CN107236317A - A kind of sponge and preparation method thereof - Google Patents
A kind of sponge and preparation method thereof Download PDFInfo
- Publication number
- CN107236317A CN107236317A CN201710497555.5A CN201710497555A CN107236317A CN 107236317 A CN107236317 A CN 107236317A CN 201710497555 A CN201710497555 A CN 201710497555A CN 107236317 A CN107236317 A CN 107236317A
- Authority
- CN
- China
- Prior art keywords
- parts
- sponge
- modifying
- preparation
- cornstarch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of sponge and preparation method thereof, belong to environment-friendly materials technical field.It, which makes raw material, includes 30 40 parts of stalk fibre powder, 15 25 parts of cornstarch, 45 parts of polipropene 25, polyvinyl chloride 20 30,13 parts of plasticizer.Specifically include following steps：(1) in parts by weight, by 30 40 parts of stalk fibre powder, 15 25 parts of cornstarch, 45 parts of polipropene 25,20 30 parts of addition high-speed mixers of polyvinyl chloride, blending and modifying is carried out 5 10 minutes；(2) 13 parts of plasticizer is added to the high-speed mixer, then carries out blending and modifying 35 minutes, row is shaped as string mixing material；(3) string mixing material heating and mould pressing is molded, cold air drying, forms sponge finished product.Low raw-material cost of the present invention, nontoxic, environmental protection, technical process is simple, with short production cycle, meets low-carbon life, can largely put into production, wide market.
Description
Technical field
The present invention relates to a kind of sponge and preparation method thereof, belong to environment-friendly materials technical field.
Background technology
Human society is constantly improving, it is meant that the utilization of continually developing to resource, various natural resources worsening shortages,
And the raw material of most of plastics are all come out by Petroleum refining, plastics cost is caused also constantly to rise.On the other hand, mesh
Before, substantial amounts of plastic products belong to non-degradable waste, while band gives people life convenient, are also polluting people's life
Soil.So, need a kind of material badly, can either realize that plastic tape gives people the facility of life, again can be to a certain extent
Reduce cost, reach the purpose of environmental protection.
The content of the invention
The present invention is to solve the above problems, the invention provides a kind of sponge and preparation method thereof, the making
Raw material includes 30-40 parts of stalk fibre powder, 15-25 parts of cornstarch, -45 parts of polipropene 25, polyvinyl chloride 20-30, plasticizer
1-3 parts.
The step of this method, is as follows：(1) in parts by weight, by 30-40 parts of stalk fibre powder, 15-25 parts of cornstarch, poly-
25-45 parts of propylene, 20-30 parts of addition high-speed mixers of polyvinyl chloride, carry out blending and modifying 5-10 minutes；(2) by plasticizer 1-3
Part is added to the high-speed mixer, then carries out blending and modifying 3-5 minutes, and row is shaped as string mixing material；(3) it will plant
Fibres mixing material heating and mould pressing is molded, cold air drying, forms sponge finished product.
Nontoxic the beneficial effects of the invention are as follows low raw-material cost, environmental protection, technical process is simple, production week
Phase is short, meets low-carbon life, can largely put into production, wide market.
Embodiment
A kind of sponge described in the embodiment of the present invention and preparation method thereof, comprises the following steps：
(1) in parts by weight, by 30-40 parts of stalk fibre powder, 15-25 parts of cornstarch, -45 parts of polipropene 25, polychlorostyrene
20-30 parts of addition high-speed mixers of ethene, carry out blending and modifying 5-10 minutes；
(2) 1-3 parts of plasticizer is added to the high-speed mixer, then carries out blending and modifying 3-5 minute, row is shaped as plant
Fibres mixing material；
(3) string mixing material heating and mould pressing is molded, cold air drying, forms sponge finished product.
It is preferred that, in step (1), the granularity of stalk fibre powder is 50-90 mesh.
Claims (3)
1. a kind of sponge and preparation method thereof, it is characterised in that the making raw material includes stalk fibre powder 30-40
Part, 15-25 parts of cornstarch, -45 parts of polipropene 25, polyvinyl chloride 20-30,1-3 parts of plasticizer.
2. a kind of sponge according to claim 1 and preparation method thereof, it is characterised in that the step of this method
It is as follows：(1) in parts by weight, by 30-40 parts of stalk fibre powder, 15-25 parts of cornstarch, -45 parts of polipropene 25, polyvinyl chloride
20-30 parts of addition high-speed mixers, carry out blending and modifying 5-10 minutes；(2) 1-3 parts of plasticizer is added to the mixed at high speed
Machine, then carry out blending and modifying 3-5 minutes, row is shaped as string mixing material；(3) by string mixing material heated mould
Molded, cold air drying forms sponge finished product.
3. a kind of sponge according to claim 2 and preparation method thereof, it is characterised in that in step (1), straw
The granularity of stalk fiber powder is 50-90 mesh.