CN107226647A - A kind of environment protection architecture heat-barrier material and preparation method thereof - Google Patents
A kind of environment protection architecture heat-barrier material and preparation method thereof Download PDFInfo
- Publication number
- CN107226647A CN107226647A CN201710610660.5A CN201710610660A CN107226647A CN 107226647 A CN107226647 A CN 107226647A CN 201710610660 A CN201710610660 A CN 201710610660A CN 107226647 A CN107226647 A CN 107226647A
- Authority
- CN
- China
- Prior art keywords
- parts
- barrier material
- environment protection
- protection architecture
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of environment protection architecture heat-barrier material and preparation method thereof, and its composition includes raw materials of compound, calcium carbonate, polyethylene, string, inorfil, spherical petroleum paraffin, foaming agent, cosolvent, binding agent and water.Mentioned component is had into effect of heat insulation, and energy-saving and environmental protection are pollution-free well by a series of construction material made from hybrid process, has the advantages that simple processing, technological process are simple and cost is low, is adapted to mass production, production efficiency can be improved.
Description
Technical field
The invention belongs to the preparing technical field of construction material, and in particular to a kind of environment protection architecture heat-barrier material and its preparation
Method.
Background technology
Building energy consumption ratio shared in the total energy consumption of countries in the world is all sizable, and for China, it is huge
Big building energy consumption has gradually had influence on the sustainable development of China's economy.Building energy conservation is a comprehensive system work
Journey, as long as it is saved depending on exterior wall, door and window and the heat-insulated effect of roof heat insulation, and the insulation that exterior wall is undertaken among these
Energy-saving effect accounts for overall 50-60%, so, the thermal and insulating performance of skin how is further improved, is to determine building
The key of whole energy effect.
In the prior art, the light wall material for building of production is typically all to use electrical heating or natural curing.
Such as the electrical heating light wall material for building that either natural curing is produced, it is necessary to could produce and dispatch from the factory for nearly one month,
Its production cycle is long, and the materials for wall of such production is heated uneven, and product quality cannot be ensured, serious shadow
Ring the turnover of production efficiency and fund.Above-mentioned materials for wall can not fully play heat-insulated performance, therefore energy-saving effect is poor.
In accordance with the above, it is desirable to provide a kind of more preferable environmental-friendly construction material, to improve deficiency of the prior art, from
And improve the quality of life of people.
The content of the invention
It is an object of the invention to provide a kind of environment protection architecture heat-barrier material and preparation method thereof, there is the present invention heat of transformation to hand over
The function of changing, balances indoor temperature, produces energy-saving effect, environment friendly and pollution-free, reduces the weight of material, and has processing letter
Just the advantage that, technological process is simple and cost is low, is adapted to mass production, can improve production efficiency.
The invention provides following technical scheme：
A kind of environment protection architecture heat-barrier material, includes the raw material of following parts by weight：28-35 parts of raw materials of compound, calcium carbonate 22-26
Part, 13-17 parts of polyethylene, 24-34 parts of string, 38-45 parts of inorfil, spherical petroleum paraffin 15-22 parts, foaming agent 8-
25-36 parts of 10 parts, 13-16 parts of cosolvent, 8-14 parts of binding agent and water.
It is preferred that, it is described to include the raw material of following parts by weight：31 parts of raw materials of compound, 22 parts of calcium carbonate, 13 parts of polyethylene,
30 parts of string, 42 parts of inorfil, 20 parts of spherical petroleum paraffin, 8 parts of foaming agent, 15 parts of cosolvent, 8 parts of binding agent and water
34 parts.
It is preferred that, the raw materials of compound is any of aluminum oxide, silica, iron oxide and magnesia or a variety of
Mixing.
It is preferred that, the inorfil is any of glass fibre, boron fibre, ceramic fibre and metallic fiber or many
The mixing planted so that the materials for wall has the function of phase transformation heat exchange.
It is preferred that, the foaming agent is rosin foaming agent, and the lower cost for material, material source is extensive, and performance, effect
It is good.
A kind of preparation method of environment protection architecture heat-barrier material, comprises the following steps：
A, by raw materials of compound, calcium carbonate and 1/3rd water be added in batch mixer mix, 120-150r/min turn
The lower stirring 40-50min of speed, obtains mixture one；
B, by polyethylene, string, inorfil, spherical petroleum paraffin, foaming agent, cosolvent, binding agent and remaining three points
Two water be added in mixture one, heat and stir at 150-180 DEG C, stir speed (S.S.) is 300-400r/min, 30-
After 45min, temperature is promoted to after 340-380 DEG C, heating 25-35min rapidly, temperature is cooled down by the way of condensation cycle
To normal temperature, mixture two is obtained；
C, mixture two is placed in closed environment to progress steam heating, temperature heats 40-60min, obtained at 400-500 DEG C
Mixture three；
D, mixture three imported while hot compressing in mould, pressure is 20-35MPa, is cooled to normal temperature and can obtain finished product.
