CN107212698A - A kind of osteoacusis music pillow and its processing method - Google Patents
A kind of osteoacusis music pillow and its processing method Download PDFInfo
- Publication number
- CN107212698A CN107212698A CN201710357484.9A CN201710357484A CN107212698A CN 107212698 A CN107212698 A CN 107212698A CN 201710357484 A CN201710357484 A CN 201710357484A CN 107212698 A CN107212698 A CN 107212698A
- Authority
- CN
- China
- Prior art keywords
- pillow
- parts
- osteoacusis
- slow
- pillowcase
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of osteoacusis music pillow and its processing method, it is related to pillow processing technique field, including pillow body, the pillow body is in butterfly structure, including the pillowcase being made up of imitation velvet fabric, the pillow being made up of slow-recovery sponge and the loudspeaker being fixed at the top of pillow, the loudspeaker is connected by audio connecting cord with the audio player outside pillow body.Osteoacusis music pillow of the present invention improves sleep quality of human body by the double action of its comfortableness and broadcasting music, user develops ears, earphone need not be worn, perspiration is brought in ear when avoiding wearing earphone a series of health and health problems, while music sound wave will not have influence on other people because of spreading in atmosphere.
Description
Technical field:
The present invention relates to pillow processing technique field, and in particular to a kind of osteoacusis music pillow and its processing method.
Background technology:
Sleep occupies 1/3rd times of life, it can be seen that how heavy sleep is for the life of people
Will.Pillow, is a kind of sleep tool, is that people are the comfortable filler used of sleep.Recognize from modern medicine study, people
The backbone of body is straight line in terms of front, but side sees it is the curve with three physiological bendings.For the normal of protection neck
Physiological bending, normal physiological activity during maintenance people's sleep, must use pillow during sleep.
The various structures of pillow, and the fashionable market of health pillow in recent years, many people with sleep-disorder are want by health care
Rest the head on to improve sleep quality.But the health pillow level sold in the market is uneven, the traditional Chinese medicine quality of some Chinese medicinal pillows filling is poor,
Do not have at all promote sleep effect, also there are problems that on the contrary Chinese medicine go mouldy caused by hygiene and health.
Osteoacusis music pillow is a kind of novel pillow, makes one to loosen by playing music, and sleep is promoted so as to play
Effect.Instead of listening music to promote the mode slept using earphone in the past, osteoacusis music pillow utilizes bone conduction technology conducted acoustic waves, without
Earphone is filled in into ear, ears are developed, it is to avoid a series of health and health problem brought of being perspired when wearing earphone in ear, simultaneously
Sound wave will not have influence on other people because of spreading in atmosphere.
The content of the invention:
It is good and without interference with other people that the technical problems to be solved by the invention are to provide a kind of hygiene and health, comfortableness
Osteoacusis music pillow and its processing method.
The technical problems to be solved by the invention are realized using following technical scheme:
A kind of osteoacusis music pillow, including pillow body, the pillow body are in butterfly structure, including by imitation velvet fabric
The pillowcase being made, the pillow being made up of slow-recovery sponge and the loudspeaker being fixed at the top of pillow, the loudspeaker pass through audio
Connecting line is connected with the audio player outside pillow body.
The audio player be selected from smart mobile phone, tablet personal computer or other have audio output and volume adjusting function concurrently
Player.
The loudspeaker is arranged with 2.
The pillowcase back side is provided with slide fastener.
A kind of processing method of osteoacusis music pillow, comprises the following steps:
(1) the high-grade velvet produced using acetate fiber and acrylic fiber as raw material is selected as pillow case fabric, through cutting out
Cut, sew, the pillowcase that outward appearance is in butterfly structure is made;
(2) using slow-recovery sponge as pillow packing material, slow-recovery sponge is processed into and matched with pillowcase structure
Pillow, and loudspeaker, slide fastener extension of the audio connecting cord of connection on a speaker through the pillowcase back side are installed at the top of pillow
To outside pillowcase;
(3) pillow for being fixed with loudspeaker is filled into pillowcase, adjusts and zipped up after pillow, produce osteoacusis sound
Happy pillow.
