CN107266755A - A kind of rubber composition - Google Patents
A kind of rubber composition Download PDFInfo
- Publication number
- CN107266755A CN107266755A CN201710665872.3A CN201710665872A CN107266755A CN 107266755 A CN107266755 A CN 107266755A CN 201710665872 A CN201710665872 A CN 201710665872A CN 107266755 A CN107266755 A CN 107266755A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber composition
- composition according
- rubber
- phenolic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of rubber composition, is made up of the raw material components of following number：20 parts~40 parts of neoprene, 15 parts~25 parts of ethylene propylene diene rubber, 10~14 parts of lauryl sulfate tri ethanol ammonium salt, 10~14 parts of zinc ricinate, 42% 10~12 parts of chlorinated paraffin, 10~18 parts of laurate, N, 10~12 parts of N dimethylanilines, 12~16 parts of benzoic ether, 4~6 parts of diglycidyl ether, 6~10 parts of benzimidazole, 1 part~1.3 parts of age resistor, 0.3 part~1 part of crosslinking agent, 3~12 parts of phenolic resin, 0.2 part~0.6 part of vulcanizing agent, rubber tube of the present invention is processed using plurality of raw materials, gained rubber tube is with low cost, resistance to acids and bases, resistance to ag(e)ing, anti-wear performance is preferable, with lasting elasticity.
Description
Technical field
The present invention relates to field of rubber technology, and in particular to a kind of rubber composition.
Background technology
The rubber tube industry of China passes through the development of more than 50 years, and indispensable supporting effect is served to national economy,
Raising and new diseases especially with China's Mechanization Level, rubber tube industry are constantly mutually oozed with association area
Thoroughly, application and the field of rubber tube band have been opened up, product is widely used in coal, metallurgy, cement, harbour, mine, stone
The fields such as oil, automobile, weaving, light industry, engineering machinery, building, ocean, agricultural, Aeronautics and Astronautics.The rubber according to contained by rubber tube
The difference of composition, rubber tube is divided into nitrile rubber pipe, fluorine rubber-pipe, neoprene pipe, natural rubber pipe, ethylene-propylene-diene monomer sebific duct
With silicone rubber tube etc..
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of rubber composition.
The present invention is achieved through the following technical solutions：
A kind of rubber composition, is made up of the raw material components of following number：20 parts~40 parts of neoprene, ethylene-propylene-diene monomer
15 parts~25 parts of glue, 10~14 parts of lauryl sulfate tri ethanol ammonium salt, 10~14 parts of zinc ricinate, 42% chlorinated paraffin 10~
12 parts, 10~18 parts of laurate, N, 10~12 parts of accelerine, 12~16 parts of benzoic ether, diglycidyl ether 4~6
Part, 6~10 parts of benzimidazole, 1 part~1.3 parts of age resistor, 0.3 part~1 part of crosslinking agent, 3~12 parts of phenolic resin, vulcanizing agent
0.2 part~0.6 part.
It is preferred that, the phenolic resin is alkyl-modified phenolic resin.
It is preferred that, the age resistor is cellosolvo.
It is preferred that, the crosslinking agent is cumyl hydroperoxide or trimethylolethane or allyl glycidol
The one or two of ether.
It is preferred that, the vulcanizing agent is peroxidized t-butyl perbenzoate, 3- amino crotonic acid cyanogen ethyl ester or amino trifluoro
The one or two of ethyl crotonate.
The beneficial effects of the present invention are：Rubber tube of the present invention is processed using plurality of raw materials, gained rubber tube cost
Cheap, resistance to acids and bases, resistance to ag(e)ing, anti-wear performance are preferable, with lasting elasticity.
Embodiment
Embodiment:A kind of rubber composition, is made up of the raw material components of following number：20 parts~40 parts of neoprene, three
First 15 parts~25 parts of EP rubbers, 10~14 parts of lauryl sulfate tri ethanol ammonium salt, 10~14 parts of zinc ricinate, 42% chlorination
10~12 parts of paraffin, 10~18 parts of laurate, N, 10~12 parts of accelerine, 12~16 parts of benzoic ether, two shrink sweet
Oily 4~6 parts of ether, 6~10 parts of benzimidazole, 1 part~1.3 parts of age resistor, 0.3 part~1 part of crosslinking agent, 3~12 parts of phenolic resin,
0.2 part~0.6 part of vulcanizing agent.
Further, the phenolic resin is alkyl-modified phenolic resin.
Further, the age resistor is cellosolvo.
Further, the crosslinking agent is that cumyl hydroperoxide or trimethylolethane or allyl glycidyl are sweet
The one or two of oily ether.
Further, the vulcanizing agent is peroxidized t-butyl perbenzoate, 3- amino crotonic acid cyanogen ethyl ester or amino three
The one or two of fluorine ethyl crotonate.
The beneficial effects of the present invention are：Rubber tube of the present invention is processed using plurality of raw materials, gained rubber tube cost
Cheap, resistance to acids and bases, resistance to ag(e)ing, anti-wear performance are preferable, with lasting elasticity.
Described above is only the preferred application implementation mode of the present invention, it is noted that for the common skill of the art
For art personnel, without departing from the technical principles of the invention, some improvement can also be made.
Claims (5)
1. a kind of rubber composition, it is characterised in that：It is made up of the raw material components of following number：20 parts~40 parts of neoprene,
15 parts~25 parts of ethylene propylene diene rubber, 10~14 parts of lauryl sulfate tri ethanol ammonium salt, 10~14 parts of zinc ricinate, 42% chlorine
10~12 parts of fossil waxes, 10~18 parts of laurate, N, 10~12 parts of accelerine, 12~16 parts of benzoic ether, two are shunk
4~6 parts of glycerin ether, 6~10 parts of benzimidazole, 1 part~1.3 parts of age resistor, 0.3 part~1 part of crosslinking agent, phenolic resin 3~12
Part, 0.2 part~0.6 part of vulcanizing agent.
2. rubber composition according to claim 1, it is characterised in that：The phenolic resin is alkyl-modified phenolic aldehyde tree
Fat.
3. rubber composition according to claim 1, it is characterised in that：The age resistor is cellosolvo.
4. rubber composition according to claim 1, it is characterised in that：The crosslinking agent be cumyl hydroperoxide or
The one or two of person's trimethylolethane or allyl glycidyl ether.
5. rubber composition according to claim 1, it is characterised in that：The vulcanizing agent is the tertiary fourth of perbenzoic acid
The one or two of ester, 3- amino crotonic acid cyanogen ethyl ester or amino trifluoroacetic ethyl crotonate.