It is preferred that, step b heating is heated in sealed environment, is conducive to the product prepared to undope matter, is improved life
Efficiency is produced, shortens manufacturing cycle.
It is preferred that, the steam-heated raw materials of step c are deionized water, are conducive to undoping in gas bath heating process
Matter.
The beneficial effects of the invention are as follows：
Fibrous material in the present invention greatly improves the toughness of material, is that material is not likely to produce crackle or breakage；Wherein add
Plus inorfil, the function with certain phase transformation heat exchange can balance indoor temperature, produce energy-conservation effect to a certain extent
Really；Its spherical petroleum paraffin added, is conducive to making materials for wall to have a heat-insulated well and heat insulation effect, its specific heat capacity compared with
Height, with good endothermic effect, so as to reach heat-insulated function.
The present invention is environment friendly and pollution-free, reduces the weight for the material prepared, and has simple processing, technological process letter
The single and low advantage of cost, is adapted to industrialization mass production, can so improve production efficiency.
Embodiment
Embodiment 1
A kind of environment protection architecture heat-barrier material, includes the raw material of following parts by weight：35 parts of raw materials of compound, 22 parts of calcium carbonate, poly- second
17 parts of alkene, 24 parts of string, 45 parts of inorfil, 15 parts of spherical petroleum paraffin, 10 parts of foaming agent, 13 parts of cosolvent, bonding
25 parts of 14 parts of agent and water.
Raw materials of compound is the mixing of aluminum oxide, silica, iron oxide and magnesia.
Inorfil is the mixing of glass fibre, boron fibre, ceramic fibre and metallic fiber so that the materials for wall has
The function of phase transformation heat exchange.
Foaming agent is rosin foaming agent, and the lower cost for material, material source is extensive, and performance, effect are good.
A kind of preparation method of environment protection architecture heat-barrier material, comprises the following steps：
A, by raw materials of compound, calcium carbonate and 1/3rd water be added in batch mixer mix, under 120r/min rotating speed
50min is stirred, mixture one is obtained；
B, by polyethylene, string, inorfil, spherical petroleum paraffin, foaming agent, cosolvent, binding agent and remaining three points
Two water be added in mixture one, heat and stir at 150 DEG C, after stir speed (S.S.) is 400r/min, 30min, rapidly
Temperature is promoted to after 380 DEG C, heating 25min, temperature is cooled to normal temperature by the way of condensation cycle, mixture is obtained
Two；
C, mixture two is placed in closed environment to progress steam heating, temperature heats 60min, obtain mixture at 400 DEG C
Three；
D, mixture three imported while hot compressing in mould, pressure is 35MPa, is cooled to normal temperature and can obtain finished product.
Step b heating is heated in sealed environment, is conducive to the product prepared to undope matter, improves production efficiency, is shortened
Manufacturing cycle.
The steam-heated raw materials of step c are deionized water, are conducive to the matter that undoped in gas bath heating process.
Embodiment 2
A kind of environment protection architecture heat-barrier material, includes the raw material of following parts by weight：Include the raw material of following parts by weight：Raw materials of compound
31 parts, 22 parts of calcium carbonate, 13 parts of polyethylene, 30 parts of string, 42 parts of inorfil, 20 parts of spherical petroleum paraffin, foaming agent 8
Part, 15 parts of cosolvent, 8 parts of binding agent and 34 parts of water.
Raw materials of compound is the mixing of aluminum oxide, silica, iron oxide and magnesia.
Inorfil is the mixing of glass fibre, boron fibre, ceramic fibre and metallic fiber so that the materials for wall has
The function of phase transformation heat exchange.
Foaming agent is rosin foaming agent, and the lower cost for material, material source is extensive, and performance, effect are good.
A kind of preparation method of environment protection architecture heat-barrier material, comprises the following steps：
A, by raw materials of compound, calcium carbonate and 1/3rd water be added in batch mixer mix, under 120r/min rotating speed
40min is stirred, mixture one is obtained；
B, by polyethylene, string, inorfil, spherical petroleum paraffin, foaming agent, cosolvent, binding agent and remaining three points
Two water be added in mixture one, heat and stir at 150 DEG C, after stir speed (S.S.) is 400r/min, 35min, rapidly
Temperature is promoted to after 340 DEG C, heating 25min, temperature is cooled to normal temperature by the way of condensation cycle, mixture is obtained
Two；
C, mixture two is placed in closed environment to progress steam heating, temperature heats 40min, obtain mixture at 400 DEG C
Three；
D, mixture three imported while hot compressing in mould, pressure is 20MPa, is cooled to normal temperature and can obtain finished product.
Step b heating is heated in sealed environment, is conducive to the product prepared to undope matter, improves production efficiency, is shortened
Manufacturing cycle.
