CN107200880A - A kind of O-ring sizing material and preparation method thereof - Google Patents
A kind of O-ring sizing material and preparation method thereof Download PDFInfo
- Publication number
- CN107200880A CN107200880A CN201710372156.6A CN201710372156A CN107200880A CN 107200880 A CN107200880 A CN 107200880A CN 201710372156 A CN201710372156 A CN 201710372156A CN 107200880 A CN107200880 A CN 107200880A
- Authority
- CN
- China
- Prior art keywords
- parts
- sizing material
- ring
- polyester
- carbon black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to fluid sealant field, a kind of O-ring sizing material, including following parts by weight of component are proposed:26 100 parts of nitrile rubber;20 parts of butadiene rubber;12 parts of dioctyl phthalate;12 parts of stearic acid;1 1.5 parts of cadmium stearate;35 parts of diphenylguanidine TDM;1.0 1.2 parts of anti-aging agent RD;First 15 20 parts of the polyester of methacrylic acid;56 parts of zinc oxide;90 95 parts of carbon black.When being used as piston rod O-ring using the O-ring sizing material of the present invention, its compressive resistance can reach 32MPa.
Description
Technical field
The present invention relates to sealing ring field, particularly a kind of O-ring sizing material and preparation method thereof.
Background technology
O-ring seal is applied in the various plant equipment, in defined temperature, pressure and different liquid and
In gas medium, sealed under static or motion state.In lathe, ship, automobile, aerospace equipment, metallurgical machine
Tool, chemical machinery, engineering machinery, building machinery, mining machinery, petroleum machinery, plastics machinery, agricultural machinery and all kinds of instrument
On instruments and meters, various types of potted components are widely applied.O-ring seal is mainly used in static seal and reciprocating movement sealing.
During for rotary movement seal, low speed rotary seal is only limitted to.O-ring seal is typically mounted at cylindrical or inner circle upper section
To be sealed in the groove of rectangle.O-ring seal still plays good close in environment such as oil resistant, soda acid, mill, chemical erosions
Envelope, cushioning effect.Therefore, O-ring seal is most popular a kind of seal in hydraulic and pneumatic transmission system.
Axle is mainly used on piston or piston rod with O-ring seal, its require compressive resistance it is big, with self lubricity
The wide requirement of energy, operating temperature.
The content of the invention
The present invention is intended to provide a kind of piston rod pressure-resistant O-ring seal and preparation method thereof.
Its concrete scheme is:A kind of O-ring sizing material, including following parts by weight of component:
100 parts of nitrile rubber -26;
20 parts of butadiene rubber;
1-2 parts of dioctyl phthalate;
1-2 parts of stearic acid;
1-1.5 parts of cadmium stearate;
3-5 parts of diphenylguanidine TDM;
1.0-1.2 parts of anti-aging agent RD;
First 15-20 parts of the polyester of methacrylic acid;
5-6 parts of zinc oxide;
90-95 parts of carbon black.
In above-mentioned O-ring sizing material, including following parts by weight of component:
100 parts of nitrile rubber -26;
20 parts of butadiene rubber;
1.5 parts of dioctyl phthalate;
1.5 parts of stearic acid;
1.2 parts of cadmium stearate;
4 parts of diphenylguanidine TDM;
1.1 parts of anti-aging agent RD;
First 17 parts of the polyester of methacrylic acid;
5.5 parts of zinc oxide;
93 parts of carbon black.
It is specially according to carbon black, anti-aging agent RD, oxidation invention additionally discloses the preparation method of O-ring sizing material described above
Zinc, dioctyl phthalate, stearic acid, cadmium stearate, methacrylic acid just polyester, butadiene rubber, nitrile rubber -26 it is suitable
Sequence is added the raw material into kneading machine, and mixing time is 7-8min, and dump temperature is 110 DEG C -115 DEG C and obtains masterbatch, by masterbatch,
Diphenylguanidine TDM is added sequentially to knead in mill, and mixing time is 4-5min, and dump temperature is 80-85 DEG C.
The beneficial effects of the present invention are:
When the O-ring sizing material of the present invention is used as piston rod O-ring, its compressive resistance can reach 32MPa.
