CN107201050A - A kind of preparation method of the strong clamp of weight capacity and its outer shell - Google Patents
A kind of preparation method of the strong clamp of weight capacity and its outer shell Download PDFInfo
- Publication number
- CN107201050A CN107201050A CN201710474835.4A CN201710474835A CN107201050A CN 107201050 A CN107201050 A CN 107201050A CN 201710474835 A CN201710474835 A CN 201710474835A CN 107201050 A CN107201050 A CN 107201050A
- Authority
- CN
- China
- Prior art keywords
- clamp
- loading plate
- support feet
- outer shell
- lines
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the preparation method of a kind of strong clamp of weight capacity and its outer shell, the clamp includes loading plate and is arranged at some support feets of loading plate bottom, the peripheral ring of described support feet is provided with one or more compression telescopic chute, the top surface of the loading plate and/or bottom surface, and the bottom surface of support feet is provided with for strengthening the lines of loading plate endurance, and circuit board is additionally provided with the loading plate.The clamp that the present invention is provided, strong with weight capacity, service life is long, is easy to user to carry out the advantage of intelligent management to clamp.
Description
Technical field
The present invention relates to cargo transport technical field, and in particular to the system of a kind of strong clamp of weight capacity and its outer shell
Preparation Method.
Background technology
Clamp is the important supporting body for packing large cargo, is not only required with relatively higher weight capacity, while also
The lighter in weight of its own is sought, to advantageously reduce cost of transportation.Traditional clamp has wooden clamp, plastics clamp, metal clamp
And paper templet etc..At present, due to timber shortage, thus the wooden clamp cost more and more higher manufactured with timber, cause wooden clamp
Price more and more higher, from the angle for reducing cost He meeting environmental protection requirement, wooden clamp is unfavorable in goods packing
Field popularization and application;Traditional plastics clamp is due to its intensity existing defects, from the angle of environmental requirement, plastics clamp
It is unfavorable in the popularization and application of goods packing field;Metal clamp, because its heavy, price is higher, from the point of view of cost,
Also it is unfavorable in the popularization and application of goods packing field.Although and paper templet have the advantages that environmental protection, lighter weight, its there is also
The shortcomings of bad mechanical property, weight capacity are small and fragile, is easily brought about great losses to cargo transport.
At present, existing clamp is in load-bearing, because the resistance to compression buffer capacity of support feet and loading plate is poor, causes support
Pin or loading plate are easily broken so that the weight capacity of clamp is not strong, and have impact on the service life of clamp.In addition,
Existing clamp is more single due to its function, lacks corresponding data information management, so as to be not easy to clamp in itself and goods
The information management of thing.In addition, existing clamp also exist it is not degradable, the shortcomings of easily cause environmental pollution.
The content of the invention
The problem of to overcome the deficiencies in the prior art and existing, a kind of weight capacity of present invention offer is strong, service life is long,
The clamp of information management is convenient for, and with environment-friendly degradable, does not result in the clamp of environmental pollution.
The present invention is achieved by the following technical solutions:A kind of strong clamp of weight capacity, the clamp includes carrying
Plate and some support feets for being arranged at loading plate bottom, the peripheral ring of described support feet is pressurized provided with one or more to be stretched
Groove.
Further, the top surface of the loading plate and/or bottom surface are provided with the lines for strengthening loading plate endurance;It is excellent
Selection of land, the lines that the top surface of the loading plate is set is made up of multiple T-shaped inner groovies;The bottom surface of the loading plate is set
The lines put is made up of multiple horizontal, vertical and/or oblique inner groovies in " one " font.
Further, the bottom of the support feet is provided with the lines for strengthening support feet endurance;The support feet bottom
The lines that portion is set is made up of the inner groovy of one or more " ten " fonts;In addition, the section of the support feet preferably in fall etc.
Waist is trapezoidal;
Further, the loading plate or support feet are built-in with circuit board, and the circuit board includes the memory being sequentially connected
Chip, master control IC and Radio Frequency ID card;The circuit board also includes locating module, and the locating module connects with the master control IC
Connect;The top surface of the loading plate or side are provided with a display window, and the circuit board is arranged in the display window.
