CN107268175B - Production process of advertising cloth - Google Patents
Production process of advertising cloth Download PDFInfo
- Publication number
- CN107268175B CN107268175B CN201610215329.9A CN201610215329A CN107268175B CN 107268175 B CN107268175 B CN 107268175B CN 201610215329 A CN201610215329 A CN 201610215329A CN 107268175 B CN107268175 B CN 107268175B
- Authority
- CN
- China
- Prior art keywords
- cloth
- soaking paste
- dacron thread
- agent
- pond
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a production process of advertisement cloth, which aims to solve the problem that the cloth is easy to deform, and the technical scheme is characterized in that: weaving the cloth: the method comprises the following steps of interweaving and overlapping and weaving uniformly distributed transverse polyester yarns and uniformly distributed vertical polyester yarns, wherein reset polyester yarns are respectively woven in the transverse polyester yarns and the vertical polyester yarns in an inserting mode, and gaps exist between weaving nodes to form meshes; and (3) slurry dipping treatment: introducing the woven cloth into a slurry dipping pool for slurry dipping treatment; cleaning: putting the cloth subjected to the pulp soaking treatment into water containing a softening agent for cleaning; tentering, setting: tentering and shaping the cleaned cloth; drying: and drying the cloth subjected to tentering setting at constant temperature. The cloth produced by the production process of the advertising cloth is not easy to deform.
Description
Technical field
The present invention relates to weaving show and colour fields, more specifically, it relates to a kind of production technology of advertising cloth.
Background technique
With the development of the society, extensive stock greatly enriches, the industries cloth such as vertically hung scroll banner, trade display window, curtain
Demand not only increases, but also need product to have air brushing effect is good, the excellent performance of gas permeability.In addition, with outdoor media
Development, show and colour are gradually sent out to direction that is beautiful, novel, attracting consumer's eyeball by the effect of single billboard publicity enterprise
Exhibition, and the characteristics of combination media and carrier, development is combined to multiplicity such as functionality.Due to the demand of these different performances, net
Eye cloth is just widely used.Eyelet fabric has an advantage that 1, good ventilative, daylighting effect, has to building good
Protective effect, will not put on advertising media because of exterior wall, and increase the external endurance of building；It is indoor also not because advertisement and
Seriously affect the effect of daylighting.2, cost is reduced, easily constructs, just operates, because it is eyed structure, is reaching the same of advertising results
When, it is very light, for installing advertisement media, the too many auxiliary facility such as backboard is not needed, cost input is greatly reduced,
And it installs and is very easy to.3, excellent air brushing eyelet fabric can accomplish single side air brushing, the excellent results of double-sided display pattern, this
On the one hand process when air brushing is reduced, the use of the consumptive materials such as ink is in addition also greatly saved, reduces advertising cost.4, it opens up
It lookes at using eyelet fabric when building, eyelet fabric when in use, has good compatibility, while completing to reflect promotional content,
The distance between visitor and exhibiter will not be hindered, there is a very big space utilization.Due to above advantages, mesh
Cloth is undoubtedly the fine carrier of ultra-wide outdoor media, so in recent years, eyelet fabric is just developed with surprising growth rate.In mall
Exterior wall, the metope of the high building in construction, large-scale exhibition exhibition booth build, may all use this material.However it is traditional
Numerial code spray drawing eyelet fabric in process of production, unbalance stress is easily generated due to the complexity of tissue, in soaking paste setting process and
The problems such as causing eyelet fabric skew of weft, deformation, influences the aesthetics and service performance of product.
Summary of the invention
In view of the deficiencies of the prior art, the present invention intends to provide a kind of on-deformable advertising cloth.
Above-mentioned technical purpose of the invention has the technical scheme that a kind of production work of advertising cloth
Skill:
One, cloth weaves: evenly arranged lateral dacron thread and evenly arranged vertical dacron thread are overlapping braiding,
It is respectively interposed in lateral dacron thread and vertical dacron thread and is woven with reset dacron thread, there are gap compositions between the braiding node
Mesh；
Two, the pre-heat treatment: woven cloth preheat by vapor；
Three, soaking paste is handled: the cloth after preheating being dipped into soaking paste pond, soaking paste processing is carried out；
Four, it cleans: the cloth handled well by soaking paste being put into the water containing softening agent and is cleaned；
Five, sizing: the cloth after cleaning is carried out stentering forming by tentering；
Six, drawing-off: 15 roller drafting machines uniformly draw cloth thin；
Seven, it dries: the cloth after stentering forming being subjected to constant temperature drying, temperature is adjusted to 90 DEG C ~ 135 DEG C.