The slow-recovery sponge is made up of the raw material of following parts by weight:50-70 parts of PPG, trihydroxy polyethers
10-20 parts, 5-10 parts of gel auxiliary agent, 3-5 parts of down fiber, 3-5 parts of foaming agent, 2-3 parts of glycerin polyether, 2-3 parts of soybean fiber,
1-2 parts of foam stabiliser, 0.2-0.5 parts of catalyst, its preparation method is:Down fiber is added into gel auxiliary agent and soybean is fine
Dimension, is warming up to 120-125 DEG C of insulation grinding 15min, the microwave treatment under microwave frequency 2450MHz, power output 700W
5min, produces gelatinous fibre;By PPG, trihydroxy polyethers, foaming agent and catalyst in rotating speed 4000-4500r/min
Lower stirring 30s, then adds gelatinous fibre, glycerin polyether and foam stabiliser, continues to stir 10s, by foamed liquid
Pour into mould, cut after 24h, produce slow-recovery sponge.
The PPG is selected from hydroxyl value 45-65, degree of functionality 2.5-4.5 PPOX triol.
The catalyst is by mass percent 50-60% amine catalyst A33,20-30% organotin catalysts T9 and 10-
20% catalyst A1 is constituted.
The gel auxiliary agent is made up of the raw material of following parts by weight:5-10 parts of polyvinyl alcohol resin, poloxamer 3-5
Part, 2-3 parts of PAMA, 1-2 parts of polyglutamic acid, 0.5-1 parts of rilanit special, hexamethylolmelamine six
0.5-1 parts of methyl ether, 0.1-0.3 parts of nanometer titanium dioxide, its preparation method is:90-95 DEG C of hot water is added into polyvinyl alcohol resin
Until being completely dissolved, poloxamer, polyglutamic acid and hexamethylolmelamine pregnancy ether are added, and at 90-95 DEG C
Insulation mixing 15min, then adds PAMA, rilanit special and nanometer titanium dioxide, is continuously heating to 115-
120 DEG C of insulation mixing 15min, finally naturally cool to room temperature, produce gel auxiliary agent.
Being added with for above-mentioned gel auxiliary agent is beneficial to strengthen the comfortableness and other performances of made slow-recovery sponge.
The foaming agent is made up of the raw material of following parts by weight:3-5 parts of PVPP, 2-3 parts of tea seed powder, polyoxygenated
0.5-1 parts of ethene, 0.5-1 parts of N hydroxymethyl acrylamide, 20-25 parts of water, its preparation method is:Xiang Shuizhong adds tea seed powder,
Soak and defibrination three times repeatedly of power 1.5kW fiberizers are utilized after 15min, cross 200 mesh sieves, and polyoxygenated is added into gained filtrate
Ethene and N hydroxymethyl acrylamide, are warming up to reflux state insulation mixing 15min, then add PVPP, continue back
Stream insulation mixing 10min, gained mixed liquor naturally cools to room temperature, produces foaming agent.
Water is replaced with above-mentioned foaming agent, the performance of made slow-recovery sponge is improved while enhanced foaming effect.
The beneficial effects of the invention are as follows:Osteoacusis music pillow of the present invention is by its comfortableness and plays the dual of music
Act on improving sleep quality of human body, the music played by loudspeaker is transmitted to human body using bone conduction technology, and user opens
Ears are sent out, without wearing earphone, it is to avoid a series of health and health problem brought of being perspired when wearing earphone in ear, while musical sound
Ripple will not have influence on other people because of spreading in atmosphere;And performance is made by the slow-recovery sponge preparation method
Excellent slow-recovery sponge, service life is long, good permeability, and comprehensive support is provided for shoulder neck, quick neutralizing shoulder neck pressure, to help
User is helped to rapidly enter entirely loose sleep state.
