CN107280842A - Self-adhesion gas permeability macromolecule medical splint - Google Patents
Self-adhesion gas permeability macromolecule medical splint Download PDFInfo
- Publication number
- CN107280842A CN107280842A CN201710413100.0A CN201710413100A CN107280842A CN 107280842 A CN107280842 A CN 107280842A CN 201710413100 A CN201710413100 A CN 201710413100A CN 107280842 A CN107280842 A CN 107280842A
- Authority
- CN
- China
- Prior art keywords
- layer
- gas permeability
- self
- medical splint
- macromolecule medical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of self-adhesion gas permeability macromolecule medical splint, separation layer, cured layer and fixation layer are followed successively by from top to bottom；The cured layer is made up of the non-woven fabrics base fabric for being impregnated with water cure polyurethane, and some air-vents are uniformly offered on the cured layer；The fixation layer is the nonwoven layer for being uniformly coated with striated adhesive tape.Cured layer is made up of the non-woven fabrics base fabric for being impregnated with water cure polyurethane in the present invention, and some air-vents are offered thereon, the weight of clamping plate is effectively reduced, while gas permeability preferably, accelerates the healing in affected part；Fixation layer is the nonwoven layer for being coated with low viscosity viscose glue, can be directly adhered on the skin of patient, reduces manpower and the time of bandage winding, and is easier to remove, and reduces the pain of the adhesion skin when removing.
Description
Technical field
The present invention relates to medical treatment consumptive materials field, more particularly to a kind of non-woven fabric clamp plate.
Background technology
When orthopaedics therapy fractured bones misplace, the material such as conventional bamboo chip, plank, gypsum is shaped to injured bone
Treatment, wherein bamboo chip or plank are in treatment using quite inconvenience, and the probability for secondary damage occur is higher.Both materials are used for a long time
Material, will cut down substantial amounts of trees and bamboo, be unfavorable for environmental protection and greening；And do mould using gypsum and fix treatment, when having sizing
Between it is long, without toughness, air-locked shortcoming.
At present clinically, when patients with fractures needs to carry out outer fixed, increasing doctor uses Medical macromolecular splint.
The Medical macromolecular splint series of advantages such as have intensity height, light weight, good permeability, setting rate fast, applied widely.Doctor
Constituted, need to be twined when using with common gauze bandage with the main cleat body by parcel bag and in parcel bag of Macromolecular splint
It is equally also more time-consuming around plastotype and fixation is carried out.
The content of the invention
The present invention solves the technical problem of a kind of high set gas permeability macromolecule medical splint of self-adhering-type is provided, subtract
The manpower in bandage winding process and time are lacked, there is anchorage height, good permeability, good fixing effect, reduce
The pain of adhesion skin during dismounting.
In order to solve the above technical problems, one aspect of the present invention is：
A kind of self-adhesion gas permeability macromolecule medical splint is provided, separation layer, cured layer and fixation layer is sequentially consisted of；It is described
Cured layer is made up of the non-woven fabrics base fabric for being impregnated with water cure polyurethane, if uniform offer parches in the non-woven fabrics base fabric
Stomata；The fixation layer be the micropore in the micro-porous permeable adhesive plaster for being coated with viscose glue, the micro-porous permeable adhesive plaster a diameter of 2 ~
3mm。
In a preferred embodiment of the present invention, the separation layer is water repellent nonwoven layer.
In a preferred embodiment of the present invention, the viscose glue on the micro-porous permeable adhesive plaster is distributed in striated.
In a preferred embodiment of the present invention, the grammes per square metre of the separation layer is 90 ~ 100g/m2。
In a preferred embodiment of the present invention, the grammes per square metre of the cured layer is 720 ~ 750g/m2。
In a preferred embodiment of the present invention, the grammes per square metre of the fixation layer is 300 ~ 380g/m2。
The beneficial effects of the invention are as follows：Self-adhesion gas permeability macromolecule medical splint of the present invention, cured layer is by being impregnated with water
The non-woven fabrics base fabric for solidifying polyurethane is constituted, and some air-vents are offered thereon, the weight of clamping plate is effectively reduced, and is breathed freely simultaneously
Property preferably, accelerate the healing in affected part；Fixation layer is the nonwoven layer for being coated with low viscosity viscose glue, can be directly adhered to patient's
On skin, the manpower in bandage winding process and time are reduced, and is easier to remove, the adhesion skin when removing is reduced
Pain.
