CN107245298A - A kind of preparation method of the fiber reinforced polypyrrole anticorrosive paint of epoxidation - Google Patents
A kind of preparation method of the fiber reinforced polypyrrole anticorrosive paint of epoxidation Download PDFInfo
- Publication number
- CN107245298A CN107245298A CN201710600593.9A CN201710600593A CN107245298A CN 107245298 A CN107245298 A CN 107245298A CN 201710600593 A CN201710600593 A CN 201710600593A CN 107245298 A CN107245298 A CN 107245298A
- Authority
- CN
- China
- Prior art keywords
- weight
- fiber
- added
- stirred
- hours
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the preparation method of the fiber reinforced polypyrrole anticorrosive paint of epoxidation; fiber and monomer are formed effective crosslinking by the coating of the present invention; can be with the compatibility between reinforcing fiber and polymer; improve the stability_intensity of finished product film; fiber can also improve the toughness and impact strength of finished product film simultaneously; the film of the present invention and the adhesiveness of metallic substrate surface are good, can effectively improve the anti-corrosion protection to metal.
Description
Technical field
The invention belongs to paint field, and in particular to a kind of preparation side of the fiber reinforced polypyrrole anticorrosive paint of epoxidation
Method.
Background technology
Electrically-conducting paint is anti electromagnetic wave interference shielding coating.It is commonly called as:Conductive paint.Conductive paint is compound micro- using cupric, silver etc.
Grain is as conductive particle, a kind of paint with excellent conductive performance.Electrically-conducting paint is sent out rapidly with modern science and technology
The special functional coating that exhibition is got up, there are about semicentennial developing history so far.1948, the U.S. was disclosed silver and asphalt mixtures modified by epoxy resin
The patent of conducting resinl is made in fat, and this is earliest disclosed electrically-conducting paint.China also begins one's study and applied in 1950s
Electrically-conducting paint.In recent decades, electrically-conducting paint is in a variety of military, civilian industrial circles such as electronics, electrical equipment, aviation, chemical industry, printing
In be applied.Corresponding to this, the theoretical research of electrically-conducting paint is also developed rapidly, and promote application technology increasingly into
It is ripe with it is perfect.Conductive paint be exactly can be used for spraying a kind of paint dry to be formed after paint film can play conduction effect, so as to shield
Cover the function of Electromagnetic Interference;
Conductive paint makes completely insulated nonmetallic or non-conducting surfaces have as metal by spraying, the method brushed
The feature absorb, conducted and decay electromagnetic wave, so as to play a part of shielding electromagnetic interference.The appearance of conductive paint, effectively
Solve nonmetallic surface and realize the problem of electrically connecting.Conductive paint is to electroplate the anti electromagnetic wave interference paint that silver particles are made, single
Component, saving of labor, time saving, convenient, adhesive force are good, smooth, cohesive force is strong, without loose particle, are base available for metal, composite
The inner walls sprayed on material such as mobile phone, calculator, precision instrument of material.Enamelled coating performance is stable after dry solidification, is sprayed on workpiece
Surface smooth has excellent electric conductivity, fine and smooth conducting particles to ensure that electronic component as fine silver conductive paint
Security.To ensure the adhesive ability of paint vehicle and basal plane, in normal conditions, conductive paint vehicle is only advised using non-in PC, ABS etc.
The surface of metal material, if using on the surface that is of little use, it may be necessary to which bottoming agent is used cooperatively;
The .7 of application number 201410635558, discloses the synthesis of a kind of antistatic coating and preparation method thereof, wherein polypyrrole
Technique is as follows:Respectively by 3,6-4 7g neopelexes, 8.9-9.6g isopropanols, 22. 9-27.0g deionizations
Water adds polymeric kettle, after stirring, and adds 1.2-2.3g ammonium persulfate, then passes to 10.9-13.8g pyrrole monomers, instead
Answer after 4-10h, plus 0.7-1.3g hydroquinones terminators, discharged after cooling, produce polypyrrole conducting polymer latex, it is first
Polypyrrole is prepared, then mixes polypyrrole with inorganic additive, by dispersed with stirring, but inorganic filler is so easily caused
Reunion, each Material Compatibility is poor, so as to reduce the stability_intensity of finished product film.
The content of the invention
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of fiber reinforced polypyrrole of epoxidation
The preparation method of anticorrosive paint.
To achieve the above object, the present invention uses following technical scheme:
A kind of preparation method of the fiber reinforced polypyrrole anticorrosive paint of epoxidation, comprises the following steps:
(1)The sisal fiber of 13-20 parts by weight is taken, is added in the acetic acid solution that concentration is 70-80%, is soaked 3-4 hours, go out
Material, air drying is added in the hydrogen peroxide solution that concentration is 15-20%, and rise temperature is 50-60 DEG C, and insulated and stirred 1-2 is small
When, precipitation is washed, is sent in 40-50 DEG C of baking oven by filtering, is dried 2-3 hours, discharging cooling, obtains hydroxylating fiber;
(2)Take in above-mentioned hydroxylating fiber, the deionized water for being added to 100-120 times of its weight, it is ultrasonic 3-5 minutes, add 1-2
The epoxychloropropane of parts by weight, is sent in 70-80 DEG C of water bath with thermostatic control, insulated and stirred 30-40 minutes, discharging, obtains epoxy fine
Tie up dispersion liquid;
(3)The pyrroles of 150-170 parts by weight is taken, in the absolute ethyl alcohol for being added to 2-3 times of its weight, is stirred, 3-5 weights are added
The triethylamine of part is measured, rise temperature is 70-75 DEG C, and insulated and stirred 1-2 hours is distilled off ethanol, obtains aminated pyrrole;
(4)Above-mentioned epocel dispersion liquid, aminated pyrrole mixing are taken, 20-30 parts by weight, 3-5mol/l hydroxide is added dropwise
It is sent to after sodium, completion of dropping in reactor, insulated and stirred 20-30 minutes at 110-120 DEG C, discharging, must alkalize crosslinking pyrrole
Cough up solution;
(5)Alkalization crosslinking chromium solution is taken, is sent in reactor, nitrogen is passed through, regulation temperature of reaction kettle is 4-6 DEG C, insulation
Reaction 4-5 hours, is discharged, and precipitation is washed in filtering, is dried 20-23 hours at 70-75 DEG C of vacuum, is cooled to normal temperature, produces institute
State the fiber reinforced polypyrrole anticorrosive paint of epoxidation.