Embodiment
With reference to embodiment, technical scheme is described in further detail, but not constituted pair
Any limitation of the present invention.
In order to which more clearly the present invention will be described, it is listed below embodiment to illustrate the superiority of the present invention.
Embodiment 1
A kind of O-ring sizing material, including following parts by weight of component:
100 parts of nitrile rubber -26;
20 parts of butadiene rubber;
1.5 parts of dioctyl phthalate;
1.5 parts of stearic acid;
1.2 parts of cadmium stearate;
4 parts of diphenylguanidine TDM;
1.1 parts of anti-aging agent RD;
First 17 parts of the polyester of methacrylic acid;
5.5 parts of zinc oxide;
93 parts of carbon black.
Preparation method is:According to carbon black, anti-aging agent RD, zinc oxide, dioctyl phthalate, stearic acid, cadmium stearate,
Just polyester, butadiene rubber, the order of nitrile rubber -26 are added the raw material into kneading machine methacrylic acid, and mixing time is
8min, dump temperature is 110 DEG C -115 DEG C and obtains masterbatch, and masterbatch, diphenylguanidine TDM are added sequentially to knead in mill, mixed
The refining time is 4min, and dump temperature is 80-85 DEG C.
Embodiment 2
A kind of O-ring sizing material, including following parts by weight of component:
100 parts of nitrile rubber -26;
20 parts of butadiene rubber;
1 part of dioctyl phthalate;
2 parts of stearic acid;
1.5 parts of cadmium stearate;
3 parts of diphenylguanidine TDM;
1.2 parts of anti-aging agent RD;
First 20 parts of the polyester of methacrylic acid;
6 parts of zinc oxide;
95 parts of carbon black.
Preparation method is:According to carbon black, anti-aging agent RD, zinc oxide, dioctyl phthalate, stearic acid, cadmium stearate,
Just polyester, butadiene rubber, the order of nitrile rubber -26 are added the raw material into kneading machine methacrylic acid, and mixing time is
8min, dump temperature is 110 DEG C -115 DEG C and obtains masterbatch, and masterbatch, diphenylguanidine TDM are added sequentially to knead in mill, mixed
The refining time is 4min, and dump temperature is 80-85 DEG C.
When the O-ring sizing material of the present embodiment 1 and 2 is used as piston rod O-ring, its compressive resistance can reach 32MPa.
Above-described is only presently preferred embodiments of the present invention, all timess made in the range of the spirit and principles in the present invention
What modifications, equivalent substitutions and improvements etc., should be included in the scope of the protection.
Claims (3)
1. a kind of O-ring sizing material, it is characterised in that including following parts by weight of component:
100 parts of nitrile rubber -26;
20 parts of butadiene rubber;
1-2 parts of dioctyl phthalate;
1-2 parts of stearic acid;
1-1.5 parts of cadmium stearate;
3-5 parts of diphenylguanidine TDM;
1.0-1.2 parts of anti-aging agent RD;
First 15-20 parts of the polyester of methacrylic acid;
5-6 parts of zinc oxide;
90-95 parts of carbon black.
2. O-ring sizing material according to claim 1, it is characterised in that including following parts by weight of component:
100 parts of nitrile rubber -26;
20 parts of butadiene rubber;
1.5 parts of dioctyl phthalate;
1.5 parts of stearic acid;
1.2 parts of cadmium stearate;
4 parts of diphenylguanidine TDM;
1.1 parts of anti-aging agent RD;
First 17 parts of the polyester of methacrylic acid;
5.5 parts of zinc oxide;
93 parts of carbon black.
3. a kind of preparation method of O-ring sizing material as claimed in claim 1 or 2, it is characterised in that be specially according to carbon black,
Anti-aging agent RD, zinc oxide, dioctyl phthalate, stearic acid, cadmium stearate, methacrylic acid first polyester, butadiene rubber, fourth
The order of nitrile rubber -26 is added the raw material into kneading machine, and mixing time is 7-8min, and dump temperature is 110 DEG C -115 DEG C and obtained
To masterbatch, masterbatch, diphenylguanidine TDM are added sequentially to knead in mill, mixing time is 4-5min, and dump temperature is 80-
85℃。