CN107216728A - 一种空调室外机外壳用金属防锈漆及其制备方法 - Google Patents

一种空调室外机外壳用金属防锈漆及其制备方法 Download PDF

Info

Publication number
CN107216728A
CN107216728A CN201710467150.7A CN201710467150A CN107216728A CN 107216728 A CN107216728 A CN 107216728A CN 201710467150 A CN201710467150 A CN 201710467150A CN 107216728 A CN107216728 A CN 107216728A
Authority
CN
China
Prior art keywords
parts
air
outdoor unit
conditioner outdoor
unit shell
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710467150.7A
Other languages
English (en)
Inventor
王飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Bo Tai Tai Electronic Technology Co Ltd
Original Assignee
Hefei Bo Tai Tai Electronic Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Bo Tai Tai Electronic Technology Co Ltd filed Critical Hefei Bo Tai Tai Electronic Technology Co Ltd
Priority to CN201710467150.7A priority Critical patent/CN107216728A/zh
Publication of CN107216728A publication Critical patent/CN107216728A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种空调室外机外壳用金属防锈漆，属于防锈漆技术领域，包括以下重量份的原料：氟碳乳液50‑60份、环氧树脂14‑16份、沥青4‑8份、膨润土1‑3份、玻璃纤维5‑7份、蛭石粉18‑30份、陶粒7‑9份、钛白粉17‑20份、磷酸锌7‑9份、异丙醇1‑3份、水20‑25份、消泡剂0.5‑1份、杀菌剂2‑4份、成膜助剂1‑2份、增稠剂3‑5份、流平剂1‑2份；本发明还公开了一种空调室外机外壳用金属防锈漆的制备方法；本发明粘结能力强，耐腐蚀，耐水耐高温，使用寿命长。

Description

一种空调室外机外壳用金属防锈漆及其制备方法
技术领域
本发明涉及防锈漆技术领域，具体的说，涉及了一种空调室外机外壳用金属防锈漆及其制备方法。
背景技术
空调即空气调节器，是指用人工手段，对建筑/构筑物内环境空气的温度、湿度、洁净度、速度等参数进行调节和控制的过程。一般包括冷源/热源设备，冷热介质输配系统，末端装置等几大部分和其他辅助设备。主要包括水泵、风机和管路系统。末端装置则负责利用输配来的冷热量，具体处理空气、温度，使目标环境的空气参数达到要求。
