CN107286765A - A kind of high-temperature resistant coating composition of hydroxyl alkyd resin - Google Patents
A kind of high-temperature resistant coating composition of hydroxyl alkyd resin Download PDFInfo
- Publication number
- CN107286765A CN107286765A CN201610191522.3A CN201610191522A CN107286765A CN 107286765 A CN107286765 A CN 107286765A CN 201610191522 A CN201610191522 A CN 201610191522A CN 107286765 A CN107286765 A CN 107286765A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating composition
- temperature resistant
- resistant coating
- polyacrylamide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-temperature resistant coating composition of hydroxyl alkyd resin, belong to coating material technical field.A kind of high-temperature resistant coating composition of hydroxyl alkyd resin, it is characterized in that, the high-temperature resistant coating composition includes the component of following parts by weight：25-40 parts, 20-30 parts of polyvinyl alcohol, 4-15 parts of expanded graphite, 5-10 parts of formaldehyde, 3-8 parts of unsaturated polyester resin, 3-4 parts of polyacrylamide, 1-3 parts of dispersant, 3-5 parts of polytetrafluoroethylwax wax.Material anti-pressure ability of the present invention is stronger, and service life is long, and resistance to elevated temperatures is splendid.
Description
Technical field
The present invention relates to a kind of coating composition, and in particular to a kind of high-temperature resistant coating composition of hydroxyl alkyd resin, belongs to technical field of coatings.
Background technology
At present, the problem of fire prevention operation of all kinds of buildings is a key.Usually used fire proofing material is generally all kinds of fire prevention coiled materials, fireproof coating, fire prevention clay etc..Coiled material of preventing fires is general based on heat construction, more roasting with fire, and main deficiency is to be bonded not comprehensively, seam, to some privileged sites, bad processing at the position such as corner, the mouth of pipe, easily seeps water, not easy-maintaining after infiltration.The general cold construction of fireproof coating, after fireproof coating is stirred, is once brushed, and seamless construction, bonding force is strong.Its weak point is that intensity is not high, and strong, resistance to elevated temperatures is not poor for self-shield power；And the function of this fire proofing material is relatively simple, construction quality and building service life are largely directly affected.
Accordingly, it would be desirable to a kind of new high-temperature resistant coating composition.
The content of the invention
It is an object of the invention to provide a kind of high-temperature resistant coating composition of hydroxyl alkyd resin, the material anti-pressure ability is stronger, and service life is long, and resistance to elevated temperatures is splendid.
The purpose of the present invention is achieved through the following technical solutions, a kind of high-temperature resistant coating composition of hydroxyl alkyd resin, it is characterized in that, the high-temperature resistant coating composition includes the component of following parts by weight：25-40 parts, 20-30 parts of polyvinyl alcohol, 4-15 parts of expanded graphite, 5-10 parts of formaldehyde, 3-8 parts of unsaturated polyester resin, 3-4 parts of polyacrylamide, dispersant
1-3 parts, 3-5 parts of polytetrafluoroethylwax wax.
It is preferred that, the high-temperature resistant coating composition includes the component of following parts by weight：28-38 parts, 20.7-28.8 parts of polyvinyl alcohol, 4.6-13.9 parts of expanded graphite, 5.4-9.6 parts of formaldehyde, 3.6-7.5 parts of unsaturated polyester resin, 3.1-3.9 parts of polyacrylamide, 1.4-2.6 parts of dispersant, 3.4-4.6 parts of polytetrafluoroethylwax wax.
It is preferred that, the high-temperature resistant coating composition includes the component of following parts by weight：30-36 parts, 22.5-28.0 parts of polyvinyl alcohol, 5.9-12.4 parts of expanded graphite, 5.9-9.0 parts of formaldehyde, 4.8-7.0 parts of unsaturated polyester resin, 3.3-3.8 parts of polyacrylamide, 1.8-2.4 parts of dispersant, 3.6-4.4 parts of polytetrafluoroethylwax wax.