Further, the surface of the clamp be provided with for the Quick Response Code as clamp authentication code and/or for
Manage the Quick Response Code of the APP links of clamp logistics information
Preferably, the loading plate and support feet are made up of the material of environment-friendly degradable, specifically, the loading plate and
Support feet is made up of outer shell and the intermediate filling layer being filled in outer shell;
Wherein, the outer shell is prepared from by the component of following mass parts:
The intermediate filling layer is prepared from by the component of following mass parts:
Further, the shell layer component also includes titanium dioxide and alundum (Al2O3), and its mass parts is as follows:
1-3 parts of titanium dioxide;
0.1-0.3 parts of alundum (Al2O3).
Present invention also offers a kind of preparation method that the outer shell is made, its step is as follows:
S1, stirring:It will be mixed evenly for being made after each component of outer shell is weighed according to mass ratio;
S2, roasting material:Material after stirring carries out roasting material, bakes material temperature degree between 60-80 DEG C, and the roasting material time is
3.5-4.5 hour;
S3, expects pipe feeding and machine-shaping:The material after roasting material process will be completed and process equipment is sent to by expects pipe, to add
Work is into sheet material or injection molding, and wherein expects pipe temperature is 130-160 DEG C.
Compared with prior art, the clamp that the present invention is provided has following advantageous effects:(1) by support feet
Peripheral ring sets compression telescopic chute, and sets in the bottom of support feet the lines of the inner groovy composition of one or more " ten " fonts,
The resistance to compression buffer capacity of support feet can effectively be strengthened, so as to greatly strengthen the bearing capacity of support feet;(2) by loading plate
Top surface and bottom surface, which are set, can play the lines of resistance to compression buffering, so that the weight capacity of clamp is greatly enhanced;In addition in carrying
Plate top surface sets the lines being made up of the inner groovy of multiple " T " fonts, can also be effectively increased the coefficient of friction of carrying plate top surface, from
And effectively strengthening anti-skidding effect so that the goods being positioned on loading plate is more consolidated;(3) top surface in loading plate, bottom are passed through
Face, the bottom surface and side of support feet are provided with the lines for strengthening resistance to compression buffer capacity, both effectively strengthen holding for clamp
Beijing South Maxpower Technology Co. Ltd's power, and effectively extend the service life of clamp;(4) by setting the memory core with imformation memory function on clamp
Piece, the locating module with positioning function and the Radio Frequency ID card of No. ID can be actively sent, be easy to chase after so that clamp has
Track clamp positional information, is easy to user to carry out the advantage of intelligent management to clamp, (5) described loading plate and support feet are by ring
The material composition of protecting degradable, is easy to natural degradation and recovery, can be prevented effectively from environmental pollution.
Brief description of the drawings
Fig. 1 is the top surface structure schematic diagram of clamp described in the embodiment of the present invention.
Fig. 2 is the schematic diagram of clamp bottom surface structure described in the embodiment of the present invention.
Fig. 3 is the dimensional structure diagram of clamp bottom surface described in the embodiment of the present invention.
Fig. 4 is the mplifying structure schematic diagram at A in Fig. 3.
Fig. 5 is the side structure schematic diagram of clamp described in the embodiment of the present invention.
Fig. 6 is the cross section structure diagram at B-B in Fig. 5.
Fig. 7 is the module signal connection figure of circuit board described in the embodiment of the present invention.
Embodiment
For the ease of the understanding of those skilled in the art, further is made to the present invention below in conjunction with the drawings and specific embodiments
It is described in detail.
As shown in accompanying drawing 1- Fig. 4, a kind of strong clamp of weight capacity, the clamp includes loading plate and is arranged at loading plate
Some support feets of bottom, the peripheral ring of described support feet is provided with one or more compression telescopic chute.By in support feet 20
Periphery compression telescopic chute 21 is set, resistance to compression buffer capacity of the support feet 20 in compression can be effectively increased, so as to increase greatly
Plus the weight capacity of support feet.In the present embodiment, the periphery of the support feet 20 is at least equipped with two compression telescopic chutes 21,
As shown in Figure 4.