By using above-mentioned technical proposal, the production technology of entire advertising cloth, will be evenly arranged since cloth braiding
Lateral dacron thread and evenly arranged vertical dacron thread are overlapping braiding, when braiding, stay between the intersection point of braiding
There is gap, so that net hole is formed, by netting the formation in hole, when cloth is pullled, the lateral dacron thread and vertical terylene of cloth
Silk is carried out laterally pullling with vertical and cloth being made to be restored to nature again, be unlikely to deform after stress is mobile；Braiding
After the completion, woven cloth is preheated, using the heat boiling cloth of vapor, the temperature of cloth is improved, is come
The temperature in soaking paste pond is adapted to, soaking paste effect is improved；Then cloth is placed in soaking paste pond and is impregnated, carried out soaking paste processing, make stock tank
The material of middle addition is sufficiently fused in cloth, and the performance of cloth is made to get a promotion；Then by soaking paste, treated that cloth is put into
It is cleaned in service sink, softening agent is also added into service sink, joined softening agent during cleaning, cloth is made to have one
Fixed flexibility, enhancing cloth are less likely to occur to be broken when stress；Then stentering forming is carried out to cloth, cloth is led to
Cross tentering and sizing；Then the uniformly drawing for cloth being carried out cloth by the drafting machine of 15 rollers is thin, is further formed to cloth,
It has been finally completed the basic production of cloth, cloth is finally subjected to constant temperature drying.
The present invention is further arranged to: the composition of the slurry are as follows: and fluorescent whitening agent 8 ~ 12%, epoxy curing agent 2 ~
5%, smooth agent 5 ~ 8%, starch distintegrant 5 ~ 8%, residual components are water.
By using above-mentioned technical proposal, fluorescent whitening agent joined in slurry pool, content is 8 ~ 12%, fluorescent brightening
Agent increases the white content of cloth, joined epoxy curing agent in pond, and content is 2 ~ 5%, so that cloth has certain heavily fortified point
Solidity joined smooth agent in pond, and content is 5 ~ 8%, increases the lubricity of cloth, joined starch distintegrant in pond, content is
5 ~ 8%, increase the breaking strength of cloth, residual components are water.
The present invention is further arranged to: cloth speed is 3m/min during the soaking paste, controls cloth by tensioning controller
Tensile force is 150N.
The speed of 3m/min is kept to advance, as far as possible during cloth is carried out soaking paste by using above-mentioned technical proposal
Make the abundant soaking paste of cloth, promotes the performance of cloth effectively, of the mobile tensioning controller control cloth of control cloth
Clamp force is 150N, and cloth is sufficiently strutted, cloth is made to fully absorb additive in stock tank.
The present invention is further arranged to: the idler wheel of two compressions, the idler wheel and cloth are rotatably connected in the soaking paste pond
Material contradicts connection.
By using above-mentioned technical proposal, when cloth moves in stock tank, cloth, which also contradicts, is connected to two compressions
Idler wheel improves the fusion degree of the additive and cloth in stock tank by roller compression cloth.
The present invention is further arranged to: the roller surface is connected with resistance wire, and constant temperature is 160 DEG C
By using above-mentioned technical proposal, it is also connected with resistance wire on the surface of idler wheel, by being powered to resistance wire, makes to roll
The surface temperature of wheel improves, and accelerates the fusion of additive and cloth, and setting temperature is 160 DEG C, reaches optimum efficiency.
The present invention is further arranged to: the ratio of the softening agent is 20%, and the ratio of water is 80%.
By using above-mentioned technical proposal, when cleaning cloth, the softness of cloth, is mentioned in order to further increase
The ability of the resistance to deformation of high cloth joined the softening agent containing 20% in service sink, remaining is then moisture.
The present invention is further arranged to: cored nylon wire is also interspersed in the warp and weft.
By using above-mentioned technical proposal, it is also interspersed with cored nylon wire in warp and weft, enhances the anti-of cloth
The structural strength of drawing property and cloth itself.
The present invention is further arranged to: the cloth is sprayed with brightening agent during the drying process.
By using above-mentioned technical proposal, finally in order to further enhance the whiteness of cloth, sprayed during drying
There is brightening agent.
In conclusion the invention has the following advantages: cloth produced by the invention is unlikely to deform, and pliability
Height, it is anti-pull.
Specific embodiment
Below with reference to embodiment, the present invention will be described in detail.