空调一般包括室内机和室外机，而室外机一般直接裸露在室外，经历风吹、雨打、日晒，所处环境很恶劣，室外机外壳一般由金属所制，在此环境下很容易生锈，使用寿命短，所以需要金属防锈漆对其进行保护，金属防锈漆主要分为物理性和化学性防锈漆两大类。前者靠颜料和漆料的适当配合，形成致密的漆膜以阻止腐蚀性物质的侵入，如铁红、铝粉、石墨防锈漆等；后者靠防锈颜料的化学抑锈作用，如红丹、锌黄防锈漆等。用于桥梁、船舶、管道等金属的防锈。
目前空调室外机一般采用环氧烤漆，但这种漆在时间久后容易粉化，使用时间不长，不能有效地保护空调室外机，防止其生锈。
在公开号为CN105907274A的专利文件中，公开了一种一种环保型水性金属防锈漆，其包括以下重量份数的原料：水性醇酸乳液20-30份、卡波树脂5-10份、聚氨酯3-10份、油酸钾1-2份、柠檬酸钠2-4份、磺化木质素0.5-1份、椰油酸钠1-3份、月桂醇硫酸铵1-2份、无机填料10-20份、改性剂1-2份、其他助剂2-8份及水10-20份。该发明通过合理原料配比，获得附着力好、干燥快、耐热性能好、环保无污染的高效、长效的环保型水性金属防锈漆制品；原料中添加了无机填料和改性剂，通过对防锈漆体系的调节改性，改善了原材料中高分子材料的优良性能，同时增加了制品的耐锈蚀性和防锈蚀的长效性，而且该发明的制备方法简单，成本低，适合大规模生产；但该发明的耐热性、耐腐蚀性、附着能力、使用寿命均能进一步提高。
发明内容
本发明的目的在于克服上述现有技术的不足，提供了一种空调室外机外壳用金属防锈漆及其制备方法，环保无污染，粘结能力强，耐腐蚀，耐水耐高温，具有较佳地防锈能力，使用寿命久。
本发明提供的一种空调室外机外壳用金属防锈漆，包括以下重量份的原料：
氟碳乳液50-60份、环氧树脂14-16份、沥青4-8份、膨润土1-3份、玻璃纤维5-7份、蛭石粉18-30份、陶粒7-9份、钛白粉17-20份、磷酸锌7-9份、异丙醇1-3份、水20-25份、消泡剂0.5-1份、杀菌剂2-4份、成膜助剂1-2份、增稠剂3-5份、流平剂1-2份。
作为优选，消泡剂为聚氧丙烯聚氧乙烯甘油醚和聚二甲基硅氧烷混合物，两者之间的重量比为3:1。
作为优选，增稠剂为硅藻土、凹凸棒石土、瓜尔胶、甲壳胺、阿拉伯树胶的一种或二种以上的混合物。
作为优选，流平剂为硅油、聚醚聚酯改性有机硅氧烷、聚二甲基硅氧烷、烷基改性有机硅氧烷的一种或二种以上的混合物。
作为优选，杀菌剂为硫酸铜、升汞、石灰波尔多液、氢氧化铜、氧化亚铜的一种或二种以上的混合物。
作为优选，成膜助剂为醇脂十二。
本发明还提供了一种空调室外机外壳用金属防锈漆的制备方法，包括以下步骤：
（1）、按上述重量份称取各种原料；
（2）、将沥青、膨润土、玻璃纤维、蛭石粉、陶粒、钛白粉、磷酸锌、增稠剂加入到反应釜内搅拌均匀，控制温度在50-60℃，静置5-10min，得到混合物；
（3）、再向反应釜内加入氟碳树脂、环氧树脂、异丙醇、水、流平剂、消泡剂、成膜助剂、杀菌剂，升高温度至60-70℃，搅拌10-15min后，静置5min，然后继续搅拌8-10min，最后冷却到室温即可。
其中，
步骤（2）和步骤（3）中的搅拌速度为300-400r/min。
本发明的一种空调室外机外壳用金属防锈漆及其制备方法，环保无污染，粘结能力强，耐腐蚀，耐水耐高温，具有较佳地防锈能力，使用寿命久，具体的有益效果如下：
（1）、氟碳乳液具有极佳地耐水性，超长耐候性，抗沾污、不黄变、抗碱、抗酸雨、抗烟雾等性能，能大大提高对空调室外机的保护能力；沥青、玻璃纤维、蛭石粉、陶粒均能有效地提高防锈漆的耐高温能力，具有较佳地保温性能，防止暴晒导致空调室外机不能有效地散热；
（2）、磷酸锌能作为缓蚀剂，可以提高防锈漆的防腐能力；环氧树脂和膨润土能提高防锈漆的粘着能力；增稠剂、流平剂、消泡剂、成膜助剂、杀菌剂的加入能有效地提高防锈漆的各项性能；