Brief description of the drawings:
Fig. 1 is structure front view of the invention;
Fig. 2 is structure rearview of the invention;
Wherein:1- pillowcases;2- pillows;3- loudspeakers;4- audio connecting cords;5- audio players;6- slide fasteners.
Embodiment:
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Conjunction is specifically illustrating and embodiment, and the present invention is expanded on further.
Embodiment 1
As depicted in figs. 1 and 2, a kind of osteoacusis music pillow, including pillow body, the pillow body is in butterfly structure,
Including the pillowcase 1 being made up of imitation velvet fabric, the pillow 2 being made up of slow-recovery sponge and the loudspeaker 3 being fixed at the top of pillow,
Loudspeaker is connected by audio connecting cord 4 with the audio player 5 outside pillow body, audio player be selected from smart mobile phone,
Tablet personal computer or other have the player of audio output and volume adjusting function concurrently, loudspeaker is arranged with 2, and the pillowcase back side is set
There is slide fastener 6.
(1) the high-grade velvet produced using acetate fiber and acrylic fiber as raw material is selected as pillow case fabric, through cutting out
Cut, sew, the pillowcase that outward appearance is in butterfly structure is made;
(2) using slow-recovery sponge as pillow packing material, slow-recovery sponge is processed into and matched with pillowcase structure
Pillow, and loudspeaker, slide fastener extension of the audio connecting cord of connection on a speaker through the pillowcase back side are installed at the top of pillow
To outside pillowcase;
(3) pillow for being fixed with loudspeaker is filled into pillowcase, adjusts and zipped up after pillow, produce osteoacusis sound
Happy pillow.
The preparation of slow-recovery sponge:3kg down fibers and 2kg soybean fibers are added into 10kg gel auxiliary agents, is warming up to
120-125 DEG C of insulation grinding 15min, the microwave treatment 5min under microwave frequency 2450MHz, power output 700W, are produced solidifying
Glue fiber;By 60kg PPGs, 10kg trihydroxies polyethers, 3kg foaming agents and 0.2kg catalyst in rotating speed 4000-
30s is stirred under 4500r/min, gelatinous fibre, 3kg glycerin polyethers and 1kg foam stabilisers is then added, continues to stir 10s, will
Foamed liquid is poured into mould, is cut after 24h, is produced slow-recovery sponge.
Wherein, PPG is selected from hydroxyl value 45-65, degree of functionality 2.5-4.5 PPOX triol.
Catalyst is by the amine catalyst A33 of mass percent 50%, 30% organotin catalysts T9 and 20% catalyst A1 groups
Into.
The preparation of gel auxiliary agent:90-95 DEG C of hot water is added until being completely dissolved into 5kg polyvinyl alcohol resins, is added
5kg poloxamers, 1kg polyglutamic acids and 0.5kg hexamethylolmelamine pregnancy ethers, and mixed in being incubated at 90-95 DEG C
15min, then adds 3kg PAMAs, 0.5kg rilanit specials and 0.2kg nanometer titanium dioxides, is continuously heating to
115-120 DEG C of insulation mixing 15min, finally naturally cools to room temperature, produces gel auxiliary agent.
The preparation of foaming agent:Power 1.5kW fiberizers are utilized after 0.5kg tea seed powder, immersion 15min are added into 5kg water
Defibrination three times repeatedly, cross 200 mesh sieves, and addition 0.2kg polyethylene glycol oxides and 0.1kgN- methylol acryloyls into gained filtrate
Amine, is warming up to reflux state insulation mixing 15min, then adds 0.8kg PVPPs, continue the insulation mixing 10min that flows back,
Gained mixed liquor naturally cools to room temperature, produces foaming agent.
Embodiment 2
The preparation of slow-recovery sponge:5kg down fibers and 3kg soybean fibers are added into 10kg gel auxiliary agents, is warming up to
120-125 DEG C of insulation grinding 15min, the microwave treatment 5min under microwave frequency 2450MHz, power output 700W, are produced solidifying
Glue fiber;By 70kg PPGs, 15kg trihydroxies polyethers, 5kg foaming agents and 0.5kg catalyst in rotating speed 4000-
30s is stirred under 4500r/min, gelatinous fibre, 2kg glycerin polyethers and 1kg foam stabilisers is then added, continues to stir 10s, will
Foamed liquid is poured into mould, is cut after 24h, is produced slow-recovery sponge.
