main shaft protruded into corrosive wear slot is socketed with cricoid Electrode, Electrode is rotated with main shaft, Electrode and spindle insulating, block stamp is set to the top of Electrode, block stamp lower part is connected with sample, in conjunction with mine, the military service operating condition of the raw materials such as machinery workshop ball grinding machine lining board, electrochemical measurement and control system are equipped on impact wear testing machine, make new testing machine that can more specifically simulate the Corrosive Impact Wear situation of ball grinding machine lining board, metal material impact attrition and attack reciprocation can more scientifically be carried out again Research, testing machine design rationally, run smoothly, it is easy to operate and have good reproducibility.

Description

A kind of testing machine of metal material impact resistance corrosive wear
Technical field
The present invention relates to impact resistances, corrosion, wear testing equipment field, rotten more particularly to a kind of metal material impact resistance Lose the testing machine of abrasion.
Background technique
Metal material is in the operating conditions such as mechanical or mine, the especially raw materials such as mine, machinery workshop ball grinding machine lining board, usually Abrasion is undergone while in corrosive medium --- it denudes, when abrasion, metal surface is thinned by mechanism, together The variation of the parameters such as Shi Yinqi current potential, electric current, is different from pure abrasion and pure corrosion, and metal loses in this complex environment operating condition Effect, while being acted on by factors such as physics, machinery, chemistry, electrochemistry.But the method for generic electrochemical test corrosive nature, It is relatively high to instrument and environmental requirement, it needs to measure under metastable stationary state, this is for existing simultaneously abrasion Corrosive wear is inappropriate, is that wear-resistant material loses when cutting the peeling of surface brittleness caused by ditch dug with a plow and Corrosive Impact Wear environment When the main reason for effect, special abrasion equipment is needed to can be carried out test to the electrochemistry of its erodable section.However it is typical Corrosion and impact erosion-wear testing machine is generally used to the three-body-abrasion under research corrosive medium environment.Although can be similar with military service operating condition, But it not can be carried out electrochemical measurement and control.
Summary of the invention
For the technical problems in the prior art, it is rotten that the object of the present invention is to provide a kind of metal material impact resistances The testing machine for losing abrasion can simulate metal material being hit in the operating conditions such as mechanical or mine, corrosion, wear situation, And test can be carried out to the electrochemistry of metal material.
In order to achieve the above object, the present invention adopts the following technical scheme:
A kind of testing machine of metal material impact resistance corrosive wear, including experimental situation analog portion and electrochemistry microcomputer are surveyed Part is controlled, experimental situation analog portion includes block stamp, main shaft and corrosive wear slot, and one end of main shaft connects driving device, main shaft Other end protrude into corrosive wear slot, the main shaft protruded into corrosive wear slot is socketed with cricoid Electrode, research electricity Pole is rotated with main shaft, Electrode and spindle insulating, and block stamp is set to the top of Electrode, and block stamp lower part is connected with examination Sample, main shaft are socketed with red copper ring, and red copper ring is located at outside corrosive wear slot, and red copper ring is rotated with main shaft, corresponding with red copper ring to set There is electrographite brush, electrographite brush is contacted with red copper ring, and main shaft is equipped with keyway, is equipped with conducting wire in keyway, conducting wire one end is electrically connected to Electrode, the other end of conducting wire are electrically connected to red copper ring;Electrochemistry microcomputer measuring and controlling part includes reference electrode, auxiliary electricity Pole, potentiostat and computer, potentiostat are electrically connected in reference electrode, auxiliary electrode and Electrode, constant potential Instrument signal is connected to computer.
Wherein, the side of Electrode is equipped with blind hole, and one end of conducting wire is equipped with elastic plug, and blind hole is inserted for inserted elastic The external cylindrical surface of head, Electrode is working face, and other surfaces of the Electrode in addition to working face and blind hole medial surface are used Epoxy resin sealing.