In order to further strengthen the resistance to compression buffer capacity of support feet 20, the bottom of the support feet 20 is preferably provided for
Strengthen the lines that support feet 20 is withstood forces.In the present embodiment, the lines that the bottom of support feet 20 is set is by one or more
The inner groovy composition of " ten " font, as shown in accompanying drawing 2 and accompanying drawing 4.In the present embodiment, the inner groovy that the bottom of support feet 20 is set
Referred to as " ten " font inner groovy 22.
In the present embodiment, the setting quantity of the support feet 20 is preferably nine, and nine support feets 20 are arranged in 3 rows × 3
Arranged distribution is propped up in the bottom of loading plate 10, and positioned at the size of middle row or the support feet 20 of the row of centre one more than remaining
The size of spike 20, (in Fig. 2, the size positioned at the support feet 20 of the row of centre one is supported more than remaining as shown in accompanying drawing 2 and Fig. 3
The size of pin 20).In addition, the section of the support feet 20 described in the present embodiment is in isosceles trapezoid, the isosceles trapezoid
The angle of inclination preferred scope of two waist edges is 30 ° -60 °, and specific angle of inclination can be chosen according to actual needs.
As preferred embodiment, the top surface of the loading plate 10 and/or bottom surface are provided with and held for strengthening loading plate 10
The lines of stress.In order to preferably strengthen top surface and the bottom surface of the loading plate 10 in the weight capacity of loading plate 10, the present embodiment
It is provided with the lines for strengthening endurance.Wherein, the lines that the top surface of the loading plate 10 is set is by multiple T-shaped
Inner groovy composition, as shown in Figure 1;And the lines that the bottom surface of the loading plate 10 is set then by multiple horizontal, vertical and
Oblique one kind or any a variety of inner groovies in " one " font are constituted, as shown in Figure 2.In the present embodiment, by loading plate 10
The inner groovy that top surface is set is referred to as " T " font inner groovy 11, and the inner groovy that the bottom surface of loading plate 10 is set then more inner groovy
Setting direction be referred to as transverse direction " one " font inner groovy 12, vertical " one " font inner groovy 13 and oblique " one " font
Inner groovy 14.
In the present embodiment, why the top surface inner groovy of loading plate 10 is set to " T " font inner groovy 11, except can be effective
Outside the resistance to compression buffer capacity for increasing the top surface of loading plate 10, the coefficient of friction of the top surface of loading plate 10 can be also effectively increased, so that effectively
The anti-skidding effect of enhancing so that the goods being positioned on loading plate 10 is more consolidated.Relative to some clamps of the prior art
In " T " font set in the waveform anti-slip veins that the top surface of loading plate 10 is set, the present embodiment with the top surface of loading plate 10
Groove 11, may be such that the coefficient of friction of the top surface of loading plate 10 is bigger, skidproof effect is more preferable.And set various in the bottom surface of loading plate 10
" one " the font inner groovy in direction (horizontal, vertical and oblique), then be the toughness in order to be effectively increased loading plate 10 and load-bearing
Ability.
