CN107285687B - 一种用于苗木供水的免烧吸水柱及其生产方法 - Google Patents
一种用于苗木供水的免烧吸水柱及其生产方法 Download PDFInfo
- Publication number
- CN107285687B CN107285687B CN201710661598.2A CN201710661598A CN107285687B CN 107285687 B CN107285687 B CN 107285687B CN 201710661598 A CN201710661598 A CN 201710661598A CN 107285687 B CN107285687 B CN 107285687B
- Authority
- CN
- China
- Prior art keywords
- powder
- brick
- water
- parts
- tile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种用于苗木供水的免烧吸水柱及其生产方法，属于林业建材技术领域，按重量份计，包括以下原料，砖瓦粉60～70份、硅酸盐水泥25～30份、废旧棉花1.0～2.0份、木屑粉5～10份、树叶粉1～5份、干草粉1～5份、水35～40份，所述砖瓦粉包括细砖瓦粉、粗砖瓦粉，且细砖瓦粉、粗砖瓦粉的用量比为1:2.35～2.87。本发明提供的免烧吸水柱，以废砖瓦砾、废旧棉花、普通硅酸盐水泥、木屑、树叶、干草为原料加水混合挤压而成，以废砖瓦和废棉花为主要原料，具有废物利用、保护环境的优点。
Description
技术领域
本发明涉及一种用于苗木供水的免烧吸水柱及其生产方法，属于林业建材技术领域。
背景技术
近年来，随着社会经济和林业科技的快速发展，现代林业中的工厂化育苗和园林立体绿化成为行业发展的新亮点。
目前，林业灌溉的方式多采用喷灌、滴灌等，土壤容易板结，利用率不高、存在浪费水资源现象，也有少数灌溉采取传感器渗灌技术，但需要电能作动力，灌溉设备成本较高，在山区不便于推广。另外，山区干旱河滩地下水位低，造林存活率普遍不高，种植苗木浇水、除草成本高，费时费力。
发明内容
针对上述现有技术存在的问题，本发明提供一种用于苗木供水的免烧吸水柱，适用于干旱河滩的育苗造林，利用吸水柱将地下水吸起来以满足苗木的正常生长。本发明还提供了上述免烧吸水柱的生产方法。
为了实现上述目的，本发明采用的一种用于苗木供水的免烧吸水柱，按重量份计，包括以下原料，砖瓦粉60～70份、硅酸盐水泥25～30份、废旧棉花1.0～2.0份、木屑粉5～10份、树叶粉1～5份、干草粉1～5份、水35～40份，所述砖瓦粉包括细砖瓦粉、粗砖瓦粉，且细砖瓦粉、粗砖瓦粉的用量比为1:2.35～2.87。
作为改进，按重量份计，该免烧吸水柱包括以下原料，砖瓦粉63～66份、硅酸盐水泥25～27份、废旧棉花1.4～1.8份、木屑粉5～7份、树叶粉2～3份、干草粉1～3份、水37～39份。
另外，本发明还提供了一种上述免烧吸水柱的生产方法，具体包括以下步骤：
1)原料的准备：
取废泥砖、泥瓦采用机械粉碎过30-80目筛，制成细砖瓦粉，再取废泥砖、泥瓦采用机械粉碎过5-30目筛，制成粗砖瓦粉，将细砖瓦粉、粗砖瓦粉分别备用；
将废旧棉花弹过后以5倍重量的水浸泡6小时，得湿废旧棉花和浸泡水，另取与浸泡水同重量的清水替换之前的浸泡水备用；
取木屑粉碎过20-40目筛，得木屑粉；
取秋后收集的五种以上等重量的阔叶树落叶，晒干粉碎过10-20目筛，得树叶粉；
取秋后收集的三种以上等重量的禾本科草本植物植株晒干粉碎过20-30目筛，得干草粉；