Wherein, auxiliary electrode is the auxiliary electrode of cyclic annular graphite, and auxiliary electrode is surrounded on around Electrode, auxiliary electrode Offer through-hole, reference electrode is inserted in lead to the hole site, and the top of auxiliary electrode opens up jagged, and upper sample can pass through notch and rush Hit Electrode.
Wherein, reference electrode is Luggin capillary.
Wherein, block stamp lower end is equipped with upper sample collet, and the bottom of upper sample collet is equipped with sample installation position, sample installation position Surface is equipped with polytetrafluoro vinyl chloride, and sample installation position is equipped with sample.
Wherein, main shaft is equipped with the capping of polytetrafluoro vinyl chloride and sealing ring close to the position in the outside of red copper ring.
Wherein, Electrode two sides are equipped with rubber seal, and position of the main shaft on the outside of Electrode is equipped with polytetrafluoro Vinyl chloride sealing shroud.
Wherein, polytetrafluoro vinyl chloride ring is equipped between Electrode and main shaft.
Wherein, driving device includes speed regulating motor and several belt pulleys, and speed regulating motor drives several pulley rotations, Several belt pulleys drive main shaft rotation.
Wherein, testing machine further includes heating and temperature control part, heating and temperature control part include heater, temperature controller with And blender, blender are set to one end of main shaft, blender is located inside corrosive wear slot, and heater is located at corrosive wear slot Bottom, temperature controller control heater temperature.
Generally speaking, the present invention has the advantage that
A kind of testing machine of metal material impact resistance corrosive wear, in conjunction with the raw materials such as mine, machinery workshop ball grinding machine lining board Military service operating condition, electrochemical measurement and control system are equipped on impact wear testing machine, makes new testing machine can be more specifically The Corrosive Impact Wear situation of ball grinding machine lining board is simulated, and can more scientifically carry out metal material impact attrition and attack interaction and make Research, testing machine design rationally, run smoothly, it is easy to operate and have good reproducibility.
Detailed description of the invention
Fig. 1 is a kind of working principle diagram of the testing machine of metal material impact resistance corrosive wear of the present invention.
Fig. 2 is a kind of solid of the experimental situation analog portion of the testing machine of metal material impact resistance corrosive wear of the present invention Structural schematic diagram.
Fig. 3 is the structural schematic diagram of the main shaft of the testing machine of kind of metal material impact resistance corrosive wear of the invention.
Fig. 4 is the upper sample of the testing machine of kind of metal material impact resistance corrosive wear of the invention and the dress of upper sample collet Distribution structure schematic diagram.
Wherein include in Fig. 1 to Fig. 4:
10 --- experimental situation analog portion, 11 --- block stamp, 111 --- upper sample collet, 112 --- upper sample, 113 --- --- --- Electrode, 123 --- red copper ring, 124 --- graphite of main shaft, 122 of polytetrafluoro vinyl chloride thin slice, 12 Brush, 125 --- keyway, 126 --- conducting wire, 127 --- polytetrafluoro vinyl chloride sealing shroud, 128 --- rubber seal, 129 --- polytetrafluoro vinyl chloride ring, 13 --- corrosive wear slot, 14 --- driving devices, 141 --- speed regulating motor, 142 --- Belt pulley.
20 --- electrochemistry microcomputer measuring and controlling part, 21 --- reference electrode, 22 --- auxiliary electrode, 221 --- through-hole, 222 --- notch, 23 --- potentiostat, 24 --- computer,
30 --- --- heater, 32 --- temperature controller, 33 --- blenders of temprature control unit, 31.
Specific embodiment
It is next below that the present invention will be further described in detail.
