CN107236077A - The preparation method of the high rigidity acrylic resin of resistance to gasoline - Google Patents
The preparation method of the high rigidity acrylic resin of resistance to gasoline Download PDFInfo
- Publication number
- CN107236077A CN107236077A CN201710580869.1A CN201710580869A CN107236077A CN 107236077 A CN107236077 A CN 107236077A CN 201710580869 A CN201710580869 A CN 201710580869A CN 107236077 A CN107236077 A CN 107236077A
- Authority
- CN
- China
- Prior art keywords
- acrylic resin
- resistance
- gasoline
- high rigidity
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high rigidity acrylic resin of resistance to gasoline and preparation method thereof, it is made up of the raw material of following weight percents：15% 25% styrene, 2.5% 25% methyl acrylates, 5% 10% hydroxy-ethyl acrylates, 0.25% 1.5% acrylic acid, 0.5% 2.5% initiator, 50% organic solvents.The present invention obtains optimal raw material by many experiments screening and constitutes and match, and optimal synthesis technique is preferably gone out by many experiments.Whole preparation technology is reasonable in design, prepares a kind of acrylic resin with excellent petrol-resistance.
Description
Technical field
The present invention relates to a kind of coating, and in particular to a kind of environmentally friendly high rigidity acrylic resin of resistance to gasoline and its preparation side
Method, belongs to technical field of polymer materials.
Background technology
The resin of resistance to gasoline is mainly used in fuel tank, and lathe etc. needs the industrial part that oil resistant corrodes, and conventional acrylic resin exists
There is paint film softening after film forming fast, gloss reduction is rapid, paint film such as can not recover at the disadvantage after oil plant volatilization
The content of the invention
Goal of the invention：The purpose of the present invention is that in view of the shortcomings of the prior art, by many experiments, there is provided a kind of environmentally friendly
High rigidity, the acrylic resin of resistance to gasoline and preparation method thereof.
Technical scheme, to realize object above, the technical solution adopted by the present invention is：
A kind of high rigidity acrylic resin of resistance to gasoline, it is made up of the raw material of following weight percents：
15%-25% styrene, 2.5%-25% methyl acrylates, 5%-10% hydroxy-ethyl acrylates, acrylic acid
0.25%-1.5%, initiator 0.5%-2.5%, organic solvent 50%.
A kind of preparation method of the high rigidity acrylic resin of resistance to gasoline, it comprises the following steps：
(1) initiator of styrene, methyl acrylate, hydroxy-ethyl acrylate, acrylic acid, total amount 90% is well mixed,
Obtain mix monomer；
(2) organic solvent is put into reactor, is heated to reflux state；
(3) monomer that step (1) is well mixed is put into dropping tank, then toward mix monomer is added dropwise in reactor, is added dropwise
Time is 2.5-3 hours；Then keep at reflux 2 hours of reaction, insulation reaction adds residue 10% after finishing
Initiator, thermal reacting for two hours；
(4) 100 DEG C are cooled to, filtering obtains acrylic resin.
Preferably, the preparation method of the above-described high rigidity acrylic resin of resistance to gasoline, it is characterised in that each
The percentage by weight of raw material is as follows：
15%-25% styrene, 2.5%-25% methyl acrylates, 5%-10% hydroxy-ethyl acrylates, acrylic acid
0.25%-1.5%, initiator 0.5%-2.5%, organic solvent 50%.
Preferably, the preparation method of the above-described high rigidity acrylic resin of resistance to gasoline, organic solvent is two
Toluene；Initiator is BPO (perbenzoic acid).
The present invention is screened by many experiments, and the monomers such as butyl acrylate and Isooctyl acrylate monomer are used in conventional formulation
When, oil resistivity is less than 12 hours.The present invention uses the shorter raw material of carbochain instead by experiment screening in material component, synthesizes
Obtained resin gasoline-resistant performance is brought up to 48 hours, achieves extraordinary technique effect.
Beneficial effect：Compared to the prior art, the present invention has the following advantages：
The present invention obtains optimal raw material by many experiments screening and constitutes and match, and is preferably gone out by many experiments optimal
Synthesis technique.Whole preparation technology is reasonable in design, and the acrylic resin prepared has excellent hardness, and with very
Good gasoline-resistant performance.
Embodiment
Embodiment 1
1st, a kind of preparation method of the high rigidity acrylic resin of resistance to gasoline, it comprises the following steps：
(1) by 15 grams of styrene, 25 grams of methyl acrylate, 6 grams of hydroxy-ethyl acrylate, 1.5 grams of acrylic acid, initiator
BPO2.25 grams (90% of total amount) is well mixed, and obtains mix monomer；
(2) by 30 grams of dimethylbenzene, 20 grams of input reactors of butyl acetate, it is heated to reflux state；
(3) step (1) mix monomer is put into dropping tank, mix monomer is uniformly added drop-wise to step (2) with 2.5-3 hours
Reactor in；Keep 2 hours after completion of dropping at reflux again；Insulation, which is finished, adds remaining 0.25 gram of initiator
(the 10% of total amount)；Continue to react 2 hours under reflux state；
(4) 100 degree are cooled to, filtering obtains acrylic resin.
2nd, performance test is carried out to obtained acrylic resin paint made above, test result is as shown in table 1 below：
Table 1 can testing result
More than test result indicates that, the acrylic resin paint for preparing of the present invention has excellent adhesive force, light
Damp degree and excellent hardness, especially gasoline-resistant performance are good, achieve extraordinary technological progress.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (4)
1. a kind of high rigidity acrylic resin of resistance to gasoline, it is characterised in that it is made up of the raw material of following weight percents：
15%-25% styrene, 2.5%-25% methyl acrylates, 5%-10% hydroxy-ethyl acrylates, 0.25%-1.5% third
Olefin(e) acid, 0.5%-2.5% initiators, 50% organic solvent.
2. a kind of preparation method of the high rigidity acrylic resin of resistance to gasoline, it is characterised in that it comprises the following steps：
(1) initiator of styrene, methyl acrylate, hydroxy-ethyl acrylate, acrylic acid, total amount 90% is well mixed, obtained
Mix monomer；
(2) organic solvent is put into reactor, is heated to reflux state；
(3) monomer that step (1) is well mixed is put into dropping tank, then toward mix monomer, time for adding is added dropwise in reactor
For 2.5-3 hours；Then keep at reflux 2 hours of reaction, insulation reaction adds the initiation of residue 10% after finishing
Agent, thermal reacting for two hours；
(4) 100 DEG C are cooled to, filtering obtains acrylic resin.
3. the preparation method of the high rigidity acrylic resin of resistance to gasoline according to claim 2, it is characterised in that each raw material
Percentage by weight is as follows：
15%-25% styrene, 2.5%-25% methyl acrylates, 5%-10% hydroxy-ethyl acrylates, acrylic acid 0.25%-
1.5%th, initiator 0.5%-2.5%, organic solvent 50%.
4. the preparation method of the high rigidity acrylic resin of resistance to gasoline according to claim 3, it is characterised in that organic solvent
For dimethylbenzene；Initiator is perbenzoic acid.