The clamp that the present embodiment is provided is provided with by interior in the bottom surface of the top surface of loading plate 10, bottom surface and support feet 20
The lines of groove composition, by these lines of setting, may be such that clamp when load-bearing is under pressure, once overstress, this
A little lines can play the leeway that the resistance to compression as spring is buffered, so as to effectively strengthen the weight capacity of clamp.If no
Above-mentioned lines is set, and is only merely plane, once overstress, due to lacking the leeway of resistance to compression buffering, loading plate 10 and branch
Spike 20 is easy for directly being destroyed.Therefore, the clamp in the present embodiment, its by the top surface in loading plate, bottom surface,
The bottom surface and side of support feet are provided with the lines for strengthening resistance to compression buffer capacity, so as to both effectively strengthen holding for clamp
Beijing South Maxpower Technology Co. Ltd's power, and effectively extend the service life of clamp.Clamp in the embodiment of the present invention, its dynamic weight capacity can reach 1-2
Ton, quiet weight capacity 3-5 ton, and its weight is 2.8-3.5kg, weight is only the 1/3 of the wood pallet of equal weight capacity to arrive
1/6。
In wherein one preferred embodiment, location tracking and intelligent pipe are carried out to the clamp for the ease of user
Reason, the clamp is also built-in with circuit board, and the circuit board can be built in loading plate or branch, and the present embodiment is preferably by circuit board
It is placed in loading plate.In the present embodiment, as shown in fig. 7, the circuit board include the memory chip being sequentially connected, master control IC,
Radio Frequency ID card, and (locating module in the present embodiment is preferably GPS location mould to the locating module being connected with the master control IC
Block).Wherein, the Radio Frequency ID card, it is also connected with hand-held reading equipment, described hand-held to realize the immediately monitoring to clamp
Reading equipment can also be connected with computer, to facilitate the data transfer read to computer end to be stored, be easy to user
Data summarization is carried out, so as to facilitate user to carry out relevant information management to clamp and goods.In addition, the Radio Frequency ID card can also lead to
Cross Data Data switching equipment to be attached with high in the clouds, so as to easily transmit related data to high in the clouds, realize Large Copacity
The safety storage of data, and it is prevented effectively from the unexpected loss of data message.And it is (excellent using the memory chip set in the present embodiment
Elect non-contact radio-frequency memory chip as), it has memory function, and the position that the clamp is followed the trail of in memory can be achieved;Swept when utilizing
Retouch rifle and scan the memory chip, you can logistics information is obtained, when the logistics information is passed through into the Internet transmission to computer end or cloud
During end, you can so that user can also grasp the dynamic of clamp in time in different places.Preferably, the carrying in the present embodiment
The top surface of plate or side are additionally provided with a display window, and the circuit board is arranged in the display window, in order to which user passes through scanning
Rifle or hand-held reading equipment obtain the data of the memory chip.In addition, the Radio Frequency ID card can also pass through the master control IC
Control under timing, on one's own initiative send No. ID.In addition, preferably, can also be provided with the surface of the clamp for making
Quick Response Code for clamp authentication code and/or for managing the Quick Response Code that the APP of clamp logistics information is linked;User is in intelligence
Mobile phone or other mobile terminals install the APP, are used for the Quick Response Code as clamp authentication code by the way that scanning is described, you can
Easily obtain clamp clamp logistics relevant information (such as clamp send starting point, receive terminal and logistics cost
Etc. information), i.e., for the Quick Response Code as clamp authentication code, it is as similar to the Quick Response Code on express delivery list;And be used to make
For with managing the Quick Response Code that the APP of clamp logistics information is linked, then the mode of equivalent to one download APP quick connection, is used
Family by the Quick Response Code can easily download it is described management clamp logistics information APP, certainly, user smart mobile phone or other
Also can be by being downloaded the APP for being used to manage clamp logistics information on other mesh networks on mobile terminal.
In summary, clamp provided in an embodiment of the present invention, its by setting compression telescopic chute in the peripheral ring of support feet, and
Top surface, bottom surface in loading plate, the bottom surface and side of support feet are provided with the lines for strengthening resistance to compression buffer capacity, both
Effectively strengthen the weight capacity of clamp, and effectively extend the service life of clamp;Meanwhile, by carrying plate top surface set by
The lines of the inner groovy composition of multiple " T " fonts, can also be effectively increased the coefficient of friction of carrying plate top surface, so as to effectively strengthen anti-
Sliding effect so that the goods being positioned on loading plate is more consolidated;In addition, also there is imformation memory work(by being set on clamp
Can memory chip, the locating module with positioning function and the Radio Frequency ID card of No. ID can be actively sent, so that clamp
With being easy to follow the trail of clamp positional information, it is easy to user to carry out the advantage of intelligent management to clamp.