As shown in Figures 1 to 4, a kind of testing machine of metal material impact resistance corrosive wear, including experimental situation simulation part Divide 10 and electrochemistry microcomputer measuring and controlling part 20, experimental situation analog portion 10 includes block stamp 11, main shaft 12 and corrosive wear slot 13, One end of main shaft 12 connects driving device 14, and the other end of main shaft 12 protrudes into corrosive wear slot 13, protrudes into corrosive wear slot Main shaft 12 in 13 is socketed with cricoid Electrode 122, and Electrode 122 is rotated with main shaft 12, Electrode 122 and main shaft 12 insulation, block stamp 11 are set to the top of Electrode 122, and 11 lower part of block stamp is connected with sample 112, and main shaft 12 is socketed with purple Copper ring 123, red copper ring 123 are located at outside corrosive wear slot 13, and red copper ring 123 is rotated with main shaft 12, corresponding with red copper ring 123 to set There is electrographite brush 124, electrographite brush 124 is contacted with red copper ring 123, and main shaft 12 is equipped with keyway 125, is equipped with conducting wire in keyway 125 126,126 one end of conducting wire is electrically connected to Electrode 122, and the other end of conducting wire 126 is electrically connected to red copper ring 123.Research electricity Pole 122 is mounted on main shaft 12, and is rotated with main shaft 12, and the export of the electric signal of Electrode 122 is relatively difficult.In order to export The electric signal of Electrode 122 is provided with a keyway 125 on the main shaft 12 of testing machine, and the electric signal of Electrode 122 is by keyway Conducting wire 126 in 125 is delivered to red copper ring 123, as shown in figure 3, importing potentiostat 23 by electrographite brush 124 again.Electrochemistry Microcomputer measuring and controlling part 20 includes reference electrode 21, auxiliary electrode 22, potentiostat 23 and computer 24, and potentiostat 23 is distinguished It is electrically connected to reference electrode 21, auxiliary electrode 22 and Electrode 122,23 signal of potentiostat is connected to computer 24.Our department Divide and is made of Electrode 122, reference electrode 21, auxiliary electrode 22, ps-168 potentiostat 23, computer 24 and slurry.It grinds As shown in the placement Fig. 2 for studying carefully electrode 122, reference electrode 21 and auxiliary electrode 22.The major function of this part is exactly to research The electrochemical behavior of electrode 122 is measured and is controlled, dynamic corrosion potential, research electricity including measuring study electrode 122 The cathodic protection of the dynamic of pole 122 and static polarization curve and Electrode 122.Reference electrode 21 in alkaline corrosion system Generally use nonstandard mercury/mercury oxide/sodium hydroxide electrode.
The side of Electrode 122 is equipped with blind hole, and one end of conducting wire 126 is equipped with elastic plug, and blind hole is used for inserted elastic The external cylindrical surface of plug, Electrode 122 is working face, and Electrode 122 is other in addition to working face and blind hole medial surface Surface is sealed with epoxy resin.Electrode 122 is ring-shaped sample, and the external cylindrical surface of ring-shaped sample is working face, sample There are the blind hole through φ 2mm, depth 4mm always, in addition to working face and blind hole, other surface rings of Electrode 122 on one side Oxygen resin seal.When Installation Research electrode 122, the elastic plug of 126 one end of conducting wire is inserted into blind hole, keeps Electrode 122 logical Conducting wire 126 is crossed to be connected with red copper ring 123.The use of polytetrafluoro vinyl chloride sealing shroud 127 and rubber seal 128 shown in Fig. 3 Way is that main shaft 12 is prevented to contact with slurry, and the purposes of polytetrafluoro vinyl chloride ring is to prevent Electrode 122 and main shaft 12 conductive.
Auxiliary electrode 22 is the auxiliary electrode 22 of cyclic annular graphite, and auxiliary electrode 22 is surrounded on around Electrode 122 and consolidates It is scheduled on corrosive wear slot 13, the top of auxiliary electrode 22 opens up jagged 222, and notch 222 is that upper sample 112 moves up and down Channel, as shown in Figure 2, upper sample 112 can pass through notch 222 and impact Electrode 122.Separately there is a diameter on auxiliary electrode 22 φ 5mm through-hole 221, reference electrode 21 are that Luggin capillary is mounted in through-hole 221, as shown in Figure 2.