2)混料：将湿废旧棉花放入新替换的清水中搅拌均匀后，按原料配方先加入细砖瓦粉，边加水边拌料，再依次加入粗砖瓦粉、硅酸盐水泥、木屑粉、树叶粉、干草粉搅拌均匀，制成泥团，揉匀后备用；
3)制坯：将步骤2)制得泥团按规定尺寸，用模具挤压成圆柱形的吸水柱毛坯；
4)凝固：将吸水柱毛坯摆放在通风的地窑内，自然风干凝固；
5)打磨：用电磨打磨凝固后吸水柱的表面，使棉花外露，促进毛细管形成，即得所述免烧吸水柱。
作为改进，所述步骤4)中，风干时间为20-30天，干燥至水份在8％以下。
另外，本发明还提供了一种上述免烧吸水柱的使用方法，将吸水柱在水中浸泡1-2小时，垂直埋在栽植苗木根部的正下方的供水层中即可。
与现有技术相比，本发明的有益效果是：
1、本发明提供的免烧吸水柱，以废砖瓦砾、废旧棉花、普通硅酸盐水泥、木屑、树叶、干草为原料加水混合挤压而成，以废砖瓦和废棉花为主要原料，具有废物利用、保护环境的优点。
2、本发明提供的免烧吸水柱，配方中加入棉花和木屑，提高了吸水柱的成型强度，防止吸水柱在风干时开裂，且在吸水柱内部形成纵横交错的供水网，提高了供水效率；另外，待废旧棉花、木屑相继腐烂后，吸水柱强度降低，在冬冻春融作用下，吸水柱开始自行分解，不产生废物，环保无污染。
3、本发明提供的免烧吸水柱，配方中加入树叶、干草等，主要作用在于提高吸水柱自身饱和含水量，还能给树木提供肥料，调节土壤PH值呈微酸性。
4、本发明免烧吸水柱的生产过程中，先向浸泡的湿废旧棉花中加入细砖瓦粉，主要作用在于提高吸水柱的供水性能，便于形成发达的毛细管吸水系统。用硅酸盐水泥凝固砖瓦粉等制成的吸水柱，具有高吸水性，温度升高时吸水加快，温度降低时吸水减慢，多余的水分自动排出，在一定范围内，自动调节土壤湿度，有利于树木正常生长。
5、本发明的生产过程中，通过硅酸盐水泥将砖瓦粉、木屑粉、树叶粉、干草粉直接凝固而成，不需要烧制，生产简单，节能环保。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚明了，下面通过实施例，对本发明进行进一步详细说明。但是应该理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限制本发明的范围。
除非另有定义，本文所使用的所有的技术术语和科学术语与属于本发明的技术领域的技术人员通常理解的含义相同，本文中在本发明的说明书中所使用的术语只是为了描述具体的实施例的目的，不是旨在于限制本发明。
一种用于苗木供水的免烧吸水柱，按重量份计，包括以下原料，砖瓦粉60～70份、硅酸盐水泥25～30份、废旧棉花1.0～2.0份、木屑粉5～10份、树叶粉1～5份、干草粉1～5份、水35～40份，砖瓦是传统工艺制作的灰泥砖、泥瓦，所述砖瓦粉包括细砖瓦粉、粗砖瓦粉，且细砖瓦粉、粗砖瓦粉的用量比为1:2.35～2.87。
作为改进，按重量份计，该免烧吸水柱包括以下原料，砖瓦粉63～66份、硅酸盐水泥25～27份、废旧棉花1.4～1.8份、木屑粉5～7份、树叶粉2～3份、干草粉1～3份、水37～39份。
另外，本发明还提供了一种上述免烧吸水柱的生产方法，具体包括以下步骤：
1)原料的准备：
取废泥砖、泥瓦采用机械粉碎过30-80目筛，制成细砖瓦粉，再取废泥砖、泥瓦采用机械粉碎过5-30目筛，制成粗砖瓦粉，将细砖瓦粉、粗砖瓦粉分别备用；
将废旧棉花弹过后以5倍重量的水浸泡6小时，得湿废旧棉花和浸泡水，另取与浸泡水同重量的清水替换之前的浸泡水备用(这部分水是另外从自来水管中接取的，原来的浸泡水要倒掉，以保证总用水量不变)；
取木屑粉碎过20-40目筛，得木屑粉；
取秋后收集的五种以上等重量的阔叶树落叶，晒干粉碎过10-20目筛，得树叶粉，常用的阔叶树落叶有国槐、海棠、白蜡、刺槐、红叶李、栾树、杨树、柳树等；
