CN107286532A - A kind of water-fast cable cover(ing) - Google Patents
A kind of water-fast cable cover(ing) Download PDFInfo
- Publication number
- CN107286532A CN107286532A CN201710652969.0A CN201710652969A CN107286532A CN 107286532 A CN107286532 A CN 107286532A CN 201710652969 A CN201710652969 A CN 201710652969A CN 107286532 A CN107286532 A CN 107286532A
- Authority
- CN
- China
- Prior art keywords
- parts
- ing
- water
- cable cover
- polyacrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water-fast cable cover(ing), including Corvic, polypropylene, EP rubbers, butadiene-styrene rubber, polyacrylate, bentonite, aluminium hydroxide, isopropyl palmitate, methyl palmitate, carbon black, odium stearate and red phosphorus.The present invention can make cable water-fast, and service life is long.
Description
Technical field
The present invention relates to a kind of water-fast cable cover(ing), belong to power cable technical field.
Background technology
Cable is the lifeblood of modern production, is related to modern Economy Development, and all modern productions of no cable will not be answered
In the presence of so cable is fine or not particularly significant.
The topmost protective layer of cable is exactly outmost sheath, and under some special construction conditions, to cable
It is required that high, it is necessary to the stronger water-resistant capacity of cable cover(ing).
The content of the invention
To overcome above-mentioned deficiency, the object of the invention provides a kind of water-fast cable cover(ing).
The solution of the present invention is as follows：A kind of water-fast cable cover(ing), is made up of according to parts by weight following raw material：Polyvinyl chloride
80 ~ 120 parts of resin, 30 ~ 70 parts of polypropylene, 25 ~ 60 parts of EP rubbers, 25 ~ 50 parts of butadiene-styrene rubber, 20 ~ 40 parts of polyacrylate,
It is 10 ~ 20 parts of bentonite, 5 ~ 10 parts of aluminium hydroxide, 5 ~ 10 parts of isopropyl palmitate, 3 ~ 8 parts of methyl palmitate, 2 ~ 6 parts of carbon black, hard
1 ~ 3 part of 2 ~ 5 parts of resin acid sodium and red phosphorus.
Further, it is made up of according to parts by weight following raw material：85 parts of Corvic, 35 parts of polypropylene, the rubber of second third
35 parts of glue, 30 parts of butadiene-styrene rubber, 25 parts of polyacrylate, 15 parts of bentonite, 6 parts of aluminium hydroxide, 7 parts of isopropyl palmitate, ten
3 parts of six sour 4 parts of methyl esters, 3 parts of carbon black, 3 parts of odium stearate and red phosphorus.
Further, it is made up of according to parts by weight following raw material：90 parts of Corvic, 45 parts of polypropylene, the rubber of second third
40 parts of glue, 35 parts of butadiene-styrene rubber, 30 parts of polyacrylate, 18 parts of bentonite, 7 parts of aluminium hydroxide, 8 parts of isopropyl palmitate, ten
2 parts of six sour 5 parts of methyl esters, 4 parts of carbon black, 2 parts of odium stearate and red phosphorus.
Further, it is made up of according to parts by weight following raw material：100 parts of Corvic, 50 parts of polypropylene, the rubber of second third
45 parts of glue, 40 parts of butadiene-styrene rubber, 35 parts of polyacrylate, 16 parts of bentonite, 8 parts of aluminium hydroxide, 6 parts of isopropyl palmitate, ten
1 part of six sour 6 parts of methyl esters, 5 parts of carbon black, 4 parts of odium stearate and red phosphorus.
Beneficial effects of the present invention：Reasonable mixture ratio of the present invention, the present invention can make cable water-fast, and service life is long.
Embodiment
Embodiment 1
Take Corvic 85kg, it is polypropylene 35kg, EP rubbers 35kg, butadiene-styrene rubber 30kg, polyacrylate 25kg, swollen
Moisten soil 15kg, aluminium hydroxide 6kg, isopropyl palmitate 7kg, methyl palmitate 4kg, carbon black 3kg, odium stearate 3kg and red phosphorus
3kg is mixed and made into cable cover(ing) premix, and cable cover(ing) is then made.
Embodiment 2
Take Corvic 90kg, it is polypropylene 45kg, EP rubbers 40kg, butadiene-styrene rubber 35kg, polyacrylate 30kg, swollen
Moisten soil 18kg, aluminium hydroxide 7kg, isopropyl palmitate 8kg, methyl palmitate 5kg, carbon black 4kg, odium stearate 2kg and red phosphorus
2kg is mixed and made into cable cover(ing) premix, and cable cover(ing) is then made.
Embodiment 3
Take Corvic 100kg, polypropylene 50kg, EP rubbers 45kg, butadiene-styrene rubber 40kg, polyacrylate 35kg,
Bentonite 16kg, aluminium hydroxide 8kg, isopropyl palmitate 6kg, methyl palmitate 6kg, carbon black 5kg, odium stearate 4kg and red
Phosphorus 1kg is mixed and made into cable cover(ing) premix, and cable cover(ing) is then made.
Although the embodiment to the present invention gives detailed description and illustrated above, it should be noted that
We can carry out various equivalent changes and modification according to the conception of the present invention to above-mentioned embodiment, and the function produced by it is made
, all should be within protection scope of the present invention during with the spirit still covered without departing from specification.
Claims (4)
1. a kind of water-fast cable cover(ing), it is characterised in that be made up of according to parts by weight following raw material：Corvic 80 ~
120 parts, 30 ~ 70 parts of polypropylene, 25 ~ 60 parts of EP rubbers, 25 ~ 50 parts of butadiene-styrene rubber, 20 ~ 40 parts of polyacrylate, bentonite
10 ~ 20 parts, 5 ~ 10 parts of aluminium hydroxide, 5 ~ 10 parts of isopropyl palmitate, 3 ~ 8 parts of methyl palmitate, 2 ~ 6 parts of carbon black, odium stearate 2
~ 5 parts and 1 ~ 3 part of red phosphorus.
2. a kind of water-fast cable cover(ing) according to claim 1, it is characterised in that according to parts by weight by following raw material group
Into：85 parts of Corvic, 35 parts of polypropylene, 35 parts of EP rubbers, 30 parts of butadiene-styrene rubber, 25 parts of polyacrylate, swelling
15 parts of soil, 6 parts of aluminium hydroxide, 7 parts of isopropyl palmitate, 4 parts of methyl palmitate, 3 parts of carbon black, 3 parts of odium stearate and red phosphorus 3
Part.
3. a kind of water-fast cable cover(ing) according to claim 1, it is characterised in that according to parts by weight by following raw material group
Into：90 parts of Corvic, 45 parts of polypropylene, 40 parts of EP rubbers, 35 parts of butadiene-styrene rubber, 30 parts of polyacrylate, swelling
18 parts of soil, 7 parts of aluminium hydroxide, 8 parts of isopropyl palmitate, 5 parts of methyl palmitate, 4 parts of carbon black, 2 parts of odium stearate and red phosphorus 2
Part.
4. a kind of water-fast cable cover(ing) according to claim 1, it is characterised in that according to parts by weight by following raw material group
Into：100 parts of Corvic, 50 parts of polypropylene, 45 parts of EP rubbers, 40 parts of butadiene-styrene rubber, 35 parts of polyacrylate, swelling
16 parts of soil, 8 parts of aluminium hydroxide, 6 parts of isopropyl palmitate, 6 parts of methyl palmitate, 5 parts of carbon black, 4 parts of odium stearate and red phosphorus 1
Part.