In order to effectively solve existing clamp exist it is not degradable, easily cause environmental pollution the shortcomings of, the present invention is real
Apply example and additionally provide a kind of technical scheme that can effectively solve the above problems, it is by the material by environment-friendly degradable to be made
State in loading plate 10 and support feet 20, the embodiment of the present invention, the loading plate and support feet are by outer shell and are filled in outer shell
Interior intermediate filling layer composition, outer shell with intermediate filling layer there are the environment-friendly materials be easy to degrade and reclaimed to constitute.Specifically,
The outer shell is prepared from by the component of following mass parts:
The intermediate filling layer is prepared from by the component of following mass parts:
Preferably, the shell layer component also includes titanium dioxide and alundum (Al2O3), its mass parts is as follows:
1-3 parts of titanium dioxide;
0.1-0.3 parts of alundum (Al2O3).
In the preferred embodiment of the invention, the ratio of the quality of the outer shell and the quality of intermediate filling layer is about
(0.9-1.1):(1.8-2.2).Wherein, the quality of the outer shell and the mass ratio of intermediate filling layer are preferably 1: 2.
Wherein, crushed for one or more of natural xylophytas or herbaceous plant 1 μm~600 μm of the Plant Powder
Powder;Described Plant Powder is mainly crushed using the herbal branch for being easy to materials, dry, leaf, skin, root, stem etc. and formed, example
Such as can be rice straw, husk, straw, bamboo pole, sugarcane bar, maize straw, the stalk of the various crops of wheat straw, certainly, institute
State Plant Powder and be not limited to herbaceous plant, or xylophyta, such as each trees, particular for be easy to materials it is woody
The branch of plant, dry, leaf, skin, root, stem etc..In the present invention, described powder particle size is arranged as required to, for example can root
According to needing to be set to 1um, 5um, 10um, 20um, 50um, 100um, 150um, 200um, 300um, 400um, 500um or 600um
Deng.In the present embodiment, the thermoplastic resin can be the mixture of one or both of polyethylene or polypropylene;The phase
Appearance agent is maleic anhydride grafted polyethylene, and the EVA is ethylene-vinyl acetate copolymer, and vinyl acetate (VA) contains in EVA resin
Measure as 5%~40%, silica can use powder;The lubricant is Tissuemat E, and the antioxidant is β-(3,5- bis- uncles
Butyl -4- hydroxy phenyls) one or both of the positive octadecanol ester of propionic acid or three (2,4- di-tert-butyl-phenyl) phosphite esters
Mixture, when for two kinds mixing when, β-positive octadecanol ester of (3,5- di-tert-butyl-hydroxy phenyl) propionic acid can be taken
0.05-0.25, three (2,4- di-tert-butyl-phenyl) phosphite ester 0.05-0.25;The dispersant is erucyl amide.
In the present embodiment, PPG abbreviation polyethers is that main chain contains ehter bond (- R-O-R-), end group or side base contain
More than the oligomer of 2 hydroxyls (- OH), by initiator (compound containing active hydrogen group) and oxirane (EO), epoxy third
Alkane (PO), epoxy butane (BO) etc. are made through sudden reaction in the presence of a catalyst.Polyethers yield the maximum is with glycerine (the third three
Alcohol) make initiator and epoxides, by the feed way (mixing adds or separately added), dosage ratio, charging time that change PO and EO
The conditions such as sequence, produce various general PPGs.The average functionality of PPG 4110 is 4.0-5.0, hydroxyl value
For 430-470mgKOH/g;The average functionality of PPG 635 is 3.5-4.2, and hydroxyl value is 470-490mgKOH/g;Polyethers
The average functionality of polyalcohol 380 is 3.4-3.8, and hydroxyl value is 380-420mgKOH/g.For example, in the present embodiment 1, polyether polyols
The degree of functionality of alcohol 4110 is 4.0, and hydroxyl value is 430mgKOH/g;The degree of functionality of PPG 635 is 3.5, and hydroxyl value is
470mgKOH/g;The degree of functionality of PPG 380 is 3.4, and hydroxyl value is 380mgKOH/g.