It is preferred that, the high-temperature resistant coating composition includes the component of following parts by weight：32-34 parts, 23.4-27.0 parts of polyvinyl alcohol, 6.9-11.5 parts of expanded graphite, 6.8-8.0 parts of formaldehyde, 5.5-6.5 parts of unsaturated polyester resin, 3.5-3.8 parts of polyacrylamide, 2.0-2.4 parts of dispersant, 3.9-4.2 parts of polytetrafluoroethylwax wax.
It is preferred that, the high-temperature resistant coating composition includes the component of following parts by weight：32.5-33.5 parts, 24.8-26.1 parts of polyvinyl alcohol, 8.9-10.4 parts of expanded graphite, 7.2-7.8 parts of formaldehyde, 5.8-6.2 parts of unsaturated polyester resin, 3.7-3.8 parts of polyacrylamide, 2.2-2.4 parts of dispersant, 4.0-4.2 parts of polytetrafluoroethylwax wax.
Compared with prior art, the invention has the advantages that：
First, anti-pressure ability is stronger, and service life is long, and resistance to elevated temperatures is splendid；With certain elongation percentage, crack resistance is strong, adhesive force is strong, effectively object can be avoided to aoxidize in body surface one layer of waterproof layer of formation.
Second, coating material is easily purchased, low cost, energy-conserving and environment-protective, makes easy.Finished product easy construction, bonding force, stretching resistance are strong, and ageing resistace is good, is not ftractureed with low temperature, the characteristics of high temperature does not play bulging.
Embodiment
Embodiment 1
A kind of high-temperature resistant coating composition, includes the component of following parts by weight：25 parts, 30 parts of polyvinyl alcohol, 4 parts of expanded graphite, 10 parts of formaldehyde, 3 parts of unsaturated polyester resin, 4 parts of polyacrylamide, 1 part of dispersant, 5 parts of polytetrafluoroethylwax wax.
Embodiment 2
A kind of high-temperature resistant coating composition, includes the component of following parts by weight：40 parts, 20 parts of polyvinyl alcohol, 15 parts of expanded graphite, 5 parts of formaldehyde, 8 parts of unsaturated polyester resin, 3 parts of polyacrylamide, 3 parts of dispersant, 3 parts of polytetrafluoroethylwax wax.
Embodiment 3
A kind of high-temperature resistant coating composition, includes the component of following parts by weight：28 parts, 28.8 parts of polyvinyl alcohol, 4.6 parts of expanded graphite, formaldehyde
9.6 parts, 3.6 parts of unsaturated polyester resin, 3.9 parts of polyacrylamide, 1.4 parts of dispersant, 4.6 parts of polytetrafluoroethylwax wax.
Embodiment 4
A kind of high-temperature resistant coating composition, includes the component of following parts by weight：38 parts, 20.7 parts of polyvinyl alcohol, 13.9 parts of expanded graphite, formaldehyde
5.4 parts, 7.5 parts of unsaturated polyester resin, 3.1 parts of polyacrylamide, 2.6 parts of dispersant, 3.4 parts of polytetrafluoroethylwax wax.
Embodiment 5
A kind of high-temperature resistant coating composition, includes the component of following parts by weight：30 parts, 28.0 parts of polyvinyl alcohol, 5.9 parts of expanded graphite, formaldehyde
9.0 parts, 4.8 parts of unsaturated polyester resin, 3.8 parts of polyacrylamide, 1.8 parts of dispersant, 4.4 parts of polytetrafluoroethylwax wax.
Embodiment 6
A kind of high-temperature resistant coating composition, includes the component of following parts by weight：36 parts, 22.5 parts of polyvinyl alcohol, 12.4 parts of expanded graphite, formaldehyde
5.9 parts, 7.0 parts of unsaturated polyester resin, 3.3 parts of polyacrylamide, 2.4 parts of dispersant, 3.6 parts of polytetrafluoroethylwax wax.
Embodiment 7
A kind of high-temperature resistant coating composition, includes the component of following parts by weight：32 parts, 27.0 parts of polyvinyl alcohol, 6.9 parts of expanded graphite, formaldehyde
8.0 parts, 5.5 parts of unsaturated polyester resin, 3.8 parts of polyacrylamide, 2.0 parts of dispersant, 4.2 parts of polytetrafluoroethylwax wax.
