CN107243416A - A kind of method that this matt Cu-S ore of Austria settles microfine Pb-Zn tailings as flocculant - Google Patents
A kind of method that this matt Cu-S ore of Austria settles microfine Pb-Zn tailings as flocculant Download PDFInfo
- Publication number
- CN107243416A CN107243416A CN201710438603.3A CN201710438603A CN107243416A CN 107243416 A CN107243416 A CN 107243416A CN 201710438603 A CN201710438603 A CN 201710438603A CN 107243416 A CN107243416 A CN 107243416A
- Authority
- CN
- China
- Prior art keywords
- ore
- matt
- tailings
- microfine
- understand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of method that this matt Cu-S ore difficult to understand settles microfine Pb-Zn tailings as flocculant, it belongs to water process environmental technology field.This matt Cu-S ore difficult to understand is added among the ore pulp of microfine Pb-Zn tailings, mixed, start sedimentation in acid condition afterwards, treat to settle completely added with the microfine Pb-Zn tailings of this matt Cu-S ore difficult to understand, complete whole infall process, the treatment of wastes with processes of wastes against one another is reached, the purpose of particulate Pb-Zn tailings ore pulp is settled.Experimental study of the present invention by settling microfine Pb-Zn tailings to this matt Cu-S ore difficult to understand finds that this matt Cu-S ore difficult to understand is a kind of good flocculant, can dramatically speed up the sinking speed of fine granule material.This method has the advantages such as technique is simple, with low cost, sinking speed is fast, it is possible to increase the value of this matt Cu-S ore difficult to understand, the flocculating setting of improvement microfine Pb-Zn tailings, with important environment protection significance and good application prospect.
Description
Technical field
The present invention relates to a kind of method that this matt Cu-S ore difficult to understand settles microfine Pb-Zn tailings as flocculant, it belongs to
Water process environmental technology field.
Background technology
During this difficult to understand matt Cu-S ore is Copper making, the waste residue that water cooled fast cooling is produced is a kind of after cooling
Highly active vitreum material, is also a kind of silicate material rich in porous micropore, this matt Cu-S ore chats difficult to understand
Thing composition is mostly fayalite and hercynite, is secondly magnetic iron ore, copper sulfide and metallic copper, in addition also a small amount of arteries and veins
Stone.Recovery in terms of the current comprehensive utilization to this matt Cu-S ore difficult to understand except carrying out the resources such as copper, iron by dressing method is sharp
With outer, moreover it is possible to be widely used as the raw material of other products, such as it is applied to cement manufacturing industry to replace iron powder to make additive, for giving birth to
Portland clinker is produced, as slag cotton material, as colour glazed tile and corrugated tile material etc..The present invention considers Austria
The flocculating setting effect of this matt Cu-S ore and cost advantage, seek a kind of this matt Cu-S ore difficult to understand fine as flocculant sedimentation
The method of grain Pb-Zn tailings, with certain economic implications and social benefit.
The content of the invention
1. goal of the invention:
It is an object of the invention to provide a kind of this matt Cu-S ore difficult to understand microfine Pb-Zn tailings are settled as flocculant
This matt Cu-S ore difficult to understand is used as the flocculating setting agent of microfine Pb-Zn tailings by method, this method, turns waste into wealth, while can subtract
Environmental pollution caused by the stacking of few this matt Cu-S ore of Austria causes great risk to the life and health of the mankind, realizes resource environment
Green coordinated development.
2. technical scheme:
Technical solution of the present invention:A kind of method that this matt Cu-S ore of Austria settles microfine Pb-Zn tailings as flocculant,
Concretely comprise the following steps and this matt Cu-S ore difficult to understand is added among the ore pulp of microfine Pb-Zn tailings, mixed, Zhi Hou
Start sedimentation under acid condition, treat to settle completely added with the microfine Pb-Zn tailings of this matt Cu-S ore difficult to understand, complete whole sedimentation
Process, reaches the treatment of wastes with processes of wastes against one another, settles the purpose of particulate Pb-Zn tailings ore pulp.
Preferably:
The first step, by weight 1:This matt Cu-S ore difficult to understand of+0.3mm grades is added to the zinc of lead containing microfine by 10 ratio
In the ore pulp of mine tailing, mixing stirring is then carried out;
Second step, adds a small amount of sulfuric acid, is maintained at acid condition pH under conditions of 6, to start sedimentation, treat added with Ao Simai
The microfine Pb-Zn tailings of special Cu-S ore are settled completely, complete whole infall process.
In above-mentioned preferred scheme second step, in acid condition, added with the microfine Pb-Zn tailings of this matt Cu-S ore difficult to understand
It can just be settled completely within 10min.