PPG 4110 is synthesized with sucrose, propane diols, expoxy propane, is sucrose initiator;And PPG
635 are sorbierite initiator.PPG 635 and PPG 4110 are rigid-foam polyether, generally PPOX
Tetrol or six alcohol, with pentaerythrite, ethylenediamine, sugar, sorbierite etc. for initiator, degree of functionality is higher, the soft bubble of reactivity ratio
Polyethers is much higher.PPG 380 (PPG SA-380) is high activity polyether, and its reactivity is high, such as Hebei
The PPG 380 of Langfang production.Pentamethylene be used as solvent, preparing polyurethane foam when foaming agent (replacement freon) and
Chromatography standard substance etc., pentamethylene is sterling, and concentration is 99.9-100%.PAPI polymethylene polyphenyl polyisocyanic acid
Ester, or thick MDI, it is light yellow to the irritant smells of brown viscous liquid, add in clamp making, clamp each group can be improved
The adhesive property divided.
Diamine ethereal solution is 70% pair of (dimethyl amido ethyl) ethereal solution, double (the diformazan ammonia for being 70% by mass fraction
Base ethyl) ether and catalyst that 30% dipropylene glycol (DPG) is made into it is the most frequently used.N, N- dimethyl cyclohexyl amine (nitrogen nitrogen diformazan
Basic ring hexylamine) it is colourless to light yellow clear liquid, alcohol and ether solvent can be dissolved in, hard polyurethane foam catalyst is mainly used as.
Hexahydrotriazine catalyst is ethoxy Hexahydrotriazine, is shaped as pale yellow transparent viscous liquid, content 74.00~78.00%.
C18 quaternary ammonium salt catalysts are 2,4,6- tri- (dimethylamino methyl) phenol, can also provide the salting liquid of C18 quaternary ammonium salts, salt is molten
The concentration of liquid is 60-80%.DBU quaternary ammonium salt catalysts are the carbon -7- alkene of 1,8- diazabicylos 11, can also provide DBU seasons
The salting liquid of ammonium salt, the concentration of salting liquid is 60-80%.Diamine ethereal solution, N, N- dimethyl cyclohexyl amines, Hexahydrotriazine catalysis
Agent, C18 quaternary ammonium salt catalysts, DBU quaternary ammonium salt catalysts are the polyurethanes catalyst with delayed-action, are Liyang chemical industry
The product of factory, when above catalyst provides salting liquid, mass ratio is 60-80%.For example, in embodiment, the salt of the above is molten
Liquid concentration mass ratio can be 60%.Above catalyst regulation foaming and gel reaction reach balance, so as to reach preferable hair
Effect is steeped, makes whole clamp that there is preferable pressure-bearing effect and air permeable effect.
Silicone oil is X 2-1401, is to be added water to hydrolyze by dimethyldichlorosilane that first minification polycyclic body, ring is made
Low ring body is made through cracking, rectifying in body, and the telomerization of putting together of ring body, closure agent, catalyst just then can obtain various differences
The mixture of the degree of polymerization, silicone oil can be made by removing low-boiling-point substance through vacuum distillation.The viscosity of silicone oil is 100-200 (25 DEG C) cs,
KS6840 silicone oil is surfactant, can be provided by Nanjing Kai Sheng companies, for example, silicon oil viscosity is 100 (25 DEG C) cs.
The clamp being made by using above-mentioned environment-friendly degradable material so that the clamp that the present invention is provided, which has, is easy to nature
Degraded and recovery, the advantages of environmental pollution being prevented effectively from.It is below outer shell of the present invention and the component of intermediate filling layer
Several preferred embodiments are provided.
Embodiment 1
The each component and mass parts of outer shell:
The each component and mass parts of intermediate filling layer:
Embodiment 2
The each component and mass parts of outer shell:
The each component and mass parts of intermediate filling layer:
Embodiment 3
The each component and mass parts of outer shell:
The each component and mass parts of intermediate filling layer:
Embodiment 4
The each component and mass parts of outer shell:
The each component and mass parts of intermediate filling layer:
Embodiment 5
The each component and mass parts of outer shell:
The each component and mass parts of intermediate filling layer:
Embodiment 6
The each component and mass parts of outer shell:
The each component and mass parts of intermediate filling layer:
Embodiment 7
The each component and mass parts of outer shell:
The each component and mass parts of intermediate filling layer:
Embodiment 8
The each component and mass parts of outer shell:
The each component and mass parts of intermediate filling layer:
As preferred embodiment, the outer shell of loading plate 10 and support feet 20 in the present invention is divided into cap rock and lower cover
Layer, wherein upper cap rock and lower cap rock are integrated formed structure.One kind is additionally provided in the embodiment of the present invention shell is made
The preparation method of layer, its step is as follows:
S1, stirring:It will be mixed evenly for being made after each component of outer shell is weighed according to mass ratio;
S2, roasting material:Material after stirring carries out roasting material, bakes material temperature degree between 60-80 DEG C, and the roasting material time is
3.5-4.5 hour;
S3, expects pipe feeding and machine-shaping:The material after roasting material process will be completed and process equipment is sent to by expects pipe, to add
Work is into sheet material or injection molding, and wherein expects pipe temperature is 130-160 DEG C.