11 lower end of block stamp is equipped with upper sample collet 111, and the bottom of upper sample collet 111 is equipped with sample installation position, sample peace Dress position surface is equipped with polytetrafluoro vinyl chloride thin slice 113, and sample installation position is equipped with sample 112.During the test, upper examination The lower half portion of sample 112 and its collet is impregnated in the slurry, and upper sample 112 is contacted with Electrode 122, installs sample Insulation measures need to be taken when 112: as shown in figure 4, upper sample 112 is sealed with epoxy resin, upper sample 112 and collet are by polytetrafluoro Vinyl chloride thin slice and two panels semicircle polytetrafluoro vinyl chloride thin slice separate, and tighten upper sample 112 with fastening screw, finally use epoxy The screw thread of the lower half portion of resin seal collet, top half cannot be sealed with epoxy resin.
Main shaft 12 is equipped with the capping of polytetrafluoro vinyl chloride and rubber seal 128 close to the position in the outside of red copper ring 123.It grinds 122 two sides of electrode are studied carefully equipped with rubber seal 128, and main shaft 12 is equipped with polytetrafluoro chloroethene close to the position in 122 outside of Electrode Alkene sealing shroud.Polytetrafluoro vinyl chloride ring 129 is equipped between Electrode 122 and main shaft 12.
Driving device 14 includes speed regulating motor 141 and several belt pulleys 142, and speed regulating motor 141 drives several belts 142 rotation of wheel, several belt pulleys 142 drive main shaft 12 to rotate.In Corrosive Impact Wear part, each belt pulley 142 is adjusted Size, as shown in fig. 1, thus it is possible to vary the frequency of impact of block stamp 11;Adjust the variable speedization research of speed regulating motor 141 The revolving speed of electrode 122;Adjust the height of block stamp 11, adjustable impact energy.The major function of this part is exactly to simulate liner plate Military service operating condition, so that Electrode 122 is born impact, the abrasion of aluminum ore and the corrosion of slurry of upper sample 112, and can be with Carry out the Corrosive Impact Wear test in various slurries.
Wherein, testing machine further includes heating and temperature control part 30, and heating and temperature control part 30 includes heater 31, temperature Control device 32 and blender 33, blender 33 are set to one end of main shaft 12, and blender 33 is located inside corrosive wear slot 13, adds Hot device 31 is located at the bottom of corrosive wear slot 13, and temperature controller 32 controls the temperature of heater 31.This part major function is to guarantee The temperature difference of slurry keeps the uniform pulp components of the slurry temperature in corrosive wear slot 13 uniform between ± 1 DEG C.In order to eliminate Influence of the heater 31 to electrochemical signals is the heater 31 of ceramic tube using shell, and by the weldering of electric wire and heater 31 Mouth and conducting wire are inserted in silicone rubber tube.
Generally speaking, the present invention has the advantage that
A kind of testing machine of metal material impact resistance corrosive wear, in conjunction with the raw materials such as mine, machinery workshop ball grinding machine lining board Military service operating condition, electrochemical measurement and control system are equipped on impact wear testing machine, makes new testing machine can be more specifically The Corrosive Impact Wear situation of ball grinding machine lining board is simulated, and can more scientifically carry out metal material impact attrition and attack interaction and make Research, testing machine design rationally, run smoothly, it is easy to operate and have good reproducibility.
The mentality of designing of this testing machine is as follows:
(1) simulation of Electrode 122 has the sample for absorbing impact load, and upper sample 112 simulates the abrading-ball of ball mill.
(2) impact of the Electrode 122 by upper sample 112.The ballistic work and frequency of impact of upper sample 112 are adjustable.
(3) revolving speed of sample is adjustable, and the rate of wear of Electrode 122 can be adjusted
(4) there is heating device, hot test (100 DEG C of ﹤) can be carried out, temperature is adjustable.
(5) Electrode 122 is immersed in corrosive medium.
(6) for guarantee that corrosive medium is uniform and etching tank in temperature it is uniform, should have agitating device.
(7) there is the electrochemical measurement coupled with computer 24 and control system, the electrochemistry of Electrode 122 can be acquired Signal realizes the electrochemical behavior of lower measurement 122 Corrosive Impact Wear of Electrode of dynamic.