Wherein, PPG is selected from hydroxyl value 45-65, degree of functionality 2.5-4.5 PPOX triol.
Catalyst is by the amine catalyst A33 of mass percent 50%, 30% organotin catalysts T9 and 20% catalyst A1 groups
Into.
The preparation of gel auxiliary agent:90-95 DEG C of hot water is added until being completely dissolved into 5kg polyvinyl alcohol resins, is added
3kg poloxamers, 2kg polyglutamic acids and 0.5kg hexamethylolmelamine pregnancy ethers, and mixed in being incubated at 90-95 DEG C
15min, then adds 2kg PAMAs, 0.5kg rilanit specials and 0.3kg nanometer titanium dioxides, is continuously heating to
115-120 DEG C of insulation mixing 15min, finally naturally cools to room temperature, produces gel auxiliary agent.
The preparation of foaming agent:Power 1.5kW fiberizers are utilized after 0.5kg tea seed powder, immersion 15min are added into 5kg water
Defibrination three times repeatedly, cross 200 mesh sieves, and addition 0.1kg polyethylene glycol oxides and 0.2kg N- methylol propylene into gained filtrate
Acid amides, is warming up to reflux state insulation mixing 15min, then adds 1kg PVPPs, continue the insulation mixing 10min that flows back,
Gained mixed liquor naturally cools to room temperature, produces foaming agent.
Reference examples 1
The preparation of slow-recovery sponge:5kg down fibers and 3kg soybean fibers are added into 10kg gel auxiliary agents, is warming up to
120-125 DEG C of insulation grinding 15min, the microwave treatment 5min under microwave frequency 2450MHz, power output 700W, are produced solidifying
Glue fiber;By 70kg PPGs, 15kg trihydroxies polyethers, 5kg water and 0.5kg catalyst in rotating speed 4000-4500r/min
Lower stirring 30s, then adds gelatinous fibre, 2kg glycerin polyethers and 1kg foam stabilisers, continues to stir 10s, will be foamed
Liquid pour into mould, after 24h cut, produce slow-recovery sponge.
Wherein, PPG is selected from hydroxyl value 45-65, degree of functionality 2.5-4.5 PPOX triol.
Catalyst is by the amine catalyst A33 of mass percent 50%, 30% organotin catalysts T9 and 20% catalyst A1 groups
Into.
The preparation of gel auxiliary agent:90-95 DEG C of hot water is added until being completely dissolved into 5kg polyvinyl alcohol resins, is added
3kg poloxamers, 2kg polyglutamic acids and 0.5kg hexamethylolmelamine pregnancy ethers, and mixed in being incubated at 90-95 DEG C
15min, then adds 2kg PAMAs, 0.5kg rilanit specials and 0.3kg nanometer titanium dioxides, is continuously heating to
115-120 DEG C of insulation mixing 15min, finally naturally cools to room temperature, produces gel auxiliary agent.
Reference examples 2
The preparation of slow-recovery sponge:10kg gel auxiliary agents are warming up to 120-125 DEG C of insulation grinding 15min, then at microwave
Microwave treatment 5min under frequency 2450MHz, power output 700W;By 70kg PPGs, 15kg trihydroxies polyethers, 5kg hairs
Infusion and 0.5kg catalyst stir 30s under rotating speed 4000-4500r/min, and gel auxiliary agent, the 2kg then added after microwave is sweet
Oily polyethers and 1kg foam stabiliser, continues to stir 10s, foamed liquid is poured into mould, cut after 24h, produces slow
Recovery sponge.
Wherein, PPG is selected from hydroxyl value 45-65, degree of functionality 2.5-4.5 PPOX triol.
Catalyst is by the amine catalyst A33 of mass percent 50%, 30% organotin catalysts T9 and 20% catalyst A1 groups
Into.