取秋后收集的三种以上等重量的禾本科草本植物植株晒干粉碎过20-30目筛，得干草粉，常用的草本植物植株有早熟禾、狗尾草、芦苇、尖草、谷子、小麦、高粱等；
2)混料：将湿废旧棉花放入新替换的清水中搅拌均匀后，按原料配方先加入细砖瓦粉，边加水边拌料，再依次加入粗砖瓦粉、硅酸盐水泥、木屑粉、树叶粉、干草粉搅拌均匀，制成泥团，揉匀后备用；
3)制坯：将步骤2)制得泥团按规定尺寸，用模具挤压成圆柱形的吸水柱毛坯；
4)凝固：将吸水柱毛坯摆放在通风的地窑内，自然风干凝固；
5)打磨：用电磨打磨凝固后吸水柱的表面，使棉花外露，促进毛细管形成，即得所述免烧吸水柱。
作为改进，所述步骤4)中，风干时间为20-30天，干燥至水份在8％以下。
另外，本发明还提供了一种上述免烧吸水柱的使用方法，将吸水柱在水中浸泡1-2小时，垂直埋在栽植苗木根部的正下方的供水层中即可。
实施例1
一种用于苗木供水的免烧吸水柱，按重量份计，包括以下原料，砖瓦粉63份、硅酸盐水泥25份、废旧棉花1.4份、木屑粉5份、树叶粉2份、干草粉1份、水37份，砖瓦是传统工艺制作的灰泥砖、泥瓦，所述砖瓦粉包括细砖瓦粉、粗砖瓦粉，且细砖瓦粉、粗砖瓦粉的用量比为1:2.35；
上述免烧吸水柱的生产方法，具体包括以下步骤：
1)原料的准备：
取废泥砖、泥瓦采用机械粉碎过30-80目筛，制成细砖瓦粉，再取废泥砖、泥瓦采用机械粉碎过5-30目筛，制成粗砖瓦粉，将细砖瓦粉、粗砖瓦粉分别备用；
将废旧棉花弹过后以5倍重量的水浸泡6小时，得湿废旧棉花和浸泡水，另取与浸泡水同重量的清水替换以前的浸泡水备用；
取木屑粉碎过20-40目筛，得木屑粉；
取秋后收集的五种以上等重量的阔叶树落叶，晒干粉碎过10-20目筛，得树叶粉，用的阔叶树落叶有国槐、海棠、白蜡、刺槐、红叶李、栾树；
取秋后收集的三种以上等重量的禾本科草本植物植株晒干粉碎过20-30目筛，得干草粉，用的草本植物植株有狗尾草、芦苇、尖草、谷子；
2)混料：将湿废旧棉花放入新替换的清水中搅拌均匀后，按原料配方先加入细砖瓦粉，边加水边拌料，再依次加入粗砖瓦粉、硅酸盐水泥、木屑粉、树叶粉、干草粉搅拌均匀，制成泥团，揉匀后备用；
3)制坯：将步骤2)制得泥团按规定尺寸，用模具挤压成圆柱形的吸水柱毛坯；
4)凝固：将吸水柱毛坯摆放在通风的地窑内，自然风干凝固；
5)打磨：用电磨打磨凝固后吸水柱的表面，即得所述免烧吸水柱。
实施例2
一种用于苗木供水的免烧吸水柱，按重量份计，包括以下原料，砖瓦粉65份、硅酸盐水泥26份、废旧棉花1.6份、木屑粉6份、树叶粉2.5份、干草粉2份、水38份，砖瓦是传统工艺制作的灰泥砖、泥瓦，所述砖瓦粉包括细砖瓦粉、粗砖瓦粉，且细砖瓦粉、粗砖瓦粉的用量比为1:2.61；
上述免烧吸水柱的生产方法，具体包括以下步骤：
1)原料的准备：
取废泥砖、泥瓦采用机械粉碎过30-80目筛，制成细砖瓦粉，再取废泥砖、泥瓦采用机械粉碎过5-30目筛，制成粗砖瓦粉，将细砖瓦粉、粗砖瓦粉分别备用；
将废旧棉花弹过后以5倍重量的水浸泡6小时，得湿废旧棉花和浸泡水，另取与浸泡水同重量的清水替换以前的浸泡水备用；
取木屑粉碎过20-40目筛，得木屑粉；
取秋后收集的五种以上等重量的阔叶树落叶，晒干粉碎过10-20目筛，得树叶粉，用的阔叶树落叶有国槐、海棠、白蜡、刺槐、红叶李、栾树、柳树；
取秋后收集的三种以上等重量的禾本科草本植物植株晒干粉碎过20-30目筛，得干草粉，用的草本植物植株有早芦苇、尖草、谷子、小麦；
2)混料：将湿废旧棉花放入新替换的清水中搅拌均匀后，按原料配方先加入细砖瓦粉，边加水边拌料，再依次加入粗砖瓦粉、硅酸盐水泥、木屑粉、树叶粉、干草粉搅拌均匀，制成泥团，揉匀后备用；
3)制坯：将步骤2)制得泥团按规定尺寸，用模具挤压成圆柱形的吸水柱毛坯；
4)凝固：将吸水柱毛坯摆放在通风的地窑内，自然风干凝固；