The steam-heated raw materials of step c are deionized water, are conducive to the matter that undoped in gas bath heating process.
Embodiment 3
A kind of environment protection architecture heat-barrier material, includes the raw material of following parts by weight：35 parts of raw materials of compound, 22 parts of calcium carbonate, poly- second
17 parts of alkene, 24 parts of string, 38 parts of inorfil, 22 parts of spherical petroleum paraffin, 8 parts of foaming agent, 13 parts of cosolvent, binding agent
14 parts and 36 parts of water.
Raw materials of compound is the mixing of aluminum oxide, silica, iron oxide and magnesia.
Inorfil is the mixing of glass fibre, boron fibre, ceramic fibre and metallic fiber so that the materials for wall has
The function of phase transformation heat exchange.
Foaming agent is rosin foaming agent, and the lower cost for material, material source is extensive, and performance, effect are good.
A kind of preparation method of environment protection architecture heat-barrier material, comprises the following steps：
A, by raw materials of compound, calcium carbonate and 1/3rd water be added in batch mixer mix, under 150r/min rotating speed
50min is stirred, mixture one is obtained；
B, by polyethylene, string, inorfil, spherical petroleum paraffin, foaming agent, cosolvent, binding agent and remaining three points
Two water be added in mixture one, heat and stir at 180 DEG C, after stir speed (S.S.) is 400r/min, 45min, rapidly
Temperature is promoted to after 380 DEG C, heating 35min, temperature is cooled to normal temperature by the way of condensation cycle, mixture is obtained
Two；
C, mixture two is placed in closed environment to progress steam heating, temperature heats 60min, obtain mixture at 500 DEG C
Three；
D, mixture three imported while hot compressing in mould, pressure is 35MPa, is cooled to normal temperature and can obtain finished product.
Step b heating is heated in sealed environment, is conducive to the product prepared to undope matter, improves production efficiency, is shortened
Manufacturing cycle.
The steam-heated raw materials of step c are deionized water, are conducive to the matter that undoped in gas bath heating process.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality
Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic.All essences in the present invention
God is with principle, and any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (8)
1. a kind of environment protection architecture heat-barrier material, it is characterised in that include the raw material of following parts by weight：28-35 parts of raw materials of compound,
22-26 parts of calcium carbonate, 13-17 parts of polyethylene, 24-34 parts of string, 38-45 parts of inorfil, spherical petroleum paraffin 15-22
Part, 8-10 parts of foaming agent, 13-16 parts of cosolvent, 8-14 parts of binding agent and 25-36 parts of water.
2. a kind of environment protection architecture heat-barrier material according to claim 1, it is characterised in that include the original of following parts by weight
Material：31 parts of raw materials of compound, 22 parts of calcium carbonate, 13 parts of polyethylene, 30 parts of string, 42 parts of inorfil, spherical oil stone
34 parts of 20 parts of wax, 8 parts of foaming agent, 15 parts of cosolvent, 8 parts of binding agent and water.
3. a kind of environment protection architecture heat-barrier material according to claim 1, it is characterised in that the raw materials of compound is oxidation
Any of aluminium, silica, iron oxide and magnesia or a variety of mixing.
4. a kind of environment protection architecture heat-barrier material according to claim 1, it is characterised in that the inorfil is glass fibers
Any of dimension, boron fibre, ceramic fibre and metallic fiber or a variety of mixing.
5. a kind of environment protection architecture heat-barrier material according to claim 1, it is characterised in that the foaming agent foams for rosin
Agent.
6. a kind of preparation method of environment protection architecture heat-barrier material described in claim any one of 1-5, it is characterised in that including with
Lower step：
A, by raw materials of compound, calcium carbonate and 1/3rd water be added in batch mixer mix, 120-150r/min turn
The lower stirring 40-50min of speed, obtains mixture one；
B, by polyethylene, string, inorfil, spherical petroleum paraffin, foaming agent, cosolvent, binding agent and remaining three points
Two water be added in mixture one, heat and stir at 150-180 DEG C, stir speed (S.S.) is 300-400r/min, 30-
After 45min, temperature is promoted to after 340-380 DEG C, heating 25-35min rapidly, temperature is cooled down by the way of condensation cycle
To normal temperature, mixture two is obtained；
C, mixture two is placed in closed environment to progress steam heating, temperature heats 40-60min, obtained at 400-500 DEG C
Mixture three；
D, mixture three imported while hot compressing in mould, pressure is 20-35MPa, is cooled to normal temperature and can obtain finished product.
7. a kind of preparation method of environment protection architecture heat-barrier material according to claim 6, it is characterised in that the step b
Heating is heated in sealed environment.
8. a kind of preparation method of environment protection architecture heat-barrier material according to claim 6, it is characterised in that the step c
Steam-heated raw material is deionized water.