The preparation of gel auxiliary agent:90-95 DEG C of hot water is added until being completely dissolved into 5kg polyvinyl alcohol resins, is added
3kg poloxamers, 2kg polyglutamic acids and 0.5kg hexamethylolmelamine pregnancy ethers, and mixed in being incubated at 90-95 DEG C
15min, then adds 2kg PAMAs, 0.5kg rilanit specials and 0.3kg nanometer titanium dioxides, is continuously heating to
115-120 DEG C of insulation mixing 15min, finally naturally cools to room temperature, produces gel auxiliary agent.
The preparation of foaming agent:Power 1.5kW fiberizers are utilized after 0.5kg tea seed powder, immersion 15min are added into 5kg water
Defibrination three times repeatedly, cross 200 mesh sieves, and addition 0.1kg polyethylene glycol oxides and 0.2kg N- methylol propylene into gained filtrate
Acid amides, is warming up to reflux state insulation mixing 15min, then adds 1kg PVPPs, continue the insulation mixing 10min that flows back,
Gained mixed liquor naturally cools to room temperature, produces foaming agent.
Reference examples 3
The preparation of slow-recovery sponge:By 70kg PPGs, 15kg trihydroxies polyethers, 5kg foaming agents and 0.5kg catalysis
30s is stirred in agent under rotating speed 4000-4500r/min, then adds 2kg glycerin polyethers and 1kg foam stabilisers, continues to stir
10s, foamed liquid is poured into mould, is cut after 24h, is produced slow-recovery sponge.
Wherein, PPG is selected from hydroxyl value 45-65, degree of functionality 2.5-4.5 PPOX triol.
Catalyst is by the amine catalyst A33 of mass percent 50%, 30% organotin catalysts T9 and 20% catalyst A1 groups
Into.
The preparation of foaming agent:Power 1.5kW fiberizers are utilized after 0.5kg tea seed powder, immersion 15min are added into 5kg water
Defibrination three times repeatedly, cross 200 mesh sieves, and addition 0.1kg polyethylene glycol oxides and 0.2kg N- methylol propylene into gained filtrate
Acid amides, is warming up to reflux state insulation mixing 15min, then adds 1kg PVPPs, continue the insulation mixing 10min that flows back,
Gained mixed liquor naturally cools to room temperature, produces foaming agent.
Embodiment 3
Performance is carried out to embodiment 1, embodiment 2, reference examples 1, reference examples 2 and the made slow-recovery sponge of reference examples 3
Test, test result is as shown in table 1.
The performance of the made slow-recovery sponge of table 1
Embodiment 1 | Embodiment 2 | Reference examples 1 | Reference examples 2 | Reference examples 3 | |
The resilience time (60kg) | 3-4s | 3-4s | 4-5s | 4-5s | 5-6s |
Resilience rate (7000 times) | 1.5% | 1.5% | 2% | 3% | 4% |
Support coefficient | 8 | 8 | 6 | 5 | 3 |
Air mass flow | 0.5 | 0.5 | 0.3 | 0.2 | 0.15 |
Fold access times | > 8,000 times | > 8,000 times | 7-8 thousand times | 7-8 thousand times | < 7,000 times |
Note:Support coefficient condition determination is the pressure limit of 80% pressure limit contrast 25%.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (10)
1. a kind of osteoacusis music pillow, including pillow body, the pillow body are in butterfly structure, it is characterised in that:Including by
Pillowcase, the pillow being made up of slow-recovery sponge and the loudspeaker being fixed at the top of pillow that imitation velvet fabric is made, it is described to raise one's voice
Device is connected by audio connecting cord with the audio player outside pillow body.
2. osteoacusis music pillow according to claim 1, it is characterised in that:The audio player be selected from smart mobile phone,
Tablet personal computer or other have the player of audio output and volume adjusting function concurrently.
3. osteoacusis music pillow according to claim 1, it is characterised in that:The loudspeaker is arranged with 2.