5)打磨：用电磨打磨凝固后吸水柱的表面，即得所述免烧吸水柱。
实施例3
一种用于苗木供水的免烧吸水柱，按重量份计，包括以下原料，砖瓦粉66份、硅酸盐水泥27份、废旧棉花1.8份、木屑粉7份、树叶粉3份、干草粉3份、水39份，砖瓦是传统工艺制作的灰泥砖、泥瓦，所述砖瓦粉包括细砖瓦粉、粗砖瓦粉，且细砖瓦粉、粗砖瓦粉的用量比为1:2.87；
上述免烧吸水柱的生产方法，具体包括以下步骤：
1)原料的准备：
取废泥砖、泥瓦采用机械粉碎过30-80目筛，制成细砖瓦粉，再取废泥砖、泥瓦采用机械粉碎过5-30目筛，制成粗砖瓦粉，将细砖瓦粉、粗砖瓦粉分别备用；
将废旧棉花弹过后以5倍重量的水浸泡6小时，得湿废旧棉花和浸泡水，另取与浸泡水同重量的清水替换以前的浸泡水备用；
取木屑粉碎过20-40目筛，得木屑粉；
取秋后收集的五种以上等重量的阔叶树落叶，晒干粉碎过10-20目筛，得树叶粉，用的阔叶树落叶有国槐、白蜡、刺槐、栾树、红叶李、杨树、柳树；
取秋后收集的三种以上等重量的禾本科草本植物植株晒干粉碎过20-30目筛，得干草粉，用的草本植物植株有芦苇、尖草、谷子、小麦、高粱；
2)混料：将湿废旧棉花放入新替换的清水中搅拌均匀后，按原料配方先加入细砖瓦粉，边加水边拌料，再依次加入粗砖瓦粉、硅酸盐水泥、木屑粉、树叶粉、干草粉搅拌均匀，制成泥团，揉匀后备用；
3)制坯：将步骤2)制得泥团按规定尺寸，用模具挤压成圆柱形的吸水柱毛坯；
4)凝固：将吸水柱毛坯摆放在通风的地窑内，自然风干凝固；
5)打磨：用电磨打磨凝固后吸水柱的表面，即得所述免烧吸水柱。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换或改进等，均应包含在本发明的保护范围之内。
Claims (4)
1.一种用于苗木供水的免烧吸水柱，其特征在于，按重量份计，包括以下原料，砖瓦粉60～70份、硅酸盐水泥25～30份、废旧棉花1.0～2.0份、木屑粉5～10份、树叶粉1～5份、干草粉1～5份、水35～40份，所述砖瓦粉包括细砖瓦粉、粗砖瓦粉，且细砖瓦粉、粗砖瓦粉的用量比为1:2.35～2.87；
所述免烧吸水柱的生产方法，具体包括以下步骤：
1)原料的准备：
取废泥砖、泥瓦采用机械粉碎过30-80目筛，制成细砖瓦粉，再取废泥砖、泥瓦采用机械粉碎过5-30目筛，制成粗砖瓦粉，将细砖瓦粉、粗砖瓦粉分别备用；
将废旧棉花弹过后以5倍重量的水浸泡6小时，得湿废旧棉花和浸泡水，另取与浸泡水同重量的清水替换之前的浸泡水备用；
取木屑粉碎过20-40目筛，得木屑粉；
取秋后收集的五种以上等重量的阔叶树落叶，晒干粉碎过10-20目筛，得树叶粉；
取秋后收集的三种以上等重量的禾本科草本植物植株晒干粉碎过20-30目筛，得干草粉；
2)混料：将湿废旧棉花放入新替换的清水中搅拌均匀后，按原料配方先加入细砖瓦粉，边加水边拌料，再依次加入粗砖瓦粉、硅酸盐水泥、木屑粉、树叶粉、干草粉搅拌均匀，制成泥团，揉匀后备用；
3)制坯：将步骤2)制得泥团按规定尺寸，用模具挤压成圆柱形的吸水柱毛坯；
4)凝固：将吸水柱毛坯摆放在通风的地窑内，自然风干凝固；
5)打磨：用电磨打磨凝固后吸水柱的表面，使棉花外露，促进毛细管形成，即得所述免烧吸水柱。
2.根据权利要求1所述的一种用于苗木供水的免烧吸水柱，其特征在于，按重量份计，包括以下原料，砖瓦粉63～66份、硅酸盐水泥25～27份、废旧棉花1.4～1.8份、木屑粉5～7份、树叶粉2～3份、干草粉1～3份、水37～39份。
3.根据权利要求1所述一种用于苗木供水的免烧吸水柱，其特征在于，所述步骤4)中，风干时间为20-30天，干燥至水份在8％以下。
4.一种权利要求1或2所述免烧吸水柱的使用方法，其特征在于，将吸水柱在水中浸泡1-2小时，垂直埋在栽植苗木根部的正下方的供水层中即可。