Advantages of the present invention:
Then pyrroles is handled first by hydroxylating fiber epoxidation, obtains aminated pyrrole, then by the present invention by triethylamine
By aminated pyrrole and epoxidation fiber blend, it is crosslinked in the basic conditions, obtains crosslinking chromium solution, be finally crosslinked with fiber
Pyrroles is that monomer will be polymerize, and obtains anticorrosive paint;
Fiber and monomer are formed effective crosslinking by the coating of the present invention, can be carried with the compatibility between reinforcing fiber and polymer
The stability_intensity of high finished product film, while fiber can also improve the toughness and impact strength of finished product film, it is of the invention
The adhesiveness of film and metallic substrate surface is good, can effectively improve the anti-corrosion protection to metal, improves the stabilization of film
Property.
Embodiment
Embodiment 1
A kind of preparation method of the fiber reinforced polypyrrole anticorrosive paint of epoxidation, comprises the following steps:
(1)The sisal fiber of 13 parts by weight is taken, is added in the acetic acid solution that concentration is 70%, soaks 3 hours, discharging, normal temperature is done
It is dry, it is added in the hydrogen peroxide solution that concentration is 15%, rise temperature is 50 DEG C, insulated and stirred 1 hour, filtering will precipitate water
Wash, be sent in 40-50 DEG C of baking oven, dry 2 hours, discharging cooling obtains hydroxylating fiber;
(2)Above-mentioned hydroxylating fiber is taken, in the deionized water for being added to 100 times of its weight, ultrasound 3 minutes adds 1 parts by weight
Epoxychloropropane, in the water bath with thermostatic control for being sent to 70 DEG C, insulated and stirred 30 minutes, discharging obtains epocel dispersion liquid;
(3)The pyrroles of 170 parts by weight is taken, in the absolute ethyl alcohol for being added to 2 times of its weight, is stirred, the three of 3 parts by weight are added
Ethamine, rise temperature is 75 DEG C, and insulated and stirred 1 hour is distilled off ethanol, obtains aminated pyrrole;
(4)Above-mentioned epocel dispersion liquid, aminated pyrrole mixing are taken, 20 parts by weight, 3mol/l sodium hydroxide is added dropwise, is added dropwise
It is sent in reactor, insulated and stirred 20 minutes at 120 DEG C, discharges after finishing, must alkalizes crosslinking chromium solution;
(5)Alkalization crosslinking chromium solution is taken, is sent in reactor, nitrogen is passed through, regulation temperature of reaction kettle is 6 DEG C, and insulation is anti-
Answer 4 hours, discharge, precipitation is washed in filtering, is dried 20 hours at 75 DEG C of vacuum, is cooled to normal temperature, produces the epoxy chemical fibre
Tie up toughness reinforcing polypyrrole anticorrosive paint.
Claims (1)
1. a kind of preparation method of the fiber reinforced polypyrrole anticorrosive paint of epoxidation, it is characterised in that comprise the following steps:
(1)The sisal fiber of 13-20 parts by weight is taken, is added in the acetic acid solution that concentration is 70-80%, is soaked 3-4 hours, go out
Material, air drying is added in the hydrogen peroxide solution that concentration is 15-20%, and rise temperature is 50-60 DEG C, and insulated and stirred 1-2 is small
When, precipitation is washed, is sent in 40-50 DEG C of baking oven by filtering, is dried 2-3 hours, discharging cooling, obtains hydroxylating fiber;
(2)Take in above-mentioned hydroxylating fiber, the deionized water for being added to 100-120 times of its weight, it is ultrasonic 3-5 minutes, add 1-2
The epoxychloropropane of parts by weight, is sent in 70-80 DEG C of water bath with thermostatic control, insulated and stirred 30-40 minutes, discharging, obtains epoxy fine
Tie up dispersion liquid;
(3)The pyrroles of 150-170 parts by weight is taken, in the absolute ethyl alcohol for being added to 2-3 times of its weight, is stirred, 3-5 weights are added
The triethylamine of part is measured, rise temperature is 70-75 DEG C, and insulated and stirred 1-2 hours is distilled off ethanol, obtains aminated pyrrole;
(4)Above-mentioned epocel dispersion liquid, aminated pyrrole mixing are taken, 20-30 parts by weight, 3-5mol/l hydroxide is added dropwise
It is sent to after sodium, completion of dropping in reactor, insulated and stirred 20-30 minutes at 110-120 DEG C, discharging, must alkalize crosslinking pyrrole
Cough up solution;
(5)Alkalization crosslinking chromium solution is taken, is sent in reactor, nitrogen is passed through, regulation temperature of reaction kettle is 4-6 DEG C, insulation
Reaction 4-5 hours, is discharged, and precipitation is washed in filtering, is dried 20-23 hours at 70-75 DEG C of vacuum, is cooled to normal temperature, produces institute
State the fiber reinforced polypyrrole anticorrosive paint of epoxidation.