The production technology of entire advertising cloth is since cloth braiding, by evenly arranged lateral dacron thread and evenly arranged
Vertical dacron thread is overlapping braiding, and when braiding, there are gaps between the intersection point of braiding, so that net hole is formed, it is logical
The formation for crossing net hole, when cloth is pullled, the lateral dacron thread and vertical dacron thread of cloth carry out again after stress is mobile
Pullling and cloth can be made to be restored to nature laterally and vertically, is unlikely to deform, cored is also interspersed in warp and weft
Nylon wire enhances the pull resistance of cloth and the structural strength of cloth itself；After the completion of braiding, cloth is placed in soaking paste pond and is soaked
Bubble carries out soaking paste processing, is fused to the material being added in stock tank sufficiently in cloth, the performance of cloth is made to get a promotion, starching
It joined fluorescent whitening agent in material pond, content is 8 ~ 12%, can use the fluorescent brightening of Hebei San Chuan Chemical Co., Ltd. sound field
Agent, fluorescent whitening agent can excite incident ray to generate fluorescence, so that contaminated substance is obtained the sparkling effect of similar fluorite, make
The substance that naked eyes are seen is very white, increases the white content of cloth, joined epoxy curing agent in pond, and content is 2 ~ 5%, can
To increase the robustness of cloth, improve cloth using the epoxy curing agent of Shenzhen Hui Te Chemical Co., Ltd. production
Tensile strength joined smooth agent in pond, and content is 5 ~ 8%, can fly the smooth agent of hair Chemical Manufacture, smooth agent using Shanghai
It is a kind of with excellent soft, smooth, bright, feel aqueous, environmental protective organic silicon emulsion, is grade textiles of new generation
Soft finishing agent can assign softness, the smooth effect of cloth brilliance, joined starch distintegrant in pond, and content is 5 ~ 8%, can be with
The starch distintegrant produced using Zhengzhou Yin He dextrin Co., Ltd, increases the breaking strength of cloth, residual components are water, are being soaked
During slurry, cloth is passed through to the idler wheel of two compressions, by roller compression cloth, so that the additive in pond is sufficiently fused to
In cloth, in order to further enhance amalgamation, it is connected with resistance wire on the surface of idler wheel, increases the Contact Temperature with cloth, it is constant
At 160 DEG C, i.e., the structure that will not destroy cloth itself can accelerate cloth to merge additive again, and cloth is carried out to the process of soaking paste
In, it keeps the speed of 3m/min to advance, makes the abundant soaking paste of cloth as far as possible, promote the performance of cloth effectively, control cloth
The tensile force of mobile tensioning controller control cloth is 150N, and cloth is sufficiently strutted, cloth can be made to fully absorb in stock tank
Additive, then by soaking paste, treated that cloth is put into service sink cleans, and joined softening agent during cleaning, soft
The ratio of agent and water is 1:4, and being added, which excessively will lead to, does not wash clean clearly, can be using the production of Hangzhou Lv Dian Chemical Co., Ltd.
Softening agent, softening agent can make cloth have certain flexibility, fiber itself can be made to have and processing conditions phase using softening agent
The flexible smooth of adaptation makes cloth be less likely to occur to be broken when stress to avoid damage；Then cloth is drawn
Width sizing completes the basic production of cloth by cloth by tentering and sizing, and cloth is finally carried out constant temperature drying,
Brightening agent is added again during drying, further enhances the white brightness of cloth.
By the above scheme, reach be unlikely to deform, pliability is higher, the cloth of tension.
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
Those of ordinary skill for, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (3)
1. a kind of production technology of advertising cloth, it is characterised in that:
One, cloth weaves: evenly arranged lateral dacron thread and evenly arranged vertical dacron thread are overlapping braiding, transverse direction
It is respectively interposed in dacron thread and vertical dacron thread and is woven with reset dacron thread, there are gaps to constitute mesh between braiding node；
Two, the pre-heat treatment: woven cloth is preheated by vapor；
Three, soaking paste is handled: the cloth after preheating being dipped into soaking paste pond, soaking paste processing is carried out；
Four, it cleans: the cloth handled well by soaking paste being put into the water containing softening agent and is cleaned；
Five, sizing: the cloth after cleaning is carried out stentering forming by tentering；
Six, drawing-off: 15 roller drafting machines uniformly draw cloth thin；
Seven, it dries: the cloth after drawing-off being subjected to constant temperature drying, temperature is adjusted to 90 DEG C ~ 135 DEG C；Slurry in the soaking paste pond
Composition are as follows: fluorescent whitening agent 8 ~ 12%, epoxy curing agent 2 ~ 5%, smooth agent 5 ~ 8%, starch distintegrant 5 ~ 8%, it is remaining at
It is divided into water；Cloth speed is 3m/min during the soaking paste, and controlling cloth tensile force by tensioning controller is 150N；The soaking paste
The idler wheel of two compressions is rotatably connected in pond, the idler wheel and cloth contradict connection；The roller surface is connected with resistance wire,
Constant temperature is 160 DEG C；Cored nylon wire is also interspersed in the transverse direction dacron thread and vertical dacron thread.
2. a kind of production technology of advertising cloth according to claim 1, it is characterised in that: the ratio of the softening agent is
20%, the ratio of water is 80%.
3. a kind of production technology of advertising cloth according to claim 1, it is characterised in that: the cloth is during the drying process
It is sprayed with brightening agent.