Embodiment 8
A kind of high-temperature resistant coating composition, includes the component of following parts by weight：34 parts, 23.4 parts of polyvinyl alcohol, 11.5 parts of expanded graphite, formaldehyde
6.8 parts, 6.5 parts of unsaturated polyester resin, 3.5 parts of polyacrylamide, 2.4 parts of dispersant, 3.9 parts of polytetrafluoroethylwax wax.
Embodiment 9
A kind of high-temperature resistant coating composition, includes the component of following parts by weight：32.5 parts, 26.1 parts of polyvinyl alcohol, 8.9 parts of expanded graphite, formaldehyde
7.8 parts, 5.8 parts of unsaturated polyester resin, 3.8 parts of polyacrylamide, 2.2 parts of dispersant, 4.2 parts of polytetrafluoroethylwax wax.
Embodiment 10
A kind of high-temperature resistant coating composition includes the component of following parts by weight：33.5 parts, 24.8 parts of polyvinyl alcohol, 10.4 parts of expanded graphite, formaldehyde
7.2 parts, 6.2 parts of unsaturated polyester resin, 3.7 parts of polyacrylamide, 2.4 parts of dispersant, 4.0 parts of polytetrafluoroethylwax wax.
Claims (5)
1. a kind of high-temperature resistant coating composition of hydroxyl alkyd resin, it is characterized in that, the high-temperature resistant coating composition includes the component of following parts by weight：25-40 parts, 20-30 parts of polyvinyl alcohol, 4-15 parts of expanded graphite, 5-10 parts of formaldehyde, 3-8 parts of unsaturated polyester resin, 3-4 parts of polyacrylamide, dispersant
1-3 parts, 3-5 parts of polytetrafluoroethylwax wax.
2. the high-temperature resistant coating composition of hydroxyl alkyd resin according to claim 1, it is characterized in that, the high-temperature resistant coating composition includes the component of following parts by weight：28-38 parts, 20.7-28.8 parts of polyvinyl alcohol, 4.6-13.9 parts of expanded graphite, 5.4-9.6 parts of formaldehyde, 3.6-7.5 parts of unsaturated polyester resin, 3.1-3.9 parts of polyacrylamide, 1.4-2.6 parts of dispersant, 3.4-4.6 parts of polytetrafluoroethylwax wax.
3. the high-temperature resistant coating composition of hydroxyl alkyd resin according to claim 1, it is characterized in that, the high-temperature resistant coating composition includes the component of following parts by weight：30-36 parts, 22.5-28.0 parts of polyvinyl alcohol, 5.9-12.4 parts of expanded graphite, 5.9-9.0 parts of formaldehyde, 4.8-7.0 parts of unsaturated polyester resin, 3.3-3.8 parts of polyacrylamide, 1.8-2.4 parts of dispersant, 3.6-4.4 parts of polytetrafluoroethylwax wax.
4. the high-temperature resistant coating composition of hydroxyl alkyd resin according to claim 1, it is characterized in that, the high-temperature resistant coating composition includes the component of following parts by weight：32-34 parts, 23.4-27.0 parts of polyvinyl alcohol, 6.9-11.5 parts of expanded graphite, 6.8-8.0 parts of formaldehyde, 5.5-6.5 parts of unsaturated polyester resin, 3.5-3.8 parts of polyacrylamide, 2.0-2.4 parts of dispersant, 3.9-4.2 parts of polytetrafluoroethylwax wax.
5. the high-temperature resistant coating composition of hydroxyl alkyd resin according to claim 1, it is characterized in that, the high-temperature resistant coating composition includes the component of following parts by weight：32.5-33.5 parts, 24.8-26.1 parts of polyvinyl alcohol, 8.9-10.4 parts of expanded graphite, 7.2-7.8 parts of formaldehyde, 5.8-6.2 parts of unsaturated polyester resin, 3.7-3.8 parts of polyacrylamide, 2.2-2.4 parts of dispersant, 4.0-4.2 parts of polytetrafluoroethylwax wax.