Specifically by taking alumina producer ball grinding machine lining board as an example:
The operating condition that ball grinding machine lining board is on active service has following features:
(1) high temperature: aluminium slurry temperature is generally at 80~90 DEG C, sometimes up to 100 DEG C;
(2) strong basicity: NaOH mass concentration is about 25%, pH14~15;
(3) impact of abrading-ball: abrading-ball is rotated with ball mill, liner plate is detached from when abrading-ball is raised to certain height, with one Fixed speed makees parabolic motion, then falls on liner plate, therefore, percussion of the liner plate by normal direction.
(4) abrasion of aluminum ore: there are aluminum ore particle (Mohs' hardness 7) between abrading-ball and liner plate, impact in abrading-ball In liner plate and thereafter motion process tangentially, aluminum ore is worn (three-body-abrasion) to backing surface.
Under the above harsh operating condition, liner plate had not only born the corrosion of hot highly basic medium, but also bore the three-body mill with impact Damage, meanwhile, it mutually promotes between corrosion and impact wear, so that the service life of liner plate is only had some months, cause to be produced into this way This rising, and influence normal production operating.
The operating condition of corrosive wear is ever-changing, and the corrosive wear mechanism of material is different under different working conditions, researcher Make every effort to simulate working condition progress research work, the more scientific announcement corrosive wear mechanism of ability.Therefore, the research of corrosive wear One of main contents of work are exactly: for the engineering background studied, development test machine.Typical corrosive wear testing machine is big Body can be divided into pin -- board-like corrosive wear testing machine, pin -- ring type corrosive wear testing machine, three-body corrosive wear testing machine and MLD-10 type impact wear testing machine, these four testing machines are generally used to Two body wear and three-body under research corrosive medium environment Abrasion.
Compared with liner plate military service operating condition, pin-board-like corrosive wear testing machine is clearly inappropriate;Three-body corrosive wear Without shock loading in the test parameters of testing machine;Also without shock loading in pin-ring type corrosive wear testing machine test parameters, But it can be carried out electrochemical measurement and control, each component of corrosive wear reciprocation can be measured;MLD-10 type impact wear test The test parameters of machine and liner plate military service operating condition are similar, but not can be carried out electrochemical measurement and control.
The characteristics of present invention is according to above four kinds of testing machines, the military service work of combined aluminum oxide factory raw material workshop ball grinding machine lining board Condition is transformed MLD-10 type impact wear testing machine, equips electrochemical measurement on MLD-10 type impact wear testing machine And control system, make new testing machine that can more specifically simulate the Corrosive Impact Wear situation of ball grinding machine lining board and more scientific Carry out the interactive research of metal material impact attrition and attack in ground.
By carrying out above-mentioned transformation to MLD-10 type impact wear testing machine, new testing machine has following basic mechanical design feature And parameter:
(1) test temperature: room temperature to 100 DEG C, accuracy of temperature control ± 1 DEG C
(2) sample rotation rate: 0~300rpm
(3) frequency of impact: 0~300 beat/min
(4) impact energy :≤50J
(5) corrosive medium: acid, neutral, alkalinity
(6) abrasive grain :≤4mm
(7) specimen size: the shape and size of lower sample, the shape and size of upper sample 112 can according to need change Size.
(8) 13 volume of corrosive wear slot :≤2 liters
(9) it is bent that the dynamic corrosion potential of lower sample, the dynamic for measuring lower sample and static polarization electrochemistry observing and controlling: are measured Line and to lower sample carry out cathodic protection.
The present invention uses machine, is not limited to impact wear testing machine, it may also be used for reciprocating friction abrasion tester sells disk Formula friction wear testing machine.
Test material, based on the metal by corrosive wear, including steel material, nonferrous materials, Metal Substrate are multiple Condensation material etc..The stronger electrode of the inertia such as gold, platinum is used to electrode.
The above embodiment is a preferred embodiment of the present invention, but embodiments of the present invention are not by above-described embodiment Limitation, other any changes, modifications, substitutions, combinations, simplifications made without departing from the spirit and principles of the present invention, It should be equivalent substitute mode, be included within the scope of the present invention.