Brief description of the drawings
Fig. 1 is the structural representation of a preferred embodiment of the present invention；
The mark of each part is as follows in accompanying drawing：1st, fixation layer, 2, cured layer, 21, air-vent, 3, separation layer.
Embodiment
Presently preferred embodiments of the present invention is described in detail below in conjunction with the accompanying drawings, so that advantages and features of the invention energy
It is easier to be readily appreciated by one skilled in the art, apparent is clearly defined so as to be made to protection scope of the present invention.
A kind of self-adhesion gas permeability macromolecule medical splint, sequentially consists of separation layer 3, cured layer 2 and fixation layer 3.
The separation layer 3 is water repellent nonwoven layer, and the cured layer 2 is made up of non-woven fabrics infiltration polyurethane glue, institute
State and some air-vents 21 are uniformly offered on cured layer 2；The fixation layer 1 is the micro-porous permeable adhesive plaster for being coated with viscose glue, described
The diameter of micropore is preferably 3mm, micro-porous permeable adhesive plaster in a diameter of 2 ~ 3mm of micropore in micro-porous permeable adhesive plaster, the present embodiment
On viscose glue can for whole face coating, can also in striated distribution（As shown in Figure 1）, viscose glue hold viscosity be less than 2.5mm, should
Viscosity can keep the Pasting of fixation layer 1 on skin, ensure that fixation layer 1 will not tear skin when removing.
The grammes per square metre of the separation layer 3 is 90 ~ 100g/m2, the grammes per square metre of the cured layer 1 is 720 ~ 750g/m2, the set
The grammes per square metre of layer 2 is 300 ~ 380g/m2。
Self-adhesion gas permeability macromolecule medical splint of the present invention, separation layer 3 is water repellent nonwoven layer, can be effectively isolated steam,
Keep the volume drying of clamping plate；Cured layer 2 is constituted for the non-woven fabrics base fabric of infiltration polyurethane glue, is offered thereon some ventilative
Hole 21, is effectively reduced the weight of clamping plate, while gas permeability preferably, accelerates the healing in affected part；Fixation layer 1 is to be coated with viscose glue
Nonwoven layer, and on fixation layer 1 have uniform micropore design, can be directly adhered on the skin of patient, reduce taut
Manpower and time during band winding, and be easier to remove, due to the adhesive tape of the striated of the low viscosity of use, reduce
The pain of adhesion skin when removing.Fixation layer 1 employs the higher non-woven fabrics of grammes per square metre, and also increase that patient uses is comfortable
Property.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
Equivalent structure or equivalent flow conversion that bright specification and accompanying drawing content are made, or directly or indirectly it is used in other related skills
Art field, is included within the scope of the present invention.
Claims (6)
1. a kind of self-adhesion gas permeability macromolecule medical splint, it is characterised in that sequentially consist of separation layer, cured layer and consolidate
Layer；The cured layer is made up of the non-woven fabrics base fabric for being impregnated with water cure polyurethane, is uniformly opened in the non-woven fabrics base fabric
Provided with some air-vents；The fixation layer is the micropore in the micro-porous permeable adhesive plaster for being coated with viscose glue, the micro-porous permeable adhesive plaster
A diameter of 2 ~ 3mm.
2. self-adhesion gas permeability macromolecule medical splint according to claim 1, it is characterised in that the separation layer is water repellent
Nonwoven layer.
3. self-adhesion gas permeability macromolecule medical splint according to claim 1, it is characterised in that the micro-porous permeable adhesive plaster
On viscose glue in striated be distributed.
4. self-adhesion gas permeability macromolecule medical splint according to claim 1, it is characterised in that the grammes per square metre of the separation layer
For 90 ~ 100g/m2。
5. self-adhesion gas permeability macromolecule medical splint according to claim 1, it is characterised in that nonwoven in the cured layer
The grammes per square metre of cloth base fabric is 720 ~ 750g/m2。
6. self-adhesion gas permeability macromolecule medical splint according to claim 1, it is characterised in that the grammes per square metre of the fixation layer
For 300 ~ 380g/m2。