（3）、制备方法简单，能稳定地制备出防锈漆；本发明采用水代替油漆中的有机溶剂，十分环保。
具体实施方式
以下结合具体实施例对发明作进一步详细的描述。
实施例1
本实施例的一种空调室外机外壳用金属防锈漆，包括以下重量份的原料：
氟碳乳液50份、环氧树脂14份、沥青4份、膨润土1份、玻璃纤维5份、蛭石粉18份、陶粒7份、钛白粉17份、磷酸锌7份、异丙醇1份、水20份、消泡剂0.5份、杀菌剂2份、成膜助剂1份、增稠剂3份、流平剂1份。
本实施例中，消泡剂为聚氧丙烯聚氧乙烯甘油醚和聚二甲基硅氧烷混合物，两者之间的重量比为3:1。
本实施例中，增稠剂为硅藻土、凹凸棒石土、瓜尔胶、甲壳胺、阿拉伯树胶的混合物。
本实施例中，流平剂为硅油、聚醚聚酯改性有机硅氧烷、聚二甲基硅氧烷、烷基改性有机硅氧烷的混合物。
本实施例中，杀菌剂为硫酸铜、升汞、石灰波尔多液、氢氧化铜、氧化亚铜的混合物。
本实施例中，成膜助剂为醇脂十二。
本实施例还提供了一种空调室外机外壳用金属防锈漆的制备方法，包括以下步骤：
（1）、按上述重量份称取各种原料；
（2）、将沥青、膨润土、玻璃纤维、蛭石粉、陶粒、钛白粉、磷酸锌、增稠剂加入到反应釜内搅拌均匀，控制温度在50℃，静置5min，得到混合物；
（3）、再向反应釜内加入氟碳树脂、环氧树脂、异丙醇、水、流平剂、消泡剂、成膜助剂、杀菌剂，升高温度至60℃，搅拌10min后，静置5min，然后继续搅拌8min，最后冷却到室温即可。
其中，
步骤（2）和步骤（3）中的搅拌速度为300r/min。
实施例2
本实施例的一种空调室外机外壳用金属防锈漆，包括以下重量份的原料：
氟碳乳液55份、环氧树脂15份、沥青6份、膨润土2份、玻璃纤维6份、蛭石粉25份、陶粒8份、钛白粉18份、磷酸锌8份、异丙醇2份、水23份、消泡剂0.8份、杀菌剂3份、成膜助剂1.5份、增稠剂4份、流平剂1.5份。
本实施例中，消泡剂为聚氧丙烯聚氧乙烯甘油醚和聚二甲基硅氧烷混合物，两者之间的重量比为3:1。
本实施例中，增稠剂为硅藻土、凹凸棒石土、瓜尔胶、甲壳胺、阿拉伯树胶的混合物。
本实施例中，流平剂为硅油、聚醚聚酯改性有机硅氧烷、聚二甲基硅氧烷、烷基改性有机硅氧烷的混合物。
本实施例中，杀菌剂为硫酸铜、升汞、石灰波尔多液、氢氧化铜、氧化亚铜的混合物。
本实施例中，成膜助剂为醇脂十二。
本实施例还提供了一种空调室外机外壳用金属防锈漆的制备方法，包括以下步骤：
（1）、按上述重量份称取各种原料；
（2）、将沥青、膨润土、玻璃纤维、蛭石粉、陶粒、钛白粉、磷酸锌、增稠剂加入到反应釜内搅拌均匀，控制温度在55℃，静置8min，得到混合物；
（3）、再向反应釜内加入氟碳树脂、环氧树脂、异丙醇、水、流平剂、消泡剂、成膜助剂、杀菌剂，升高温度至65℃，搅拌13min后，静置5min，然后继续搅拌9min，最后冷却到室温即可。
其中，
步骤（2）和步骤（3）中的搅拌速度为350r/min。
实施例3
本实施例的一种空调室外机外壳用金属防锈漆，包括以下重量份的原料：
氟碳乳液60份、环氧树脂16份、沥青8份、膨润土3份、玻璃纤维7份、蛭石粉30份、陶粒9份、钛白粉20份、磷酸锌9份、异丙醇3份、水25份、消泡剂1份、杀菌剂4份、成膜助剂2份、增稠剂5份、流平剂2份。
本实施例中，消泡剂为聚氧丙烯聚氧乙烯甘油醚和聚二甲基硅氧烷混合物，两者之间的重量比为3:1。
本实施例中，增稠剂为硅藻土、凹凸棒石土、瓜尔胶、甲壳胺、阿拉伯树胶的混合物。
本实施例中，流平剂为硅油、聚醚聚酯改性有机硅氧烷、聚二甲基硅氧烷、烷基改性有机硅氧烷的混合物。