4. osteoacusis music pillow according to claim 1, it is characterised in that:The pillowcase back side is provided with slide fastener.
5. a kind of processing method of osteoacusis music pillow, it is characterised in that comprise the following steps:
(1) the high-grade velvet that selection is produced as raw material using acetate fiber and acrylic fiber is as pillow case fabric, clipped, stitch
System, is made the pillowcase that outward appearance is in butterfly structure;
(2) using slow-recovery sponge as pillow packing material, slow-recovery sponge is processed into the pillow matched with pillowcase structure
Core, and loudspeaker is installed at the top of pillow, slide fastener of the audio connecting cord through the pillowcase back side of connection on a speaker extends to pillow
Set is outside;
(3) pillow for being fixed with loudspeaker is filled into pillowcase, adjusts and zipped up after pillow, produce osteoacusis music
Pillow.
6. osteoacusis music pillow according to claim 5, it is characterised in that the slow-recovery sponge is by following parts by weight
Raw material be made:50-70 parts of PPG, 10-20 parts of trihydroxy polyethers, 5-10 parts of gel auxiliary agent, 3-5 parts of down fiber,
3-5 parts of foaming agent, 2-3 parts of glycerin polyether, 2-3 parts of soybean fiber, 1-2 parts of foam stabiliser, 0.2-0.5 parts of catalyst, it is made
Preparation Method is:Down fiber and soybean fiber are added into gel auxiliary agent, 120-125 DEG C of insulation grinding 15min is warming up to, then at
Microwave treatment 5min under microwave frequency 2450MHz, power output 700W, produces gelatinous fibre;PPG, trihydroxy are gathered
Ether, foaming agent and catalyst stir 30s under rotating speed 4000-4500r/min, then add gelatinous fibre, glycerin polyether and bubble
Foam stabilizers, continue to stir 10s, foamed liquid are poured into mould, cut after 24h, produce slow-recovery sponge.
7. osteoacusis music pillow according to claim 6, it is characterised in that:The PPG be selected from hydroxyl value 45-65,
Degree of functionality 2.5-4.5 PPOX triol.
8. osteoacusis music pillow according to claim 6, it is characterised in that:The catalyst is by mass percent 50-
60% amine catalyst A33,20-30% organotin catalysts T9 and 10-20% catalyst A1 is constituted.
9. osteoacusis music pillow according to claim 6, it is characterised in that the gel auxiliary agent is by following parts by weight
Raw material is made:5-10 parts of polyvinyl alcohol resin, 3-5 parts of poloxamer, 2-3 parts of PAMA, polyglutamic acid 1-2
Part, 0.5-1 parts of rilanit special, 0.5-1 parts of hexamethylolmelamine pregnancy ether, 0.1-0.3 parts of nanometer titanium dioxide, it is prepared
Method is:90-95 DEG C of hot water is added until being completely dissolved into polyvinyl alcohol resin, adds poloxamer, polyglutamic acid
With hexamethylolmelamine pregnancy ether, and at 90-95 DEG C insulation mixing 15min, then add PAMA,
Rilanit special and nanometer titanium dioxide, are continuously heating to 115-120 DEG C of insulation mixing 15min, finally naturally cool to room temperature, i.e.,
Obtain gel auxiliary agent.
10. osteoacusis music pillow according to claim 6, it is characterised in that the foaming agent is by following parts by weight
Raw material is made:3-5 parts of PVPP, 2-3 parts of tea seed powder, 0.5-1 parts of polyethylene glycol oxide, N hydroxymethyl acrylamide 0.5-1
Part, 20-25 parts of water, its preparation method is:Xiang Shuizhong utilizes power 1.5kW fiberizers repeatedly after adding tea seed powder, immersion 15min
Defibrination three times, crosses 200 mesh sieves, and adds polyethylene glycol oxide and N hydroxymethyl acrylamide into gained filtrate, is warming up to backflow
State insulation mixing 15min, then adds PVPP, continues flow back insulation mixing 10min, gained mixed liquor natural cooling
To room temperature, foaming agent is produced.