Claims (9)

1. a kind of testing machine of metal material impact resistance corrosive wear, it is characterised in that: including experimental situation analog portion and electricity Chemical microcomputer measuring and controlling part, experimental situation analog portion include block stamp, main shaft and corrosive wear slot, and one end of main shaft connects driving Device, the other end of main shaft protrude into corrosive wear slot, and the main shaft protruded into corrosive wear slot is socketed with cricoid research electricity Pole, Electrode are rotated with main shaft, Electrode and spindle insulating, and block stamp is set to the top of Electrode, and block stamp lower part is solid It is connected to sample, main shaft is socketed with red copper ring, and red copper ring is located at outside corrosive wear slot, and red copper ring is rotated with main shaft, with red copper Ring is correspondingly provided with electrographite brush, and electrographite brush is contacted with red copper ring, and main shaft is equipped with keyway, is equipped with conducting wire, conducting wire one end in keyway It is electrically connected to Electrode, the other end of conducting wire is electrically connected to red copper ring;Electrochemistry microcomputer measuring and controlling part include reference electrode, Auxiliary electrode, potentiostat and computer, potentiostat are electrically connected in reference electrode, auxiliary electrode and Electrode, Potentiostat signal is connected to computer;Auxiliary electrode is the auxiliary electrode of cyclic annular graphite, and auxiliary electrode is surrounded on Electrode Around, auxiliary electrode offers through-hole, and reference electrode is inserted in lead to the hole site, and the top of auxiliary electrode opens up jagged, upper sample Notch shock Electrode can be passed through.
2. a kind of testing machine of metal material impact resistance corrosive wear described in accordance with the claim 1, it is characterised in that: research electricity The side of pole is equipped with blind hole, and one end of conducting wire is equipped with elastic plug, and blind hole is used for inserted elastic plug, the outside cylinder of Electrode Face is working face, and other surfaces of the Electrode in addition to working face and blind hole medial surface are sealed with epoxy resin.
3. a kind of testing machine of metal material impact resistance corrosive wear described in accordance with the claim 1, it is characterised in that: reference electricity Extremely Luggin capillary.
4. a kind of testing machine of metal material impact resistance corrosive wear described in accordance with the claim 1, it is characterised in that: under block stamp End is equipped with upper sample collet, and the bottom of upper sample collet is equipped with sample installation position, and sample installation position surface is equipped with polytetrafluoro chlorine Ethylene, sample installation position are equipped with sample.
5. a kind of testing machine of metal material impact resistance corrosive wear described in accordance with the claim 1, it is characterised in that: main shaft leans on The position in the outside of nearly red copper ring is equipped with the capping of polytetrafluoro vinyl chloride and sealing ring.
6. a kind of testing machine of metal material impact resistance corrosive wear according to claim 5, it is characterised in that: research electricity Pole two sides are equipped with rubber seal, and position of the main shaft on the outside of Electrode is equipped with polytetrafluoro vinyl chloride sealing shroud.
7. a kind of testing machine of metal material impact resistance corrosive wear described in accordance with the claim 1, it is characterised in that: research electricity Polytetrafluoro vinyl chloride ring is equipped between pole and main shaft.
8. a kind of testing machine of metal material impact resistance corrosive wear described in accordance with the claim 1, it is characterised in that: driving dress It sets including speed regulating motor and several belt pulleys, speed regulating motor drives several pulley rotations, several belt pulleys drive master Axis rotation.
9. according to a kind of testing machine of metal material impact resistance corrosive wear described in claim 1 to 8 any one, feature Be: testing machine further includes heating and temperature control part, and heating and temperature control part includes heater, temperature controller and stirring Device, blender are set to one end of main shaft, and blender is located inside corrosive wear slot, and heater is located at the bottom of corrosive wear slot Portion, temperature controller control the temperature of heater.
CN201710591771.6A 2017-07-19 2017-07-19 A kind of testing machine of metal material impact resistance corrosive wear Active CN107300508B (en)