This matt Cu-S ore single point surface area difficult to understand is 0.7325 (m2/ g), specific surface area is 0.7404 (m2/ g), pore volume
0.00126(cm3/ g), pore size 68.0996 (angstrom).This matt clinker difficult to understand is what is occurred in the range of 0~0.5 in relative pressure
Lag loop comes from N2Capillary condensation, contain the uniform cylindric mesopore of a large amount of both ends opens.The slag rough surface has many
Mostly below 5 microns, there is partial gap between particle in irregular blocky-shaped particle attachment, particle.The slag particle footpath is substantially 50
Micron is following, and only small part particle is in 50 microns, and with the presence of part fine grained surface crack, and these show that the slag can
Open space can be contained.This matt Cu-S ore difficult to understand is after pulverizing and jevigating to certain fineness, to the lead zinc tail of microfine in ore pulp
Ore deposit has flocculating setting effect, and efficiency is higher, and because this matt Cu-S ore difficult to understand is a kind of tailings, it is extremely low using cost.
3. beneficial effect:
Beneficial effects of the present invention:1. reduce environmental pollution caused by the stacking of this matt Cu-S ore difficult to understand;2. with more
Cheap price settles the ore pulp of Pb-Zn tailings, the treatment of wastes with processes of wastes against one another.Under the same conditions, the inventive method and existing flocculating setting
Agent and adsorption method compare, in the case where the sedimentation time is more or less the same, and this matt Cu-S ore difficult to understand has in Costco Wholesale
Clear superiority, therefore a kind of this matt Cu-S ore difficult to understand disclosed by the invention settles the side of microfine Pb-Zn tailings as flocculant
Method, with certain economic implications and social benefit.
Embodiment
With reference to embodiment, the invention will be further described.
What the present invention was realized in:This matt Cu-S ore difficult to understand is added among the ore pulp of microfine Pb-Zn tailings, entered
Row is mixed, and starts sedimentation in acid condition afterwards, treats that the microfine Pb-Zn tailings added with this difficult to understand matt Cu-S ore are complete
Sedimentation, completes whole infall process, reaches the treatment of wastes with processes of wastes against one another, settles the purpose of particulate Pb-Zn tailings ore pulp.
Comprise the following steps that:
The first step, by weight proportion 1:10 are added to this matt Cu-S ore difficult to understand of+0.3mm grades containing microfine lead zinc
In the ore pulp of mine tailing, mixing stirring is then carried out;
Second step, adds a small amount of sulfuric acid, is maintained at acid condition pH under conditions of 6, to start sedimentation, treat added with Ao Simai
The microfine Pb-Zn tailings of special Cu-S ore are settled completely, complete whole infall process.
In second step, in acid condition, added with this difficult to understand matt Cu-S ore microfine Pb-Zn tailings within 10min just
It can settle completely.
The method disclosed in the present can achieve the effect that:1. reduce ring caused by the stacking of this matt Cu-S ore difficult to understand
Pollute in border;2. the ore pulp of Pb-Zn tailings, the treatment of wastes with processes of wastes against one another are settled with more cheap price.Under the same conditions, present invention side
Technical indicator of the method compared with existing flocculating setting agent and adsorption method such as following table:
The index contrast table of table 1
As can be seen from Table 1, in the case where the sedimentation time is more or less the same, this matt Cu-S ore difficult to understand has in Costco Wholesale
Clear superiority, the method that this kind of difficult to understand matt Cu-S ore disclosed by the invention settles microfine Pb-Zn tailings as flocculant,
With certain economic implications and social benefit.
Embodiment described above only expresses the preferred embodiment of the present invention, and it describes more specific and detailed, but simultaneously
Therefore the limitation to the scope of the claims of the present invention can not be interpreted as.It should be pointed out that for one of ordinary skill in the art
For, without departing from the inventive concept of the premise, some deformations can also be made, improves and substitutes, these belong to this hair
Bright protection domain.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (2)
1. a kind of method that this matt Cu-S ore of Austria settles microfine Pb-Zn tailings as flocculant, is concretely comprised the following steps:By it is difficult to understand this
Matt Cu-S ore is added among the ore pulp of microfine Pb-Zn tailings, is mixed, and starts to sink afterwards in acid condition
Drop, treats to settle completely added with the microfine Pb-Zn tailings of this matt Cu-S ore difficult to understand, completes whole infall process.
2. the method that a kind of this matt Cu-S ore difficult to understand as claimed in claim 1 settles microfine Pb-Zn tailings as flocculant,
It is characterized in that comprising the following steps that:
The first step, by weight 1:This matt Cu-S ore difficult to understand of+0.3mm grades is added to containing microfine lead zinc tail by 10 ratio
In the ore pulp of ore deposit, mixing stirring is then carried out;
Second step, adds a small amount of sulfuric acid, is maintained at acid condition pH under conditions of 6, to start sedimentation, treat added with this matt copper difficult to understand
The microfine Pb-Zn tailings of clinker are settled completely, complete whole infall process.