As preferred embodiment, in the step S2, the optimum temperature for baking material is 75 DEG C, and it is about 4 hours to bake the material time;
And in step S3, it should be noted that in expects pipe feeding process, the temperature of expects pipe is no more than 160 DEG C, and otherwise material can be carbonized.
Above-mentioned upper cap rock and lower cap rock are made up of above-mentioned preparation method, is then filled between upper cap rock and lower cap rock
The intermediate filling layer, you can be made to have and be easy to natural degradation and recovery, the clamp for the advantages of environmental pollution can be prevented effectively from;
It is specific clamp to be embedded in when reclaiming clamp in damp warm soil, clamp starts to decay after about 7 days, then decompose completely within 14 days or so.
Above-described embodiment is the preferably implementation of the present invention, is not limited to the present invention, is not departing from this hair
On the premise of bright inventive concept, any obvious replacement is within protection scope of the present invention.
Claims (10)
1. a kind of strong clamp of weight capacity, the clamp includes loading plate and is arranged at some support feets of loading plate bottom,
It is characterized in that:The peripheral ring of described support feet is provided with one or more compression telescopic chute.
2. clamp according to claim 1, it is characterised in that:The top surface of the loading plate and/or bottom surface, which are provided with, to be used for
Strengthen the lines of loading plate endurance.
3. clamp according to claim 2, it is characterised in that:The lines that the top surface of the loading plate is set is in by multiple
The inner groovy composition of " T " font.
4. clamp according to claim 2, it is characterised in that:The lines that the bottom surface of the loading plate is set is by multiple horizontal strokes
Constituted to, the vertical and/or oblique inner groovy in " one " font.
5. the clamp according to any one in Claims 1 to 4, it is characterised in that:The bottom of the support feet is provided with
Lines for strengthening support feet endurance;The support foot bottom set lines by one or more " ten " fonts inner groovy
Composition.
6. clamp according to claim 5, it is characterised in that:The loading plate or support feet are built-in with circuit board, the electricity
Road plate includes the memory chip being sequentially connected, master control IC and Radio Frequency ID card;The circuit board also includes locating module,
The locating module is connected with the master control IC.
7. clamp according to claim 5, it is characterised in that:The surface of the clamp is provided with for being identified as clamp
The Quick Response Code of code and/or the Quick Response Code linked for the APP with management clamp logistics information.
8. clamp according to claim 5, it is characterised in that:The loading plate and support feet by outer shell and filling outside
Intermediate filling layer composition in shell;
Wherein, the outer shell is prepared from by the component of following mass parts:
The intermediate filling layer is prepared from by the component of following mass parts:
9. clamp according to claim 8, it is characterised in that:The shell layer component also includes titanium dioxide and three oxygen
Change two aluminium, its mass parts is as follows:
1-3 parts of titanium dioxide;
0.1-0.3 parts of alundum (Al2O3).
10. a kind of preparation method that outer shell as claimed in claim 8 or 9 is made, its step is as follows:
S1, stirring:It will be mixed evenly for being made after each component of outer shell is weighed according to mass ratio;
S2, roasting material:Material after stirring carries out roasting material, bakes material temperature degree between 60-80 DEG C, and it is 3.5- to bake the material time
4.5 hour;
S3, expects pipe feeding and machine-shaping:The material after roasting material process will be completed and process equipment is sent to by expects pipe, to be processed into
Sheet material or injection molding, wherein expects pipe temperature are 130-160 DEG C.