本实施例中，杀菌剂为硫酸铜、升汞、石灰波尔多液、氢氧化铜、氧化亚铜的混合物。
本实施例中，成膜助剂为醇脂十二。
本实施例还提供了一种空调室外机外壳用金属防锈漆的制备方法，包括以下步骤：
（1）、按上述重量份称取各种原料；
（2）、将沥青、膨润土、玻璃纤维、蛭石粉、陶粒、钛白粉、磷酸锌、增稠剂加入到反应釜内搅拌均匀，控制温度在60℃，静置10min，得到混合物；
（3）、再向反应釜内加入氟碳树脂、环氧树脂、异丙醇、水、流平剂、消泡剂、成膜助剂、杀菌剂，升高温度至70℃，搅拌15min后，静置5min，然后继续搅拌10min，最后冷却到室温即可。
其中，
步骤（2）和步骤（3）中的搅拌速度为400r/min。
实施例1-3中的检测结果如下：
表干：≤0.5h；实干：≤15h；黏度：≥140s；耐冲击：≥50kg.cm；耐盐水（500h）：漆膜无起泡、龟裂、剥落、锈斑，耐盐雾（600h）：1级；耐水性（500h）：漆膜无起泡、龟裂、剥落、锈斑；耐油性：漆膜无起泡、不脱落。
以上所述仅是本发明的优选实施方式，本发明的保护范围并不仅局限于上述实施例，凡属于本发明思路下的技术方案均属于本发明的保护范围。应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理前提下的若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (8)

1.一种空调室外机外壳用金属防锈漆，其特征在于：包括以下重量份的原料：
氟碳乳液50-60份、环氧树脂14-16份、沥青4-8份、膨润土1-3份、玻璃纤维5-7份、蛭石粉18-30份、陶粒7-9份、钛白粉17-20份、磷酸锌7-9份、异丙醇1-3份、水20-25份、消泡剂0.5-1份、杀菌剂2-4份、成膜助剂1-2份、增稠剂3-5份、流平剂1-2份。
2.根据权利要求1所述的空调室外机外壳用金属防锈漆，其特征在于：消泡剂为聚氧丙烯聚氧乙烯甘油醚和聚二甲基硅氧烷混合物，两者之间的重量比为3:1。
3.根据权利要求1所述的空调室外机外壳用金属防锈漆，其特征在于：增稠剂为硅藻土、凹凸棒石土、瓜尔胶、甲壳胺、阿拉伯树胶的一种或二种以上的混合物。
4.根据权利要求1所述的空调室外机外壳用金属防锈漆，其特征在于：流平剂为硅油、聚醚聚酯改性有机硅氧烷、聚二甲基硅氧烷、烷基改性有机硅氧烷的一种或二种以上的混合物。
5.根据权利要求1所述的空调室外机外壳用金属防锈漆，其特征在于：杀菌剂为硫酸铜、升汞、石灰波尔多液、氢氧化铜、氧化亚铜的一种或二种以上的混合物。
6.根据权利要求1所述的空调室外机外壳用金属防锈漆，其特征在于：成膜助剂为醇脂十二。
7.根据权利要求1-6任意一项所述的一种空调室外机外壳用金属防锈漆的制备方法，其特征在于：包括以下步骤：
（1）、按上述重量份称取各种原料；
（2）、将沥青、膨润土、玻璃纤维、蛭石粉、陶粒、钛白粉、磷酸锌、增稠剂加入到反应釜内搅拌均匀，控制温度在50-60℃，静置5-10min，得到混合物；
（3）、再向反应釜内加入氟碳乳液、环氧树脂、异丙醇、水、流平剂、消泡剂、成膜助剂、杀菌剂，升高温度至60-70℃，搅拌10-15min后，静置5min，然后继续搅拌8-10min，最后冷却到室温即可。
8.根据权利要求7所述的空调室外机外壳用金属防锈漆的制备方法，其特征在于：步骤（2）和步骤（3）中的搅拌速度为300-400r/min。
CN201710467150.7A 2017-06-20 2017-06-20 一种空调室外机外壳用金属防锈漆及其制备方法 Withdrawn CN107216728A (zh)